Nickel sulfide microsphere film on Ni foam as an efficient bifunctional electrocatalyst for overall water splitting

Abstract

Developing low-cost, efficient, and bifunctional electrocatalysts for both the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) is an appealing yet challenging task. Herein, for the first time, a NiS microsphere film was grown in situ on Ni foam (NiS/Ni foam) via a sulfurization reaction as an efficient bifunctional electrocatalyst for overall water splitting with superior activity and good durability. This NiS/Ni foam electrode delivers 20 mA cm−2 at an overpotential of 158 mV for the HER and 50 mA cm−2 at an overpotential of 335 mV for the OER in 1.0 M KOH. This bifunctional electrode also enables a high-efficiency alkaline water electrolyzer with 10 mA cm−2 at a cell voltage of only 1.64 V, which could be promising in water splitting devices for large-scale hydrogen production.

Graphical abstract: Nickel sulfide microsphere film on Ni foam as an efficient bifunctional electrocatalyst for overall water splitting

Supplementary files

Article information

Article type
Communication
Submitted
26 9月 2015
Accepted
23 11月 2015
First published
25 11月 2015

Chem. Commun., 2016,52, 1486-1489

Nickel sulfide microsphere film on Ni foam as an efficient bifunctional electrocatalyst for overall water splitting

W. Zhu, X. Yue, W. Zhang, S. Yu, Y. Zhang, J. Wang and J. Wang, Chem. Commun., 2016, 52, 1486 DOI: 10.1039/C5CC08064A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements