Synergetic effect in water treatment with mesoporous TiO2/BDD hybrid electrode

Norihiro Suzuki *a, Akihiro Okazakib, Haruo Kuriyamab, Izumi Serizawab, Yuki Hiramic, Aiga Harac, Yuiri Hiranoc, Yukihiro Nakabayashiae, Nitish Royaf, Chiaki Terashimaa, Kazuya Nakataacg, Ken-ichi Katsumataad, Takeshi Kondoc, Makoto Yuasac and Akira Fujishimaa
aPhotocatalysis International Research Center, Research Institute for Science and Technology, Tokyo University of Science, 2641 Yamazaki, Noda, Chiba 278-8510, Japan. E-mail: suzuki.norihiro@rs.tsu.ac.jp
bORC Manufacturing Co., Ltd, 4896 Tamagawa, Chino, Nagano 391-0011, Japan
cFaculty of Science and Technology, Tokyo University of Science, 2641 Yamazaki, Noda, Chiba 278-8510, Japan
dFaculty of Industrial Science and Technology, Tokyo University of Science, 6-3-1 Niijyuku, Katsushika, Tokyo 125-8585, Japan
eFaculty and Graduate School of Urban Environmental Sciences, Department of Applied Chemistry for Environment, Tokyo Metropolitan University, 1-1 Minami-Osawa, Hachioji, Tokyo 192-0397, Japan
fDepartment of Chemistry, University of North Bengal, Raja Rammohunpur, Darjeeling, West Bengal-734013, India
gGraduate School of Bio-Applications and Systems Engineering, Tokyo University of Agriculture and Technology, 2-24-16 Nakacho, Koganei, Tokyo 184-0012, Japan

Received 9th December 2019 , Accepted 24th December 2019

First published on 8th January 2020


Abstract

Boron-doped diamond (BDD) electrodes have a wide potential window and can produce ozone by water electrolysis at high voltage. Though ozone has strong oxidative power (standard oxidation potential: 2.07 V vs. NHE), it cannot decompose certain types of recalcitrant organic matter completely. We developed an advanced oxidation process (AOP), in which hydroxy radicals with stronger oxidative power (standard oxidation potential: 2.85 V vs. NHE) are formed using a combination of ozone, photocatalyst, and UV. In this study, we fabricated a mesoporous TiO2/BDD hybrid electrode and examined its potential for AOPs. A synergetic effect between electrochemical water treatment and photocatalytic water treatment was observed with the hybrid electrode that did not occur with the BDD electrode.


1. Introduction

Boron-doped diamond (BDD) electrodes have a wide potential window, and low background current, and physical/chemical stability.1 The wide potential window allows BDD to be used for the production of ozone (O3) by the electrolysis of water at high voltage. Because ozone is a strong oxidizing agent (standard oxidation potential: 2.07 V vs. Normal Hydrogen Electrode (NHE))2 that decomposes to form harmless oxygen (O2), ozonation has attracted great interest as an environmentally benign water purification technique. However, the oxidative power of O3 is sometimes insufficient to decompose recalcitrant organic compounds that are widely used as agricultural chemicals, medicines, dyes, and industrial products.

Advanced oxidation processes (AOPs), in which UV light, photocatalysts, and O3 are used together, have been studied as methods to more effectively treat contaminated water. These processes aim to efficiently produce hydroxy radicals (OH˙), which have greater oxidative power (standard oxidation potential: 2.80 V vs. NHE)2 than oxidants such as O3 and H2O2 (standard oxidation potential: 1.77 V vs. NHE).2 Ochiai et al. proposed an AOP system in which O3 gas was introduced into a reactor containing a titanium mesh impregnated photocatalyst (TMiP) and an ultraviolet light source.3 Their study found that using the photocatalyst and O3 in combination resulted in greater degradation of phenol in water than using either the photocatalyst or ozone individually. Water treatment using O3 produced by a water electrolysis unit composed of a BDD anode and a Pt cathode was found to deactivate water-borne pathogens.4 This water electrolysis unit used in combination with a photocatalyst was also found to effectively decompose toxic chemicals (perfluorooctanoic acid, C7F15COOH).5 The system used in this study was large because the electrochemical and photocatalytic units were separate, but simpler and more compact AOP systems are preferable for a wide variety of uses.

