Low-temperature de-alloying and unique self-filling interface optimization mechanism of layered silicon for enhanced lithium storage

Abstract

Layered silicon (L–Si) anodes are celebrated for their high theoretical capacity but face significant challenges regarding safety and material purity during preparation. This study addresses these challenges by employing NH4Cl–CaSi2 as the raw material in a gas-solid de-alloying process, which enhances both safety and purity compared to traditional methods. The L–Si anodes produced demonstrate outstanding electrochemical performance, delivering a high reversible lithium storage capacity of 1497.7 mA h g−1 at a current density of 0.5 A g−1, and exhibiting stable performance over 1200 charge–discharge cycles. In situ and ex situ characterizations reveal that electrolyte decomposition products effectively fill the voids within the electrode, while the gradual disintegration of the L–Si structure contributes to the formation of a dense, conductive network. This process enhances lithium ion transport and exploits the capacitive storage benefits of layered silicon.

Graphical abstract: Low-temperature de-alloying and unique self-filling interface optimization mechanism of layered silicon for enhanced lithium storage

Supplementary files

Article information

Article type
Communication
Submitted
31 7月 2024
Accepted
19 8月 2024
First published
19 8月 2024

Chem. Commun., 2024,60, 10500-10503

Low-temperature de-alloying and unique self-filling interface optimization mechanism of layered silicon for enhanced lithium storage

W. Ji, M. Li, Y. Nong, J. Luo, X. Liang, X. Wang, L. Ming, X. Ou, J. Zhang, B. Zhang, X. Fu, L. Dong, J. Feng and J. Liang, Chem. Commun., 2024, 60, 10500 DOI: 10.1039/D4CC03857F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements