Preeti Waribama,
Kanticha Jaiyena,
Chanatip Samartab,
Makoto Ogawac,
Guoqing Guand and
Suwadee Kongparakul*ab
aDepartment of Chemistry, Faculty of Science and Technology, Thammasat University, Pathumthani 12120, Thailand. E-mail: ksuwadee@tu.ac.th
bBioenergy and Biochemical Refinery Technology Program, Faculty of Science and Technology, Thammasat University, 12120, Thailand
cDepartment of Chemical and Biomolecular Engineering, School of Energy Science and Engineering, Vidyasirimedhi Institute of Science and Technology, Rayong 21210, Thailand
dInstitute of Regional Innovation, Hirosaki University, Aomori 030-0813, Japan
First published on 1st March 2021
A cross-linked sulfonated polyether ether ketone (C-SPEEK) was incorporated with MXene/potassium titanate nanowire (MKT-NW) as a filler and applied as a proton exchange membrane for photocatalytic water splitting. The prepared hybrid composite PEM had proton conductivity of 0.0097 S cm−1 at room temperature with an ion exchange capacity of 1.88 meq g−1. The hybrid composite proton exchange membrane is a reactive membrane which was able to generate hydrogen gas under UV light irradiation. The efficiency of hydrogen gas production was 0.185066 μmol within 5 h for 12% wt of MKT-NW loading. The results indicated that the MKT-NW/C-SPEEK membrane is a promising candidate for ion exchange with hydrogen gas evolution in photocatalytic water splitting and could be applied as a renewable source of energy to use in various fields of applications.
Water electrolysis through proton exchange membrane (PEM) is one of those green methods which can produce H2 and is utilized in a wide range of applications. Production of H2 occurs by the redox reaction that takes place in an electrolyzer cell. PEM water electrolysis is accrued by pumping of water to the anode side where water is splitted into oxygen (O2), protons (H+) and electrons (e−). These protons transport via a proton conducting membrane to the cathode side. The PEM allows only the proton (H+) produced at the anode to transfer towards the cathode to produce H2. Nafion, a conventional commercialized PEM, had been used extensively for the PEM water electrolysis, which is expensive with complicated synthesis steps and toxic to the environment due to the presence of fluorine. Considering the cost-effectiveness, and mechanical and chemical properties, polyether ether ketone (PEEK) is an alternative hydrocarbon-based polymer that can be used for the PEM water electrolysis by the sulfonation of polyether ether ketone. Cross-linking of the sulfonated polyether ether ketone (SPEEK) membrane using ethylene glycol (EG) as a crosslinker increased chemical and mechanical stabilities and decreased swelling ratio which made it suitable for the application as PEM.3 The proton conductivity of SPEEK would be reduced when diols are used as a cross-linker, therefore many researchers have incorporated hygroscopic inorganic metal oxide such as SiO2, TiO2, Al2O3 and ZrO2,4 as fillers to improve physiochemical properties and conductivity of the membrane.
