Facile synthesis of novel NH2-MIL-53(Fe)/AgSCN heterojunction composites as a highly efficient photocatalyst for ciprofloxacin degradation and H2 production under visible-light irradiation
Received
18th August 2021
, Accepted 19th October 2021
First published on 19th October 2021
Abstract
With the aim of solving the increasingly serious problem of environmental pollution and the energy crisis, in this work a novel NH2-MIL-53(Fe)/AgSCN (NMFA) composite photocatalyst was successfully prepared through a one-step chemical precipitation method. The prepared composites demonstrate an excellent photocatalytic performance for ciprofloxacin (CIP) and rhodamine B (RhB) degradation under visible-light irradiation. Within 60 min, the degradation rate for CIP and RhB reached 90% and 100%, respectively, which was 1.84/3.33 times and 1.79/2.04 times greater than that of the single NH2-MIL-53(Fe) and AgSCN samples. Furthermore, the H2 production rate of the NMFA-5 composite was 4742 μmol g−1 h−1, which was 5.25 and 17.37 times greater than that of the pure samples. Owing to the combination of NH2-MIL-53(Fe) and AgSCN, the separation and transmission efficiency of the photon-generated carriers in the composites was improved, which was demonstrated using optical characterization and a series of electrochemical characterization techniques. In addition, a possible mechanism for the excellent photocatalytic performance of the NMFA composites is discussed. The work in this paper may provide a technical reference for the application of silver modified metal organic frameworks (MOFs)-based composite photocatalysts for the treatment of environmental remediation.
1 Introduction
The environment has been extensively damaged by rapid changes in the way humans live, resulting in soil, atmospheric and water pollution.1–3 Specifically, industrial sewage containing organic dyes and antibiotics is a particularly problematic form of pollution owing to the structural stability and low concentration of the pollutants. Many technological advances have focused on dealing with this problem, such as the physical–chemical precipitation method, membrane separation method, adsorption method, biodegradation method, ultrafiltration and reverse osmosis techniques, and so on.4–8 Nevertheless, there are many disadvantages to these methods, such as a lack of complete degradation, weak selectivity, high costs, complicated operation, and the formation of secondary pollutants. Therefore, finding an efficient technique to deal with these pollutants that is cheap, easy to operate and environment friendly is urgently needed and would be of great significance. On the other hand, air pollution can be caused by CO, CO2, SO2 and other gases, resulting from the burning of fossil fuels and coal and emissions from motor vehicle exhaust fumes.9,10 Therefore, finding a clean and sustainable energy source can not only avoid environmental pollution, but also be an important means to solve the energy crisis. The higher calorific value and clean final product (H2O) of H2 fuel has been highly praised by scientists, and it is deemed to be one of the most ideal novel energy sources.11 For example, the electrolysis of water, the biological enzyme method and the photocatalytic water splitting method have been used for the treatment of sewage.12–14 The photocatalytic H2 emission reaction (HER) accomplished by water decomposition is regarded as the most economical method of water splitting.15
Photocatalytic technology has resulted in major achievements in the treatment of water, energy development and N2 fixation and reduction since the field of photocatalysis was first reported in 1972 by Fujishima.16 In a recent report, Sun et al. synthesized Co/Bi composites using an in situ calcination process, which was used for the degradation of ciprofloxacin (CIP) under visible light.17 In addition, Huang et al. successfully synthesized urchin-like CeO2/ZnO@Au composite photocatalysts that can almost completely remove rhodamine B (RhB) from a sample within 20 min.18 Chen et al. prepared novel Ag3PO4/P-g-C3N4 composites through a two-step chemical route, which enabled highly efficient photocatalytic hydrogen production.19 Chen et al. prepared the novel Bi2S3/KTa0.75Nb0.25O3 (KTN) and CuS/KTa0.75Nb0.25O3 (KTN) heterojunction composites and applied them for N2 fixation and reduction.20,21 In short, photocatalysis is a green and efficient oxidation technology and has shown advantages such as a wide range of selectivity, the synthesis of green products under mild conditions, and a good recyclability. In particular, it has been widely used for the degradation of antibiotics and organic dye pollution (such as CIP and RhB), as well as to efficiently produce hydrogen at room temperature.
Recently, metal organic frameworks (MOFs), which are a combination of metal ions and organic ligands, have attracted widespread attention from scientists because of their large specific surface area, convenient processing techniques, simple synthesis and other features, such as the lack of pollution resulting from them.22 As they contain a high energy density Fe–O bond, Fe-MOFs possess an excellent stability in organic solvents and water compared with other MOFs.23 However, the Fe-MOFs still face challenges in practical applications owing to problems such as a low separation between the electrons and holes and the poor transfer efficiency. In order to solve this problem, the construction of heterostructure Fe-MOFs based composites with other semiconductors seems to be a feasible method. Among the various Ag-based materials, AgSCN has been reported to be an excellent photocatalyst because of its high structural stability and reasonable band gap structure. Therefore, the Fe-MOFs and AgSCN composites may improve the separation and transfer efficiency of the electrons and holes, effectively enhancing the photocatalytic performance of the composites.24–26
Herein, in this work a NH2-MIL-53(Fe)/AgSCN (NMFA) composites photocatalyst was successfully prepared using a simple method, and the composites exhibited an excellent photocatalytic activity, successfully removing the CIP and RhB, and evolving H2. The field emission scanning electron microscope (FESEM) and high resolution transmission electron microscopy (HRTEM) results indicated there is close contact between the NH2-MIL-53(Fe) and AgSCN. Furthermore, the photoluminescence (PL), electrochemical impedance spectroscopy (EIS) and transient photocurrent response indicated that the separation and transfer efficiency of the photogenerated electrons and holes were improved by recombining a certain proportion of the AgSCN, therefore the photocatalytic performance of the NMFA composites was significantly improved. The stability and recyclability of the NMFA composites was evaluated for five cycles. Quenching experiments and electron spin resonance (ESR) tests were used to detect the activity of the free radicals in the catalytic process. Furthermore, the possible photocatalytic mechanism of degradation and H2 evolution of the NMFA composites were discussed, respectively.
2 Experimental
2.1 Reagents
All chemicals were commercially available and of analytical grade, they were used without further purification. Sodium thiocyanate (NaSCN), silver nitrate (AgNO3), 2-aminoterephthalic acid (NH2-BDC), CIP and RhB were purchased from Aladdin. Chloroplatinic acid (H2PtCl6), iron(III) chloride hexahydrate (FeCl3·6H2O), triethanolamine (TEOA), eosin Y (EY), N,N-dimethyl-formamide (DMF), hydrogen peroxide (30%, v/v), ethylenediaminetetraacetic acid disodium salt (EDTA-2Na), isopropyl alcohol (IPA), ascorbic acid (AC) and ethanol (EtOH) were all purchased from Sinopharm Chemical Reagent Co., Ltd (China).
2.2 Synthesis of the NMFA composites
2.2.1 Synthesis of NH2-MIL-53(Fe).
NH2-MIL-53(Fe) was prepared using the solvothermal method. Typically, 2 mmol of NH2-BDC and 2 mmol of FeCl3·6H2O were dissolved in 42 mL of DMF. After stirring uniformly at room temperature, the solution was transferred to a Teflon-lined auto-clave and kept at 150 °C for 3 h. Upon cooling to ambient temperature, the slurry was vacuum filtered to obtain a brown product. The filter cake was then washed with DMF and EtOH. The product was dried overnight in a vacuum oven at 60 °C.
2.2.2 Synthesis of the NMFA composites.
The NMFA composites were obtained using the chemical precipitation method by controlling the mass proportions of NH2-MIL-53(Fe) versus AgSCN. Firstly, 0.2 g of NH2-MIL-53(Fe) was dispersed in 40 mL of the mixed solution and ultrasound was applied for 15 min. Then, a certain amount of NaSCN (0.1 M) solution was added into the mixed solution at the specific ratio. Subsequently, the suspension was transferred to a magnetic stirrer and stirred vigorously for 1 h. After that, the corresponding proportion of the AgNO3 (1 M) solution was dropped slowly into the suspension, and the mixed solution was stirred for 24 h in the dark. Finally, after being filtered and washed, the composite sample was vacuum dried overnight at 60 °C, and the composites materials were designated as NMFA-X, X = 3, 4, 5, 6, corresponding to the amount of added AgSCN of 30, 40, 50, and 60 wt%. The preparation process is shown in Fig. 1.
![image file: d1re00349f-f1.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f1.gif) |
| Fig. 1 Schematic illustration of the process for preparing the NH2-MIL-53(Fe)/AgSCN composites. | |
2.3 Characterization of the as-prepared composites
The morphology of the composite material was analyzed using FESEM (ZEISS GeminiSEM 500, Germany) and HRTEM (TecnaiG2 F20 S-TWIN, FEI, USA). The elemental mapping of NMFA-5 was carried out based on the FESEM characterization. The functional groups of the as-prepared simples were analyzed using Fourier transform infrared spectroscopy (FT-IR, NICOLET 5700, USA). The crystal structures were recorded using X-ray diffractometry (XRD, Bruker D8 Advance, Germany), and the scanning angle range was 5 to 60°. The ultraviolet-visible diffuse reflectance spectroscopy (DRS) spectrum of the as-prepared sample was obtained on a UV-vis spectrophotometer (U-3900, Japan). The binding energies of the elements in NH2-MIL-53(Fe), AgSCN and NMFA-5 were performed using X-ray photoelectron spectroscopy (XPS, Escalab 250XI, Thermo Fisher, USA). The surface areas of the as-prepared sample were obtained using Brunauer–Emmett–Teller (BET) analysis (Quantachrome autosorb-iQ-2MP). The PL spectra with excitation wavelengths of 375 nm were analyzed using a fluorescence spectrometer (F-4600 FL, Japan). The photocurrent, EIS and Mott–Schottky analysis were performed on a CHI 600 electrochemical workstation (Shanghai, China). The light source used was a 300 W xenon lamp (PLS-SXE 300).
2.4 Photocatalytic degradation of CIP and RhB
In this study, the photocatalytic activity was recorded by degradation of the CIP and RhB in solution and a 300 W Xe lamp (λ > 420 nm) was used. Specifically, 20 mg of the catalysts and 100 μL of H2O2 (30%, V/V%) were added into an aqueous solution of CIP or RhB aqueous solution (200 ml, 10%, V/V%) and stirred for 60 min in the dark. Then, 3 mL of the reaction solution was extracted every 10 min for analysis. The solid residues were removed using high speed centrifugation before testing. The concentration of CIP was analyzed via a PerkinElmer Lambda 35 spectrophotometer at 272 nm, and the inspection wavelength for RhB was set as 554 nm.
In addition, the highly efficient hydrogenation (HER) was performed in a 150 mL quartz reactor, in which 20 mg of the catalysts and quantitative EY and TEOA were added in 100 mL of aqueous solution. The solution was then kept under an uninterrupted vacuum for 30 min to remove the dissolved gas in the water. Before the reaction began, the gas chromatography collecting system was purged with nitrogen. During the reaction period, the total H2 production was analyzed every 30 min, and the HER system was run for 4 h to capture the full reaction.
3 Results and discussion
3.1 Characterization
The microstructures of the samples were observed by FESEM and TEM and the images are shown in Fig. 2 and 3. The microstructures of the AgSCN were observed to be spherical from Fig. 2a and 3a.27 NH2-MIL-53(Fe) appeared to be spindle-shaped and was surrounded by irregular debris (Fig. 2b and 3b), which could be attributed to the incomplete growth process.28 As shown in Fig. 2c–e and 3c and d, the FESEM and HRTEM images of the NMFA-5 composite indicate that the AgSCN nanoparticles were anchored on the surface of NH2-MIL53(Fe). The element mapping (Fig. 2g) and HRTEM images (Fig. 3c and d) of the NMFA-5 composite clearly show that the interface contact was formed between the spindle-shaped NH2-MIL53(Fe) and AgSCN nanoparticles, which is beneficial for the transmission of electrons. The results of the element mapping and EDX characterization both proved the existence of AgSCN nanoparticles on the surfaces of the NH2-MIL53(Fe), which also demonstrated that the NMFA composites were successfully synthesized. In addition, as shown in the SEM (Fig. 2f), element mapping (Fig. 2h), and EDX (Fig. 2j) images of the NMFA-5 composite after H2 production, it was observed that the morphology of NH2-MIL-53(Fe) did not show any significant changes after the reaction. In addition, the element mapping and EDX characterization also show that the AgSCN nanoparticles still exist on the surfaces of the NMFA-5 composite after the reaction. Furthermore, as shown in Fig. 3e for the NMFA-5 composite, the interplant spacing of AgSCN was 0.241 nm, which represented the (021) planes of the AgSCN. The connection pitch of the composites was 0.402 nm, which indicated that the composites were successfully synthesized.
![image file: d1re00349f-f2.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f2.gif) |
| Fig. 2 SEM images of (a) AgSCN, (b) NH2-MIL-53(Fe), (c)–(e) NMFA-5 and (f) NMFA-5 after H2 production, element mapping results (g) and (h), and EDX spectra (i) and (j) of fresh NMFA-5 and after H2 production. | |
![image file: d1re00349f-f3.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f3.gif) |
| Fig. 3 TEM images of (a) NH2-MIL-53(Fe) and (b) AgSCN; and HRTEM images of (c–f) NMFA-5. | |
The characteristic functional groups and crystal type information of the as-prepared NH2-MIL-53(Fe) and NMFA composites was identified using FT-IR and XRD characterization. As shown in Fig. 4a, the NMFA composites contained both the characteristics of AgSCN and NH2-MIL-53(Fe). Specifically, the vibrational bands located at 505, 707, 1069, and 2089 cm−1 represented the bending, symmetric stretching, bending overtones and asymmetric stretching vibrations of the SCN−1 group,29 respectively. More precisely, the characteristic vibrational bands of 707 and 2089 cm−1 could be attributed to the S–C and C–N groups.30,31 At the same time, the broad peak at 3450 cm−1 for all of the prepared samples could be attributed to the ν(OH) stretching, and the weak band at 1620 cm−1 indicated that the composite existed in the AgSCN structure. The bands at 521, 768, 1255 and 3454 cm−1 were attributed to the Fe–O, C–H vibration of the benzene rings, and the C–N and N–H vibrations of the amino group, respectively.32,33 In short, the characteristic vibrational bands of the NMFA composites were very similar to those of the SCN−1 functional group, for which the bands were close to 770 and 2000 cm−1. This conclusion proved that the NMFA composites were successfully synthesized. Notably, the vibrational band of the C–N functional group of AgSCN could overlap with the C–H vibrational band of the benzene ring of NH2-MIL-53(Fe), which might lead to only one absorption peak being observed. XRD patterns of the as-prepared samples are shown in Fig. 4c. From the figure, it can easily be seen that the crystallographic features of NH2-MIL-53(Fe) and AgSCN were consistent with those reported previously.34 Specifically, the characteristic peaks at 9.2, 10.4, 13.1, 18.6, 20.8, and 25.1° were well matched with the standard in the card library for the Fe-MOFs, indicating that the NH2-MIL-53(Fe) was successful synthesized. Otherwise, the four strong peaks at 15.0, 18.9, 28.9, and 32.8° of the AgSCN composite also matched well with the standard in the card library (PDF #29-1443), which could be indexed to the lattice plane of (−110), (111), (−202), and (221). The diffraction peaks of the NMFA composites were well-matched with the corresponding pure samples, which not only show that the structure was not changed during the synthesis process, but also further proved that the composites were successfully prepared. Furthermore, it can be observed that the characteristic peak of NH2-MIL-53(Fe) became much weaker following the increase in the proportion of AgSCN in the NMFA-x compounds. Whereas the characteristic peak of AgSCN became much more obvious in contrast.
![image file: d1re00349f-f4.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f4.gif) |
| Fig. 4 (a) and (b) FT-IR spectra of the as-prepared samples; and (c) and (d) XRD patterns of the as-prepared samples. | |
XPS measurements were used to reveal the chemical composition of the samples, and the results are displayed in Fig. 5. The full spectrum shows that NMFA-5 consisted of C, N, O, S, Fe, and Ag elements. Fig. 5b shows the C 1s spectrum of the NMFA-5 composite, the four peaks at 284.8, 286.1, 286.6 and 288.4 eV can be attributed to the C–C, C–O, SCN−1 and C–C
N groups,26 respectively. This indicates that the NMFA composites were successfully synthesized, and the subtle difference in the C–O group can be attributed to the SCN− groups. As shown in Fig. 5b in the N 1s spectrum of the NMFA-5 composite, there was only one peak located at 398.8 eV. Fig. 5d shows the S 2p spectrum of the composites, from which the two peaks at 163.2 and 164.4 eV can be easily found. The N 1s and S 2p characteristic peaks were both attributed to the SCN− group of the NMFA-5 composite. However, it is worth noting that the N 1s peak shows a greater difference, while the S 2p does not. This indicates that the S element may play a major role in the SCN− group. As shown in Fig. 5e, the two peaks at 368.5 and 374.5 eV could be attributed to the 3d2/5 and 3d2/3 states of Ag+.25 Finally, as shown in Fig. 5f in the spectrum of Fe 2p, the two characteristic peaks at 712.0 and 725.5 eV correspond to Fe 2p3/2 and Fe 2p1/2. Meanwhile, there was a satellite signal located at 715.5 eV, which suggested that the Fe exists as a positive trivalent state.35 However, the satellite signal peak of the NMFA-5 composites was centered at 716.5 eV, which was higher in energy than that of the pure NH2-MIL-53(Fe). In particular, it can be observed that the satellite signal of Fe 2p3/2 shows a slight change in the peak offset intensity (from 1.1 to 1.0 eV). This negative shift can be attributed to the increased electron density of Fe3+, and the binding energy of the peak representing Fe 2p1/2 shifts slightly (from 712.0 to 711.9 eV). Furthermore, this negative movement phenomenon indicates that the Fe3+ electron density is increased in the NMFA-5 composite. On the other hand, it is indicated that van der Waals forces (VDW) may exist between NH2-MIL-53 (Fe) and AgSCN. In summary, the binding energies of the characteristic peaks for the C, N, and Ag elements of the NMFA-5 composites do not show much difference compared to those of the pure AgSCN, which can be attributed to the effect of the electronegativity of S in the SCN− group. The binding energies of Fe3+ in the NMFA-5 composites became stronger, which could be caused by the effect of intimate contact between the surfaces of these two composites.
![image file: d1re00349f-f5.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f5.gif) |
| Fig. 5 XPS spectra of (a) the survey scan, and (b) C 1s, (c) N 1s, (d) S 2p, (e) Ag 3d, and (f) Fe 2p for the samples. | |
The optical adsorption performances of the synthesized samples were further measured using a UV-vis spectrophotometer and the spectra are shown in Fig. 6a. These results indicate that the NMFA composites exhibited a slightly weaker adsorption in the visible light region than in the pure light region. This indicates that the improvement of the photocatalytic performance might be significantly affected by some of the other aspects, such as the separation and transportation of the photo-generated electron–hole. Furthermore, the band-gap energy (Eg) was obtained using Tauc plots ((αhν)2 = A(hν − Eg)).36 As shown in Fig. 6b and c, the optical band gap of NH2-MIL-53(Fe) and the AgSCN composites were calculated and found to be 2.70 and 3.55 eV. The conduction band (ECB) potential of the catalysts was obtained from the Mott–Schottky plot (Fig. 6c). In addition, the valence band (EVB) potential could be obtained using the formula Eg = EVB − ECB.37 Detailed results are listed in Table 1.
![image file: d1re00349f-f6.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f6.gif) |
| Fig. 6 (a) UV-vis DRS spectra, (b) plots of (αhν)2versus (hν) and (c) Mott–Schottky plots for the samples. | |
Table 1 Calculated Eg, EVB and ECB potentials of the prepared samples based on the UV-vis results
Sample serial number |
E
g (eV) |
E
VB potential (eV) |
E
CB potential (eV) |
NH2-MIL-53(Fe) |
2.70 |
2.23 |
−0.47 |
AgSCN |
3.55 |
3.16 |
−0.39 |
Fig. 7 and Table 2 exhibit the surface area and pore structure parameters of the samples obtained using the BET method. The surface area of the samples follows the rule of NH2-MIL-53(Fe) > NMFA-3 > NMFA-4 > NMFA-5 > NMFA-6 > AgSCN. The results showed that the introduction of AgSCN could increase the thickness of NH2-MIL-53(Fe), thereby the average particle size of the NMFA composite increased while the specific surface area decreased. Furthermore, all the curves for the samples showed typical type IV isotherms and type H3 hysteresis rings, which could be attributed to the overlap between the composites.38
![image file: d1re00349f-f7.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f7.gif) |
| Fig. 7 The N2 adsorption–desorption isotherms for the (a) AgSCN and NMFA-x, (b) NH2-MIL-53(Fe). | |
Table 2 Detailed list of the surface area, pore volume and pore size of the samples
Sample |
S
BET (m2 g−1) |
Average pore diameter (nm) |
Pore volume (cm3 g−1) |
Average particle size (nm) |
NH2-MIL-53(Fe) |
119.569 |
17.321 |
0.588 |
22.806 |
AgSCN |
3.105 |
4.888 |
0.018 |
878.371 |
NMFA-3 |
103.861 |
3.852 |
0.219 |
26.259 |
NMFA-4 |
83.683 |
3.812 |
0.180 |
32.590 |
NMFA-5 |
69.457 |
3.806 |
0.147 |
39.266 |
NMFA-6 |
60.253 |
3.823 |
0.106 |
45.264 |
3.2 Photocatalytic activity
Fig. 8 shows that the photocatalytic activity of the NMFA-5 composites was the highest among the as-prepared catalysts. The degradation rate reached more than 90% for CIP within 60 min over the NMFA-5 composites, while for the pure NH2-MIL-53(Fe) and AgSCN it only reached 50% and 27%. In addition, the degradation constants (k) of the NMFA-5, pure NH2-MIL-53(Fe) and AgSCN were calculated as 0.03666, 0.00334, and 0.00088 min−1, respectively (Fig. 8e). In the same way, the degradation rate reached almost 100% for RhB within 60 min over the NMFA-5 composites, while for the pure NH2-MIL-53(Fe) and AgSCN the rates were just 55% and 49%. In addition, the degradation constants (k) of the NMFA-5, pure NH2-MIL-53(Fe) and AgSCN were calculated as 0.09652, 0.00793, and 0.01044 min−1, respectively (Fig. 8f). As NH2-MIL-53(Fe) possesses a much larger surface area (119.569 m2 g−1) than the AgSCN (3.105 m2 g−1), which may be conducive to the high adsorption properties. Furthermore, the band gap of NH2-MIL-53(Fe) was 2.70 eV, which should, in theory, show a good photocatalytic performance, while the results showed that the photocatalytic activity was not as high as expected. This may be related to the low separation and transfer efficiency of the photogenerated electrons and holes for the single NH2-MIL-53(Fe). In sharp contrast, the NMFA composites all exhibited a much higher photocatalytic performance than that of the pure samples, which could be attributed to the fact that the contact surface between NH2-MIL-53(Fe) and AgSCN improved the separation and transport efficacy of the photogenerated electrons and holes. The detailed effects of NMFA on CIP and RhB photodegradation are shown in Table 3. In addition, Table 4 lists some of the typical photocatalysts used for the degradation of CIP or RhB that have been reported in recent years. Notably, although the dosage of the catalyst was significantly lower than the others, the photocatalytic activity of the NMFA composite was as high as that of the other novel photocatalysts. Furthermore, the photocatalytic performance of the NMFA composite was still maintained at a high level when the light source was restricted in the visible region. In light of these results, it can be concluded that the as-prepared NMFA composites exhibit competitive photocatalytic performances.
![image file: d1re00349f-f8.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f8.gif) |
| Fig. 8 The photocatalytic performance of the samples for the degradation of CIP and RhB (a and b), the Pseudo-first-order kinetics curves (c and d) and the degradation constants k (e and f). | |
Table 3 Detailed list of the photocatalytic performances of the prepared samples
Sample |
CIP (%) |
RhB (%) |
k (CIP) |
k (RhB) |
NH2-MIL-53(Fe)(single) |
49 |
56 |
0.00334 |
0.00793 |
NH2-MIL-53(Fe) |
63 |
78 |
0.00857 |
0.02120 |
AgSCN(single) |
27 |
49 |
0.00088 |
0.01044 |
AgSCN |
32 |
45 |
0.00678 |
0.00892 |
None |
4 |
3 |
0.00006 |
0.00023 |
H2O2 |
12 |
9 |
0.00046 |
0.00110 |
NMFA-5(single) |
43 |
40 |
0.00497 |
0.00411 |
NMFA-3 |
81 |
82 |
0.02420 |
0.02596 |
NMFA-4 |
84 |
90 |
0.02950 |
0.03599 |
NMFA-5 |
90 |
100 |
0.03666 |
0.09652 |
NMFA-6 |
71 |
80 |
0.01695 |
0.02310 |
Table 4 Comparison of the photocatalytic efficiency of the NMFA composites and relevant catalysts reported in recent years
Samples |
Amount of catalyst (g L−1) |
Pollutants (ppm) |
Xenon lamp (W) |
Degradation rate (%) |
Ref. |
AgSCN |
3 |
10, RhB |
300 (<420 nm) |
93.2 |
39
|
Bi2O3-TiO2/PAC |
1 |
20, CIP |
300 (<420 nm) |
96.9 |
40
|
NH2-MIL-53(Fe) |
0.25 |
10, RhB |
500 (>420 nm) |
86.16 |
41
|
NMFA-5 |
0.1 |
10, CIP |
300 (>420 nm) |
90.0 |
— |
NMFA-5 |
0.1 |
10, RhB |
300 (>420 nm) |
100 |
— |
Furthermore, the photocatalytic stability is an important parameter that can be used to evaluate the catalysts from the perspective of practical applications. Cycling experiments were performed using the NMFA-5 composite for the degradation of CIP and RhB (Fig. 9a and b). The degradation rate of CIP and RhB for the NMFA-5 composite was maintained above 80% and 85% after five cycle experiments, respectively. The small decrease in the degradation rate can obviously be attributed to the inescapable leaching of the catalysts during the cycling experiments. Furthermore, there was no obvious difference displayed from the XRD pattern, which indicates the good stability of the as-prepared NMFA-5 composite (Fig. 9c). This could be attributed to the good protective effect of NH2-MIL-53(Fe) with the introduction of AgSCN. Therefore, the NMFA composites exhibited a good structural and catalytic stability during the degradation.
