A.
Swanepoel
ab,
I.
du Preez
a,
T.
Mahlangu
a,
A.
Chetty
a and
B.
Klumperman
*b
aPolymers and Composites, Materials Science and Manufacturing, Council for Scientific and Industrial Research, Pretoria, South Africa
bDepartment of Chemistry and Polymer Science, Stellenbosch University, Stellenbosch, South Africa. E-mail: bklump@sun.ac.za
First published on 13th February 2015
Fluorescent dye-doped poly(styrene-co-maleimide) nanoparticles were synthesised and functionalized with amine groups and avidin and the dye-loading was varied. The nanoparticles showed great potential as bioprobes when conjugated with biotinylated antibodies.
High molecular weight PSMA was obtained from Polyscope (Geleen, The Netherlands) with a weight average molecular weight of 80000 g mol−1 (Đ ≅ 2) and a maleic anhydride content of 26 wt%. Exalite 613 (Perylene Red) dye was purchased from Exciton Inc (USA). Formaldehyde (37% aqueous solution) and 1,4-diaminobutane (DAB) were obtained from Sigma. 1-[3-(Dimethylamino)propyl]-3-ethylcarbodiimide methiodide (EDC) (Aldrich), N-hydroxysuccinimide (NHS) (Aldrich), bovine serum albumin (BSA) (Fluka), rabbit anti Escherichia coli:biotin antibodies (AdB Serotec) and avidin from egg white were used for bioconjugation, as well as Tween 20 (Aldrich), trisma hydrochloride (Tris–HCl) (Aldrich) and biotin(5-fluorescein) (B5F) (Sigma). Phosphate buffer saline (PBS) at 0.1 M (1×) was prepared and used for nanoparticle preparation and for preparation of E. coli suspensions.
Dye-doped PSMI nanoparticles were prepared via the imidization of PSMA in a 250 mL picoclave reactor (Büchi, Switzerland). The reactor was charged with PSMA (20 g), deionised water (100 mL), ammonium hydroxide solution (5 mL, 25%), and Exalite 613 dye (5 mg, 7.5 mg or 10 mg). Imidization was allowed to proceed at a bath temperature of 180 °C, with stirring at 1000 rpm, for 6 hours. After completion of the reaction and cooling of the latex, nanoparticle dispersions were dialysed with a 10000 molecular weight cut off snake skin dialysis tube to remove unreacted molecules. PSMI nanoparticles were consecutively functionalized with molar excesses of formaldehyde and DAB, and dialysed after each step, in order to introduce reactive amine groups onto the nanoparticle surfaces. All reactions were performed in the liquid media of the nanoparticle dispersion. The proposed reactions for nanoparticle synthesis and surface functionalization are shown in Scheme 1.
Scheme 1 Reaction scheme for the imidization of PSMA to PSMI and the surface functionalization of the PSMI with formaldehyde and DAB. |
The molecular structure of Exalite 613 as given by the supplier is shown in Fig. 1. Exalite 613, apart from its excellent stability and fluorescent intensity, is also hydrophobic in nature. It was postulated that, upon addition of a hydrophobic dye to the aqueous suspension in the reactor, the dye would preferably be encapsulated inside the nanoparticles rather than remain in the aqueous media. Interaction between dye and PSMI was thus expected to be either physical in nature, or as a result of π–π stacking between the aromatic rings of the styrene and the dye molecules.
Avidin was attached to amine-functionalized dye-loaded NPs via a published method using EDC and NHS.12 It was postulated that the amine groups functionalised onto the nanoparticles would form amide bonds with carboxylic acids present on the avidin molecule, a process that would be mediated via carbodiimide chemistry. The reaction mechanism is shown in Scheme 2. Nanoparticle dispersions were reacted with EDC, NHS and avidin in a 0.05% PBS-Tween 20 solution for 24 hours at 37 °C while being gently agitated. The nanoparticles were washed and resuspended in a Tris–HCl buffer with a 0.05% BSA content and incubated for 1 hour at 25 °C under gentle agitation to block any unreacted sites. The avidin modified nanoparticles were resuspended in PBS-Tween with rabbit anti-E. coli biotinylated antibodies at 37 °C for 1 hour, and after washing was resuspended in 1× PBS-Tween (0.05%) solution for use with bacteria.
Scheme 2 Proposed reaction mechanism for the carbodiimide assisted bioconjugation of the PSMI nanoparticle surfaces with avidin. |
Quantitative detection of avidin immobilized onto the nanoparticle surfaces was performed indirectly via quenching of the inherent fluorescence of a B5F conjugate by avidin present in the liquid supernatant separated from the bioconjugated nanoparticles.4 Titration assays were performed with both the nanoparticle supernatant and pure avidin, and the fluorescence of the solutions measured with a spectrofluorometer at λex/λem = 485 nm/528 nm.