A BDD photocatalyst combined with water electrolysis to produce O3 under illumination results in a simpler AOP system because the photocatalytic and electrochemical treatment of water treatment can be performed simultaneously. Previous studies of nanostructured composite n-type metal oxides (TiO2, ZnO) and BDD found that their photocatalytic performance was enhanced because of photocarrier separation at the hetero-interface.6 However, no voltage was applied to these composites, and electrochemical effects were not studied. Recently, Zhao et al. synthesized a TiO2/Sb-doped SnO2/BDD hybrid electrode with a double-layer three-dimensional macro–mesoporous structure. This hybrid electrode showed superior water treatment performance when it was used as a photoanode because of the accumulation of photogenerated holes on the surface under a strong positive potential.7 However, the voltage applied to this hybrid electrode was not high enough to produce O3 by water electrolysis. Therefore, it seems that the potential of this hybrid electrode has not been fully explored.

In our previous study, we fabricated a mesoporous TiO2 layer on BDD and found that its photocatalytic efficiency was enhanced by deep-UV illumination.8 In this paper, we used this hybrid electrode to electrolyze water to produce O3 and other reactive oxygen species (ROS). In addition, we conducted water treatment tests with the electrochemically-created ROS under UV light irradiation and demonstrated the capability of the system for an AOP.

2. Experimental

2.1 Materials

Phosphate buffer powder (consisting of Na2HPO4 and KH2PO4), methylene blue, sodium hydroxide (NaOH), potassium iodide (KI), and ammonium molybdate tetrahydrate ((NH4)6Mo7O24·4H2O) were obtained from FUJIFILM Wako Pure Chemicals Corporation (Osaka, Japan). Potassium hydrogen phthalate (C6H4(COOK)(COOH)) was purchased from Tokyo Chemical Industry Co, Ltd (Tokyo, Japan). These chemicals were used without further purification.

2.2 Electrochemical analysis for mesoporous TiO2/BDD hybrid electrode

Mesoporous TiO2/BDD hybrid electrodes were synthesized as described in our previous study.8 Cyclic voltammograms were measured using a VersaSTAT 4 (AMETEK, Berwyn, PA, USA), while the relationship between applied voltage and current was examined using a HABF5001-B10 potentiostat/galvanostat (HOKUTO DENKO, Tokyo, Japan). A BDD electrode (without the TiO2 layer) was used as a reference. A 0.25 M phosphate aqueous buffer solution (pH = 6.8) was used as the electrolyte.

2.3 Detection of reactive oxygen species (ROS)

To prevent reduction by hydrogen gas resulting from the electrolysis of water, an H-type cell consisting of two separate glass half-cells was used and the mesoporous TiO2/BDD hybrid electrode (working electrode) and Pt (counter electrode) were placed in different half-cells. The half-cells were connected by a Nafion® NRE-212 membrane (Sigma-Aldrich, St. Louis, MO, USA), and 50 mL of 0.25 M phosphate aqueous buffer solution (pH = 6.8) was added to each one to increase the conductivity of the water in the half-cells and maintain its pH during the experiment.

Ozone gas was detected using a Kitagawa gas detector tube system consisting of an air sampling pump and a precision gas detector tube. Prior to the measurement, the 0.25 M phosphate aqueous buffer solution in the half-cells with BDD or hybrid electrodes was purged with N2 gas for 30 min to remove dissolved oxygen. A constant current (50 mA, 75 mA, or 100 mA) was then applied to the electrodes (hybrid electrode or BDD) for 3 min while N2 gas was bubbled through the solution at a constant flow rate of 0.15 L min−1. The gas flow rate was maintained using an RK-1650 flow meter (KOFLOC, Kyotanabe, Japan). The outlet gas was collected in 2L Tedlar® bags and passed through a 182U O3 detector tube (KOMYO RIKAGAKU KOGYO K.K., Kawasaki, Japan) to determine how much O3 gas was produced. A schematic illustration of this experimental setup is shown in Fig. S1(a).