![image file: d1re00349f-f9.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f9.gif) |
| Fig. 9 (a and b) Catalytic cycle test results and (c) the XRD patterns of the NMFA-5 sample before and after the cycling test. | |
Furthermore, the yield of H2 evolution during the photocatalytic process under visible light radiation was also used to evaluate the photocatalytic performance of the as-prepared samples. The effect of the photosensitizer EY on the hydrogen production performance of the NMFA-5 composite is discussed first. As shown in Fig. 10a and b, the photocatalytic system with 30 mg EY showed the highest hydrogen production, the amount and rate of H2 evolution were 298.09 μmol and 4742.43 μmol g−1 h−1, respectively. This result indicates that the amount and rate of hydrogen generated at different EY concentrations initially increased in the early stage and then decreased. This phenomenon could be attributed to the shielding effect of the photosensitizer.42 Furthermore, the effect of TEOA on the hydrogen production performance of the NMFA-5 composite was also discussed. As shown in Fig. 10c and d, the photocatalytic system with 10 mL of TEOA showed the highest hydrogen production performance, and the amount of H2 evolved was 298.21 μmol. It is worth noting that the highest hydrogen production rate in the first 30 min was 6305.80 μmol g−1 h−1 when the content of TEOA was 5 mL, after that the rate decreases sharply. This phenomenon could be attributed to the contact area of the TEOA and the catalysts. As the reaction progresses, the contact surface cannot be replenished and leads to a sharp decrease in the hydrogen production rate when the TEOA concentration is low. In addition, the NMFA-5 composite was repeatedly measured under the optimal conditions (the system contains 30 mg of EY and 10 mL of TEOA). As shown in Fig. 11a–c, the NMFA-5 composite showed a stable performance for the photocatalytic cracking of water to produce H2. Fig. 11d–f shows the time course and rate of hydrogen generation for the NH2-MIL-53(Fe), AgSCN and NMFA-x photocatalysts. The NMFA composites showed an obviously higher activity for photocatalytic hydrogen generation and the amounts of hydrogen produced were 142.48, 242.58, 298.21, and 244.18 μmol, respectively. The amount of hydrogen produced using NMFA-x was 1.97, 3.36, 3.13, 3.38, 6.52, 11.11, 13.65, and 11.18 times higher than that produced using NH2-MIL-53(Fe) and AgSCN, respectively. At the same time, the amount of H2 evolution was only 72.26 and 21.84 μmol for the pure samples. This may be due to the lower transfer efficiency of the photogenerated electrons and holes. Furthermore, the high recombination rate of the electron–hole pairs may not be conducive to the reduction of H+ in water by the photogenerated electrons to generate H2.43
![image file: d1re00349f-f10.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f10.gif) |
| Fig. 10 The effect of the photosensitizer EY (a) and (b) and TEOA (c) and (d) on the H2 production performance. | |
![image file: d1re00349f-f11.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f11.gif) |
| Fig. 11 The H2 evolution performances of the NMFA-5 composites for five cycles (a)–(c), and different samples (d)–(f) under the same reaction conditions. | |
3.3 Charge separation efficiency and radical capture
In order to verify the mechanism of the enhanced photocatalytic performance for the NMFA composites, the spectra for the separation, migration and recombination of the photogenerated electron–hole pairs in the NMFA composites were studied. Firstly, the transient photocurrent response spectrum was used to analyze the separation efficiency of the electrons and holes. As shown in Fig. 12a, the NMFA-5 composite showed obviously enhanced photocurrent intensities compared to those of the pure samples. Similarly, the transfer efficiency of the photogenerated charges for the as-prepared composites was analyzed using EIS and Nyquist plots. As shown in Fig. 12b, the NMFA-5 composite obviously exhibited the smallest sized radius arc compared to those of the pure samples. The results indicated that the rapid movement of photogenerated carriers through close contact between NH2-MIL-53(Fe) and AgSCN was more effective. Furthermore, the PL emission intensity reflected the separation effect of the photo-generated charge. As shown in Fig. 12c, the peak for the NMFA-5 composite was much lower than that of the pure samples. The results indicated that the close contact between NH2-MIL-53(Fe) and AgSCN could enhance the separation efficiency of the photogenerated electrons and holes.
![image file: d1re00349f-f12.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f12.gif) |
| Fig. 12 Spectra showing the instantaneous photocurrent (a), EIS (b), and PL (c) of the samples. | |
Generally, the photocatalytic mechanism is studied using active species trapping experiments. The hydroxyl radicals (˙OH), superoxide radicals (˙O2−) and holes (h+) were eliminated using IPA (1 mmol), BQ (benzoquinone, 1 mmol), and EDTA-2Na (1 mmol) during the photocatalytic removal of pollutants in wastewater, respectively. The quencher was dissolved in wastewater before the adsorption and desorption equilibrium was reached. As shown in the experimental results shown in Fig. 13, it is indicated that the photocatalytic performance of the NMFA-5 composites was significantly inhibited compared with the results obtained without the addition of an elimination agent. From the experimental results, it can be easily observed that the greatest inhibitory effect was found upon adding IPA during CIP degradation. This indicated that the ˙OH occupies an important position in the CIP degradation process. Correspondingly, the h+ played a more prominent role than the ˙OH radicals in the RhB degradation process, which might be attributed to the characteristics of different pollutants. In addition, the superoxide radicals (˙O2−) only provided a small contribution to the degradation of CIP and RhB, indicating that ˙O2− played a small role in the reaction.
![image file: d1re00349f-f13.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f13.gif) |
| Fig. 13 The radical quenching results of the NMFA-5 composite for the degradation process of the CIP (a) and RhB (b), and the results comparison (c). | |
To further understand the influence of the h+ and ˙OH radicals in the photocatalytic process, ESR measurement was performed for the NMFA-5 composite. During the ESR measurement, the free radical signals were recorded in the same period of time at room temperature under xenon lamp radiation. Specifically, about 20 mg of the samples were added into the solution containing 50 mM of the spin trapped reagents, which were 5,5-dimethyl-1-pyrroline N-oxide (DMPO)/H2O, methanol/DMPO and 2,2,6,6-tetramethyl-piperidinooxy (TEMPO)/chlorpromazine hydrochloride for the trapping of the radicals ˙OH, ˙O2−, and h+, respectively. As shown in Fig. 14a, the three strong characteristic peaks belonging to the h+ decreased as the illumination time increased, which indicated that the h+ radical participated in the process of degradation. As shown in Fig. 14a, the peak intensity of the four characteristic peaks increased with the increased irradiation time, which indicated that the h+ radical participated in the process of degradation. Furthermore, as shown in Fig. 14b, four characteristic peaks for ˙OH were detected after the light was switched on. In addition, the peak intensity increased with the prolonged irradiation time, which indicated the existence of the ˙OH radical during the process of degradation. In addition, as shown in Fig. 14c, the peak intensity of the six characteristic peaks also increased with the prolonged irradiation time. The results indicated that the ˙O2− radicals were also produced during the photocatalytic degradation process. The oxidation potential of the free radicals was proportional to the oxidation capacity in the optical Fenton system. In particular, the oxidation potentials for the OH˙ and ˙O2− radicals were 2.73 and 1.3 eV, respectively. As expected, the ˙OH radicals were obtained before the ˙O2− radicals in the optical Fenton system. Therefore, the ˙O2− radicals played a small role in the contaminant photo-degradation process.
![image file: d1re00349f-f14.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f14.gif) |
| Fig. 14 The ESR spectra of (a) h+, (b) ˙OH and (c) ˙O2− generated using the NMFA-5 composites. | |
3.4 Mechanism of photocatalysis
UV-vis DRS and Mott–Schottky characterizations are considered, in theory, to be the most effective means to explore the photocatalytic mechanism of the composites. As shown in Fig. 7, the Eg of NH2-MIL-53(Fe) and AgSCN were calculated as 2.70 and 3.55 eV, and the ECB values were found to be −0.47 and −0.39 eV, respectively. Therefore, the EVB of NH2-MIL-53(Fe) and AgSCN were +2.23 and +3.16 eV according to the formula Eg = EVB − ECB. As shown in Fig. 15, when the NMFA-5 composites were irradiated using visible light, the photogenerated electrons were excited on the surfaces of the NH2-MIL-53(Fe) and participated in the reduction of Fe3+. At the same time, the electrons on the conduction band (CB) of AgSCN undergo directional migration to the valence band (VB) of NH2-MIL-53(Fe) owing to the large number of h+ that accumulate on the VB of NH2-MIL-53(Fe). In addition, the h+ could take part in the degradation of the pollutants, which originates from that remaining in the VB of AgSCN. At the same time, the mutual conversion between Fe3+ and Fe2+ in the optical Fenton system could generate free radicals for the degradation of pollutants molecules. However, the free radicals h+, ˙OH, ˙O2− played difference roles in the degradation of different pollutant molecules. This may be caused by the selectivity of the NMFA-5 photocatalyst to the pollutants with different characteristic groups. However, the mechanism for the visible-light photocatalytic H2 evolution of the NMFA-5 photocatalyst was different from the photo-degradation reaction. Owing to the wide band gap of AgSCN (Eg = 3.55 eV) and the fact that EY and AgSCN were employed as the photosensitizer and co-catalyst during the photocatalytic reaction, respectively. The photogenerated electrons at a high potential on EY could migrate in the direction of a low potential if the system absorbs visible light (route 1). After that, the electrons accumulated on the CB of NH2-MIL-53(Fe) could migrate to the more negative CB of AgSCN. On the other hand, the electrons on the CB of EY could also directly migrate to the CB of AgSCN in one step (route 1). Finally, the high concentration of electrons accumulated on the CB of AgSCN could reduce the H+ in the water to produce H2. Furthermore, the h+ in the VB of eosin Y and NH2-MIL-53(Fe) reconverted to the ground state using the electron donor to maintain the balance of electrons and holes in the photocatalyst. This mechanism allowed H2 production to proceed in an orderly manner.
![image file: d1re00349f-f15.tif](/image/article/2022/RE/d1re00349f/d1re00349f-f15.gif) |
| Fig. 15 Proposed schematic diagram of the possible charge transfer approach of the NMFA composite for the degradation of pollutants and hydrogen production. | |
4 Conclusion
In this research, highly active NMFA composites photocatalyst was successfully preparation through a chemical precipitation method. The prepared photocatalyst shows highly effective photocatalytic activity for CIP and RhB degradation, as well as excellent H2 evolution efficacy. For the NMFA-5 composite, a degradation rate as higher as 90% and 100% was achieved for CIP and RhB degradation within 60 min. In particular, the degradation rate for the NMFA-5 composite was 1.8 and 1.82 times greater than that of the pure NH2-MIL-53(Fe) and AgSCN samples for CIP degradation, and 3.3 and 2.08 times for the degradation of RhB. In addition, the highest H2 production rate obtained for the NMFA-5 composites catalyst was 4742 μmol g−1 h−1, which was 5.25 and 17.37 times greater than that of the pure samples. Optical characterization and a series of electrochemical characterization methods were used to analyze the composite microstructure and morphology. The PL, EIS and transient response current results jointly indicate that the composite material showed an excellent charge separation and transfer efficiency. In summary, the excellent photocatalytic performance of the NMFA-5 composites may provide potential solutions to environmental and energy issues.
Conflicts of interest
The authors declare that there is no conflict of interest regarding the publication of this paper.
Acknowledgements
This project was financially supported by the Scientific Research Plan Project of the Education Department of the Hubei Province [grant number B2019377], the Open Project of Key Laboratory of Green Chemical Process of Ministry of Education [grant number GCP20190205] and the Principal Fund of Wuhan Institute of Technology [grant number XZJJ2020005].
References
- H. Li, L. Zhang, H. Lu, J. Ma, X. Zhou, Z. Wang and C. Yi, Macro−/nanoporous Al-doped ZnO/cellulose composites based on tunable cellulose fiber sizes for enhancing photocatalytic properties, Carbohydr. Polym., 2020, 250, 116873 CrossRef CAS
.
- B. Janani, K. M. Alarjani, L. L. Raju, A. M. Thomas, A. Das and S. S. Khan, A potent multifunctional Ag/Co-polyvinylpyrrolidone nanocomposite for enhanced detection of Cr(III) from environmental samples and its photocatalytic and antibacterial applications, Spectrochim. Acta, Part A, 2020, 243, 118766 CrossRef CAS PubMed
.
- L. Chen, X. Wang, Y. Chen, Z. Zhuang, F.-F. Chen, Y.-J. Zhu and Y. Yu, Recycling heavy metals from wastewater for photocatalytic CO2 reduction, Chem. Eng. J., 2020, 402, 125922 CrossRef CAS
.
- X. He, Z. Liu, Y. Yang, L. Li, L. Wang, A. Li, Z. Qu and F. Xu, Sensitivity Enhancement of Nucleic Acid Lateral Flow Assays through a Physical-Chemical Coupling Method: Dissoluble Saline Barriers, ACS Sens., 2019, 4, 1691–1700 CrossRef CAS PubMed
.
- L. S. M. Nazir, Y. F. Yeong and T. L. Chew, Methods and synthesis parameters affecting the formation of FAU type zeolite membrane and its separation performance: a review, J. Asian Ceram. Soc., 2020, 8, 553–571 CrossRef
.
- Z. Zhou, Z. Shen, Z. Cheng, G. Zhang, M. Li, Y. Li, S. Zhan and J. C. Crittenden, Mechanistic insights for efficient inactivation of antibiotic resistance genes: a synergistic interfacial adsorption and photocatalytic-oxidation process, Sci. Bull., 2020, 65, 2107–2119 CrossRef CAS
.
- Y. Zhen, Q. Zhang, X. Zhang, G. Zhang, X. Chen and C. Zhao, A novel tubular up-flow magnetic film photocatalytic system optimized by main factors control for efficient removal of chlorophenols wastewater, J. Hazard. Mater., 2020, 398, 122963 CrossRef CAS PubMed
.
- L. Sun, S. Yin, D. Shen, Y. Zhou, J. Li, X. Li, H. Wang, P. Huo and Y. Yan, Fabricating acid-sensitive controlled PAA@Ag/AgCl/CN photocatalyst with reversible photocatalytic activity transformation, J. Colloid Interface Sci., 2020, 580, 753–767 CrossRef CAS
.
- J. Zhang, Y. Guo, B. Shang, T. Fan, X. Lian, P. Huang, Y. Dong, Z. Chen and X. Yi, Unveiling the Synergistic Effect between Graphitic Carbon Nitride and Cu2O toward CO2 Electroreduction to C2H4, ChemSusChem, 2021, 14, 929–937 CrossRef CAS PubMed
.
- H. Huang, J. Zhao, Y. Du, C. Zhou, M. Zhang, Z. Wang, Y. Weng, J. Long, J. Hofkens, J. A. Steele and M. B. J. Roeffaers, Direct Z-Scheme Heterojunction of Semicoherent FAPbBr3/Bi2WO6 Interface for Photoredox Reaction with Large Driving Force, ACS Nano, 2020, 14, 16689–16697 CrossRef CAS
.
- Y. Xu, J. Xu, W. Yan, H. Tang and G. Tang, Synergistic effect of a noble metal free MoS2 co-catalyst and a ternary Bi2S3/MoS2/P25 heterojunction for enhanced photocatalytic H2 production, Ceram. Int., 2021, 47, 8895–8903 CrossRef CAS
.
- D. Z. Zee, M. Nippe, A. E. King, C. J. Chang and J. R. Long, Tuning Second Coordination Sphere Interactions in Polypyridyl-Iron Complexes to Achieve Selective Electrocatalytic Reduction of Carbon Dioxide to Carbon Monoxide, Inorg. Chem., 2020, 59, 5206–5217 CrossRef CAS
.
- X. Fang, S. Kalathil and E. Reisner, Semi-biological approaches to solar-to-chemical conversion, Chem. Soc. Rev., 2020, 49, 4926–4952 RSC
.
- H. Yang, H. Amari, L. Liu, C. Zhao, H. Gao, A. He, N. D. Browning, M. A. Little, R. S. Sprick and A. I. Cooper, Nano-assemblies of a soluble conjugated organic polymer and an inorganic semiconductor for sacrificial photocatalytic hydrogen production from water, Nanoscale, 2020, 12, 24488–24494 RSC
.
- J. Cho, N. S. Suwandaratne, S. Razek, Y. H. Choi, L. F. J. Piper, D. F. Watson and S. Banerjee, Elucidating the Mechanistic Origins of Photocatalytic Hydrogen Evolution Mediated by MoS2/CdS Quantum-Dot Heterostructures, ACS Appl. Mater. Interfaces, 2020, 12, 43728–43740 CrossRef CAS PubMed
.
- A. Fujishima and K. Honda, Electrochemical photocatalysis of water at semiconductor electrode, Nature, 1972, 238, 37–38 CrossRef CAS
.
- J. Sun, C. H. Shen, J. Guo, H. Guo, Y. F. Yin, X. J. Xu, Z. H. Fei, Z. T. Liu and X. J. Wen, Highly efficient activation of peroxymonosulfate by Co3O4/Bi2WO6 p-n heterojunction composites for the degradation of ciprofloxacin under visible light irradiation, J. Colloid Interface Sci., 2021, 588, 19–30 CrossRef CAS
.
- L. Huang, D. Bao, X. Jiang, J. Li, L. Zhang and X. Sun, Fabrication of stable high-performance urchin-like CeO2/ZnO@Au hierarchical heterojunction photocatalyst for water remediation, J. Colloid Interface Sci., 2021, 588, 713–724 CrossRef CAS PubMed
.
- P. Chen, L. Chen, S. Ge, W. Zhang, M. Wu, P. Xing, T. B. Rotamond, H. Lin, Y. Wu and Y. He, Microwave heating preparation of phosphorus doped g-C3N4 and its enhanced performance for photocatalytic H2 evolution in the help of Ag3PO4 nanoparticles, Int. J. Hydrogen Energy, 2020, 45, 14354–14367 CrossRef CAS
.
- X. Dai, L. Chen, Z. Li, X. Li, J. Wang, X. Hu, L. Zhao, Y. Jia, S. X. Sun, Y. Wu and Y. He, CuS/KTa0.75Nb0.25O3 nanocomposite utilizing solar and mechanical energy for catalytic N2 fixation, J. Colloid Interface Sci., 2021, 603, 220–232 CrossRef CAS
.
- L. Chen, X. Dai, X. Li, J. Wang, H. Chen, X. Hu, H. Lin, Y. He, Y. Wu and M. Fan, A novel Bi2S3/KTa0.75Nb0.25O3 nanocomposite with high efficiency for photocatalytic and piezocatalytic N2 fixation, J. Mater. Chem. A, 2021, 9, 13344–13354 RSC
.
- Y. S. Wei, M. Zhang, R. Zou and Q. Xu, Metal-Organic Framework-Based Catalysts with Single Metal Sites, Chem. Rev., 2020, 120, 12089–12174 CrossRef CAS
.
