CuS@Cu-CD composites as efficient heterogeneous Fenton-like catalysts for the photodegradation of tetracycline
Received
21st June 2022
, Accepted 27th January 2023
First published on 2nd February 2023
Abstract
In this work, CuS@Cu-CD composites were synthesized and employed as Fenton-like catalysts. CuS significantly enhanced the photodegradation activity of tetracycline (TC) when decorated with Cu-doped-carbon dots (Cu-CDs). The influence of initial pH, dosage of catalyst, and H2O2 concentration on the catalyst performance was investigated. Radical trapping experiments proved that ·O2− and h+ played critical roles and ·OH played a moderate role in the degradation of TC. Mechanism analyses demonstrated that Cu2+/Cu+ redox circulation could be accelerated by the introduction of Cu into carbon dots, which further facilitated H2O2 consumption and resulted in higher TC degradation efficiency.
Environmental significance
Tetracycline (TC) is widely used as a broad-spectrum antibiotic for treating a wide range of diseases. However, the continuous abuse and overuse of TC results in environmental pollution. Photocatalysis is one of the environmentally friendly and sustainable strategies to eliminate TC pollution. Here, we have successfully developed a novel CuS@Cu-CD composite to act as an efficient heterogeneous Fenton-like catalyst for the photocatalytic degradation of tetracycline in solution with the assistance of H2O2. It provides important insights into photocatalytic devices, promoting the further development of unconventional Fenton-like catalysts in the catalytic field.
|
Introduction
Organic chemicals, which may be found as pollutants in wastewater effluents from industrial or domestic sources, must be removed or destroyed before discharge into the environment. The Fenton process is considered to be the most powerful catalytic technology for oxidative degradation of organic contaminants.1 However, the classical Fenton processes suffer from the problems of poor activity under neutral conditions and excessive consumption and waste of H2O2 due to the restriction of the electron cycle caused by the rate limiting pathway for the high-valence metal reduction by H2O2.2 Recently, Fenton-like catalysts with electron-rich metal centers such as Cu, Ru, Mn, Co, and Ce have attracted considerable attention because they have the same effect as iron.3 Copper with multiple valences (Cu0, Cu+, and Cu2+) has shown to be a promising candidate to catalyze Fenton-like reactions by virtue of its favorable redox ability and higher electron transfer rate than Fe(II)/Fe(III) and better solubility of Cu2+ than Fe3+ in water, as well as reduced generation of metal solid wastes. A variety of copper-based composites have been reported and applied to degrade organic pollutants.4–10 For example, Cu2O–Cu/C can degrade methyl orange, methyl blue, and rhodamine B in aqueous solutions in the presence of H2O2.11 The Cu+–graphitic carbon nitride complex exhibits an efficient Fenton-like activity for the removal of Rhodamine B from the aqueous solution.12 The experimental results show that CDs@CuOx can trigger the Fenton reaction and increase the reaction velocity by nearly 35 times compared with CuOx alone.13 Even so, the design and synthesis of more efficient Cu-based Fenton-like catalysts are still actively pursued.
As is well known, electron transfer plays a key role in Fenton/Fenton-like chemistry. Utilizing electrons to enhance reaction efficiency is a strategy used to optimize the photocatalytic performance of Fenton-like catalysts.14 Copper sulfide (CuS), a semiconductor material, can be excited upon light irradiation and produce photogenerated electrons and holes.15 Carbon materials such as carbon dots with abundant electrons and strong electron transfer abilities are natural adjuvants for accelerating the high valence metal ion reduction process.16 Furthermore, it has been found that the doping of metal promoted electron transfer and enhanced the performance of carbon dots in photo-oxidation reactions.17 We assumed that the strategy of integrating copper-doped carbon dots (Cu-CDs) with CuS would endow the composites with the eminent properties of CDs and CuS. It is worth exploring in depth their photocatalytic activity.
Herein, we present CuS@Cu-CD composites in which Cu-CDs act as decorated accessories to heighten the photocatalytic activity of CuS. Related studies show that the composites are excellent catalysts to photodegrade tetracycline (TC) with the assistance of H2O2. The degradation mechanism and kinetics were also investigated. The enhanced photocatalytic performances were ascribed to the doped copper in CDs, which accelerated the electron transfer rate and CuS generated electron (e−) and hole (h+) carriers under the irradiation to form chemical active radicals superoxide radical (·O2−) and hydroxyl radical (·OH) to attack pollutants directly. These results provide important insights into photocatalytic devices, promoting the further development of unconventional Fenton-like catalysts in the catalytic field.
Experimental
Materials
Reagents and solvents employed were commercially available and used as received. CuCl2, Cu(Ac)2, folic acid, and DMF (AR grade) were purchased from Shanghai Lingfeng Chemical Reagent Co., Ltd., China. Thiourea, H2O2, K2S2O8, disodium ethylenediaminetetraacetic acid (EDTA-2Na), p-benzoquinone (BQ), and tert-butanol (TB) were purchased from the Tianjin Chemicals Company and used as received. Tetracycline hydrochloride (TC) was purchased from Aladdin Chemical Reagent Co., Ltd. Water was deionized and bi-distilled.
Characterization
Fourier transform infrared spectroscopy (FT-IR) was recorded on a Nicolet iZ10 FT-IR spectrophotometer (Thermo Electron Co., USA). X-ray diffraction (XRD) patterns were recorded on a German Brooke XRD-D8 Advance D8 with Cu Kα radiation (λ = 0.15406 nm, voltage 40 kV, current 40 mA). Ultraviolet-visible (UV-vis) spectra experiments were performed on Hitachi UV-vis 3010 spectrophotometer (Hitachi Ltd. Tokyo, Japan). The morphology and microstructure of the samples were characterized by scanning electron microscopy (SEM, Hitachi Ltd. Tokyo, Japan) and field emission scanning electron microscopy (FESEM, Hitachi S-4800, Hitachi Ltd. Tokyo, Japan). X-ray photoelectron spectroscopy (XPS, Thermo Scientific, EscaLab 250Xi spectrometer, America) with a monochromatic Al Kα X-ray source was used to analyze elements (hν = 1486.6 eV, power 150 W, beam spot 650 μm, voltage 14.8 kV, current 1.6 A, and testing software is avantange). Photoluminescence spectroscopy (PL) was carried out using a Hitachi F-4500 fluorescence spectrophotometer (Hitachi Ltd. Tokyo, Japan). UV-vis diffuse reflectance spectroscopy (DRS) was performed in absorption mode at 200–800 nm by a Shimadzu UV-2450 spectrometer (Shimadzu Ltd. Japan). Electrochemical tests were carried out on a CHI760E electrochemical analyzer (CHIIns., Chenhua Ltd., Shanghai, China) in a conventional three-electrode configuration with a Pt foil as the counter electrode and Ag/AgCl (saturated KCl) as the reference electrode.
