Hydrodeoxygenation of 2,5-dimethyltetrahydrofuran over bifunctional Pt–Cs2.5H0.5PW12O40 catalyst in the gas phase: enhancing effect of gold

Hanan Althikrallah ab, Elena F. Kozhevnikova a and Ivan V. Kozhevnikov *a
aUniversity of Liverpool, Department of Chemistry, Liverpool L69 7ZD, UK. E-mail: kozhev@liverpool.ac.uk
bDepartment of Chemistry, King Faisal University, College of Science, P.O. Box 400, Al-Ahsa 31982, Saudi Arabia. E-mail: halhekrallh@kfu.edu.sa

Received 16th December 2021 , Accepted 10th January 2022

First published on 14th January 2022


Abstract

2,5-Dimethyltetrahydrofuran (DMTHF) is deoxygenated to n-hexane with >99% selectivity at mild conditions (90 °C, 1 bar H2 pressure, fixed-bed reactor) in the presence of the bifunctional metal-acid catalyst Pt–CsPW comprising Pt and Cs2.5H0.5PW12O40 (CsPW), an acidic Cs salt of Keggin-type heteropoly acid H3PW12O40. Addition of gold to the Pt–CsPW catalyst increases the turnover rate at Pt sites more than twofold, whereas the Au alone without Pt is not active. The enhancement of catalyst activity is attributed to PtAu alloying, which is supported by STEM-EDX and XRD analysis.


Biomass-derived furanic compounds are of interest as a renewable feedstock, which can be processed into a range of value-added chemicals and green fuels via catalytic hydroconversion.1–8 Hydrodeoxygenation (HDO) of furanic compounds using bifunctional metal–acid catalysis has been demonstrated to be an effective strategy to produce green fuels under mild conditions3,4,6,8–12 and references therein. The HDO over bifunctional metal-acid catalysts is much more efficient compared to the reaction over monofunctional metal catalysts.11,12 Previously, we have reported HDO of a wide range of oxygenates in the gas phase to produce alkanes in the presence of bifunctional catalysts comprising Pt, Ru, Ni and Cu as metal components and Keggin-type heteropoly acids, with their activity decreasing in the order Pt > Ru > Ni > Cu.13,14 Pt–CsPW comprising Pt and strongly acidic heteropoly salt Cs2.5H0.5PW12O40 (CsPW) has been reported to be a highly efficient catalyst for the HDO of 2,5-dimethylfuran (DMF) and 2,5-dimethyltetrahydrofuran (DMTHF) to produce n-hexane with 100% yield at 90–120 °C and ambient pressure.11,12 The HDO of DMTHF over Pt–CsPW occurs through a sequence of hydrogenolysis, dehydration and hydrogenation steps catalysed by Pt and proton sites of the bifunctional catalyst (Scheme 1). These include the ring opening of DMTHF to form 2-hexanol on Pt sites followed by its dehydration on proton sites of CsPW to hexene, which is finally hydrogenated to n-hexane on Pt sites.12 It is the facile dehydration of the secondary alcohol intermediate that drives the HDO process forward.11,12 The rate-limiting step is either the ring hydrogenolysis or 2-hexanol dehydration depending on the ratio of accessible surface metal and acid sites Pt/H+.12 Other platinum group metals such as Pd, Ru and Rh, that have high selectivity to ring hydrogenation rather than ring hydrogenolysis,2,7 have low activities in HDO of DMF and DMTHF.11
image file: d1ra09105k-s1.tif
Scheme 1 Reaction pathway for hydrodeoxygenation of DMTHF over Pt–CsPW.

Bimetallic PtAu and PdAu catalysts have been reported to have an enhanced performance in comparison to monometallic Pt and Pd catalysts,15–31 for example, in hydrogenation,16,21,29 hydrodesulphurisation,27,28 oxidation,22,24 isomerisation15,19,30,31 and other reactions.17,18,20,25,26 The enhancement of catalyst performance by addition of gold can be attributed to geometric (ensemble) and electronic (ligand) effects of the constituent elements in PtAu and PdAu bimetallic species.25,26

Here we looked at the effect of Au on the performance of Pt–CsPW catalysts in the HDO of DMTHF in the gas phase (see the ESI for experimental details). The CsPW heteropoly salt is a well-known solid acid catalyst; it possesses strong proton sites, large surface area and high thermal stability (∼500 °C decomposition temperature).9,32–34 Supported bimetallic catalysts PtAu/SiO2 and PtAu/CsPW were prepared by co-impregnation of H2PtCl6 and HAuCl3 onto SiO2 and CsPW followed by reduction with H2 at 250 °C (ESI). This method gives supported bimetallic PtAu nanoparticles of a random composition together with various Pt and Au nanoparticles.15,16,31 Information about the catalysts studied is given in Table 1.

Table 1 Catalyst characterisation
Catalyst Surface areaa (m2 g−1) Pore volumeb (cm3 g−1) Pore diameterc (Å) D d d e (nm)
a BET surface area. b Single point total pore volume. c Average BET pore diameter. d Metal dispersion. e Metal particle size. f Calculated from the equation d (nm) = 0.9/D. g Metal particle diameter from powder XRD (Scherrer equation). h Pt dispersion determined by H2/O2 titration (average from three measurements); for PtAu catalysts, assumed negligible H2 adsorption on gold (see the ESI). i From STEM.
Cs2.5H0.5PW12O40 (CsPW) 135 0.089 27    
6.5% Au/SiO2 257 1.01 157 0.019f 46g, 38i
4.7% Au/CsPW 103 0.048 33 0.016f 60g
6.4% Pt/SiO2 266 1.06 159 0.28 ± 0.04h 3.2f, 8.0g, 5i
6.0% Pt/CsPW 84 0.052 25 0.17 ± 0.03h 5.3f
6.6% Pt/5.9% Au/SiO2 240 1.08 179 0.29 ± 0.05h 3.1f
5.9% Pt/4.4% Au/CsPW 91 0.082 36 0.17 ± 0.04h 5.3f


Powder X-ray diffraction (XRD) has been widely used for the characterization of supported Au alloy catalysts.26 The XRD patterns for the silica-supported catalysts 6.4% Pt/SiO2, 6.5% Au/SiO2 and 6.6% Pt/5.9% Au/SiO2 are shown in Fig. 1. As expected, the 6.4% Pt/SiO2 and 6.5% Au/SiO2 catalysts display the fcc pattern of Pt and Au metal nanoparticles. The Pt peaks are broader than the Au peaks, which indicates a higher dispersion of Pt particles, with an average particle size of 8.0 nm for Pt and 46 nm for Au, which is in agreement with the STEM values (Table 1).


image file: d1ra09105k-f1.tif
Fig. 1 Powder XRD patterns of 6.4% Pt/SiO2, 6.5% Au/SiO2 and 6.6% Pt/5.9% Au/SiO2; the pattern for 6.6% Pt/5.9% Au/SiO2 shows broad [111], [200], [220] and [311] fcc PtAu alloy peaks in the range 38–40°, 44–48°, 65–68° and 78–81°, respectively.

The pattern for the 6.6% Pt/5.9% Au/SiO2 catalyst clearly shows the presence of PtAu bimetallic particles with broad [111], [200], [220] and [311] diffraction peaks of the fcc PtAu alloy between the corresponding diffractions of the pure metals in the range 38–40°, 44–48°, 65–68° and 78–81°, respectively.

Fig. 2 shows the high-angle annular dark field (HAADF) STEM images of the three silica-supported catalysts 6.4% Pt/SiO2, 6.5% Au/SiO2 and 6.6% Pt/5.9% Au/SiO2 with metal nanoparticles indicated as bright spots on the darker background. In the Pt/SiO2 catalyst, there are two populations: small Pt particles of 5 nm size and coalesced Pt particles of a larger size. The Au/SiO2 catalyst displays Au particles of spherical, rectangular and triangular morphology, with an average size of 38 nm. The bimetallic PtAu/SiO2 catalyst shows a high agglomeration and different kinds of morphology of metal particles.


image file: d1ra09105k-f2.tif
Fig. 2 HAADF-STEM images of (a) 6.4% Pt/SiO2, (b) 6.5% Au/SiO2 and (c) 6.6% Pt/5.9% Au/SiO2 catalysts, showing noble metal nanoparticles as bright spots.

The energy dispersive X-ray spectroscopic analysis (EDX) of metal particles in the PtAu/SiO2 catalyst shows that these particles contain both platinum and gold. EDX elemental mapping clearly demonstrates that Pt and Au maps cover the same areas of PtAu/SiO2 catalyst (Fig. 3), indicating PtAu alloying with formation of a non-uniform bimetallic PtAu particles. More EDX mapping is presented in the ESI (Fig. S1).


image file: d1ra09105k-f3.tif
Fig. 3 HAADF-STEM image of 6.6% Pt/5.9% Au/SiO2 catalyst and the corresponding STEM-EDX elemental maps showing the spatial distribution of Au (red) and Pt (green) in the sample.