TiO2 has useful properties among the above-mentioned metal oxides that can be used as a filler material. It is capable of becoming super hydrophilic when exposed to UV light which arises due to the increasing number of hydroxyl groups (–OH) of the TiO2 surfaces during UV light irradiation.5 TiO2 is a nontoxic, cost-effective, abundant material and possesses high chemical stability against the oxidative environment in photocatalytic water splitting.6 TiO2 particles can be converted to nanowire via a hydrothermal reaction using a strong basic solution such as NaOH or KOH solution.7 Potassium titanate nanowire is one of the fascinating forms of TiO2 that could be utilized as a reinforcing agent as it possesses good mechanical, chemical and thermal stability. Additionally, it was also used as a photocatalyst in water electrolysis.8 TiO2/graphene nanocomposites have been studied as a filler in PEMs to enhance numerous properties of the membrane.9
MXenes are a new versatile inorganic material of 2D transition metal carbides or nitrides, which were produced by selective chemical etching of MAX phases (M is an early transition metal, A is an A-group (mostly IIIA and IVA element) and X is carbon and/or nitrogen). Mostly Ti3C2Tx layers are uniformly terminated by –OH and –O– and –F groups after the exfoliation, where T and x represent the terminating group and their numbers, respectively.10 These surface termination of MXene make them a prominent filler to increase the proton conductivity and physicochemical properties of SPEEK.11 MXene has been utilized as an electrocatalyst for H2 evolution reaction (HER) in water splitting.12 When MXene was employed as a co-catalyst with TiO2 in photocatalysis, higher H2 evolution has been observed without the addition of any noble metal co-catalyst.13 Besides, the addition of co-catalyst with TiO2 such as copper (Cu) could obtain a highly active H2 production catalyst, Cu/TiO2/MXene photocatalyst in which MXene acted as a hole mediator and Cu acted as an electron mediator and reduction co-catalyst. The coupled photocatalyst promoted H2 evolution via dual-carrier-separation mechanism.14
Thus, the present work focuses on the preparation of hybrid PEM, by utilizing sulfonated poly(ether ether ketone) (SPEEK) as a polymer matrix for the PEM water electrolysis. SPEEK with a high degree of sulfonation (DS) had been prepared via sulfonation and cross-linked with ethylene glycol (EG) to improve its dimensional stability. To further increase its proton conductivity, inorganic metal oxide; MXene-potassium titanate nanowire (MKT-NW) was embedded into the polymer matrix to prepare MKT-NW/C-SPEEK hybrid PEM. The PEM was prepared by a simple solution casting technique using ethanol and water (1:1) as a green solvent. The properties of hybrid composite PEM including photocatalytic activity under UV radiation were characterized.
For MKT-NW composite, an exfoliated MXene was firstly synthesized via an in situ production of hydrofluoric acid (HF) protocol using LiF and 37% HCl as an etching agent where the exfoliation was carried out at 50 °C for 48 h.16 Potassium titanate nanowire (KT-NW) was prepared by a hydrothermal treatment of TiO2 anatase with 10 M KOH solution in a Teflon-lined stainless autoclave at 200 °C for 24 h as reported previously.17 MXene potassium titanate nanowire (MKT-NW) was obtained by the hydrothermal reaction of MXene and KT-NW (weight ratio 1:1) in DI water/ethanol mixture (3:1) using a Teflon-lined autoclave at 120 °C for 3 h. The structure of MXene and MKT-NW was characterized by wide-angle X-ray diffractometry (XRD, Bruker, D8 ADVANCE) with Cu-Kα radiation (λ = 1.54 Å) in the range from 5° to 80 °C at the rate of 0.02°/0.5 s.
X-ray photoelectron spectroscopy (XPS) was recorded on JEOL JPS-9010MC with a Mg Kα source (1253.6 eV) at 12 kV and 25 mA. All XPS spectra were measured under a high vacuum pressure of 10–8 Pa at a room temperature. Software for running experiment is SpecSurf ver.1.9.3. The sample was fixed on carbon tape. The analyzed area was a cycle spot with a diameter of 6 mm. The survey scan spectra were measured with a pass energy of 50 eV, a binding energy range of 0–1100 eV and an electron-volt step of 1 eV. The narrow scan spectra were measured with a pass energy of 10 eV and an electron-volt step of 0.1 eV. The obtained spectra were evaluated using JEOL software to obtain the chemical state of the probing elements and elemental composition. All the binding energy values were referenced to the carbon peak C 1s at 284.70 eV.
In a typical procedure of the composite membrane preparation, SPEEK particles (5 wt%) were dissolved in ethanol/DI water mixture (1:1), then the amount of ethylene glycol was added as a cross-linker and stirred vigorously for 2 h. The MKT-NW suspension (MKT-NW in ethanol/water mixture) was added to the SPEEK solution, then the final mixture was sonicated and stirred vigorously for 24 h, to make the uniform dispersion. The solution was cast on a Petri dish, dried at room temperature, and cured at 120 °C for 24 h to obtain a cross-linking membrane. After that, it was cooled down to room temperature and the membrane was peeled off using DI water and protonated by the immersion in 1 M H2SO4 for 24 h. Then, the membrane was washed with DI water until neutral and dried at 60 °C for 12 h. The composite membranes were named as MKT-NWx/C-SPEEK where x is the amount of MKT-NW (5 to 20 wt%). Pristine SPEEK membrane, as well as cross-linked SPEEK (C-SPEEK) membrane, were also prepared and used. The overall steps involved in the preparation of the composite PEM is described in Scheme 1.