Synthesis of Cu-CDs
Folic acid (0.1 g) and DMF (10 mL) were mixed with CuCl2 (0.05 g). The solution was stirred and then transferred to a 25 mL Teflon steel autoclave and heated at 190 °C for 12 h. The solution of Cu-CDs was obtained by dialysis against deionized water through a dialysis bag (MWCO: 1000 Da). It was evaporated to dryness for further use. A control sample without metal doping (bare CDs) was prepared under conditions similar to that of Cu-CDs.
Synthesis of CuS@Cu-CDs
CuS was prepared based on a previous report with some modifications.18 Cu(Ac)2 (0.3993 g, 3.5 mmol) and thiourea (0.1522 g, 3.5 mmol) were dissolved in ultrapure water (10 mL) and stirred continuously to form a microemulsion. Then, the mixture was transferred to a Teflon-lined autoclave (15 mL) and heated at 160 °C for 10 h. Afterwards, the mixture was cooled to room temperature naturally. The obtained black powder product was washed several times with ultrapure water and ethanol, respectively, and then dried in a vacuum oven and stored for later use.
100 mg CuS was added to the suspension of Cu-CDs (30 mg, 100 mL H2O), then subjected to ultrasound for 20 min to obtain the final product CuS@Cu-CDs. CuS@CD composites were obtained with the same procedures for comparison.
Photocatalytic degradation of tetracycline
The photocatalytic activity of CuS@Cu-CD composites was determined by the photodegradation of TC. The mixture was irradiated by a 500 W xenon lamp for photodegradation under stirring. In a typical process, 10 mg of photocatalyst CuS@Cu-CDs was added to 100 mL of the TC solution and stirred for 60 min in the dark to attain the adsorption/desorption equilibration. For the photocatalytic process, 3 mL mixture was extracted and centrifuged to obtain clear liquor for the next residual TC detection using the spectrophotometer at a maximum absorption wavelength of 371 nm. Photocatalytic efficiency was calculated by the following formula:
where C0 and C represent concentrations of TC before and after irradiation, respectively.
Additives that could scavenge different active radicals were utilized in comparative trials to illuminate the degradation process of TC. AgNO3 (1 mmol L−1), disodium ethylenediaminetetraacetic acid (EDTA-2Na, 1 mmol L−1), p-benzoquinone (BQ, 1 m mol L−1), and tert-butanol (TBA, t-BuOH, 1 mmol L−1) were introduced into the Fenton-like reaction system to capture electrons (e−), holes (h+), superoxide anion free radicals (·O2−), and hydroxyl free radicals (·OH). These tests were performed following the photocatalytic degradation process mentioned above.
Fenton-like reaction
Degradation experiments were carried out at room temperature (approximately 25 °C). The solution pH was adjusted by HCl (0.1 mol L−1) or NaOH (0.1 mol L−1). In each experiment, 100 mg catalyst was added to the TC aqueous solution (10 mg L−1, 100 mL), followed by the addition of 1 mL of H2O2 (30%) into the solution to initiate the Fenton-like reaction. Before illumination, the suspensions were magnetically stirred in the dark for 30 min to ensure the establishment of an adsorption–desorption equilibrium between the catalyst and TC. The sampling analysis was conducted in 10 min intervals, and a 3 mL suspension was sampled and centrifuged to remove the catalyst particles. The TC degradation efficiency (η) was calculated by η (%) = (1 − Ct/C0) × 100%, where C0 and Ct are the TC concentrations at the initial time and time t, respectively.
Results and discussion
Synthesis of CuS@Cu-CDs
Two-step procedures have been used to prepare CuS@Cu-CD composites, as shown in Scheme 1. Copper-doped carbon dots (Cu-CDs) were obtained by pyrolysis of the mixture of CuCl2 and folic acid in DMF, in which cupric ions can coordinate with the –COOH groups on the surface of carbon dots, forming a π-electron conjugated system via the C–O–Cu bond.19 CuS was prepared by heating the mixture of Cu(Ac)2 and thiourea. Then, it was added to the suspension of Cu-CDs and ultrasound to form CuS@Cu-CDs, in which CuS wrapped the Cu-CDs.
![image file: d2va00139j-s1.tif](/image/article/2023/VA/d2va00139j/d2va00139j-s1.gif) |
| Scheme 1 Synthesis of CuS@Cu-CDs. | |
Characterization of CuS@Cu-CDs
Powder X-ray diffraction (PXRD) was used to evaluate the structure and phase composition of CuS@Cu-CDs and other related materials. On the 2θ scale, a broad diffraction peak was observed around 2θ = 25°, which is related to the graphitic (002) peak (Fig. 1a). For the pure CuS, the major diffraction peaks were found at 2θ = 27.7°, 29.3°, 31.8°, 32.9°, 47.7°, 47.9°, 52.7°, and 59.4°, which were well indexed to (101), (102), (103), (006), (007), (110), (108), and (116) crystal planes of covellite CuS (JCPDS no. 06-0464),20 and revealing that adding CDs or Cu-CDs did not change the molding of CuS. The intense and sharp diffraction peaks in the XRD patterns manifested high crystallinity of the CuS component. However, the XRD peaks of CDs and Cu-CDs were not observed in CuS@Cu-CDs due to the weak diffraction intensity and less content of CDs. Energy-dispersive X-ray spectroscopy (EDX) was performed on the as-prepared composites, which determined the elemental composition to comprise Cu (43.81), N (2.55), O (2.45), C (14.78), and S (11.24) wt% (Fig. 1b).
![image file: d2va00139j-f1.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f1.gif) |
| Fig. 1 (a) XRD (b) EDX (c) IR (d) Raman spectra of CuS@Cu-CDs. | |
As shown in Fig. 1c, the black and red lines represent CDs and Cu-CDs, respectively, in the FT-IR spectra. The broad peaks centered at around 3100–3500 cm−1 were assigned to the stretching vibrations of O–H and –NH2.21–23 The typical peaks at 1600 cm−1 and 1691 cm−1 were associated with the stretching vibrations of C
N and C
O.24 The peaks at 1396 cm−1 and 1040 cm−1 were ascribed to the vibration of C–O.25 These typical peaks of CDs were also observed in CuS@Cu-CDs. Beyond that, the peak at 625 cm−1 was assigned to the stretching band of Cu–S.26 These results indicated that CuS@Cu-CD composites were successfully synthesized.