STEM–EDX for CsPW-supported Pt, Au and PtAu catalysts has been reported elsewhere.16 These STEM images are difficult to analyse due to W, Pt and Au having similar large atomic numbers Z (74, 78, and 79, respectively). Crystalline CsPW containing 70 wt% of W displays a strong background which makes it difficult to discern smaller Pt and Au particles from the Z-contrast HAADF images and determine accurately metal particle size. Nevertheless, the STEM-EDX analysis indicates the presence of bimetallic PtAu particles in the PtAu/CsPW catalyst with a wide range of Pt/Au atomic ratios.16

Representative results for HDO of DMTHF in the presence of bifunctional metal-acid catalysts Pt–CsPW and PtAu–CsPW, which were used as physical mixtures of metal and acid components at similar Pt loadings, are shown in Table 2. The HDO reaction was carried out in flowing hydrogen at 90 °C and ambient pressure in a fixed-bed reactor (ESI). The molar ratio of surface metal and proton sites in the catalysts was chosen low enough (Pt/H+ = 0.03–0.1) to ensure the reaction being limited by the DMTHF ring opening step.12 The density of surface Pt sites was estimated from the Pt dispersion (Table 1), the density of surface proton sites in CsPW was calculated assuming a cross section of the PW12O403− Keggin unit of 144 Å32,33 and the CsPW surface area of 135 cm2 g−1 (Table 1).

Table 2 Hydrodeoxygenation of DMTHF over bifunctional metal-acid catalystsa
Entry Catalyst Conversion (%) TOFb (h−1) Product selectivity (% mol)
n-Hexane 2-Hexanol
a 0.20 g total catalyst weight (physical mixture of 0.020 g metal catalyst + 0.18 g CsPW), 0.6% Pt, 90 °C, 2.3 kPa DMTHF, 20 ml min−1 H2 flow rate, catalyst pre-treatment at 90 °C for 1 h in H2 flow, 1 h TOS. b TOF values per Pt surface site, the contribution of Au and CsPW subtracted. c Catalyst bed contained 0.005 g metal catalyst + 0.18 g CsPW; catalyst pre-treatment at 250 °C for 1 h in H2 flow.
1 CsPW 2.1      
2 4.7% Au/CsPW + CsPW 2.2      
3 6.0% Pt/CsPW + CsPW 8.6 70 98.6 0.7
4 5.9% Pt/4.4% Au/CsPW + CsPW 17 170 98.6 0.8
5 6.5% Au/SiO2 + CsPW 1.9      
6 6.4% Pt/SiO2 + CsPW 64 390 99.4 0.5
7 6.6% Pt/5.9% Au/SiO2 + CsPW 85 490 99.6 0.3
8 6.4% Pt/SiO2 + CsPWc 8.0 150 98.6 1.2
9 6.6% Pt/5.9% Au/SiO2 + CsPWc 13 260 98.5 0.7


In the absence of Pt, the CsPW alone (entry 1) and Au–CsPW (entries 2 and 5) showed a negligible activity (1.9–2.2% DMTHF conversion with practically no 2-hexanol and n-hexane formed). Physically mixed Pt–CsPW catalysts, Pt/CsPW + CsPW and Pt/SiO2 + CsPW (1[thin space (1/6-em)]:[thin space (1/6-em)]9 w/w), exhibited a high activity giving >99% n-hexane selectivity at 8.0 to 85% DMTHF conversion depending on the catalyst and reaction conditions, in agreement with the previous report.12 It should be noted that the catalyst based on Pt/SiO2 had almost 6-fold greater activity than the one based on Pt/CsPW in terms of turnover frequency (TOF) per surface Pt site (cf. entries 3 and 6), thus demonstrating a strong effect of Pt support.

As can be seen from Table 2, the addition of gold to Pt/CsPW and Pt/SiO2 caused a significant enhancement of catalyst activity, with DMTHF conversion increasing 1.3–2 times compared to the corresponding Pt only catalysts (cf. entries 3 and 4, 6 and 7, 8 and 9). As the gold alone was practically inactive, the increase in catalyst activity can be attributed to the enhancement of activity of the Pt sites. For the bimetallic PtAu catalysts, the TOF values at Pt sites increased 1.3–2.4 times as compared to the monometallic Pt catalysts (Table 2). The results at lower DMTHF conversions of 8–17% give a more accurate estimate of the TOF enhancement reaching 1.7–2.4 times (cf. entry 3 with 4 and 8 with 9). Previously, the gold enhancement on a similar scale has been reported for alkane isomerisation on PtAu–CsPW catalysts.15,31