E. coli K-12 suspensions were prepared via serial dilutions and contacted with 0.02 mg of dye-doped nanoparticles for 1 hour under gentle agitation. The samples were also stained with SYTO 9 green fluorescent nucleic acid stain and viewed with a fluorescence confocal microscope. E. coli cells contacted with dye-doped nanoparticles were added to 1 mL of a 2.5% glutaraldehyde solution and fixed for an hour for sectioning and imaging via SEM.
The imidization of PSMA to PSMI as well as dye-doping and surface functionalization of the PSMI nanoparticles was characterized via ATR-FT-IR spectroscopy. The FT-IR spectra of pristine PSMI, dye-doped PSMI and pure Exalite 613 dye are given Fig. 2. Successful imidization of PSMA is evidenced by the appearance of characteristic peaks at 1709 cm−1, (CO or N–CO stretch, imide I), 1345 cm−1 and at 1177 cm−1 (imide II and imide III bending respectively), all indicative of imide groups. Comparison of the FT-IR spectra of the pristine and the dye-doped PSMI nanoparticles showed no differences in characteristic absorption peaks detected. Surface functionalization with an excess of formaldehyde yielded a new characteristic peak at 1400 cm−1, and this peak increased in intensity after the addition of the diamine compound, as indicated in Fig. 3. The appearance of this peak was attributed to the additional CH2–OH linkages introduced onto the NPs after formaldehyde functionalization and additional CH2 linkages introduced after amine surface functionalization. Amine functionalization resulted in the appearance of a significant peak at 1555 cm−1, indicative of primary N–H bending. The appearance of this peak confirmed successful amine surface functionalization (indicated by arrows on the graph).
Fig. 2 FT-IR absorption spectra of (a) pristine PSMI nanoparticles, (b) pure reference Exalite 613 dye and (c) dye-doped PSMI nanoparticles. |
The size and morphology of the pristine and dye-doped PSMI NPs characterized via TEM displayed a narrow size range distribution with average particle sizes of between 20 and 50 nm, as shown in Fig. 4. Surface functionalization with formaldehyde and DAB as well as dye-doping did not alter the size or morphology of the particles when compared to the pristine nanoparticles.
The glass transition temperature (Tg) of the PSMI nanoparticles was determined via differential scanning calorimetry (DSC). The Tg of the pristine PSMI NPs was found to be 179 °C, which is in good agreement with the published value of 181 °C for PSMI with a 26% maleimide content.11 Dye-doped PSMI nanoparticles showed a Tg of 183 °C. The effect of surface functionalization on the Tg of dye-doped nanoparticles is shown in Table 1.
Sample | T g (°C) |
---|---|
PSMI nanoparticles | 183 ± 0.1 |
Nanoparticles functionalized with formaldehyde | 190 ± 0.1 |
Nanoparticles functionalized with DAB | 190 ± 0.9 |
For the surface-functionalized nanoparticles (with formaldehyde and subsequently DAB), the Tg increased significantly to 190 °C when compared to the non-functionalized PSMI nanoparticles. This increase could be explained by inter- and intramolecular interactions between the newly introduced hydroxyl group terminated structure that effectively replaced the H atom of the maleimide ring. This is in spite of the disappearance of the strong hydrogen-bonding N–H of the original maleimide as a result of functionalization. This increase also means that the nanoparticles are always far below their Tg and will act as rigid glassy materials.
In order to assess the stability of the nanoparticle dispersion, zeta-potentials were measured via photon correlation spectroscopy. The pure PSMI nanoparticles possessed high negative zeta-potentials of −67.3 ± 1.3 mV (at in situ pH of 7.1), corresponding well with previously reported values11 and indicating good particle stability. These high negative surface charges were not affected by dye loading, with a charge of −67.8 ± 1.3 mV recorded. However, upon amine modification, the surface charge of the PSMI nanoparticles were (in 1× PBS at pH 7.4) −32.3 ± 0.8 mV. The reduction in surface charge is due to partial charge neutralisation due to the amine groups. The nanoparticles would however still be stable for the bioconjugation process as particle stability is widely accepted to be associated with surface charges of greater than ±30 mV.13
Spectrofluorometry results of the pure reference dye indicated a maximum absorption peak at 569 nm and a maximum emission peak at 600 nm, as shown in Fig. 5. The position of this maximum emission peak was not altered by encapsulation of the dye into the PSMI nanoparticles, as can be seen from the emission profiles of dye-doped PSMI nanoparticles shown in Fig. 6.
Fig. 6 Comparison of the fluorescence emission intensity of 0.3 mg mL−1 of the 5%, 7% and 10% dye-loaded nanoparticles, respectively. |
Comparison of the emission intensity profiles of the 5%, 7% and 10% dye-loaded nanoparticles (see Fig. 6) indicated that for a similar particle concentration of 0.3 mg mL−1, the 10% dye-loaded nanoparticles showed the highest emission intensity. Fluorescence emission intensity was measured for serial dilutions of the pure reference Exalite 613 dye as well as for serial dilutions of nanoparticles loaded with 5%, 7% and 10% dye-loadings. A linear relationship between reference dye concentration and emission intensity was established at reference dye concentrations of 0.1 μg mL−1 or lower, as seen in Fig. 7. The three different concentrations of dye-loaded nanoparticles showed linear relationships between nanoparticle concentration and emission intensity at less than 0.4 to 1 mg mL−1, as shown in Fig. 8. The data was fitted with linear regression curves. The emission intensity of an arbitrary concentration of reference dye was compared to that of an equivalent concentration of dye-doped nanoparticles (determined via the weight % of dye loaded to PSMI polymer during synthesis) using the regression curves fitted to the data shown in Fig. 7 and 8.
Fig. 8 Relationship between fluorescence intensity and nanoparticle concentration for the 5%, 7% and 10% dye-loaded nanoparticles, respectively. |
Based on these calculations it was concluded that the fluorescence intensity of the encapsulated dye was close to that of the pure reference dye in solution.
Quantification of the immobilized avidin was performed indirectly using a B5F conjugate.12 In the presence of avidin, the inherent fluorescence of the B5F conjugate is quenched as a result of the reaction between biotin on the conjugate and avidin in solution. A normalized curve was constructed that indicated the quenching of fluorescence of a specific concentration of B5F associated with a specific avidin concentration (shown in Fig. 9). A linear regression line with descriptive equation was fitted to the normalized curve. The avidin concentration in the supernatant was determined by correlating the maximum amount of fluorescence quenching inflicted on 52.5 μL of a 1 μg mL−1 solution of the B5F conjugate by different concentrations of nanoparticle supernatant samples to this normalized curve. A volume of 150 μL of each point in the dilution series of supernatant was analysed via spectrofluorometry, and the inflection point (point of minimum fluorescent intensity) was taken as the point at which all avidin present in the sample quenched the total concentration of B5F conjugate used.14 The difference between this minimum fluorescence signal and the fluorescence signal generated by the total volume of 52.5 μL of B5F conjugate only was correlated to an avidin concentration via the standard curve shown in Fig. 9. Using this method it was determined that only 6% of the total avidin added to the nanoparticles was present in the nanoparticle supernatant, and thus not conjugated to the nanoparticle surfaces. This indicates that 94% of the avidin added to the pure PSMI NPs during bioconjugation was immobilized onto the NP surfaces.
Fig. 9 Avidin standard curve depicting the change in fluorescence of a B5F conjugate resulting from a known concentration of avidin. |
Fixed and sectioned E. coli bacteria contacted with anti-E. coli dye-doped PSMI nanoparticles displayed distinctively rougher surfaces when compared to the native E. coli not contacted with nanoparticles, as shown in Fig. 10a and b, respectively. The increased surface roughness of the bacteria contacted with nanoparticles could thus be taken as a positive indication of successful binding between nanoparticles and the targeted receptors on the E. coli cell walls.
Fig. 10 SEM images of E. coli contacted with dye-doped PSMI nanoparticles conjugated with biotinylated antibodies (a) and control E. coli K-12 bacteria samples (b). |
Confocal fluorescence microscopy images of E. coli contacted with dye-loaded bioconjugated PSMI nanoparticles and counterstained with SYTO 9 green fluorescent nucleic acid stain are shown in Fig. 11. The E. coli present could be clearly identified by the fluorescent signals generated by the clustering of the anti-E. coli dye-loaded nanoparticles around the individual cells, as demonstrated in Fig. 11a. Fluorescent signals generated by the E. coli could be distinguished from background noise by the characteristic size and shape of the cells, and was confirmed by a SYTO 9 counterstain, as shown in Fig. 11b. Noise signals from unbound nanoparticles were expected as an excess of nanoparticles were added to the E. coli samples in order to ensure that all cells present would be labelled successfully.
Fig. 11 Confocal fluorescence microgaphs of E. coli K-12 cells labelled with (a) dye-loaded bioconjugated PSMI nanoparticles, and (b) counterstained with SYTO 9 nucleic acid stain. |