The quantity of H2O2 formed by the application of current to the electrodes (either hybrid or BDD) for 10 min was determined using the coloring reaction.9 To detect H2O2, 500 mL of an aqueous solution of 1 g of NaOH, 33 g of KI, and 0.1 g of (NH4)6Mo7O24·4H2O (Solution A) and 500 mL of an aqueous solution of 10 g of C6H4(COOK)(COOH) (Solution B) were first separately prepared. Treated water, Solution A, and Solution B were then mixed in a 1[thin space (1/6-em)]:[thin space (1/6-em)]1[thin space (1/6-em)]:[thin space (1/6-em)]1 ratio. If H2O2 exists in the treated water, I3 (which has an absorption maximum at approximately 350 nm) is formed by the following reactions:

 
H2O2 + 2I + 2H+ → I2 + 2H2O (1)
 
I2 + I ⇄ I3 (2)

The concentration of H2O2 was estimated from the peak intensity (at around 350 nm) of the optical absorption spectrum measured by a V-670 UV-VIS spectrometer (JASCO, Hachioji, Japan).

2.4 Water treatment test

The efficacy of water treatment was evaluated based on the decomposition of methylene blue (MB). The glass half-cell containing the mesoporous TiO2/BDD hybrid electrode was filled with 50 mL of a solution of MB (20 μM) dissolved in 0.25 M phosphate aqueous buffer solution, while the other half-cell (i.e., the Pt electrode side) was filled with the same amount of pure phosphate aqueous buffer solution (0.25 M). The hybrid electrode was placed horizontally in the dark until adsorption equilibrium was reached. It was then irradiated with 1.2 mW cm−2 of 222 nm UV light from an excimer lamp (ORC Manufacturing Co., Ltd, Machida, Japan) in a quartz sample tube. A schematic illustration is shown in Fig. S1(b). The glass cup was capped with a Teflon cap to prevent evaporation during the test, and samples of the MB solution were taken by opening the cap. The absorption spectrum of the MB solution was measured using a V-670 UV-VIS spectrometer (JASCO, Hachioji, Japan). During the test, the MB solution was constantly stirred.

3. Results and discussion

Fig. 1(a) summarizes the cyclic voltammograms. Wide potential windows, which are typical of BDD electrodes, were clearly observed and were retained even after modification with mesoporous TiO2. In the hybrid electrode, current density decreased dramatically because most of the BDD surface was covered with TiO2, although some BDD remained exposed through mesopores and/or cracks (Fig. S2).
image file: c9ra10318j-f1.tif
Fig. 1 (a) Typical cyclic voltammogram of BDD and mesoporous TiO2/BDD hybrid electrodes in a 0.25 M phosphate aqueous buffer solution at a scan rate of 0.1 V s−1. The current density in the hybrid electrode was multiplied by five. (b) Relationship between applied voltage and current in BDD and mesoporous TiO2/BDD hybrid electrodes in a 0.25 M phosphate aqueous buffer solution.

Water oxidation typically produces O2 at the anode by the following reaction:

 
2H2O → O2 + 4H+ + 4e (3)

When BDD is used as an anode, the voltage required to electrolyze water becomes higher than the theoretical value (1.23 V) due to its wide potential window. This leads to other reactions such as O3 production by water electrolysis:

 
3H2O → O3 + 6H+ + 6e (4)

Fig. 1(b) shows that at high voltage, the current flow increased linearly with applied voltage in both electrodes and that the mesoporous TiO2 layer had little influence on the current flow.

Fig. 2 shows the quantities of reactive oxygen species detected. The quantity of O3 gas produced by the electrolysis of water (eqn (4)) increased linearly with the applied current (Fig. 2(a)). The mesoporous TiO2/BDD hybrid electrode produced less O3 gas than the BDD electrode because it had less exposed BDD. Indeed, no O3 gas was detected when a current of 50 mA was applied to the hybrid electrode.


image file: c9ra10318j-f2.tif
Fig. 2 Concentrations of (a) O3 gas from the glass cell and (b) H2O2 dissolved in treated water caused by the application of different constant currents to BDD and mesoporous TiO2/BDD hybrid electrodes.

If O3 is dissolved in the treated water, an absorption peak at around 260 nm occurs in the UV-VIS spectrum.10 However, no such peak was detected in the treated water (not shown). Hydrogen peroxide (H2O2) was, however, detected in the treated water in quantities that increased linearly with the current applied to the electrodes (Fig. 2(b)). Because high voltage was applied to electrodes, not only O3 but also other highly oxidative species (H2O2 and OH˙) were produced by the electrolysis of water:

 
2H2O → H2O2 + 2H+ + 2e (5)
 
H2O → OH˙ + H+ + e (6)

Therefore, substantial direct production of H2O2 by water electrolysis (eqn (5)) and annihilation of the OH˙ produced by water electrolysis (eqn (7)) were observed.

 
2OH˙ → H2O2 (7)

However, O3 gas production (eqn (4)) predominates at lower bias voltage. Most of the H2O2 was thus produced by the reaction between O3 gas and water. A previous study revealed that dissolved O3 forms H2O2 by the following chain reactions:11

 
image file: c9ra10318j-t1.tif(8)
 
image file: c9ra10318j-t2.tif(9)
 
image file: c9ra10318j-t3.tif(10)
 
HO˙ + O3 → {O3OH} → HO˙2 + O2 (11)
 
Termination: 2{O3OH} → H2O2 + 2O3 (12)

Because the hybrid electrode produced less O3 gas, the H2O2 concentration in the treated water was also lower. However, when a current of 100 mA was applied, the H2O2 concentration in the treated water became almost the same as when the BDD electrode was used. This probably occurred because the TiO2 layer peeled off.

We decided to apply a 75 mA current to the electrodes for further studies by following reasons. Lower current (50 mA) will lead to the formation of OH˙ in BDD. However, because O3 gas was not detected from the hybrid electrode, while it was formed from BDD, an experimental condition becomes different. At higher current (100 mA), if TiO2 layer in the hybrid electrode was truly peeled off, there are no difference between the hybrid electrode we made and the BDD electrode. Even if not, once BDD electrode is at a relatively high potential, the OH˙ will easily to take further reaction to form other oxidative species, which reduces the water treatment ability in BDD. Therefore, a comparative experiment between these two electrode is difficult at lower and higher current.

The effectiveness of the hybrid electrode for water treatment was evaluated based on the decomposition of methylene blue (MB). Photocatalytic water treatment was conducted under deep-UV light (λ = 222 nm) in order to photoexcite not only TiO2 but also BDD, which has a band gap of 5.5 eV (λ = 225 nm). Fig. 3 shows the relationship between MB concentration and photoirradiation time. When the hybrid electrode was used with deep-UV irradiation (Fig. 3(a)), the total amount of MB decomposed was greater than the sum of the amounts decomposed photocatalytically and electrochemically. This synergetic effect was not observed when the BDD electrode was used (Fig. 3(b)). The synergetic effect therefore originated from the mesoporous TiO2 layer. Deep-UV light can form OH˙ by decomposing O3 and H2O2 by the following reactions:12

 
O3 + → O1(D) + O2 (13)
 
O1(D) + H2O → H2O2 (14)
 
H2O2 + → 2HO˙ (15)


image file: c9ra10318j-f3.tif
Fig. 3 Time dependence of MB concentration estimated from the visible spectra during the photocatalytic (under 222 nm illumination without bias voltage), electrochemical (without illumination while bias voltage was applied), and photoelectrochemical (under 222 nm illumination with bias voltage) water treatment tests of (a) mesoporous TiO2/BDD hybrid and (b) BDD electrodes. C and C0 are the remaining and initial concentrations of MB, respectively. The black dotted line is a simulated value assuming that the total amount of decomposed MB is a summation of the amounts of MB decomposed by the photocatalytic and electrochemical effects.

However, the synergetic effect did not occur in the pure BDD electrode (without the mesoporous TiO2 layer), probably because the light intensity was too weak (1.2 mW cm−2).

Photoexcitation in TiO2 creates holes (hvb+) in the valence band (VB) that directly oxidize MB and/or form OH˙ via surface oxygen ions of the TiO2 lattice (Os2−):13

 
Os2− + Haq+ + hvb+ → OH˙ (16)

By contrast, electrons (ecb) in the conduction band (CB) reduce the dissolved O2 to form superoxide radicals image file: c9ra10318j-t4.tif:

 
image file: c9ra10318j-t5.tif(17)

from which OH˙ can then be formed by the following sequence of reactions.13

 
image file: c9ra10318j-t6.tif(18)
 
HO2˙ + H+ + ecb → H2O2 (19)
 
Ti3+ + H2O2 → Ti4+ + OH˙ + OH (20)
 
image file: c9ra10318j-t7.tif(21)

To clarify the mechanism of the photocatalytic reaction, formic acid was added to react sacrificially with holes.7 As shown in Fig. 4, when formic acid was added, the photocatalytic activity decreased dramatically, and the initial MB concentration change was almost identical to that caused by photolysis alone. This means that oxidation induced by holes in the VB was the main factor, and electrons in the CB were not used sufficiently to decompose MB in the hybrid electrode. This is because the oxidative power of image file: c9ra10318j-t8.tif is much lower than those of hvb+ and OH˙.14


image file: c9ra10318j-f4.tif
Fig. 4 Time dependence of MB concentration estimated from visible spectra during the photocatalytic (under 222 nm illumination) water treatment test of mesoporous TiO2/BDD hybrid electrode with and without 1 mM formic acid (a sacrificial reagent added to react with holes). C and C0 are the remaining and initial concentrations of MB, respectively.

Under electrochemical conditions (i.e., with current applied to the electrode), as mentioned above, H2O2 was produced in the treated water. This is probably because the reduction potential of the H2O2/OH˙ couple is more positive (E = +0.87 V vs. NHE)15 than that of the image file: c9ra10318j-t9.tif couple (E = −0.16 V vs. NHE; at a concentration of 1 M in water),16 photoexcited electrons (ecb) in the CV of TiO2 preferentially reduced electrochemically formed H2O2 to form OH˙.17

 
H2O2 + ecb → OH˙ + OH (22)

Electrons in the conduction band therefore played a significant role in decomposing MB by creating more OH˙ and thus promoting the advanced oxidation process. Such H2O2-assisted photocatalytic reactions have been reported previously.17

4. Conclusions

Mesoporous TiO2/BDD hybrid electrodes were prepared using a surfactant-assisted sol–gel method. By applying a current, O3 gas was produced by the electrolysis of water, and dissolved O3 gas formed H2O2 through a chain reaction. Under UV irradiation, electrochemically-formed H2O2 was reduced by photoexcited electrons in the CB of TiO2 to form OH˙, which promotes MB decomposition because of its strong oxidative power. A synergetic effect occurred, demonstrating that the hybrid electrode is effective in promoting AOPs. This simple water treatment system can be applied to decompose recalcitrant organic compounds in wastewater, and further studies of this process are currently underway.

Author Contributions

A. O., A. H., Y. H., Y. N., and N. R. synthesized the BDD electrode. N. S. and A. O. fabricated the mesoporous TiO2 thin film on the BDD electrode and conducted the experiments. Y. H. and C. T. gave scientific suggestions on this work. H. K. and I. S. supported this work financially. K. N., K.-i. K., T. K., and M. Y. contributed to the arrangement of the research environment. A. F. acted as a supervisor.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

This study was partly supported by the Joint Usage/Research Program of the Photocatalysis International Research Center, Research Institute for Science and Technology, Tokyo University of Science and Tokyo Ohka Foundation for The Promotion of Science and Technology. We thank Manohar Murthi, PhD, from Edanz Group (www.edanzediting.com/ac) for editing a draft of this manuscript.

References

  1. (a) Y. Einaga, J. Appl. Electrochem., 2010, 40, 1807–1816 CrossRef CAS ; (b) Y. Einaga, Bull. Chem. Soc. Jpn., 2018, 91, 1752–1762 CrossRef CAS .
  2. I. Sirés, E. Brillas, M. A. Oturan, M. A. Rodrigo and M. Panizza, Environ. Sci. Pollut. Res., 2014, 21, 8336–8367 CrossRef PubMed .
  3. T. Ochiai, K. Masuko, S. Tago, R. Nakano, K. Nakata, M. Hara, Y. Nojima, T. Suzuki, M. Ikekita, Y. Morito and A. Fujishima, Water, 2013, 5, 1101–1115 CrossRef CAS .
  4. Y. Yao, Y. Kubota, T. Murakami, T. Ochiai, H. Ishiguro, K. Nakata and A. Fujishima, J. Water Health, 2011, 9, 534–543 CrossRef CAS PubMed .
  5. T. Ochiai, H. Moriyama, K. Nakata, T. Murakami, Y. Koide and A. Fujishima, Chem. Lett., 2011, 40, 682–683 CrossRef CAS .
  6. (a) H. Yu, S. Chen, X. Quan, H. Zhao and Y. Zhang, Environ. Sci. Technol., 2008, 42, 3791–3796 CrossRef CAS PubMed ; (b) J. Yuan, H. Li, S. Gao, Y. Lin and H. Li, Chem. Commun., 2010, 46, 3119–3121 RSC ; (c) S. Gao, S. Jiao, B. Lei, H. Li, J. Wang, Q. Yu, D. Wang, F. Guo and L. Zhao, J. Mater. Sci.: Mater. Electron., 2015, 26, 1018–1022 CrossRef CAS .
  7. J. Fan, H. Shi, H. Xiao and G. Zhao, ACS Appl. Mater. Interfaces, 2016, 8, 28306–28315 CrossRef CAS PubMed .
  8. N. Suzuki, A. Okazaki, H. Kuriyama, I. Serizawa, A. Hara, Y. Hirano, Y. Nakabayashi, N. Roy, C. Terashima, K. Nakata, K. Katsumata, T. Kondo, M. Yuasa and A. Fujishima, Molecules, 2018, 23, 3095 CrossRef PubMed .
  9. (a) A. O. Allen, C. J. Hochanadel, J. A. Ghormley and T. W. Davis, J. Phys. Chem., 1952, 56, 575–586 CrossRef ; (b) N. V. Klassen, D. Marchington and H. C. E. McGowan, Anal. Chem., 1994, 66, 2921–2955 CrossRef CAS .
  10. A. V. Levanov, O. Y. Isaikina, A. N. Tyutyunnik, E. E. Antipenko and V. V. Lunin, J. Anal. Chem., 2016, 71, 549–553 CrossRef CAS .
  11. K. Ikemizu, S. Morooka and Y. Kato, J. Chem. Eng. Jpn., 1987, 20, 77–81 CrossRef CAS .
  12. R. Andreozzi, V. Caprio, A. Insola and R. Marotta, Catal. Today, 1999, 53, 51–59 CrossRef CAS .
  13. P. Salvador, J. Phys. Chem. C, 2007, 111, 17038–17043 CrossRef CAS .
  14. H. Park, Y. Park, W. Kim and W. Choi, J. Photochem. Photobiol., C, 2013, 15, 1–20 CrossRef CAS .
  15. A. C. da Silva, M. R. Almeida, M. Rodriguez, A. R. T. Machado, L. C. A. de Oliveira and M. C. Pereira, J. Photochem. Photobiol., A, 2017, 332, 54–59 CrossRef CAS .
  16. P. Wardman, J. Phys. Chem. Ref. Data, 1989, 18, 1637–1755 CrossRef CAS .
  17. C. C. Wong and W. Chu, Environ. Sci. Technol., 2003, 37, 2310–2316 CrossRef CAS PubMed .

Footnotes

Electronic supplementary information (ESI) available. See DOI: 10.1039/c9ra10318j
Both these authors contributed equally.

This journal is © The Royal Society of Chemistry 2020
Click here to see how this site uses Cookies. View our privacy policy here.