Open Access Article
This Open Access Article is licensed under a Creative Commons Attribution-Non Commercial 3.0 Unported Licence

Hydrophilicity and surface charge modulation of Ti3C2Tx MXene based membranes for water desalination

Laxmi Pandeya, Wentao Lianga, Armin VahidMohammadid, Teng Zhangd, Yury Gogotsid and Meni Wanunu*abc
aDepartment of Physics, Northeastern University, Boston, MA 02115, USA
bDepartment of Bioengineering, Northeastern University, Boston, MA 02115, USA
cDepartment of Chemistry and Chemical Biology, Northeastern University, Boston, MA 02115, USA
dDepartment of Materials Science and Engineering, Drexel University, Philadelphia, PA 19104, USA

Received 10th April 2024 , Accepted 29th June 2024

First published on 8th July 2024


Abstract

Lamellar membranes obtained by stacking 2D layers possess ample transport pathways due to their intricate network of interlayer gaps. This makes them suitable for molecular separation applications. However, controlling the surface chemistry of the nanochannels within the membrane to tune the desired transport properties of water and ions is challenging. Ti3C2Tx has been considered for water desalination because of its hydrophilic surface and negative surface charge. Most of the studies of Ti3C2Tx membranes have presented promising salt rejection values in forward osmosis mode, which is less practical for water purification. Here, we investigate two types of reverse osmosis MXene-based lamellar membranes consisting of Ti3C2Tx nanosheets hybridized with (i) WS2 nanosheets and (ii) polyvinyl phosphonic acid (PVPA). When hydrophilic and flexible Ti3C2Tx nanosheets are interleaved with softer and more hydrophobic WS2 nanosheets in 2[thin space (1/6-em)]:[thin space (1/6-em)]1 mass ratio, nano capillaries with Janus chemistry are created with comparable rejection to bare Ti3C2Tx membrane and threefold higher permeance values. Further, we find that decorating Ti3C2Tx nanosheets with anionic polymers improves salt rejection. Our Ti3C2Tx/PVPA composite membranes reject ∼97% of divalent ions and ∼80% of monovalent ions with ∼0.2 Lm−2 h−1 bar−1 of water permeance when tested with brackish water, and exhibit significantly improved chlorine resistance and cost benefits over the commercial Toray membranes.


1. Introduction

Meeting the increasing demand for water for drinking and irrigation is an increasingly important challenge in water security that requires new exploration of new materials and device configurations.1 One approach involves using advanced two-dimensional (2D) materials with a very large surface-to-volume ratio, as scalable production of these materials is now possible.2–4 Membrane laminates prepared from 2D materials consist of numerous interconnected interlayer pathways, which can be tuned to allow a particular type of molecule or ion to pass through them, depending on the size,5 charge,5 and other characteristics.6 Among the 2D materials, graphene oxide (GO) is most studied for nanofiltration and water desalination as GO nanosheets consist of the unoxidized hydrophobic region, which allows ultrafast water transport7 as well as the hydrophilic region, which consists of different functional groups that act as spacers.7 A challenge with GO membranes is that interactions of water molecules with the oxygenated functional groups (especially –COOH) lead to uncontrolled swelling.8 Some attempts, such as physical confinement,9 cross-linking10 and reduction of GO nanosheets5,11,12 have addressed the swelling problem in part, but these solutions are not amenable to pressure-driven water desalination.5,10 Some studies have shown promising results utilizing membranes made from transition metal dichalcogenides (MoS2, WS2) by controlling their wetting state13 and introducing spacers with covalent13–15 and non-covalent16 functionalization as the membrane is water-impermeable in its dry state without functionalization.13,14,17 MXenes, a broad class of 2D materials consisting of carbide or nitride layers terminated with surface functional groups,18 have also been explored for various applications such as energy storage,19,20 catalysis,21 biomolecule sensing22 and membrane separation.23–26 Ti3C2Tx, where T represents surface terminations such as O, OH, F, and x represents the fraction of surface groups, is the first introduced and most studied MXene.27 Most studies on Ti3C2Tx membranes have shown promising ion sieving properties, but only in forward osmosis mode.23,24,26 Some studies have used pressurized systems and either observed water permeance only25,28 or salt rejection for low salt concentrations.29 To determine whether these membranes are suitable for practical water desalination, the membranes require testing in pressure-driven mode.

Here, we have introduced two types of MXene composite membranes. (Type 1) Ti3C2Tx + WS2 composite lamellar membrane, which has a van der Waals interaction between Ti3C2Tx and WS2 nanosheets. (Type 2) Ti3C2Tx + polymer composite lamellar membrane where chemisorption of anionic polymer (polyvinyl phosphonic acid (PVPA)) on Ti3C2Tx nanosheet surface takes place. For Type 1 membranes, mixing hydrophilic and flexible Ti3C2Tx nanosheets with less hydrophilic and rigid WS2 helps tune the surface properties, which is beneficial for water desalination. The composite membrane with a 2[thin space (1/6-em)]:[thin space (1/6-em)]1 mass ratio of Ti3C2Tx and WS2 allowed a more than 3-fold increase in water flux and almost the same salt rejection as the Ti3C2Tx membrane. For Type 2 membranes, PVPA modification rendered the membrane highly negatively charged, improving salt rejection while maintaining a water permeance similar to the bare Ti3C2Tx membrane. Hydrophilicity, and surface charge modulation help improve the membrane's performance.

2. Results

2.1. Ti3C2Tx + WS2 composite membrane

Exfoliated Ti3C2Tx sheets with dimensions ranging from 10–100 μm were sonicated (up to 1.5 hours) using a 100 W ultrasonic probe at 60% amplitude to obtain nanosheets. Fig. 1a and b show an AFM image of nanosheets before and after 1.5 hours of ultrasonic probe treatment, respectively. While before sonication, the sheets appear faceted and have straight edges, upon sonication, we observed nanosheets with a more rounded edge structure and a ∼30-fold reduction in nanosheet size (Fig. S1a and b). Likewise, WS2 nanosheets obtained from the liquid phase exfoliation method (see Fig. 1c) exhibit a similar structure to Ti3C2Tx nanosheets. We prepared Ti3C2Tx membranes from different-sized nanosheets using the vacuum filtration method on 0.03 μm pore-sized poly (ether sulfone) (PES, see Methods) substrate as shown in Fig. 1d and measured X-ray diffraction (XRD) spectra. For the Ti3C2Tx membrane made of unsonicated Ti3C2Tx sheets, an intense 002 peak was observed at 6.7° with a full width at half maximum (FWHM) of 0.5°. A slight shift in the 002-peak position from 6.7° to 6.6°, but a significant reduction in peak intensity with a larger FWHM (1.0°) for the same mass per unit area of Ti3C2Tx was observed after 1.5 hours of ultrasonic probe treatment (Fig. 1e). The reduced intensity and the broad XRD peak from the membrane prepared from sonicated nanosheets are due to a less regular lamellar structure. Based on the XRD patterns, the interlayer spacing in the Ti3C2Tx membrane is 13.2–13.4 Å. An interlayer void space of 3.4–3.6 Å, obtained after subtracting the crystallographic monolayer thickness of Ti3C2Tx (9.8 Å),30–32 is minimal and may lead to slow water transport. To increase the void space, we prepared a composite membrane from a mixed dispersion of Ti3C2Tx and WS2 nanosheets in a 2[thin space (1/6-em)]:[thin space (1/6-em)]1 mass ratio using vacuum-assisted filtration. The XRD pattern of the composite membrane includes two peaks corresponding to Ti3C2Tx at 6.2° with a FWHM of 1.8° and to WS2 at 14.3° with a FWHM of 0.7° but with reduced intensity (Fig. 1d, inset), which confirms that Ti3C2Tx and WS2 nanosheets are intermixed within the membrane. The mean water contact angles of Ti3C2Tx (Fig. 1f) are slightly lower than for the composite membrane, revealing that the composite membrane is more hydrophobic than the Ti3C2Tx membrane, possibly due to the contribution of the more hydrophobic WS2 nanosheets. Slightly increased surface parameters, root mean square roughness (Rq, pixel) from 61 to 67 and average roughness (Ra, pixel) from 37 to 41, due to intermixing of different types of nanosheets were also observed (see Fig. S1d and e, and Table S1). Based on the SEM cross-section image and EDX elemental mapping (Fig. S2a), the presence of W and Ti throughout the membrane thickness further confirms the uniform distribution of Ti3C2Tx and WS2 nanosheets within the membrane. HAADF-STEM images, along with their EDX elemental maps (Fig. 1g, h, S2b–d), show that multilayer Ti3C2Tx and WS2 stack within the membrane interchangeably and with a good degree of alignment. The SEM cross-section image (Fig. 1i) shows that the membrane is ∼0.5 μm thick.
image file: d4ra02678k-f1.tif
Fig. 1 Nanosheets and membrane characterization for Ti3C2Tx + WS2 (2[thin space (1/6-em)]:[thin space (1/6-em)]1) composite membranes; (a–c) AFM images of Ti3C2Tx nanosheets before (a) and after (b) 1.5 hours of ultrasonic probe treatment, as well as WS2 nanosheets after sonication (c). Bright spots, shown by red arrows in (a), (b) and (c), might be residues. (d) Schematic showing vacuum filtration for membrane fabrication. (e) Comparison of XRD spectra before and after ultrasonic treatment; inset compares the XRD spectra of the Ti3C2Tx, WS2 and Ti3C2Tx + WS2 composite membrane (Ti3C2Tx used in the inset was treated with ultrasonic probe for 1.5 hours). (f) Water contact angle comparison of Ti3C2Tx, Ti3C2Tx + WS2, and WS2 membrane (error bars represent the standard deviations of at least three measurements). (g and h) Cross section of Ti3C2Tx + WS2 composite membrane; (g) HAADF-STEM image along with its false-color EDX elemental maps for Ti (green) and W (red) (h), and (i) side-view SEM image of the membrane. For all characterization, Ti3C2Tx + WS2 composite membranes were prepared with 2[thin space (1/6-em)]:[thin space (1/6-em)]1 mass ratio of Ti3C2Tx and WS2.

The composite membranes were tested in a cross-flow system,33 as shown in Fig. 2a and S4. First, a dispersion of Ti3C2Tx in de-ionized (DI) water with a concentration of 0.2 mg mL−1 was sonicated using a 100 W ultrasonic probe at 60% amplitude for 30 min, and the membranes were prepared by varying the WS2 and Ti3C2Tx content in the membrane and tested for desalination against sodium sulphate salt. The water permeance of the Ti3C2Tx membrane without WS2 reported in this study is smaller than reported in the previous studies.25,28 In Ti3C2Tx membranes, the water flow through the membrane depends on the distribution of surface terminations, which in turn depends on the nanosheet synthesis process. Here, Ti3C2Tx nanosheets were synthesized using a method different (direct use of hydrofluoric acid)34 from those used in previous studies. Furthermore, the applied pressure during filtration experiments was much higher (20 bar) than in the previous studies (∼1 bar). Based on an earlier study, applied pressure and electrostatic interactions between nanosheets are critical in controlling interlayer spacing. High-pressure compaction leads to the shrinkage of nanochannels, while electrostatic repulsion, resulting from negative surface charges, prevents the nanosheets from collapsing onto each other, thereby maintaining the interlayer spacing.35 As the WS2 mass ratio increases in the composite, water permeance through the membrane increases and salt rejection decreases (Fig. 2b); both changes are non-linear, possibly due to the impact of WS2 on the degree of disorder within the lamellar membrane. We find for Ti3C2Tx[thin space (1/6-em)]:[thin space (1/6-em)]WS2 that a 2[thin space (1/6-em)]:[thin space (1/6-em)]1 mass ratio is optimal.


image file: d4ra02678k-f2.tif
Fig. 2 Ti3C2Tx + WS2 composite membrane's test in cross-flow systems; (a) Illustration of Ti3C2Tx + WS2 composite membrane in the cross-flow cell. (b) Performance of Ti3C2Tx + WS2 composite membrane based on WS2 content, Ti3C2Tx was sonicated for 30 min. (c) Performance of Ti3C2Tx + WS2 composite membrane by varying sonication time of Ti3C2Tx nanosheets. (d) Salt rejection of Ti3C2Tx + WS2 composite membrane for different salts (each salt at 0.02 M concentration). (e) Stability test of Ti3C2Tx + WS2 composite membrane for up to 7 hours. In each figure, error bars represent standard deviations from >3 replicates.

Ti3C2Tx nanosheets were sonicated for up to 1.5 hours, mixed with WS2 nanosheets to prepare different membranes, and tested against 0.02 M Na2SO4 salt. The results are reported in Fig. 2c. We find that water permeance increases linearly with the sonication time of Ti3C2Tx nanosheets while salt rejection is constant. Since the nanosheet size decreases with an increasing sonication time, the number of pathways for water within the membrane increases, consequently increasing the water permeance. The mixed membrane with a mass ratio of 2[thin space (1/6-em)]:[thin space (1/6-em)]1 between Ti3C2Tx (1.5 hours of probe-sonicated nanosheets) and WS2 gives ∼90% of Na2SO4 rejection (at 0.02 M Na2SO4 concentration) and >0.6 Lm−2 h−1 bar−1 of water permeance, 3 times higher than that of the Ti3C2Tx membrane (made from 1.5 hours of sonicated nanosheets as shown in Fig. S5). The observation of higher water permeance during the vacuum filtration of mixed nanosheets, as compared to Ti3C2Tx nanosheets, indicates that the WS2 nanosheets provide less resistance to water flow (shown in Fig. S3). Previous studies have also reported higher water permeance through the WS2 membrane36 compared to the MXene membrane25 for the same thickness. Thus, water permeance increases by increasing the content of WS2 nanosheets in the mixed membrane. The altered surface chemistry due to the mixing of two kinds of nanosheets, with a similar nanosheet size (shown in Fig. S1b and c), a similar membrane thickness (shown in Fig. S9) and a similar value of zeta potential around −60 mV (shown in Fig. S6), maintains a higher Na2SO4 rejection. Different salt solutions were pressurized through the membrane at a pressure of 20 bar; the membrane rejected >85% of salts with a divalent anion and >67% of salts with a monovalent anion (shown in Fig. 2d and S7i). The rejection of monovalent salt reported here is higher than that of most of the 2D-based lamellar membranes reported in the literature10,37,38 (shown in Fig. S11) but lower than that of the TFC membrane.39 The membrane's performance was stable to within (2%) for up to 7 hours of tested time (Fig. 2e). The membrane was also tested for pressure-dependent performance, and the result is shown in Fig. S7ii. The membrane maintained >67% NaCl rejection (at 0.04 M NaCl concentration) when tested up to 32 bar of applied.

2.2. Ti3C2Tx + PVPA composite membrane

Based on the XRD spectra of the Ti3C2Tx membrane, the interlayer void space of the dry membrane (3.3 to 3.5 Å) is minimal, due to which a small amount of water permeates through the membrane. To increase interlayer spacing by a minimal amount and alter the surface chemistry, we chose polyvinyl phosphonic acid (PVPA), an anionic polymer with a molecular weight of 24[thin space (1/6-em)]000 Da and polydispersity of 1.24, as an intercalant.

