Tapas Ghosha,
Prasanta Karmakarb and
Biswarup Satpati*a
aSurface Physics and Material Science Division, Saha Institute of Nuclear Physics, 1/AF Bidhannagar, Kolkata-700064, India. E-mail: biswarup.satpati@saha.ac.in; Fax: +91 33 2337 4637
bVariable Energy Cyclotron Centre, 1/AF Bidhannagar, Kolkata 700064, India
First published on 19th October 2015
We report the role of electrochemical Ostwald ripening and the galvanic displacement reaction in uniform particle formation on ion bombarded amorphous (i.e., composed of random atomic spacings) Ge (a-Ge) surfaces compared to crystalline germanium (c-Ge). Silver growth on c-Ge and a-Ge substrates by electroless deposition has been studied by atomic force microscopy (AFM), cross-sectional transmission electron microscopy (XTEM), and energy dispersive X-ray spectroscopy (EDX). Introduction of defects can provide a control over particle growth by the galvanic displacement reaction that may offer continuous film growth up to a definite thickness. The possibility of surface diffusion and its consequences have also been discussed.
To illustrate its mechanism, applicability and substrate dependency we restrict ourselves to discussing the galvanic displacement reaction only. The galvanic displacement reaction has been successfully implemented in micro electromechanical systems (MEMS),2 where the requisite selective deposition is provided by the displacement process. Availing the galvanic displacement technique, scanning force microscope cantilevers have been successfully coated to minimize their stress factor.3 Magnetic nanodot formation is also conceivable by this technique, which has applications in ultrahigh density ROM and RAM devices. For instance, nickel deposition at a high pH value of 8 has been attained.4–7 Turning to the structural aspects, diverse nanostructure formation by the galvanic displacement technique has also been studied. Inukshuk-like silver nanostructures made up of hexagonal building blocks have been obtained with a long period of deposition; dendritic structures have also been found to be achievable.8–16 Our surface enhanced Raman scattering (SERS) study on such silver nano-inukshuks revealed an electromagnetic field enhancement, demonstrating them to be a SERS effective substrate,17 that can eventually find use in sensing devices.
To augment understanding of the underlying mechanism in the galvanic displacement reaction, several investigations have already been performed.6–8,18–29 In assistance of this reaction, metallic films on metal and metal alloy surfaces have been deposited.18–20 The deposition of noble metals such as gold, silver, platinum and palladium has been studied on semiconducting surfaces, leading to the formation of metal semiconductor interfaces.9,17,21–24,30–34 A comparative study made by depositing Au on Ge and Si surfaces revealed the formation of bonds in the case of Au–Ge interfaces where they were absent in the case of Au–Si systems.30 Strong adhesion of Au was found on GaAs, GaP and InP surfaces when the substrates were activated in an acidified solution of palladium chloride. Faceted gold nanoparticles have been produced on InP in the presence of H2SO4.25,31 The detailed mechanism of the galvanic displacement reaction is still not well understood when substrate has different disorder. Here, the extensive use of TEM and associated techniques such as EDX and high angle annular dark-field scanning transmission electron microscopy (STEM-HAADF) allowed us to successfully demonstrate the role of electrochemical Ostwald ripening and the galvanic displacement reaction in uniform particle formation on a-Ge surfaces compared to c-Ge during Ag deposition. The advantageous selection of Ge in the galvanic displacement reaction provides us a fluoride-source free deposition, since the reaction product GeO is water soluble and hence we end up with a simple dip and rinse Ag deposition on Ge substrate. Improve on continuity of Ag formation on ion bombarded surfaces implies the role of electrochemical Ostwald ripening in addition to the galvanic displacement reaction, governed by the particle size dependent electrochemical potential.35,36
In this work we propose and demonstrate the synergetic effect between electrochemical Ostwald ripening and the galvanic displacement reaction in order to interpret the ambiguity in particle growth on surfaces with different disorder. Our work offers control over the particle formation in the galvanic displacement reaction to some extent and may pave a way to continuous film growth up to a limited thickness.