The chemical structure of the membrane was characterized by attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectroscopy (PerkinElmer Spectrum 100 FT-IR spectrometer) in the wavenumber range of 4000–500 cm−1. The morphologies of the synthesized inorganic powders and composite membranes were characterized by a field emission scanning electron microscope (FE-SEM, model Versa) with energy dispersive X-ray spectroscopy (EDS) mapping. Transmission electron microscope (TEM, JEOL, JEM-2100Plus) was carried out to study the structural change of pristine MXene and after deposition with KT-NW. The elemental distribution in the MKT-NW/C-SPEEK composite membrane was carried out using X-ray fluorescence microscopy (XRF, Horiba, XGT-7200). Dynamic mechanical analysis (DMA) of the membranes were carried out using Mettler Toledo DMA1 analyzer in the tension mode at an oscillation frequency of 1 Hz and the temperature range of 30–260 °C with the heating rate of 3 °C min−1. The storage modulus (E′), loss modulus (E′′) and loss tangent (tanδ) were determined.
For the membrane properties, water uptake and swelling area of the membrane were obtained by immersing the membrane in DI water for 24 h, wiped of the excess of water, then weighed and measured the dimension to find the water uptake percentage and swelling percentage by a gravitational calculation. The ion exchange capacity (IEC) value of the membrane was determined using acid–base titration. The sample was immersed in 2.0 M NaCl solution at room temperature for 24 h to complete liberate H+ by exchanging with Na+. Then, the liberated H+ was then titrated against 0.01 M NaOH solution using phenolphthalein as an indicator. The membrane resistance was determined by using an electrochemical impedance spectroscopy (EIS, Corrtest CS310). In this method, the membrane was immersed in DI water for 24 h to make a completely hydrated membrane. The proton conductivity was calculated based on the area, thickness, and resistance of the membrane from EIS measurement.
All calculations and measurements such as the degree of sulfonation, water uptake percentage, swelling percentage, ion exchange capacity (IEC, meq g−1), and proton conductivity (σ, S cm−1) were explained in ESI.†
Scheme 2 Workstation for photocatalytic activity testing. Photographs of glassware and membranes taken with digital camera. |
Fig. 1 (a) 1H NMR spectrum of SPEEK particle (in 25 °C using DMSO-d6) and (b) ATR-FTIR spectra of (b1) SPEEK, (b2) C-SPEEK, (b3–b5) 5%, 10%, and 12% MKT-NW/C-SPEEK hybrid composite PEM. |
From the FTIR spectra of all prepared MKT-NW/C-SPEEK composite membranes as depicted in Fig. 1(b), the hydroxyl group (–OH) at 3394 cm−1 had been shifted to lower wavenumber for C-SPEEK sample due to cross-linking between –SO3H of SPEEK and –OH of ethylene glycol, the crosslinker.19 Besides, the characteristic peak of –SO3H remained unchanged and no new peak observed which implied that there was no chemical reaction and only interfacial interaction between C-SPEEK and MKT-NW.11 However, the decrease in the peak intensity of –SO3H was observed which may be due to physical interaction of MKT-NW composite with –SO3H of SPEEK. For the incorporation of MKT-NW in C-SPEEK, the –OH functional group intensity slightly decreased which may be attributed to the extensive hydrogen bonding interaction between –OH terminated MKT-NW surface and –SO3H of C-SPEEK.20
In this work, KT-NW led to the formation of TiO6 octahedral by a zigzag pattern by connecting the edges and the potassium ion (K+) are trapped into this structure. In the KT NW synthesis process, longer Ti–O bonds might be attacked by –OH ions of strong aqueous KOH solution and were broken down but shorter Ti–O bonds remained unchanged, leading to the formation of Ti–O–K bonds.21 Thus, KT-NW was successfully formed by a simple hydrothermal method at 200 °C. From XRD patterns in Fig. 2(a), the pristine TiO2 nanoparticles showed intense peaks at 2θ of 25.37°, 37.87°, 48.16°, 54.00°, 55.21°, and 62.84° which are perfectly aligned to TiO2 anatase (COD ID 7206075) phase. The synthesized KT-NW corresponded to the crystal phase of K2Ti6O13 (AMCSD no: 0010602)22 and the intense peaks can be indexed as 200, 110, 310, 112, 402, 404, 020, and 422.