The enhancement of catalyst activity by addition of gold has been attributed to geometric (ensemble) and electronic (ligand) effects of the constituent metals in PtAu bimetallic nanoparticles.26 The XRD and STEM-EDX data shown above clearly demonstrate PtAu alloying in the PtAu/SiO2 catalyst leading to the formation of bimetallic PtAu species. The same has also been reported for the PtAu/CsPW catalyst.16 Previously, it has been shown that the HDO of DMTHF on Pt–CsPW is a structure-sensitive reaction,12 hence the geometric effects may be expected to contribute to the gold enhancement. However, in order to prove the role of geometric and electronic effects as the cause of the gold enhancement, more accurate metal dispersion measurements complemented by spectroscopic characterisation will be required.

We also tested the performance of bifunctional PdAu/SiO2 + CsPW and PtPd/SiO2 + CsPW bimetallic catalysts under similar conditions in comparison to the corresponding monometallic Pd and Pt catalysts. However, no enhancement of activity was observed. This is in agreement with XRD analysis, which showed no distinct PdAu alloying in PdAu/SiO2 (Fig. S2 in the ESI).

In conclusion, we have demonstrated that the addition of gold to the Pt–CsPW catalyst has an enhancing effect on the HDO of DMTHF, increasing the turnover rate at Pt sites more than twofold. The enhancing effect is attributed to PtAu alloying. The formation of bimetallic PtAu nanoparticles in the PtAu–CsPW catalyst is confirmed by STEM-EDX and XRD.

Author contributions

The manuscript was written through contributions of all authors.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

The STEM work was performed in the Albert Crewe Centre for Electron Microscopy, a University of Liverpool Shared Research Facility (SRF). We thank the Deanship of Scientific Research at King Faisal University, Saudi Arabia for the financial support under Nasher Track (Grant No. NA0043).