The shift in the leftmost UV-vis absorbance peak from 268 nm to 274 nm (Fig. 3a) after introducing PVPA intercalant in the suspension confirms the chemisorption of PVPA by Ti3C2Tx nanosheet. The bonding nature between PVPA and Ti3C2Tx nanosheets40 may involve covalent and hydrogen bonding. Phosphorous of PVPA can interact with hydroxyl groups of Ti3C2Tx through a hetero-condensation reaction to form a P–O–Ti bond. In addition, functional groups of Ti3C2Tx, mainly [double bond, length as m-dash]O and –OH, can form hydrogen bonding with –OH and [double bond, length as m-dash]O groups coordinated to the phosphorous of PVPA. Fig. 3b compares the XRD spectra of Ti3C2Tx and Ti3C2Tx + PVPA composite membrane. The shift in the 002 XRD peak towards a smaller angle from 6.6° with a FWHM of 0.8° to 6.4° with a FWHM of 1.3° after PVPA functionalization shows that PVPA increases the interlayer void space from 3.6 Å to 4.0 Å. The zeta potentials of different dispersions were measured and compared in Fig. S6. The change in zeta potential after PVPA modification is around −20 mV at pH 7, which makes the composite membrane highly negatively charged. To further confirm the presence of PVPA within the membrane, we imaged the surface of the composite membrane using SEM and collected EDX data (see Fig. 3c). The presence of a phosphorous peak in the EDX spectrum confirms PVPA intercalation. The sulfur peak comes from the poly(ether-sulfone) substrate. The membrane's cross-section was ∼0.5 μm thick, confirmed with SEM, as shown in Fig. 3d and S9. The inset shows a high-resolution TEM image of the composite membrane with the arrows pointing to the interlayer expanded regions; the interlayer expansion might have been caused by intercalated PVPA molecules.


image file: d4ra02678k-f3.tif
Fig. 3 Characterization and performance of Ti3C2Tx + PVPA composite membrane. (a) Comparison of UV-vis spectra of Ti3C2Tx + PVPA with that of Ti3C2Tx dispersion. (b) XRD of different membranes. (c) EDX spectrum from the surface of the Ti3C2Tx + PVPA composite membrane. (d) High-resolution TEM image of a cross-section of Ti3C2Tx + PVPA composite membrane with arrows showing possible binding sites of PVPA with Ti3C2Tx nanosheets and schematic illustration of the cross-section. (e) Salt rejection and water permeance of Ti3C2Tx + PVPA composite membrane for different salts (concentration of Na2SO4 salt solution was 0.02 M and that of KCl was 0.04 M); error bars represent the standard deviations of three independent replicates. (f) Mass-dependent performance of the composite membrane; error bars represent the standard deviations of >3 replicates. Solid curves are provided to guide the eye.

For optimization, PVPA was mixed with Ti3C2Tx dispersion, and the membranes were prepared under 3 different conditions: for type I membrane, the membrane was prepared by mixing 1% PVPA with 0.05 mg mL−1 of Ti3C2Tx dispersion and drying at room temperature; for type II membrane, the membrane was prepared by mixing 1% PVPA with 0.05 mg mL−1 of Ti3C2Tx dispersion and drying at 80 °C for one day; for type III membrane, the dispersion (1% PVPA with 0.1 mg mL−1) was heated at 80 °C to 90 °C for about 20 min, and the membrane was manufactured and dried at room temperature. In Fig. S8, the performance of these three types of membranes was compared with the performance of the bare Ti3C2Tx membrane. The performance of type III membranes was better than that of other membranes. MXene and PVPA composite dispersion was further optimized by heating 1% of PVPA with 0.2 mg mL−1 of MXene at 80 °C to 90 °C for ∼20 min to improve the binding between MXene and PVPA. According to previous studies, heat helps the hetero-condensation reaction by promoting P–O–Ti covalent bonding via hydrogen bonding interactions between P–OH and Ti–OH.40,41 The membrane prepared from this dispersion was referred to as Ti3C2Tx + PVPA composite membrane. Fig. 3e shows the performance of the membrane against salts with monovalent and divalent anions. The rejection of sodium sulphate salt (0.02 M) is greater than 97%, while the rejection of potassium chloride (0.04 M) is ∼80%. Salt rejection observed here is higher than that of the functionalized MoS2 membranes,15 GO-based membranes,37,38,42 and MXene-based membranes29 reported earlier (shown in Fig. S11) but lower than that of the TFC membrane.39 The high rejection for both salts is due to the synergistic effect of charge repulsion and size exclusion, as the membrane is highly negatively charged and possesses a small interlayer spacing. A previous study suggests that increasing salt rejection is more important than increasing water permeance for energy efficient desalination.43 We have also investigated the rejection and permeance dependence on the mass of Ti3C2Tx per unit area (while keeping PVPA at 1% by mass) and found that rejection increases with the mass per unit area, but permeance decreases, as shown in Fig. 3f. We also note that the Ti3C2Tx membranes quickly delaminated from the substrate (both PES and AAO) when soaked in an aqueous solution, while PVPA functionalization improved the adhesion of the Ti3C2Tx membrane to the PES substrate.

2.3. Comparison of performance of MXene-based composite membranes

Fig. 4a and b compare the performance of different Ti3C2Tx-based membranes prepared in this study, all having a similar thickness (as evidenced by SEM cross-section images, see Fig. S9), under brackish water (0.02 M Na2SO4, 0.04 M NaCl) and seawater (0.5 M NaCl) conditions. Surface chemistry modulation by mixing Ti3C2Tx and WS2 with different hydrophilicity in a 2[thin space (1/6-em)]:[thin space (1/6-em)]1 mass ratio but similar surface charge and nanosheet size helps to increase the water permeance while maintaining a similar salt rejection as a 100% Ti3C2Tx membrane, whereas surface charge modulation with the help of anionic polyelectrolyte improves salt rejection while keeping similar water permeance as the Ti3C2Tx membrane as shown in Fig. 4a. Ti3C2Tx + PVPA membrane exhibits superior rejection of NaCl compared to Ti3C2Tx + WS2 (2[thin space (1/6-em)]:[thin space (1/6-em)]1) membrane in both brackish and seawater conditions (see Fig. 4b).
image file: d4ra02678k-f4.tif
Fig. 4 Effect of hydrophilicity and surface charge modulation on the performance of MXene-based membranes. Comparison of performance of Ti3C2Tx-based membranes in the cross-flow filtration system for 0.02 M Na2SO4 (a), and 0.04 M and 0.5 M NaCl (b). Error bars represent the standard deviations of at least three replicates.

2.4. Chlorine resistance

Chlorination is an essential step in water purification and desalination processes to control microbes and other fouling agents in the water. The current water desalination industry heavily depends on polymeric membranes whose performance degrades when exposed to chlorine in solution. So, there should be three additional steps in addition to desalination to protect the membrane from chlorination. First, the water is chlorinated to kill microbes present in the feed water, and next, the water feed is dechlorinated before passing to the desalination chamber, and finally, desalinated water is chlorinated again before sending to the water distribution center; these additional steps make the desalination industry costly.44 The double-chlorination step is necessary because the desalination membranes have poor chlorine tolerance. Here, we have compared the chlorine tolerance of Ti3C2Tx + PVPA with that of Toray membranes with and without exposure to 4000 ppmh of NaOCl in cross-flow for 0.02 M Na2SO4. We find that both salt and water permeation increase after bleach treatment through both types of membranes, while the relative level of degradation in the Ti3C2Tx + PVPA membrane is much lower than for the Toray membrane. The increase in water flux after chlorine treatment is 24% through Ti3C2Tx + PVPA membrane and 39% through Toray membrane (see Fig. 5). This result confirms that our Ti3C2Tx + PVPA is ∼62% more resistant to chlorine exposure than the commercial Toray membrane, with a slightly superior salt rejection. However, the Toray membrane still has a higher water permeance than our membranes. Further optimization of the 2D membrane layer (flake size, membrane thickness, porosity, chemical intercalants) may help to further increase the desalination performance of MXene-based membranes.
image file: d4ra02678k-f5.tif
Fig. 5 Comparison of chlorine-resistance test of our Ti3C2Tx + PVPA membranes Toray Flat sheet membranes, UTC-82V PA RO membrane (Sterlitech). Membranes (not treated with NaOCl solution and treated with 4000 ppmh of NaOCl solution) were tested in a cross-flow system with 0.02 M Na2SO4 as feed solution. Error bars represent the standard deviations of at least three replicates.

3. Conclusions

We have investigated Ti3C2Tx-based membranes comprising surface-functionalized nanosheets for water desalination and found that an optimum balance between water permeance and salt rejection requires optimization of the preparation method and Ti3C2Tx surface functionalization. Composite membranes that contain WS2 added to the Ti3C2Tx sheets offer improved water permeance without compromising salt rejection at optimal mass ratio of Ti3C2Tx and WS2, presumably due to the more hydrophobic surface properties of WS2. On the other hand, hydrophilic polymer-based functionalization with the help of surface terminations present on the Ti3C2Tx nanosheet surface helped improve salt rejection while maintaining water permeance similar to the Ti3C2Tx membrane. Both membranes maintain high salt rejection when tested in the cross-flow pressurized system. However, there is still room for improvement in both salt rejection and water permeance of the membranes studied here compared to the commercial membrane. Ti3C2Tx + PVPA membrane can also tolerate 4000 ppmh of chlorine (sodium hypochlorite) exposure significantly better than the commercially available Toray membrane, which confirms the applicability of Ti3C2Tx-based membranes for water desalination. Given its low cost of manufacture, with further exploration of MXene membrane functionalization, we anticipate that MXene membranes for desalination/separation can reach commercialization in the coming years.

4. Methods and materials

4.1. 2D nanosheets synthesis and membrane fabrication

Ti3C2Tx nanosheets were synthesized as described in a previous work.45 The Ti3C2Tx suspension was sonicated with the ultrasonic probe (Hielscher UP100H) at 60% amplitude for 30–90 min to reduce the size of nanosheets. The suspension was then centrifuged at 3500 rpm for 1 hour, and the supernatant was collected for further experiments. A well-established liquid phase exfoliation method46 was utilized to obtain few-layered WS2 nanosheets. In short, 1.5 g of bulk WS2 powder (Sigma-Aldrich) with ∼2 μm lateral-sized sheets was mixed with 100 mL of NMP (Fisher chemicals) solvent in a round bottom flask. The solution was treated with ultrasound in an ultrasonic bath (Branson 2510 Ultrasonic) for 5 hours and then in an ultrasonic probe for 3 hours to get desired-sized nanosheets. Then, the nanosheets were transferred from NMP to water. To remove the unexfoliated WS2 sheets, the dispersion was centrifuged at 3000 rpm for 20 min. To eliminate unwanted chemicals, the suspension was dialyzed twice against 1 L of deionized water overnight.

Ti3C2Tx and WS2 were mixed in different mass ratios to fabricate various composite membranes. PES (0.03 μm pore-sized poly(ether sulfone), Sterlitech) was covered with an impermeable film, leaving a 2.5 cm diameter circular membrane area at the center. The mixed nanosheets were collected on a substrate using vacuum-assisted filtration with a mass loading of 1222 mg m−2, unless otherwise mentioned. The membrane was left at room temperature overnight to dry. Quick-curing silicone elastomer (Ecoflex 5, Smooth-On) was applied to seal the gap between the deposited composite membrane and the impermeable membrane. The prepared membrane is shown in Fig. S4. The optimized result was observed for the 2[thin space (1/6-em)]:[thin space (1/6-em)]1 mass ratio of MXene and WS2, so further experiments have proceeded with the same mass ratio.

The Ti3C2Tx dispersions with concentrations of 0.05 mg mL−1 to 0.2 mg mL−1 were mixed with 0.5% to 1% of polyvinyl phosphonic acid PVPA. The optimized solution was prepared by mixing 0.02 mg mL−1 of Ti3C2Tx dispersion with 0.5% to 1% of PVPA, and the suspension was heated at 80–90 °C for 20 min to facilitate PVPA binding on Ti3C2Tx nanosheets and cooled to room temperature and stored at 4 °C. The mixed solution was vacuum filtered to collect these modified nanosheets on the 0.03 μm pore-sized PES substrate.

4.2. Characterization

The nanosheets obtained after centrifugation were diluted in water, then deposited on a smooth silicon wafer and scanned using FastScan AFM (Bruker) using ScanAsyst air mode to see the size distribution of nanosheets in the dispersion. ImageJ was used to analyze the AFM images. X-ray diffraction (XRD) (Rigaku Ultima IV) with a Cu Kα radiation source operating at 40 kV and 44 mA was used to observe the XRD patterns of the dry and wet membranes. Interlayer spacing was calculated using Bragg's law:
 
2d[thin space (1/6-em)]sin(θ) = (1)
where d is interlayer spacing, θ is the Bragg's angle which is the angle at the position of (002) peak, n is an integer representing diffraction series, and λ is the wavelength of the X-ray used.

The pH of the dispersion was adjusted to neutral by adding hydrochloric acid and potassium hydroxide drop by drop and continuously stirring the solution using a magnetic stirrer. The zeta potential and size distribution of different dispersions at neutral pH were measured using Zetasizer Nano ZS.

JEOL JSM-7000F was used for SEM and EDX. FEI Titan Themis 300 STEM in bright field mode was used for high-resolution TEM imaging.

Contact angles were measured using a homemade device, where images were recorded using a digital camera with Amscope software.

4.3. Membrane performance

For the filtration experiment, a CF016 cross-flow cell (Sterlitech) consisting of 39 mm long, 39 mm wide, and 2.3 mm deep rectangular channel was used. The membrane was fitted in the cross-flow cell and the feed tank was filled with the salt solution. The permeate was collected after the high-pressure pump (Hydra-cell pump, Wanner Engineering, Inc) pressurized the salt solution at 20 bar for brackish water and at 38 bar for sea water condition respectively through Ti3C2Tx, WS2 and Ti3C2Tx + WS2 membranes, and at 18 bar through the Toray Flat sheet membrane (UTC-82V PA RO membrane, Sterlitech). The active area of the Toray membrane was 20.6 cm2 and that of MXene based membrane was 1.1–3.1 cm2. The flow rate was 2 L min−1 for all experiments. Prior to beginning experiments, membranes were dried overnight in the air before starting desalination. Permeate flux was calculated with the following formula:
 
image file: d4ra02678k-t1.tif(2)
where ΔV is permeated volume, A – effective membrane area, t – time required to collect a specific volume of permeate, and ΔP is the applied pressure and Δπ is osmotic pressure of the salt solution. To calculate salt rejection, the following formula was used:
 
image file: d4ra02678k-t2.tif(3)
where Cp is the concentration of salt in permeate and Cf is the concentration of salt in feed. First, the conductivities of feed and permeate were measured using a Mettler Toledo InLab 751-4mm Conductivity sensor, and the concentration of the salt solution was evaluated from the conductivity vs. concentration curve. The rejection value calculated from conductivity is the same as that calculated from concentration since concentration and conductivity are linearly related, as shown in Fig. S10.

4.4. Chlorine resistance

Membranes were immersed in 4000 ppm of NaOCl for 1 h for the chlorine-resistance test. Then, membranes were tested in a cross-flow filtration system against 0.02 M Na2SO4. Applied pressures were in the range of 18–20 bar.

Data availability

All data collected for this manuscript is available in https://figshare.com/s/17fbd60939147b766379.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

The authors are grateful to Dr Mehrnaz Mojtabavi for training on the use of MXenes in this work and for providing helpful suggestions. The authors thank Professor Sanjeev Mukerjee (Northeastern University) for the use of XRD for membrane characterization, Professor Ke Zhang (Northeastern University) for the use of the ZetaSizer Nano ZS for nanosheet characterization, and Dr Shirin Kaboli for her assistance with an experiment. The authors acknowledge the National Institutes of Health (R21HG011689) for funding this work.