The starting material Ti3AlC2 (MAX) shows the standard XRD pattern (attached in Fig. S2†) as reported in the literature.23 MXene or Ti3C2Tx was obtained after chemically etching the MAX phase with HCl and LiF at 50 °C for 48 h, where HF was produced in situ in the reaction. The characteristic peaks for the MAX phase were disappeared but several peaks remained even after selective chemical etching of Al by HCl/LiF as the mild etching agent.24 The intense peak at 002 (9.5°) of MAX phase has reduced in MXene while a new characteristic sharp peak appeared at a low angle (6.4°) confirming the delaminated layered MXene structure. The XRD pattern of the MXene is in accordance with the literatures.24,25
The hydrothermal treatment at 120 °C led the formation of MKT-NW composite. The XRD pattern of MKT-NW composite ascribes the relevant peaks for MXene as well as KT-NW which confirmed the existence of the KT-NW in the MKT-NW composite. Furthermore, KT-NW would form less agglomeration compared to the TiO2 particle when introduced directly to MXene.26
FE-SEM images illustrates the formation of a layer structure of MXene that has been formed due to the delamination and exfoliation by in situ HF. Furthermore, EDS mapping has been conducted to determine the amount of chemically etched Al from the MAX phase during its transition to form MXene (Fig. S3†). TiO2 nanoparticles were completely transformed by a hydrothermal technique in the presence of concentrated KOH aqueous solution in the reaction system. Additionally, FE-SEM and TEM images shows the nanowire morphology of KT-NW on the surfaces of MXene as illustrates in Fig. 2(c2). The KT-NW has been compactly deposited on the surface of MXene as pleated nano wires by covering most of the surface area by developing a strong electrostatic interaction between them. The formation of MKT-NW had similar morphology with that of the work carried out to prepare MXene with TiO2 nanofibers.27
In Fig. 3, the survey spectrum of MKT-NW shows the presence of C 1s, K 2p, Ti 2p, O 1s, and F 1s. All peaks precisely coincide with the binding energies given in the XPS database.28,29 The core level high resolution XPS analyses of MKT-NW powder shows the peaks of carbon (C 1s) is mainly found at 285.5, 286.8, and 289.7 eV which are assigned to sp3 C (C–C), C–O, and C–F, respectively. The K 2p signals (K 2p3/2 at 293.5 eV and K 2p1/2 at 296.8 eV) and KF at 296.1 eV were revealed to formation of potassium titanates from hydrothermal of TiO2 in alkaline media. The Ti 2p region shows two signals at Ti 2p3/2 (ranging from 453 to 462 eV) and Ti 2p1/2 (462 to 468 eV) with oxidation states (Ti2+, Ti3+ and Ti4+) according to the formation of mixed oxides (TiOxFy) and titanium oxycarbide (TiCxOy) which revealed non-uniform surface of MKT-NW. Deconvolution of O 1s also confirms the formation of Ti(IV) oxide and the presence of OH/Ox groups. The F 1s spectrum exhibited a strong signal at 685.2 eV which assigned to fluorine binding to the Ti carbide (Ti–F), thereby creating a C–Ti–Fx bond. The F 1s signal at the slightly higher binding energy of 687.2 eV can be attributed to C–Ti–OFx or a fluorine bridging atom (C–Ti–F–Ti–C) or even an Al–F in MAX phase.30 This result is consistent with EDS mapping (Fig. S3†), about 2.9% wt of Al (or 2.6% atom) left in MXene after chemical etching from the MAX phase.