The Raman spectra of CuS@Cu-CDs exhibit two bands at 1529 cm−1 and 1356 cm−1, as shown in Fig. 1d. They were assigned to the D (sp3-hybridized) and G (sp2-hybridized) bands of the Cu-CDs. The D band was related to the vibrations of carbon atoms with dangling bonds in the termination plane of disordered graphite or glassy carbon.27,28 The G band was associated with the vibration of sp2-hybridized carbon atoms.29 The intensity ratio of the disordered D band to the crystalline G band (ID/IG) was 0.87, indicating that it had a structure similar to graphite. It demonstrated that the intensity of the G band decreased with the addition of Cu into CDs (Fig. 1d). With Cu2+ doping into CDs, they chelated with carboxyl groups on the surface of CDs, which affected the in-plane stretching vibration of sp2 hybridized C atoms of CDs. A sharp peak at 469 cm−1 is attributed to the S–S stretching vibration in CuS, which was consistent with the previous result.30 There were no additional impurity peaks present for any copper substrate and unreacted precursor compound. It indicated that the CuS@Cu-CD composites were synthesized successfully.
SEM image illuminated that the morphologies of CuS and CuS@Cu-CDs were spherical in shape with a size of about 10–20 nm (Fig. 2a and b). The nanosphere was rough owing to the aggregation of CuS nanoparticles. The TEM image of Cu-CDs exhibited that the carbon dots had good monodispersity with a size < 5.0 nm (Fig. 2c). CuS@Cu-CDs sample showed that Cu-CDs deposited or inlaid on the CuS nanosphere as small dots (Fig. 2d). Fig. 3a–f are the elemental mapping diagrams of Cu, S, C, O, and N in CuS@Cu-CDs, respectively. It can be seen from the figures that these elements were evenly distributed on the hybrid material. These findings suggest that CuS is a good supporting matrix for Cu-CDs.
![image file: d2va00139j-f2.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f2.gif) |
| Fig. 2 SEM of (a) CuS (b) CuS@Cu-CDs and TEM of (c) Cu-CDs (d) CuS@Cu-CDs. | |
![image file: d2va00139j-f3.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f3.gif) |
| Fig. 3 Mapping of (a) CuS@Cu-CDs (b) Cu (c) S (d) C (e) O (f) N. | |
The chemical composition and valence states of CuS@Cu-CDs were characterized by XPS. As shown in Fig. 4a, the survey spectrum displayed that the main component elements of CuS@Cu-CDs were C, O, S, N, and Cu. The “shakeup” peak of the Cu2+ satellite is obviously observed at a binding energy of 943.1 eV. The peak at 933.3 eV corresponded to the oxidation of copper species (Cu2+), whereas the peak located at 932.2 eV corresponds to the reduced copper species (Cu+) according to previous reports,31,32 and the ratio of Cu2+/Cu+ equals to 1.98
:
1 (Fig. 4b). These results signified that both Cu2+ and Cu+ existed in CuS@Cu-CDs and the efficiency of the Fenton-like reaction might be regulated by the cycle of Cu2+/Cu+. XPS spectrum of S2p was split into two peaks centered at 161.75 eV and 162.9 eV, which correspond to the binding energy of S 2p3/2 and S 2p1/2 states for S2− in CuS (Fig. 4c).33 C 1s spectrum was fitted into three separate peaks, which were located at 284.7 eV, 285.7 eV, and 288.2 eV, corresponding to C–C, C–O and C
O, respectively (Fig. 4d).34 The peaks of O 1s are centered at 531.3 and 532.3 eV, which are aligned with the literature (Fig. 4e).35 The high-resolution spectrum of N 1s revealed a dominant peak at 398.9 eV, which deconvoluted into two peaks at 398.7 eV and 400.1 eV and corresponded to N–C or N–H, respectively (Fig. 4f).36 These results showed that the Cu-CDs were successfully loaded on CuS, fully consistent with that obtained from various characterizations.
![image file: d2va00139j-f4.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f4.gif) |
| Fig. 4 XPS (a) survey spectrum (b) Cu 2p (c) S 2p (d) C 1s (e) O 1s (f) N 1s. | |
The optical absorption properties of CuS@Cu-CDs, CuS, and Cu-CDs are exhibited in Fig. 5a. Cu-CDs and CuS@Cu-CDs displayed solar energy absorbance and their band edges approximately at 520 nm, while CuS clearly showed adsorption ability in the full spectrum region. The observation indicated that the absorption range of CuS@Cu-CDs was slightly wider than that of Cu-CDs. The band gap energies (Eg) of direct transition semiconductors can be calculated according to the plot of (αhν)2 versus photon energy (hν).37 As shown in Fig. 5b, the Eg of CuS@Cu-CDs is estimated to be 2.09 eV, which was wider than that of CuS (1.83 eV). It denoted that the Cu-CDs addition in CuS can promote their solar energy absorption.
![image file: d2va00139j-f5.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f5.gif) |
| Fig. 5 (a) UV-vis DRS of prepared catalysts (b) plot of (αhν)2versus hν of CuS@Cu-CDs and its valence band spectra. | |
The fluorescence spectra of the CDs and Cu-CDs exhibited emission peaks centered at around 450 nm (Fig. 6a and b). The absorbance intensity of Cu-CDs increased due to the introduction of Cu into CDs. It is well known that the radius of each arc is relevant to the charge-transfer resistance: the smaller the radius of the arc, the lower the corresponding impedance.38 CuS@Cu-CDs showed the smallest charge-transfer resistance than CuS and CuS@CDs, coinciding with the conclusion of the EIS results (Fig. 6c). The transient photocurrent responses were employed to further explore the separation efficiency of photogenerated charge carriers.39 In comparison with CuS and CuS@CDs, CuS@Cu-CDs exhibited the highest photocurrent density (Fig. 6d). It can generate considerably enhanced photocurrents with three visible-light irradiation on–off cycles.
![image file: d2va00139j-f6.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f6.gif) |
| Fig. 6 Fluorescence emission of (a) CDs (b) Cu-CDs. (c) Electrochemical impedance spectrum and (d) transient photocurrent response of CuS@Cu-CDs. | |
Catalytic performance of CuS@Cu-CDs
Tetracycline has drawn widespread concern in society. It is widely used as a broad-spectrum antibiotic for treating a wide range of diseases. However, the continuous abuse and overuse of TC result in environmental pollution.40–42 Photocatalysis is one of the environmentally friendly and sustainable strategies to eliminate TC pollution.
TC degradation by the as-prepared catalyst was carried out to investigate the reaction conditions. The experimental results are presented in Fig. 7a. Before the photocatalysis experiments, the suspension containing the catalyst and TC was magnetically stirred in the dark for 60 min to ensure an adsorption–desorption equilibrium without illumination.