References

  1. A. Boretti and L. Rosa, npj Clean Water, 2019, 2, 15 CrossRef.
  2. R. Yang, Y. Fan, L. Mei, H. S. Shin, D. Voiry, Q. Lu, J. Li and Z. Zeng, Nat. Synth., 2023, 2, 101–118 CrossRef.
  3. Q. Zhang, L. Mei, X. Cao, Y. Tang and Z. Zeng, J. Mater. Chem. A, 2020, 8, 15417–15444 RSC.
  4. C. E. Shuck, A. Sarycheva, M. Anayee, A. Levitt, Y. Zhu, S. Uzun, V. Balitskiy, V. Zahorodna, O. Gogotsi and Y. Gogotsi, Adv. Eng. Mater., 2020, 22, 1901241 CrossRef CAS.
  5. Y. Han, Z. Xu and C. Gao, Adv. Funct. Mater., 2013, 23, 3693–3700 CrossRef CAS.
  6. P. Sun, F. Zheng, M. Zhu, Z. Song, K. Wang, M. Zhong, D. Wu, R. B. Little, Z. Xu and H. Zhu, ACS Nano, 2014, 8, 850–859 CrossRef CAS.
  7. R. R. Nair, H. A. Wu, P. N. Jayaram, I. V. Grigorieva and A. K. Geim, Science, 2012, 335, 442–444 CrossRef CAS PubMed.
  8. C.-N. Yeh, K. Raidongia, J. Shao, Q.-H. Yang and J. Huang, Nat. Chem., 2015, 7, 166–170 CrossRef CAS.
  9. J. Abraham, K. S. Vasu, C. D. Williams, K. Gopinadhan, Y. Su, C. T. Cherian, J. Dix, E. Prestat, S. J. Haigh, I. V. Grigorieva, P. Carbone, A. K. Geim and R. R. Nair, Nat. Nanotechnol., 2017, 12, 546–550 CrossRef CAS.
  10. M. Hu and B. Mi, Environ. Sci. Technol., 2013, 47, 3715–3723 CrossRef CAS PubMed.
  11. H. Liu, H. Wang and X. Zhang, Adv. Mater., 2015, 27, 249–254 CrossRef CAS PubMed.
  12. K. Guan, S. Wang, Y. Ji, Y. Jia, L. Zhang, K. Ushio, Y. Lin, W. Jin and H. Matsuyama, J. Mater. Chem. A, 2020, 8, 25880–25889 RSC.
  13. E. Hoenig, S. E. Strong, M. Wang, J. M. Radhakrishnan, N. J. Zaluzec, J. L. Skinner and C. Liu, Nano Lett., 2020, 20, 7844–7851 CrossRef CAS PubMed.
  14. L. Ries, E. Petit, T. Michel, C. C. Diogo, C. Gervais, C. Salameh, M. Bechelany, S. Balme, P. Miele, N. Onofrio and D. Voiry, Nat. Mater., 2019, 18, 1112–1117 CrossRef CAS PubMed.
  15. W. Hirunpinyopas, E. Prestat, S. D. Worrall, S. J. Haigh, R. A. W. Dryfe and M. A. Bissett, ACS Nano, 2017, 11, 11082–11090 CrossRef CAS PubMed.
  16. B. Sapkota, W. Liang, A. VahidMohammadi, R. Karnik, A. Noy and M. Wanunu, Nat. Commun., 2020, 11, 2747 CrossRef CAS PubMed.
  17. Z. Wang, Q. Tu, S. Zheng, J. J. Urban, S. Li and B. Mi, Nano Lett., 2017, 17, 7289–7298 CrossRef CAS PubMed.
  18. B. Anasori, M. R. Lukatskaya and Y. Gogotsi, Nat. Rev. Mater., 2017, 2, 16098 CrossRef CAS.
  19. M. R. Lukatskaya, S. Kota, Z. Lin, M.-Q. Zhao, N. Shpigel, M. D. Levi, J. Halim, P.-L. Taberna, M. W. Barsoum, P. Simon and Y. Gogotsi, Nat. Energy, 2017, 2, 17105 CrossRef CAS.
  20. A. VahidMohammadi, A. Hadjikhani, S. Shahbazmohamadi and M. Beidaghi, ACS Nano, 2017, 11, 11135–11144 CrossRef CAS.
  21. Z. W. Seh, K. D. Fredrickson, B. Anasori, J. Kibsgaard, A. L. Strickler, M. R. Lukatskaya, Y. Gogotsi, T. F. Jaramillo and A. Vojvodic, ACS Energy Lett., 2016, 1, 589–594 CrossRef CAS.
  22. M. Mojtabavi, A. VahidMohammadi, W. Liang, M. Beidaghi and M. Wanunu, ACS Nano, 2019, 13, 3042–3053 CrossRef CAS PubMed.
  23. Z. Lu, Y. Wei, J. Deng, L. Ding, Z.-K. Li and H. Wang, ACS Nano, 2019, 13, 10535–10544 CrossRef CAS PubMed.
  24. L. Ding, L. Li, Y. Liu, Y. Wu, Z. Lu, J. Deng, Y. Wei, J. Caro and H. Wang, Nat Sustainability, 2020, 3, 296–302 CrossRef.
  25. C. E. Ren, K. B. Hatzell, M. Alhabeb, Z. Ling, K. A. Mahmoud and Y. Gogotsi, J. Phys. Chem. Lett., 2015, 6, 4026–4031 CrossRef CAS PubMed.