Fig. 3 MKT-NW powder (a) XPS wide scan and deconvolution of (b) C 1s, (c) K 2p, (d) Ti 2p, (e) O 1s, and (f) F 1s regions. |
The surface morphology of pristine C-SPEEK and MKT-NW/C-SPEEK composites film revealed smooth and rough surface characteristics, respectively (Fig. S4†). The XRF elemental mapping of 12%MKT-NW/C-SPEEK hybrid composite PEM (Fig. 4) exhibited mainly S, Ti, K and Al with a uniform spatial dispersion within the polymer matrix. The distribution of Ti element within the polymer matrix was observed which were derived from MXene and KT-NW, along with the trace amount of K and Al elements.
Samples | Water uptake (%) | Swelling area (%) | Proton conductivity (S cm−1) |
---|---|---|---|
SPEEK | 23.40 | 21.01 | 0.0076 |
C-SPEEK | 10.00 | 18.91 | 0.0034 |
5%MKT-NW/C-SPEEK | 21.05 | 16.74 | 0.0038 |
10%MKT-NW/C-SPEEK | 47.36 | 10.35 | 0.0061 |
12%MKT-NW/C-SPEEK | 48.57 | 8.15 | 0.0097 |
14%MKT-NW/C-SPEEK | 51.42 | 12.46 | 0.0078 |
20%MKT-NW/C-SPEEK | 38.88 | 16.73 | 0.0066 |
In the proton exchange membrane, ion exchange capacity is one of the important factors that insight the ionic sites of each PEM which relates to the proton conductivity. Here, C-SPEEK membrane had low IEC of 1.42 meq g−1 due to the cross-linking of ethylene glycol with the –SO3H group of SPEEK which caused the reduction of acidic sites.31 An IEC increased after MKT-NW was incorporated with C-SPEEK and further increased with an increasing in the amount of MKT-NW32 The 12%MKT-NW/C-SPEEK composite hybrid membrane performed highest IEC of 1.88 meq g−1 according to the well distribution of MKT-NW within the membrane compared to the others. Moreover, a further decrease in the IEC was observed at the amount of MKT-NW more than 12% which may be due to the agglomeration of the inorganic filler.33 The IEC of all the prepared membrane is presented in Fig. 5(a).
Fig. 5 (a) Ion exchange capacity and proton conductivity of MKT-NW/C-SPEEK composite membranes with different amount of MKT-NW and (b) storage modulus (E′) and tanδ of membranes. |
The proton conductivity of all MKT-NW/C-SPEEK composite membranes at room temperature is shown in Table 1. The pristine SPEEK membrane exhibits high proton conductivity according to the presence of a large number of –SO3H group in the hydrophilic domain part of the polymer. In addition, the casted membrane using ethanol and water (SPEEK) which have lower interaction as compared to the other casted SPEEK membranes using an organic solvent, leading to high proton conductivity of membranes.33 However, the conductivity thereby decreased as it was cross-linked with EG because the number of –SO3H group would become lower as it will be cross-linked with –OH group of EG. Furthermore, after MKT-NW was incorporated with C-SPEEK, the proton conductivity increased as shown in Fig. 5(a). It was due to the hydrophilic nature of MXene as well as KT-NW which absorbed more water molecules that acts as the proton carrier in vehicular type mechanism. Nevertheless, the presence of –SO3H from SPEEK and –OH from composite as well as EG would develop an extensive interconnected hydrogen bond network and shorten the distance for faster proton transfer pathway, through Grotthuss mechanism, thereby increasing proton conductivity.35,36 The proton conductivity increased with an increasing in the amount of MKT-NW and the addition of MKT-NW more than 12% decreased the proton conductivity, which may be due agglomeration and non-uniform distribution of the composite. The 12%MKT-NW/C-SPEEK exhibits proton conductivity of 0.0097 S cm−1 which was higher than that of the commercially available Nafion-212 (0.0093 S cm−1) due to the well distribution of composite in the polymer matrix.