- Y. Li, Y. Xia, K. Liu, K. Ye, Q. Wang, S. Zhang, Y. Huang and H. Liu, Constructing Fe-MOF-Derived Z-Scheme Photocatalysts with Enhanced Charge Transport: Nanointerface and Carbon Sheath Synergistic Effect, ACS Appl. Mater. Interfaces, 2020, 12, 25494–25502 CrossRef PubMed
.
- X. Zhao, X. Yi, S. Tian and J. Zhang, Excellent photocatalytic degradation and disinfection performance of a novel bifunctional Ag@AgSCN nanostructure with exposed {−112} facets, New J. Chem., 2018, 42, 11811–11818 RSC
.
- J. Zhang, X. Liu, Q. Liu, Y. Licao, G. Liu and X. Shi, Z-scheme AgSCN/Ag3PO4/C3N4 heterojunction with excellent photocatalytic degradation of ibuprofen, Ceram. Int., 2020, 46, 106–113 CrossRef CAS
.
- J. Song, M. Zhang, C. Yan, X. Zhao, G. Liu and J. Zhang, AgSCN/AgCl/FeOCl nanosheets heterojunction with novel interface structure and excellent photocatalytic performance, J. Alloys Compd., 2020, 836, 155544 CrossRef CAS
.
- M. Yang and J. Ma, Synthesis and characterizations of AgSCN nanospheres using AgCl as the precursor, Appl. Surf. Sci., 2009, 255, 9323–9326 CrossRef CAS
.
- S. M. Khoshfetrat, H. Khoshsafar, A. Afkhami, M. A. Mehrgardi and H. Bagheri, Enhanced Visual Wireless Electrochemiluminescence Immunosensing of Prostate-Specific Antigen Based on the Luminol Loaded into MIL-53(Fe)-NH2 Accelerator and Hydrogen Evolution Reaction Mediation, Anal. Chem., 2019, 91, 6383–6390 CrossRef CAS PubMed
.
- A. I. Ogarkov, A. S. Chernyavskii, S. G. Sakharov and K. A. Solntsev, Single-step incorporation of oh groups into the monosubstituted dodecahydro-closo-dodecaborate(2-) anion derivatives [B12H11SCN]2−, [B12H11I]2−, and [B12H11OC(O)CH3]2−, Inorg. Mater., 2011, 47, 1268–1270 CrossRef CAS
.
- E. Diana, G. Gervasio, E. Priola and E. Bonometti, A new heterometallic multiligand 3D coordination polymer: synthesis and structure of [Pb(OH)]n[Ag(SCN)(CN)]n, CrystEngComm, 2014, 16, 10040–10045 RSC
.
- X. Liu, P. Long, X. Wang, Z. Gao, Y. Lü and Z. Yi, Efficient Raman scattering response and large piezoelectricity in noncentrosymmetric MnHg(SCN)4 crystals, J. Mater. Chem. C, 2017, 5, 3238–3246 RSC
.
- Y. Tian, J. Song, Y. Zhu, H. Zhao, F. Muhammad, T. Ma, M. Chen and G. Zhu, Understanding the desulphurization process in an ionic porous aromatic framework, Chem. Sci., 2019, 10, 606–613 RSC
.
- Z. Yuan, X. Ma, X. Wu, G. Zhang, X. Wang, S. Wang and Y. Jia, Characterization of Fe5(AsO3)3Cl2(OH)4.5H2O, a new ferric arsenite hydroxychloride precipitated from FeCl3-As2O3-HCl solutions relevant to arsenic immobilization, J. Environ. Sci., 2020, 90, 205–215 CrossRef
.
- F. Dai, Y. Wang, X. Zhou, R. Zhao, J. Han and L. Wang, ZnIn2S4 decorated Co-doped NH2-MIL-53(Fe) nanocomposites for efficient photocatalytic hydrogen production, Appl. Surf. Sci., 2020, 517, 146161 CrossRef CAS
.
- L. Shi, T. Wang, H. Zhang, K. Chang, X. Meng, H. Liu and J. Ye, An Amine-Functionalized Iron(III) Metal-Organic Framework as Efficient Visible-Light Photocatalyst for Cr(VI) Reduction, Adv. Sci., 2015, 2, 1500006 CrossRef
.
- A. Alshehri and K. Narasimharao, PtOx-TiO2 anatase nanomaterials for photocatalytic reformation of methanol to hydrogen: effect of TiO2 morphology, J. Mater. Res. Technol., 2020, 9, 14907–14921 CrossRef CAS
.
- A. Das, P. M. Kumar, M. Bhagavathiachari and R. G. Nair, Hierarchical ZnO-TiO2 nanoheterojunction: A strategy driven approach to boost the photocatalytic performance through the synergy of improved surface area and interfacial charge transport, Appl. Surf. Sci., 2020, 534, 146161 CrossRef
.
- J. Yu, W. Xiong, X. Li, Z. Yang, J. Cao, M. Jia, R. Xu and Y. Zhang, Functionalized MIL-53(Fe) as efficient adsorbents for removal of tetracycline antibiotics from aqueous solution, Microporous Mesoporous Mater., 2019, 290, 109642 CrossRef CAS
.
- S. Zhang, S. Zhang, L. Song, X. Wu and S. Fang, Synthesis and photocatalytic property of a new silver thiocyanate semiconductor, Chem. Eng. J., 2014, 243, 24–30 CrossRef CAS
.
- X. Zhuang, X. Li, Y. Yang, N. Wang, Y. Shang, Z. Zhou, J. Li and H. Wang, Enhanced Sulfamerazine Removal via Adsorption–Photocatalysis Using Bi2O3–TiO2/PAC Ternary Nanoparticles, Water, 2020, 12, 2273 CrossRef CAS
.
- Q. Zhao, L. Zhang, X. Wang, X. Jia, P. Xu, M. Zhao and R. Dai, Simultaneous efficient adsorption and photocatalytic degradation of methylene blue over iron(III)-based metal–organic frameworks: a comparative study, Transition Met. Chem., 2019, 44, 789–797 CrossRef CAS
.
- D. D. Liu, Z. L. Jin, Y. K. Zhang, G. R. Wang and B. Z. Ma, Light harvesting and charge management by Ni4S3 modified metal-organic frameworks and rGO in the process of photocatalysis, J. Colloid Interface Sci., 2018, 529, 44–52 CrossRef CAS PubMed
.
- X. Han, D. Y. Xu, L. An, C. Y. Hou, Y. G. Li, Q. H. Zhang and H. Z. Wang, Ni-Mo nanoparticles as co-catalyst for drastically enhanced photocatalytic hydrogen production activity over g-C3N4, Appl. Catal., B, 2019, 243, 136–144 CrossRef CAS
.
Footnote |
† These authors contributed equally to this work and should be considered co-first authors. |
|