Notes and references

  1. (a) A. Corma, S. Iborra and A. Velty, Chem. Rev., 2007, 107, 2411–2502 CrossRef CAS PubMed; (b) Y. Román-Leshkov, J. N. Chheda and J. A. Dumesic, Science, 2006, 312, 1933–1937 CrossRef PubMed; (c) R. M. West, Z. Y. Liu, M. Peter and J. A. Dumesic, ChemSusChem, 2008, 1, 417–424 CrossRef CAS PubMed; (d) G. W. Huber, J. N. Chheda, C. J. Barrett and J. A. Dumesic, Science, 2005, 308, 1446–1450 CrossRef CAS PubMed; (e) Z. J. Brentzel, K. J. Barnett, K. Huang, C. T. Maravelias, J. A. Dumesic and G. W. Huber, ChemSusChem, 2017, 10, 1351–1355 CrossRef CAS PubMed; (f) V. Vorotnikov and D. G. Vlachos, J. Phys. Chem. C, 2015, 119, 10417–10426 CrossRef CAS; (g) J. Kang, A. Vonderheide and V. V. Guliants, ChemSusChem, 2015, 8, 3044–3047 CrossRef CAS PubMed; (h) R. C. Runnebaum, T. Nimmanwudipong, J. Doan, D. E. Block and B. C. Gates, Catal. Lett., 2012, 142, 664–666 CrossRef CAS; (i) J. Kang, X. Liang and V. V. Guliants, ChemCatChem, 2017, 9, 282–286 CrossRef CAS.
  2. Y. L. Louie, J. Tang, A. M. L. Hell and A. T. Bell, Appl. Catal., B, 2017, 202, 557–568 CrossRef CAS.
  3. A. Corma, O. de la Torre, M. Renz and N. Villandier, Angew. Chem., Int. Ed., 2011, 50, 2375–2378 CrossRef CAS PubMed.
  4. J. Yang, S. Li, L. Zhang, X. Liu, J. Wang, X. Pan, N. Li, A. Wang, Y. Cong, X. Wang and T. Zhang, Appl. Catal., B, 2017, 201, 266–277 CrossRef CAS.
  5. H. Goto, A. Takagaki, R. Kikuchi and S. T. Oyama, Appl. Catal., A, 2017, 548, 122–127 CrossRef CAS.
  6. F. Xue, D. Ma, T. Tong, X. Liu, Y. Hu, Y. Guo and Y. Wang, ACS Sustainable Chem. Eng., 2018, 6, 13107–13113 CrossRef CAS.
  7. H. Althikrallah, C. Kunstmann-Olsen, E. F. Kozhevnikova and I. V. Kozhevnikov, Catalysts, 2020, 10, 1171 CrossRef CAS.
  8. D. M. Alonso, J. Q. Bond and J. A. Dumesic, Green Chem., 2010, 12, 1493–1513 RSC.
  9. J. Zhong, J. Pérez-Ramírez and N. Yan, Green Chem., 2021, 23, 18–36 RSC.
  10. S. Li, L. Yan, Q. Liu, J. Liu, Q. Liu, W. Fan, X. Zhao, X. Zhang, C. Wang, L. Maa and Q. Zhang, Green Chem, 2020, 22, 2889–2900 RSC.
  11. H. Althikrallah, E. F. Kozhevnikova and I. V. Kozhevnikov, Chem. Commun., 2021, 57, 227–230 RSC.
  12. H. Althikrallah, E. F. Kozhevnikova and I. V. Kozhevnikov, Mol. Catal., 2021, 510, 111711 CrossRef CAS.
  13. K. Alharbi, E. F. Kozhevnikova and I. V. Kozhevnikov, Appl. Catal., A, 2015, 504, 457–462 CrossRef CAS.
  14. K. Alharbi, W. Alharbi, E. F. Kozhevnikova and I. V. Kozhevnikov, ACS Catal., 2016, 6, 2067–2075 CrossRef CAS.
  15. A. Alazman, D. Belic, E. F. Kozhevnikova and I. V. Kozhevnikov, J. Catal., 2018, 357, 80–89 CrossRef.
  16. O. Poole, K. Alharbi, D. Belic, E. F. Kozhevnikova and I. V. Kozhevnikov, Appl. Catal., B, 2017, 202, 446–453 CrossRef CAS.
  17. L. Guczi and Z. Schay, Stud. Surf. Sci. Catal., 1986, 27, 313–336 CrossRef CAS.
  18. G. C. Bond, Metal-catalysed reactions of hydrocarbons, Springer, New York, 2005 Search PubMed.
  19. G. Riahi, D. Guillemot, M. Polisset-Thfoin, A. A. Khodadadi and J. Fraissard, Catal. Today, 2002, 72, 115–121 CrossRef CAS.
  20. G. J. Hutchings, Chem. Commun., 2008, 1148–1164 RSC.
  21. K. Sun, A. R. Wilson, S. T. Thompson and H. H. Lamb, ACS Catal., 2015, 5, 1939–1948 CrossRef CAS.
  22. Y. F. Han, J. H. Wang, D. Kumar, Z. Yan and D. W. Goodman, J. Catal., 2005, 232, 467–475 CrossRef CAS.
  23. E. K. Hanrieder, A. Jentys and J. A. Lercher, J. Catal., 2016, 333, 71–77 CrossRef CAS.
  24. J. Xu, T. White, P. Li, C. He, J. Yu, W. Yuan and Y. F. Han, J. Am. Chem. Soc., 2010, 132, 10398–10406 CrossRef CAS PubMed.
  25. B. Coq and F. Figueras, J. Mol. Catal. A, 2001, 173, 117–134 CrossRef CAS.
  26. F. Gao and D. W. Goodman, Chem. Soc. Rev., 2012, 41, 8009–8020 RSC.
  27. A. M. Venezia, V. La Parola, V. Nicoli and G. Deganello, J. Catal., 2002, 212, 56–62 CrossRef CAS.
  28. A. M. Venezia, V. La Parola, G. Deganello, B. Pawelec and J. L. G. Fierro, J. Catal., 2003, 215, 317–325 CrossRef CAS.
  29. T. J. Schwartz, S. D. Lyman, A. H. Motagamwala, M. A. Mellmer and J. A. Dumesic, ACS Catal., 2016, 6, 2047–2054 CrossRef CAS.
  30. J. Fraissard, V. Gerda, K. I. Patrylak and Y. G. Voloshyna, Catal. Today, 2007, 122, 338–340 CrossRef CAS.
  31. A. Alazman, D. Belic, A. Alotaibi, E. F. Kozhevnikova and I. V. Kozhevnikov, ACS Catal., 2019, 9, 5063–5073 CrossRef CAS.
  32. T. Okuhara, N. Mizuno and M. Misono, Adv. Catal., 1996, 41, 113–252 CAS.
  33. I. V. Kozhevnikov, Chem. Rev., 1998, 98, 171–198 CrossRef CAS PubMed.
  34. J. B. Moffat, Metal-oxygen clusters: The surface and catalytic properties of heteropoly oxometalates, Kluwer, New York, 2001 Search PubMed.

Footnote

Electronic supplementary information (ESI) available: Experimental details and STEM-EDX images. See DOI: 10.1039/d1ra09105k