Samples | Storage modulus (E′) (×103 MPa) | Tg (°C) | ||||
---|---|---|---|---|---|---|
30 °C | 50 °C | 100 °C | 150 °C | 200 °C | ||
C-SPEEK | 3.76 | 3.62 | 3.38 | 3.29 | 2.36 | 221 |
5%MKT-NW/C-SPEEK | 4.37 | 4.59 | 4.67 | 4.60 | 3.85 | 222 |
20%MKT-NW/C-SPEEK | 5.43 | 5.25 | 4.82 | 4.60 | 3.86 | 223 |
The glass transition temperature (Tg) of C-SPEEK, 5%MKT-NW/C-SPEEK, and 20%MKT-NW/C-SPEEK membranes were depicted using the plot of tanδ various with temperature. The Tg of C-SPEEK membranes was 221 °C while the addition of MKT-NW leads to the small increment of Tg membrane (∼1 °C for 5%MKT-NW and ∼2 °C for 20%MKT-NW) because of the formation of dense intermolecular hydrogen bonding within MKT-NW and C-SPEEK.
C-SPEEK had higher Tg value than SPEEK membranes as reported by X. Zhang et al. (181 °C)37 after cross-linking with EG and the addition of MKT-NW does not bring noteworthy change in the Tg of C-SPEEK membranes. Although it is worth mentioning that MKT-NW had significantly affected to the mechanical strength of C-SPEEK membranes as observed from the storage modulus data at the different temperatures as summarized in Table 2. The C-SPEEK using EG as a cross linker had shown higher storage modulus as compared to the cross linked membrane using polyethylene glycol (PEG) or 1,4-cyclohexane dimethanol (CDM) as a cross linker.38 Additionally, the MKT-NW/C-SPEEK had shown higher storage modulus than SPEEK composite membranes which was due to the cross-linking of SPEEK with EG as well as MKT-NW composite to form a strongly hydrogen-bonded within the hybrid composite membranes.39
As the ∼30% irradiated membrane with higher intensity could produce more H2 gas, this irradiation was considered to study the effect of the MKT-NW composite in the photocatalytic activity of membranes. Two-hybrid composite membranes namely – 12%MKT-NW/C-SPEEK and 5%MKT-NW/C-SPEEK had been selected to study the photocatalytic H2 production. In order to know the effect of MKT-NW content to the photocatalytic activity, 5% and 12%MKT-NW/C-SPEEK were used in this study. It had been observed that both membranes could produce H2 linearly with respect to time within 5 h. The H2 production of 12%MKT-NW/C-SPEEK was slightly different from 5%MKT-NW/C-SPEEK. This might depend on the higher amount of MKT-NW in 12%MKT-NW/C-SPEEK composite PEM as shown in Fig. 6(b).
When UV light was irradiated the KT-NW in the polymer matrix, KT-NW would be excited to produced electron–hole pair (e− and H+). Meanwhile, the valance band (VB) of KT-NW would remain with H+ since the e− in the conduction band (CB) of KT-NW would swiftly move towards MXene and accumulated on the surface because of the superior metallic and electronic properties. Then, a Schottky barrier would develop on the interface of MKT-NW composite blocking the back transfer of e− to KT-NW. And the H+ in the aqueous methanol solution would undergo reduction with the help of the photo-induced e− on MXene producing H2 (ref. 13–40) as presented in Scheme 3. Thus, making this hybrid composite PEM as a photocatalytic active membrane that produces H2 from water without the addition of any noble metals as co-catalysts in the same way as that of the photocatalytic membranes prepared by immobilizing rGO/TiO2 into Nafion membranes.41
Scheme 3 Illustration of photolytic production of H2 from water using MKT-NW/C-SPEEK membrane under UV light. |
The membranes before and after H2 evolution testing under UV irradiation were characterized by XPS wide scan and core level high resolution. Fig. 7 illustrates XPS spectra for MKT-NW and their composites with SPEEK. The spectra of MKT-NW (before and after H2 evolution testing) shows the signals of F 1s, O 1s, Ti 2p, K 2p, and C 1s. For the MKT-NW/SPEEK composites, new peak of S 2p region ranging from 164 to 176 eV, which revealed the presence of sulfonyl entirely in the composite membranes, and the disappearance of the peak due to F 1s were observed. The depth of the XPS surface analysis is about 10 nm, which is the limitation of XPS characterization. The deconvolution of F 1s, O 1s, Ti 2p, K 2p, C 1s, and S 2P are presented in Fig. S5 and S6† and summarized in Table 3. XPS peak due to S decreased after the H2 evolution testing, suggesting the degradation via loss of sulfonic bonds within the SPEEK membrane and further structural deformation after long term exposure to UV irradiation.