Ge → Ge4+ + 4e− (E0 = −0.12) |
Ag+ + e− → Ag (E0 = 0.8) |
Fig. 1a–c present the AFM topographic images of the virgin germanium substrate, Ag nanoparticles deposited on crystalline Ge, and the 14 keV oxygen ion bombarded Ge substrate, respectively. Here the substrates were dipped into 1 mM AgNO3 solution for 2 min under identical conditions in the latter two cases. The silver nanoparticles deposited via the galvanic displacement reaction on crystalline and the oxygen ion bombarded germanium substrates are shown also by the XTEM images in Fig. 2a–c. Substrate ‘1’ and ‘2’ represent the ion bombarded and crystalline germanium surfaces, respectively after deposition. In the inset of Fig. 2b we show one ion bombarded Ge substrate where the lighter contrast represents the amorphous area (thickness ∼ 46.2 nm). The corresponding STEM-HAADF images from the same area are shown in Fig. 2d and S1†. The higher intensity in the STEM-HAADF images is due to the silver particles having a higher atomic number, whereas the lower intensity is due to the lower atomic number germanium. Fig. 2e shows the elemental mappings corresponding to the STEM-HAADF images from area 1 and 2 in Fig. 2d. Fig. 2e successively, from left to right, shows the STEM-HAADF images, germanium maps, silver maps and the composite maps of germanium and silver. Elemental mapping is described in Fig. 2e, where X-rays were collected from both the substrates (marked by the orange coloured rectangular boxes in Fig. 2d) by selecting the energy window of the silver L line and germanium K line in the X-ray spectra while a beam of about 1 nm is scanning the area. Thus the two elemental maps precisely confirm the formation of silver nanoparticles on crystalline and ion bombarded germanium surfaces. One can see from XTEM and AFM study that the particles’ distribution is random and much bigger in size on the crystalline germanium surfaces compared to the ion bombarded surfaces. As the time of deposition (two minutes) and other experimental conditions are same in both the cases, one could expect the same result. But since the substrates have a different nature, a different mechanism is taking place in silver nanoparticle formation on c-Ge and a-Ge by the galvanic displacement reaction. In search of such mechanisms we conducted a few controlled experiments which are described in the following sections.
![]() | ||
Fig. 1 AFM images (a) virgin Ge(100), (b) and (c) Ag nanoparticles deposited on crystalline and O+ ion bombarded Ge substrate, respectively under identical conditions. |
C. Colliex and co-workers have studied the influence of surface defects on graphite by depositing antimony clusters produced by a gas-aggregation cluster source at room temperature by varying the density of defects in the substrate.38 They have observed that as the density of surface defects increases, the density of islands increases and their size decreases. Compared to the galvanic displacement reaction, with a completely different source of deposition, the diffusion of the antimony clusters is strongly dependent on the island temperature and the diffusion is principally thermal energy driven. To investigate the different type of particle growth in the galvanic displacement reaction depending on the substrate having different disorder we recall the size dependent electrochemical potential and the activation energy of nanoparticles.39–42
Brus et al. have reported that thermally evaporated silver nanoparticles on a conducting substrate spontaneously grow to a larger size when the substrate, containing nanoparticles, is immersed into pure water.43 A particle reconstruction to form larger particles starting with a particle size as small as 1.5 nm was shown and the mechanism was explained as electrochemical Ostwald ripening, where particle enlargement occurs as the smaller metal nanoparticles which are more easily oxidized than bulk material dissolve by transferring Ag+ ions into the water, which then got deposited onto the larger particles and made them even larger.
In this work, the galvanic displacement reaction and subsequent deposition occur atom by atom and we have conducted experiments on crystalline and amorphous substrates, under identical conditions. The discrepancy between the particle growth on crystalline and amorphous substrate indicates that the electrochemical Ostwald ripening took place during the process of the galvanic displacement reaction. Plieth showed that the chemical potential of nanoparticles increases negatively as their size is decreased and is described by the following equation.35
ΔE = −(2Mγ/zFr) | (1) |
![]() | ||
Fig. 3 Variation of chemical potential as described in eqn (1). |
Silver particle formation on crystalline and amorphous Ge substrates shows that the amorphization reduces the contact angle of the Ag particles deposited on the Ge substrate (see Fig. S1†).45,46 This observation also indicates the decrease of the surface energy of the a-Ge substrate. The reduction in contact angle increases the radius of curvature (r) of the particle. Now, according to eqn (1), if the r value of Ag particle increases (on a-Ge) then the negative shift in electrode potential will be less and the Ag will not be easily oxidized, and eventually electrochemical Ostwald ripening will be diminished. This observation is in agreement with the uniform Ag particle formation on a-Ge surfaces.
Ag particle growth on ion bombarded germanium surfaces gave rise to regular and continuous growth as the electrochemical Ostwald ripening is hindered by the amorphous nature of the substrate. The amorphization also decreases the conductivity by a few orders of magnitude.47 This reduction in conductivity prevents the electron transfer from the smaller particle to the bigger particle in the process of electrochemical Ostwald ripening. This causes localized particle formation leading to the growth of uniform and ordered particles. We extended our study for the Ag particles growth on Ar2+ ion (energy: 24 keV, angle of incidence: 0° and fluence 7 × 1017 ions per cm2) bombarded Ge substrate also to examine the role of oxygen ions in the amorphization process and their presence in the ion bombarded region. Oxygen atoms can saturate the dangling bonds appearing on the surfaces of voids, locally forming compounds such as GeO, and thus decreasing the extrinsic conduction. The AFM topographic image and cross sectional TEM image (Fig. 5a and b, respectively) depict a similar regular particle formation in the case of Ar ion bombarded Ge substrate. The magnified TEM image in Fig. 5c clearly shows the amorphous layer due to Ar ion bombardment and Ag particle growth on the a-Ge surface. Lighter Ge contrast in the sub-surface region clearly demonstrates that the Ag particle formation is at the expense of Ge. Detailed EDX elemental maps and line profiles for the Ag particle deposition on O+ and Ar2+ ion bombarded Ge are presented in Fig. S2 and S3.†
![]() | ||
Fig. 5 (a) AFM image of Ag particles grown on Ar bombarded Ge surface. (b) Low magnification cross sectional TEM image. (c) Magnified TEM image of the sub-surface region from an area shown in (b). |
Silver particle growth on O+ and Ar2+ ion bombarded Ge substrates collectively suggest that the uniform particle growth arises mainly due to the amorphization, which reduces the electron mobility during electrochemical Ostwald ripening in the early stages of the galvanic displacement reaction.
In the process of electrochemical Ostwald ripening, when an Ag atom was deposited on the Ge surface by the galvanic displacement reaction very close to a bigger particle, it donates an electron to the bigger particle as described previously. This Ag+ ion may now move towards the bigger nanoparticle as elucidated in Fig. 6. Such diffusion processes will also lead to a discrepancy in the particle growth on crystalline and amorphous surfaces because amorphization by the ion bombardment creates many defects that will interrupt the diffusion of the Ag+ ions on the a-Ge surface.
When an atom moves on a crystalline surface it experiences a periodic potential (Fig. 7a), the presence of defects can create certain minima in the periodic potential (Fig. 7b) that disturb the motion of the atom and try to make it stabilize.48 So for a less defective surface, it is easier for the Ag atoms to diffuse towards the bigger nanoparticles. For a more defective surface the probability of the Ag atom getting trapped is greater and these trapped Ag atoms locally accumulate more Ag ions to create nanoparticles, giving rise to a more continuous particle formation with uniform size.
![]() | ||
Fig. 7 The periodic potential experienced by an atom when moving on (a) a perfect crystalline surface, (b) a defect induced surface. |
To understand the growth of Ag particles on the c-Ge substrate further we have deposited Ag particles for various short intervals of time on p-type and n-type substrates (presented in Fig. S4 and Table S1†). One can see from these images and the corresponding particle size distributions that larger particles are formed and also inter particle separations increase gradually as the time of deposition increases. This is an indication of the Ostwald ripening process. To investigate the role of the electronic conductivity of different substrates, one can compare the 30 s, 60 s and 120 s Ag deposition on n-type and p-type crystalline Ge (depicted in Fig. S4†). More regular Ag particle growth on p-type Ge was observed compared to the n-type, which is consistent with the earlier observation made by Buriak et al.9 The lower mobility of holes in the p-type substrate than that of electrons in the n-type substrate makes the Ostwald ripening slower to give rise to a uniform particle distribution in the p-type c-Ge in a similar fashion to that observed in the ion bombarded amorphous substrate.
Now to separate out these two processes (viz., Ostwald ripening and the galvanic displacement reaction) we conducted the following experiments. First, we grew Ag particles on c-Ge by floating the thin substrates (p-type and n-type of the same resistivity (0.3 Ω cm) and ready for plan-view TEM measurements) on 1 mM AgNO3 solution and allowed the reaction to happen for 30 seconds (here we assume that both the galvanic displacement reaction and Ostwald ripening are happening) then observed and recorded TEM images (Fig. 8a and b). Then, the same substrates containing Ag particles grown previously were dipped into water for 3 hours (here we assume only Ostwald ripening is happening). Again we carried out TEM measurement and recorded TEM images (Fig. 8d and e). One can see from these TEM images, the corresponding particle size distributions and Table 1 that the Ag particles are becoming larger in size and the inter-particle separation also increases, which is a result of electrochemical Ostwald ripening. One can see that the particle enlargement in p-type c-Ge is smaller than that in the n-type c-Ge as the Ostwald ripening is delayed. Thus our observations confirm the occurrence of electrochemical Ostwald ripening in the galvanic displacement reaction and particle growth is the result of a synergetic effect.
Substrate | Water immersion | Particle counts | % of areal coverage | Mean size (nm) | Standard deviation (nm) |
---|---|---|---|---|---|
c-Ge (n-type) | Before | 2466 | 18.63 | 17.2 | 9.1 |
After | 399 | 11.87 | 32.1 | 21.2 | |
c-Ge (p-type) | Before | 1610 | 15.55 | 17.1 | 13.6 |
After | 1325 | 14.25 | 20.6 | 10.6 | |
a-Ge (n-type) | Before | 1895 | 17.92 | 16.9 | 13.6 |
After | 1340 | 16.22 | 20.0 | 14.2 |
Similarly, we have deposited Ag particles on an n-type a-Ge substrate for 30 seconds by the galvanic displacement reaction and then dipped the same Ag deposited substrate into water for 3 hours. Much less change (Fig. 8c and f and Table 1) in the size of these Ag particles has been observed as the Ostwald ripening is hindered due to the amorphization which causes an increase in resistivity.49
These results are summarized in Table 1. One can see from this table that the average particle size is increasing at the same time as the percentage of area coverage is decreasing when the substrate is immersed in water, which is a clear case of Ostwald ripening.
Footnote |
† Electronic supplementary information (ESI) available. See DOI: 10.1039/c5ra20297c |
This journal is © The Royal Society of Chemistry 2015 |