![image file: d2va00139j-f7.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f7.gif) |
| Fig. 7 (a) TC degradation in various reaction systems (b) linear relationship of degradation kinetics over CuS@Cu-CDs and related materials (c) TC degradation with different catalyst dosages (d) with different initial pH (e) with different H2O2 concentrations (f) effect of different inorganic anions, natural water, and tap water on TC degradation by CuS@Cu-CDs ([anion concentration] = 20 mM; [catalyst dosage] = 20 mg; [H2O2] = 7 mM; [TC] = 20 mg L−1; pH = 5.6). | |
The photolysis of TC can be neglected in the absence of a catalyst, which indicates that TC was very stable and hardly decomposed. About 5%, 10%, and 20% of TC were adsorbed on the surface of CuS, CuS@CDs, and CuS@Cu-CDs, respectively, in the part of the adsorption/desorption equilibrium experiment. Obviously, the adsorption ability of CuS@Cu-CDs is higher than that of CuS. TC degradation performance greatly improved (85%) under a Fenton-like system by CuS@Cu-CD composites. This acceleration is compactly related to the produced photoelectrons on the semiconductor CuS surface along with its intrinsic Cu2+/Cu+ circulation during catalysis reaction, which indicated that Cu-CDs introduction contributed to catalytic activity in the composites. Kinetics also show that significant degradation of TC occurred when CuS hybridized with Cu-CDs (Fig. 7b).
Catalyst dosage, which is strongly associated with the quantities of active sites, is a key parameter in a Fenton-like degradation reaction.43Fig. 7c depicted the influence of catalyst dosage on TC catalytic degradation at pH 5.6. TC removal efficiency shows a significant increase from 70% to 80% in 30 min, with the catalyst dosage rising from 10 mg to 50 mg. Indeed, more catalyst means more active sites for H2O2 decomposition, hence facilitating organics degradation. However, an overdose of catalyst would lead to unsuitable radical consumption via the reactions (eqn (1) and (2)) as follows:44
| Cu+ + ·OH → Cu2+ + OH− | (1) |
| Cu2+ + ·O2− → Cu+ + O2 | (2) |
In the traditional Fenton system, the organic oxidation efficiencies are remarkably associated with the solution pH. Besides, tetracycline is sensitive to pH. Thus, the effect of initial pH on TC degradation in this Fenton-like system was investigated. As shown in Fig. 7d, the highest degradation efficiency of TC was achieved at pH = 5.6 in the initial 30 min, and the efficiencies decreased in the order of pH (5.6) > pH (3.2) > pH (7.2) > pH (9.3). Under acidic conditions, the reaction depicted in eqn (3) will easily occur. The reaction in eqn (4) would be inhibited and the generation rate of ·OH would be reduced. Therefore, the catalytic activity becomes weak under pH = 3.2, as shown in Fig. 7d. Furthermore, increased pH also leads to decreased ·OH oxidation potential. As for basic conditions around 9.3, the relatively lower degradation efficiency could be caused by the fact that hydroxyl radical has a redox potential of +2.8 V in acidic media and +1.5 V in basic media.45
| 4Cu+ + 4H+ + O2 → 4Cu2+ + 2H2O | (3) |
| Cu+ + H2O2 → Cu2+ + ·OH + OH− | (4) |
The effect of H2O2 concentration on TC oxidation process was also explored, and the results are presented in Fig. 7e. When H2O2 concentration increased from 5 mM to 7 mM, TC oxidative efficiency evidently enhanced (from 60% to 85%). This stated the fact that higher H2O2 concentration leads to sufficient ·O2− for attacking the TC molecules. However, with H2O2 concentration continuously increasing to 10 mM, the degradation rate of TC declined to 70%. This is because the redundant H2O2 can be a scavenger of hydroxyl radicals (eqn (5)). Similar results were also reported in Fenton-like systems for antibiotic oxidative degradation.43
| H2O2 + ·OH → HO2˙ + H2O | (5) |
Various inorganic anions and other substances may coexist in wastewater and potentially affect the Fenton-like photocatalytic activity. Fig. 7f displays TC degradation curves in the presence of four typical anions (Cl−, NO3−, SO42−, and CO32−) and natural water (river or tap water). NO3− and Cl− displayed relatively weak impacts on the TC degradation procedure,46 while SO42− and CO32− weakened TC degradation rates from 50.3% and 80.0%, respectively. SO42− can be adsorbed onto the CuS surface to compete for active sites with TC molecules. CO32− quenched ·OH with the formation of less-reactive radicals of ·CO32−viaeqn (6).47,48
| CO32−+ ·OH →·CO32− + OH− | (6) |
The catalytic activities were further analyzed using natural water (river water obtained from Huajing river in the campus of Anhui Normal University) and tap water (from Water Company, Wuhu) as the base. The TC removal efficiency was interfered with in an actual water body compared to ideal ultrapure water, and this might be closely associated with their water qualities of anions and pH.
Table 1 lists a comparison of removal efficiencies of tetracycline in the present work with some reported Fenton-like catalysts.43,49–51 As displayed, our designed catalyst exhibits relatively higher catalytic activity than those reported in the literature for the photodegradation of TC in the water.
Table 1 Comparison of CuS@Cu-CDs with other reported Fenton-like photocatalysts for the degradation of tetracycline
Catalyst |
Dosage (g L−1) |
H2O2 (mM) |
TC (mg L−1) |
pH |
Time (min) |
Degradation efficiency (%) |
Ref. |
yCeO2/Fh |
0.4 |
50.0 |
20 |
4.0 |
60 |
85.0 |
43
|
Mn2O3/pSiO2 |
0.5 |
326.0 |
80 |
3.0–11.0 |
300 |
80.0 |
55
|
Fe/N–C |
0.2 |
60.0 |
100 |
7.0 |
80 |
86.0 |
56
|
Fe3O4/α-FeOOH |
0.75 |
20.0 |
20 |
5.0–9.0 |
80 |
100.0 |
57
|
CuS@Cu-CDs |
0.5 |
7.0 |
100 |
5.6 |
30 |
85.0 |
This work |
Active radical identification
In order to ascertain the reactive species that directly participate in the CuS@Cu-CDs photocatalytic system, active species trapping experiments were performed (Fig. 8a). In this research, tert-butylalcohol (TBA), p-benzoquinone (BQ), ethylenediaminetetraacetic acid disodium (EDTA-2Na), and AgNO3 were employed as scavengers of hydroxyl radicals (·OH), superoxide radicals (·O2−), photo-generated holes (h+), and photo-generated electrons (e−), respectively. The catalytic activity was significantly inhibited when BQ or EDTA-2Na appeared in the reaction system. The results demonstrate that ·O2− and h+ are the main reactive species in the photocatalytic process of CuS@Cu-CDs.52 AgNO3 and TBA have a moderate inhibitory influence on TC degradation, which indicated that e− and ·OH played auxiliary roles in the photocatalytic degradation process.
![image file: d2va00139j-f8.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f8.gif) |
| Fig. 8 (a) Active species trapping experiments and (b) ·O2− quenching experiments under air and the solution treated with N2 before the reaction on TC Fenton-like photodegradation by CuS@Cu-CDs [catalyst dosage] = 20 mg; [H2O2] = 7 mM; [TC] = 20 mg L−1; pH = 5.6. | |
To explore the contribution of the dissolved oxygen, we bubbled N2 in the mixture of CuS@Cu-CDs, H2O2, and TC before the reaction. The result shows that the concentration of TC was much higher than that under air (Fig. 8b). It illuminated that the dissolved oxygen played an important key role in the reaction, which was indispensable for the formation of ·O2−.53
ESR analysis was also performed as supporting evidence for the above results. As shown in Fig. 9a, four peaks of 1
:
2
:
2
:
1 proportion emerged in the DMPO–·OH spectra, and the intensity of signals increased in the presence of light, which stated that ·OH was generated in the CuS@Cu-CDs Fenton-like system and played key functions. The signal ratio of 1
:
1
:
1
:
1 in DMPO–·O2− adducts was significantly enhanced by lighting (Fig. 9b). Combined with the fact of ·O2− produced from O2 absorbed on the photocatalyst surface via electron transformation,43,53 we can deduce that ·O2− played an important role in the oxidative degradation of TC. The combination of the above results reflected that the ·O2− and ·OH were the valid species during TC degradation in CuS@Cu-CDs Fenton-like system.
![image file: d2va00139j-f9.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f9.gif) |
| Fig. 9 ESR spectrum of CuS@Cu-CDs/H2O2 system (a) DMPO–·OH (b) DMPO–·O2−. | |
Possible degradation mechanism by CuS@Cu-CD composites
On the basis of the above experimental results, we propose the Fenton-like photocatalysis mechanism of CuS@Cu-CDs (Scheme 2). First, TC in solutions can be adsorbed on the surface of CuS@Cu-CDs. The electron donor groups of TC were bound to the carboxylic groups of CDs via hydrogen bonds to form an electron-donor molecular structure intermediate.54 Once illuminated under visible light, CuS absorbed energy and produced photogenerated e− and h+ on its conduction band, then photogenerated e− transferred to the interface of CuS@Cu-CDs (eqn (7)), which prompted the reduction of Cu2+ to Cu+ (eqn (8)). Cu+ can react with O2 to produce active radicals ·O2− (eqn (9)) since the conduction band of CuS@Cu-CDs (−1.08 V) was more negative than O2/·O2− potential (−0.046 V vs. NHE). Cu2+ was reduced by H2O2 to generate Cu+ and simultaneously produced ·O2− (eqn (10)). Cu+ could be oxidized by H2O2 to form Cu2+ and ·OH (eqn (11)).55 Undoubtedly, electrons play an important role in improving the efficiency of Fenton-like photocatalytic reactions by accelerating the Cu2+ to Cu+ process, which promotes the regeneration of Cu2+ reaction centers. The holes (h+) will be repelled to Cu-CDs, reacting with surface hydroxyl groups to form OH˙ radicals (eqn (12)).52 ·O2−, h+, and ·OH on the composite surface diffused to the solution and broken TC down into small molecules, even mineralized into CO2 and H2O (eqn (13)). | Cu2+ + H2O2 → Cu+ + ·O2− + 2H+ (major) | (10) |
| Cu+ + H2O2 → Cu2+ + ·OH (minor) | (11) |
| Cu-CDs–OH + h+ → Cu-CDs + ·OH (minor) | (12) |
| ·O2−/h+/·OH + TC → degradation products | (13) |
![image file: d2va00139j-s2.tif](/image/article/2023/VA/d2va00139j/d2va00139j-s2.gif) |
| Scheme 2 Proposed mechanism of photocatalytic degradation of TC. | |
As we know, Cu2+ was coordinated with –COOH via bidentate coordination in Cu-CDs. The electron transfer between CDs and Cu2+ induced by π electron-withdrawing carboxylic groups improved the electron migration of CuS.54 Therefore, doping Cu2+ into CDs accelerated the electron transfer rate and prompted CuS generated electron (e−) and hole (h+) carriers. The synergistic effect between CuS and Cu-CDs endows the composites with high catalytic performance.
The stability of CuS@Cu-CDs was also investigated through the cyclic degradation of TC with the assistance of H2O2 under visible light irradiation. CuS@Cu-CDs and CuS (100 mg) were used in the recycling experiment. After the photocatalysis, the mixture was centrifuged and reduced by ascorbic acid to obtain a catalyst for the next reaction. The photocatalytic activity decreased by about 5–15% after four cycles (Fig. 10a). At this moment, Cu2+ concentration was almost undetectable. It demonstrated that hardly any copper ions leached during the cycle. However, the catalytic efficiency of CuS decreased by about 20–35% (Fig. 10b). The result indicated that the incorporation of Cu-CDs into CuS was therefore thought to enhance the visible light activity of CuS and also inhibit the photo-corrosion of CuS, leading to a stable and durable photocatalytic activity.
![image file: d2va00139j-f10.tif](/image/article/2023/VA/d2va00139j/d2va00139j-f10.gif) |
| Fig. 10 Cycling runs with (a) CuS@Cu-CDs (b) CuS; XPS of CuS@Cu-CDs before and after the reaction (c) Cu 2p and (d) S 2p. | |
To reveal the active centers of the catalyst, we carried out an XPS analysis of CuS@Cu-CDs after catalysis (Fig. 10c and d). The peaks of Cu 2p and S 2p in the used sample have visibly shifted to a high binding energy (1–3 eV). The fact suggested that there was interfacial interaction between CuS and Cu-CDs.50 Compared with the freshly synthesized composites, the binding energies of Cu 2p3/2 and Cu 2p1/2 for the used catalyst shifted to higher positions (935.3.0 and 956.0 eV), indicating the increasing amount of Cu2+ after the Fenton-like reaction. Two satellite peaks of Cu 2p3/2 and Cu 2p1/2 were enhanced, further confirming the increased quantities of Cu2+ in the sample.57 Furthermore, the comparison of Cu+ peaks at 932.8, 955.0 eV and Cu2+ peaks at 935.3, 956.0 eV after the reaction shows a noticeable decrease in the peak intensity of Cu+ relative to that of Cu2+: the peak intensity ratio Cu+/Cu2+ decreases from 1.98
:
1 to 0.69
:
1 upon the reaction. These results indicated that the interfacial electron cycle of Cu+ and Cu2+ occurred on the surface of CuS@Cu-CDs and the oxidation of Cu+ to Cu2+ by H2O2 after the reaction. The circulation played a key role in Fenton-like photocatalysis. The enhanced photocatalytic performance of CuS@Cu-CDs was derived from CDs doped with Cu2+, which promoted electron migration and increased the separation of electrons and holes in CuS under irradiation.10,58–60
Conclusion
In summary, CuS@Cu-CDs exhibited excellent Fenton-like photocatalytic activity for the degradation of tetracycline. ·O2− and h+ radicals were the primary contributors, and ·OH played an auxiliary role in the photodegradation process. The experiment indicated that the electron migration and the redistribution of local electrons in the catalyst system improved the Fenton-like activity. Our work may provide more thought in designing metal-doped carbon dot-decorated semiconductor composites that utilize visible light to solve environmental problems.
Conflicts of interest
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Acknowledgements
This work was supported by the National Natural Science Foundation of China (grant no. 21771004) and Natural Science Foundation of Education Department of Anhui Province (KJ2020A0092).
Notes and references
- E. Neyens and J. Baeyens, A review of classic Fenton's peroxidation as an advanced oxidation technique, J. Hazard. Mater., 2003, 98, 33–50 CrossRef CAS PubMed
.
- Y. P. Zhu, R. L. Zhu, Y. F. Xi, J. X. Zhu, G. Q. Zhu and H. P. He, Strategies for enhancing the heterogeneous Fenton catalytic reactivity: a review, Appl. Catal. B: Environ., 2019, 255, 117739 CrossRef CAS
.
- A. D. Bokare and W. Choi, Review of iron-free Fenton-like systems for activating H2O2 in advanced oxidation processes, J. Hazard. Mater., 2014, 275, 121–135 CrossRef CAS PubMed
.
- C. Dai, X. Tian, Y. Nie, H.-M. Lin, C. Yang, B. Han and Y. Wang, Surface facet of CuFeO2 nanocatalyst: a key parameter for H2O2 activation in Fenton-like reaction and organic pollutant degradation, Environ. Sci. Technol., 2018, 52, 6518–6525 CrossRef CAS PubMed
.
- H. Jin, X. Tian, Y. Nie, Z. Zhou, C. Yang, Y. Li and L. Lu, Oxygen vacancy promoted heterogeneous Fenton-like degradation of ofloxacin at pH 3.2-9.0 by Cu substituted magnetic Fe3O4@FeOOH nanocomposite, Environ. Sci. Technol., 2017, 51, 12699–12706 CrossRef CAS PubMed
.
- T. Chen, Z. Zhu, H. Zhang, X. Shen, Y. Qiu and D. Yin, Enhanced removal of veterinary antibiotic florfenicol by a Cu-based Fenton-like catalyst with wide pH adaptability and high efficiency, ACS Omega, 2019, 4, 1982–1994 CrossRef CAS PubMed
.
- W. Cao, M. Han, L. Lyu, C. Hu and F. Xiao, Efficient Fenton-like process induced by fortified electron-rich O microcenter on the reduction state Cu-doped CNO polymer, ACS Appl. Mater. Interfaces, 2019, 11, 16496–16505 CrossRef CAS PubMed
.
- C. Zhang, L. Yan, X. Wang, X. Dong, R. Zhou, Z. Gu and Y. Zhao, Tumor microenvironment-responsive Cu2(OH)PO4 nanocrystals for selective and controllable radiosentization via the X-ray-triggered Fenton-like reaction, Nano Lett., 2019, 19, 1749–1757 CrossRef CAS PubMed
.
- R. Rehman, S. K. Lahiri, A. Islam, P. Wei and Y. Xu, Self-assembled hierarchical CuxO@C18H36O2 nanoflakes for superior Fenton-like catalysis over a wide range of pH, ACS Omega, 2021, 6, 22188–22201 CrossRef CAS PubMed
.
- H. H. Wang, L. L. Zhang, C. Hu, X. K. Wang, L. Lyu and G. D. Sheng, Enhanced degradation of organic pollutants over Cu-doped LaAlO3 perovskite through heterogeneous Fenton-like reactions, Chem. Eng. J., 2018, 332, 572–581 CrossRef CAS
.
- B. F. Sun, H. L. Li, X. Y. Li, X. W. Liu, C. H. Zhang, H. Y. Xu and X. S. Zhao, Degradation of organic dyes over Fenton-like Cu2O-Cu/C catalysts, Ind. Eng. Chem. Res., 2018, 57, 14011–14021 CrossRef CAS
.
- J. Q. Ma, N. Z. F. Jia, C. S. Shen, W. P. Liu and Y. Z. Wen, Stable cuprous active sites in Cu+-graphitic carbon nitride: structure analysis and performance in Fenton-like reactions, J. Hazard. Mater., 2019, 378, 120782 CrossRef CAS PubMed
.
- T. T. Cai, Q. Chang, B. Liu, C. H. Hao, J. L. Yang and S. L. Hu, Triggering photocatalytic activity of carbon dot based nanocomposites by a self-supplying peroxide, J. Mater. Chem. A, 2021, 9, 8991–8997 RSC
.
- Z. Tang, P. Zhao, H. Wang, Y. Liu and W. Bu, Biomedicine meets Fenton chemistry, Chem. Rev., 2021, 121, 1981–2019 CrossRef CAS PubMed
.
- K. J. Huang, J. Z. Zhang, Y. Liu and Y. M. Liu, Synthesis of reduced graphene oxide wrapped-copper sulfide hollow spheres as electrode material for supercapacitor, Int. J. Hydrogen Energy, 2015, 40, 10158–10167 CrossRef CAS
.
- Y. Wang, X. Liu, J. Liu, B. Han, X. Hu, F. Yang, Z. Xu, Y. Li, S. Jia, Z. Li and Y. Zhao, Carbon quantum dot implanted graphite carbon nitride nanotubes: excellent charge separation and enhanced photocatalytic hydrogen evolution, Angew. Chem., Int. Ed., 2018, 57, 5765–5771 CrossRef CAS PubMed
.
- Y. Cheng, X. Wang, Y. Mei, D. Wang and C. Ji, ZnCDs/ZnO@ZIF-8 zeolite composites for the photocatalytic degradation of tetracycline, Catalysts, 2021, 11, 934 CrossRef CAS
.
- X. Wang, L. Li, Z. Fu and F. Cui, Carbon quantum dots decorated CuS nanocomposite for effective degradation of Methylene blue and antibacterial performance, J. Mol. Liq., 2018, 268, 578–586 CrossRef CAS
.
- S. Xu, H. Zhu, W. Cao, Z. Wen, J. Wang, C. P. Francois-Xavier and T. Wintgens, Cu-Al2O3-g-C3N4 and Cu-Al2O3-C-dots with dual reaction centres for simultaneous enhancement of Fenton-like catalytic activity and selective H2O2 conversion to hydroxyl radicals, Appl. Catal., B, 2018, 234, 223–233 CrossRef CAS
.
- H. Peng, G. Ma, K. Sun, J. Mu, H. Wang and Z. Lei, High-performance supercapacitor based on multi-structural CuS@polypyrrole composites prepared by in situ oxidative polymerization, J. Mater. Chem. A, 2014, 2, 3303–3307 RSC
.
- J. Hou, J. Yan, Q. Zhao, Y. Li, H. Ding and L. Ding, A novel one-pot route for large-scale preparation of highly photoluminescent carbon quantum dots powders, Nanoscale, 2013, 5, 9558–9561 RSC
.
- L. Li, B. Yu and T. You, Nitrogen and sulfur Co-doped carbon dots for highly selective and sensitive detection of Hg (II) ions, Biosens. Bioelectron., 2015, 74, 263–269 CrossRef CAS PubMed
.
- V. Gupta, N. Chaudhary, R. Srivastava, G. D. Sharma, R. Bhardwaj and S. Chand, Luminescent graphene quantum dots for organic photovoltaic devices, J. Am. Chem. Soc., 2011, 133, 9960–9963 CrossRef CAS PubMed
.
- Z. Yang, M. Xu, Y. Liu, F. He, F. Gao, Y. Su, H. Wei and Y. Zhang, Nitrogen-doped, carbon-rich, highly photoluminescent carbon dots from ammonium citrate, Nanoscale, 2014, 6, 1890–1895 RSC
.
- S. Zhu, Q. Meng, L. Wang, J. Zhang, Y. Song, H. Jin, K. Zhang, H. Sun, H. Wang and B. Yang, Highly photoluminescent carbon dots formulticolor patterning, sensors, and bioimaging, Angew. Chem., Int. Ed., 2013, 125, 3953–3957 CrossRef PubMed
.
- X. Chen, H. Li, Y. Wu, H. Wu, L. Wu, P. Tan, J. Pan and X. Xiong, Facile fabrication of novel porous graphitic carbon nitride/copper sulfide nanocomposites with enhanced visible light driven photocatalytic performance, J. Colloid Interface Sci., 2016, 476, 132–143 CrossRef CAS PubMed
.
- X. Wen, L. Shi, G. Wen, Y. Li, C. Dong, J. Yang and S. Shuang, Green and facile synthesis of nitrogen-doped carbon nanodots for multicolor cellular imaging and Co2+, sensing in living cells, Sens. Actuators, B, 2016, 235, 179–187 CrossRef CAS
.
- H. Wang, Z. Wei, H. Matsui and S. Zhou, Fe3O4/carbon quantum dots hybrid nanoflowers for highly active and recyclable visible-light driven photocatalyst, J. Mater. Chem. A, 2014, 2, 15740–15745 RSC
.
- R. Liu, D. Wu, S. Liu, K. Koynov, W. Knoll and Q. Li, An aqueous route to multicolor photoluminescent carbon dots using silica spheres as carriers, Angew. Chem., Int. Ed., 2009, 48, 4598–4601 CrossRef CAS PubMed
.
- Y. Y. Lu, Y. Y. Zhang, J. Zhang, Y. Shi, Z. Li, Z. C. Fengc and C. Li, In situ loading of CuS nanoflowers on rutile TiO2 surface and their improved photocatalytic performance, Appl. Surf. Sci., 2016, 370, 312–319 CrossRef CAS
.
- H. Wang, L. Zhang, C. Hu, X. Wang, L. Lyu and G. Sheng, Enhanced degradation of organic pollutants over Cu-doped LaAlO3 perovskite through heterogeneous Fenton-like reactions, Chem. Eng. J., 2018, 332, 572–581 CrossRef CAS
.
- F. E. Lopez-Suarez, S. Parres-Esclapez, A. Bueno-Lopez, M. J. Illan-Gomez, B. Ura and J. Trawczynski, Role of surface and lattice copper species in copper-containing (Mg/Sr)TiO3 perovskite catalysts for soot combustion, Appl. Catal., B, 2009, 93, 82–89 CrossRef CAS
.
- P. Ajibade and N. Botha, Synthesis, optical and structural properties of copper sulfide nanocrystals from single molecule precursors, Nanomaterials, 2017, 7, 32–44 CrossRef PubMed
.
- J. Xiao, X. Zhang and Y. Li, A Ternary g-C3N4/Pt/ZnO photoanode for efficient photoelectrochemical water splitting, Int. J. Hydrogen Energy, 2015, 40, 9080–9087 CrossRef CAS
.
- S. Zhao, M. Lan, X. Zhu, H. Xue, T. Ng, T. Meng, C. Lee, P. Wang and W. Zhang, Green synthesis of bifunctional fluorescent carbon dots from garlic for cellular imaging and free radical scavenging, ACS Appl. Mater. Interfaces, 2015, 7, 17054–17060 CrossRef CAS PubMed
.
- C. Mahala, M. D. Sharma and M. Basu, Type-II heterostructure of ZnO and carbon dots demonstrates enhanced photoanodic performance in photoelectrochemical water splitting, Inorg. Chem., 2020, 59, 6988–6999 CrossRef CAS PubMed
.
- Y. Cheng, Y. Mei, S. Y. Deng and J. Li, In situ synthesis and photocatalytic performance of three dimensional composites CdS@DMSA-GO, Chin. J. Inorg. Chem., 2020, 36, 714–729 Search PubMed
.
- Y. Li, Y. Jiang, Z. Ruan, K. Lin, Z. Yu, Z. Zheng, X. Xu and Y. Yuan, Simulation-guided synthesis of graphitic carbon nitride beads with 3D interconnected and continuous meso/macropore channels for enhanced light absorption and photocatalytic performance, J. Mater. Chem. A, 2017, 5, 21300–21312 RSC
.
- S. Bian, C. Zhou, P. Li, J. Liu, X. Dong and F. Xi, Graphene quantum dots decorated titania nanosheets heterojunction efficient charge separation and enhanced visible-light photocatalytic performance, ChemCatChem, 2017, 9, 3349–3357 CrossRef CAS
.
- M. Bilal, S. Mehmood, T. Rasheed and H. M. N. Iqbal, Antibiotics traces in the aquatic environment: persistence and adverse environmental impact, Curr. Opin. Environ. Sci. Health, 2020, 13, 68–74 CrossRef
.
- D. Cheng, H. H. Ngo, W. Guo, S. W. Chang, D. D. Nguyen, Y. Liu, Q. Wei and D. Wei, A critical review on antibiotics and hormones in swine wastewater: water pollution problems and control approaches, J. Hazard. Mater., 2020, 387, 121682 CrossRef CAS PubMed
.
- P. Välitalo, A. Kruglova, A. Mikola and R. Vahala, Toxicological impacts of antibiotics on aquatic micro-organisms: a mini-review, Int. J. Hyg. Environ. Health, 2017, 220, 558–569 CrossRef PubMed
.
- X. Huang, N. Zhu, F. Mao, Y. Ding, S. Zhang, H. Liu, F. Li, P. Wu, Z. Dang and Y. Ke, Enhanced heterogeneous photo-Fenton catalytic degradation of tetracycline over yCeO2/Fh composites: performance, degradation pathways, Fe2+ regeneration and mechanism, Chem. Eng. J., 2020, 392, 123636 CrossRef CAS
.
- A. Babuponnusami and K. Muthukumar, Advanced oxidation of phenol: a comparison between Fenton, electro-Fenton, sono-electro-Fenton and photo-electro-Fenton processes, Chem. Eng. J., 2012, 183, 1–9 CrossRef CAS
.
- J. L. Wang and L. J. Xu, Advanced oxidation processes for wastewater treatment: formation of hydroxyl radical and application, Crit. Rev. Environ. Sci. Technol., 2012, 42, 251–325 CrossRef CAS
.
- C. Lai, F. L. Huang, G. M. Zeng, D. L. Huang, L. Qin, M. Cheng, C. Zhang, B. Li, H. Yi, S. Liu, L. Li and L. Chen, Fabrication of novel magnetic MnFe2O4/bio-char composite and heterogeneous photo-Fenton degradation of tetracycline in near neutral pH, Chemosphere, 2019, 224, 910–921 CrossRef CAS PubMed
.
- H. Zheng, J. Bao, Y. Huang, L. Xiang, B. Faheem, J. Ren, M. N. Du and D. D. D. Nadagouda, Efficient degradation of atrazine with porous sulfurized Fe2O3 as catalyst for peroxymonosulfate activation, Appl. Catal., B, 2019, 259, 118056 CrossRef CAS
.
- H. Liang, R. Liu, X. An, C. Hu, X. Zhang and H. Liu, Bimetal-organic frameworks with coordinatively unsaturated metal sites for highly efficient Fenton-like catalysis, Chem. Eng. J., 2021, 414, 128669 CrossRef CAS
.
- Q. Zhang, M. Yu, N. Wang, J. Qian, Y. Gu, F. Du, Y. Lin, F. Chen, Z. Chen, Z. Wu and L.-B. Sun, Porous Mn2O3/pSiO2 nanocomposites on bio-scaffolds for tetracycline degradation, ACS Appl. Nano Mater., 2022, 5, 9117–9128 CrossRef CAS
.
- Y. Yang, X. Zhang, Q. Chen, S. Li, H. Chai and Y. Huang, Ultrasound-assisted removal of tetracycline by a Fe/N−C hybrids/H2O2 Fenton-like system, ACS Omega, 2018, 3, 15870–15878 CrossRef CAS PubMed
.
- X. Huang, H. Zhou, X. Yue, S. Ran and J. Zhu, Novel magnetic Fe3O4/α-FeOOH nanocomposites and their enhanced mechanism for tetracycline hydrochloride removal in the visible photo-Fenton process, ACS Omega, 2021, 6, 9095–9103 CrossRef CAS PubMed
.
- N. Li, W. Fu, C. Chen, M. Liu, F. Xue, Q. Shen and J. Zhou, Controlling the core–shell structure of CuS@CdS heterojunction via seeded growth with tunable photocatalytic activity, ACS Sustainable Chem. Eng., 2018, 6, 15867–15875 CrossRef CAS
.
- H. Wang, L. Zhang, C. Hu and X. Wang, Enhanced Fenton-like catalytic performance of Cu-Al/KIT-6 and the key role of O2 in triggering reaction, Chem. Eng. J., 2020, 387, 124006 CrossRef CAS
.
- T. Zhang, Y. Wen, Z. Pan, Y. Kuwahara, K. Mori, H. Yamashita, Y. Zhao and X. Qian, Overcoming acidic H2O2/Fe(II/III) redox-induced low H2O2 utilization efficiency by carbon quantum dots Fenton-like catalysis, Environ. Sci. Technol., 2022, 56, 2617–2625 CrossRef CAS PubMed
.
- W. Xiang, T. Zhou, Y. Wang, M. Huang, X. Wu, J. Mao, X. Lu and B. Zhang, Catalytic oxidation of diclofenac by hydroxylamine enhanced Cu nanoparticles and the efficient neutral heterogeneous homogeneous reactive copper cycle, Water Res., 2019, 153, 274–283 CrossRef CAS PubMed
.
- D. Xiang, X. Hao and Z. Jin, Cu/CdS/MnOx nanostructure-based photocatalyst for photocatalytic hydrogen evolution, ACS Appl. Nano Mater., 2021, 4, 13848–13860 CrossRef CAS
.
- F. C. De Godoi, E. Rodriguez-Castellon, E. Guibal and M. M. Beppu, An XPS study of chromate and vanadate sorption mechanism by chitosan membrane containing copper nanoparticles, Chem. Eng. J., 2013, 234, 423 CrossRef CAS
.
- G. K. Grandhi, K. Swathi, K. S. Narayan and R. Viswanatha, Cu doping in ligand free CdS nanocrystals: conductivity and electronic structure study, J. Phys. Chem. Lett., 2014, 5, 2382–2389 CrossRef CAS PubMed
.
- Q. Xu, Y. Liu, R. Su, L. Cai, B. Li, Y. Zhang, L. Zhang, Y. Wang, Y. Wang, N. Li, X. Gong, Z. Gu, Y. Chen, Y. Tan, C. Dong and T. S. Sreeprasad, Highly fluorescent Zn-doped carbon dots as Fenton reaction-based bio-sensors: an integrative experimental-theoretical consideration, Nanoscale, 2016, 8, 17919–17927 RSC
.
- W. Wu, L. Zhan, W. Fan, J. Song, X. Li, Z. Li, R. Wang, J. Zhang, J. Zheng, M. Wu and H. Zeng, Cu–N dopants boost electron transfer and photooxidation reactions of carbon dots, Angew. Chem., Int. Ed., 2015, 54, 6540–6544 CrossRef CAS PubMed
.
|
This journal is © The Royal Society of Chemistry 2023 |