Materials | Atomic composition (%) | |||||
---|---|---|---|---|---|---|
C 1s | O 1s | Ti 2P | F 1s | K 2p | S 2p | |
a N/A is not applicable according to the depth of the XPS surface analysis is 10 nm. H2 evolution testing for 5 h under UV irradiation. | ||||||
MKT-NW | 36.2 | 44.7 | 15.6 | 1.35 | 2.16 | 0.00 |
5%MKT-NW/C-SPEEK | ||||||
Before testing | 77.4 | 19.4 | 0.28 | N/A | 0.40 | 2.58 |
After testing | 71.5 | 27.1 | 0.15 | N/A | 0.66 | 0.63 |
12%MKT-NW/C-SPEEK | ||||||
Before testing | 78.8 | 17.7 | 0.24 | N/A | 0.72 | 2.51 |
After testing | 88.8 | 9.85 | 1.03 | N/A | 0.15 | 0.22 |
To predict the photophysical and photochemical properties, absorption and diffuse reflectance spectra of all composites were investigated by UV-Vis spectrometer (UV-2600, Shimadzu) at the range of 200 to 800 nm from the transmission and diffuse-reflectance modes as shown in Fig. S7.† Apparent differences in the spectra shapes were seen depending on the composition, confirming the successful incorporation of potassium titanate and MXene. However, it is difficult to isolate the absorption to be ascribed into the components (polymer and additives) due to the overlapping. More systematic studies will be done in the future studies.
Table 4 presents composites activity over the reported SPEEK-functionalized materials.11,20,42–44 It was found that the MKT-NW/C-SPEEK composite membrane of this work had shown quite a good proton conductivity at room temperature while the other SPEEK composite membranes were studied at higher temperature. Our recent work assumed that the present composite membrane was able to transfer proton faster without being influenced by temperature because of the hydrophilic nature of MKT-NW as well as the hydrogen bonding. Additionally, the MKT-NW/C-SPEEK possessed photocatalytic activity and able to produce H2 from the membrane.
MXene (Ti2C2Tx) | Titanium carbide |
KT-NW (K2Ti6O13) | Potassium titanate nanowire |
SPEEK | Sulfonated polyether ether ketone |
EG | Ethylene glycol |
C-SPEEK | Cross-linked sulfonated polyether-ether ketone |
MKT-NW/C-SPEEK | MXene-potassium titanate nanowire/cross-linked sulfonated polyether-ether ketone |
DS | Degree of sulfonation |
PEM | Proton exchange membrane |
IEC | Ion exchange capacity |
HER | Hydrogen evolution reaction |
Footnote |
† Electronic supplementary information (ESI) available: Characterization of materials and membranes; ATR-FTIR spectra of PEEK and SPEEK (Fig. S1), WXRD of MAX and MXene (Fig. S2), EDS mapping of MAX phase and MXene (Fig. S3), FE-SEM images of MAX phase, potassium titanate nanowire, C-SPEEK and 12%MKT NW/C-SPEEK membranes (Fig. S4), deconvolution of composite membranes before and after H2 evolution testing for 5 h (Fig. S5 and S6), absorption spectra and diffuse reflectance spectra (Fig. S7), and photocatalytic H2 production of the membranes under UV irradiation for 5 h (Tables S1 and S2). See DOI: 10.1039/d0ra09935j |
This journal is © The Royal Society of Chemistry 2021 |