  26. C. E. Ren, M. Alhabeb, B. W. Byles, M.-Q. Zhao, B. Anasori, E. Pomerantseva, K. A. Mahmoud and Y. Gogotsi, ACS Appl. Nano Mater., 2018, 1, 3644–3652 CrossRef CAS.
  27. M. Naguib, M. Kurtoglu, V. Presser, J. Lu, J. Niu, M. Heon, L. Hultman, Y. Gogotsi and M. W. Barsoum, Adv. Mater., 2011, 23, 4248–4253 CrossRef CAS PubMed.
  28. G. Zeng, Q. Lin, K. Wei, Y. Liu, S. Zheng, Y. Zhan, S. He, T. Patra and Y.-H. Chiao, J. Mater. Sci., 2021, 56, 6814–6829 CrossRef CAS.
  29. J. Zhu, L. Wang, J. Wang, F. Wang, M. Tian, S. Zheng, N. Shao, L. Wang and M. He, ACS Nano, 2020, 14, 15306–15316 CrossRef CAS.
  30. J. Halim, M. R. Lukatskaya, K. M. Cook, J. Lu, C. R. Smith, L.-Å. Näslund, S. J. May, L. Hultman, Y. Gogotsi, P. Eklund and M. W. Barsoum, Chem. Mater., 2014, 26, 2374–2381 CrossRef CAS.
  31. X. Wang, X. Shen, Y. Gao, Z. Wang, R. Yu and L. Chen, J. Am. Chem. Soc., 2015, 137, 2715–2721 CrossRef CAS PubMed.
  32. A. Lipatov, M. Alhabeb, M. R. Lukatskaya, A. Boson, Y. Gogotsi and A. Sinitskii, Adv. Electron. Mater., 2016, 2, 1600255 CrossRef.
  33. W. Koros, Y. Ma and T. Shimidzu, Pure Appl. Chem., 1996, 68, 1479–1489 CrossRef CAS.
  34. T. S. Mathis, K. Maleski, A. Goad, A. Sarycheva, M. Anayee, A. C. Foucher, K. Hantanasirisakul, C. E. Shuck, E. A. Stach and Y. Gogotsi, ACS Nano, 2021, 15, 6420–6429 CrossRef CAS.
  35. H. Huang, Y. Mao, Y. Ying, Y. Liu, L. Sun and X. Peng, Chem. Commun., 2013, 49, 5963–5965 RSC.
  36. L. Sun, Y. Ying, H. Huang, Z. Song, Y. Mao, Z. Xu and X. Peng, ACS Nano, 2014, 8, 6304–6311 CrossRef CAS PubMed.
  37. Q. Yang, Y. Su, C. Chi, C. T. Cherian, K. Huang, V. G. Kravets, F. C. Wang, J. C. Zhang, A. Pratt, A. N. Grigorenko, F. Guinea, A. K. Geim and R. R. Nair, Nat. Mater., 2017, 16, 1198–1202 CrossRef CAS PubMed.
  38. Y. Han, Y. Jiang and C. Gao, ACS Appl. Mater. Interfaces, 2015, 7, 8147–8155 CrossRef CAS.
  39. M. Kadhom and B. Deng, J. Water Proc. Engineering, 2019, 30, 100542 CrossRef.
  40. P. J. Hotchkiss, S. C. Jones, S. A. Paniagua, A. Sharma, B. Kippelen, N. R. Armstrong and S. R. Marder, Acc. Chem. Res., 2012, 45, 337–346 CrossRef CAS PubMed.
  41. G. Guerrero, P. H. Mutin and A. Vioux, Chem. Mater., 2001, 13, 4367–4373 CrossRef CAS.
  42. A. Akbari, P. Sheath, S. T. Martin, D. B. Shinde, M. Shaibani, P. C. Banerjee, R. Tkacz, D. Bhattacharyya and M. Majumder, Nat. Commun., 2016, 7, 10891 CrossRef CAS.
  43. J. R. Werber, A. Deshmukh and M. Elimelech, Environ. Sci. Technol. Lett., 2016, 3, 112–120 CrossRef CAS.
  44. J. M. Gohil and A. K. Suresh, J. Membr. Sci., 2017, 541, 108–126 CrossRef CAS.
  45. M. Mojtabavi, W.-Y. Tsai, A. VahidMohammadi, T. Zhang, Y. Gogotsi, N. Balke and M. Wanunu, Small, 2022, 18, 2105857 CrossRef CAS PubMed.
  46. J. N. Coleman, M. Lotya, A. O'Neill, S. D. Bergin, P. J. King, U. Khan, K. Young, A. Gaucher, S. De, R. J. Smith, I. V. Shvets, S. K. Arora, G. Stanton, H.-Y. Kim, K. Lee, G. T. Kim, G. S. Duesberg, T. Hallam, J. J. Boland, J. J. Wang, J. F. Donegan, J. C. Grunlan, G. Moriarty, A. Shmeliov, R. J. Nicholls, J. M. Perkins, E. M. Grieveson, K. Theuwissen, D. W. McComb, P. D. Nellist and V. Nicolosi, Science, 2011, 331, 568 CrossRef CAS PubMed.

Footnote

Electronic supplementary information (ESI) available. See DOI: https://doi.org/10.1039/d4ra02678k

This journal is © The Royal Society of Chemistry 2024