Carbon quantum dots derived from mango leaves exhibited red fluorescence. These negatively charged particles underwent coating with the positively charged lipid molecule N-[1-(2,3-dioleyloxy)propyl]-N,N,N-trimethylammonium chloride (DOTMA). However, the bioconjugate displayed reduced uptake compared to the standalone mQDs in cancer cells (SUM 159A), and increased uptake in case of non-cancerous (RPE-1) cells. Upon in vitro testing, the bioconjugate demonstrated a mitigating effect on the individual toxicity of both DOTMA and mQDs in SUM-159 (cancerous cells). Conversely, it exhibited a proliferative effect on RPE-1 (normal cells).
Lipids are pivotal to biological systems, as fundamental structural and functional components of cellular membranes. Predominantly constituting the phospholipid bilayer, these amphipathic molecules create a dynamic, semi-permeable barrier that regulates the selective exchange of ions, nutrients, and signaling molecules between the intracellular and extracellular environments. Lipids, particularly phospholipids, cholesterol, and glycolipids, contribute to membrane fluidity, asymmetry, and membrane protein functionality.10
Beyond structural roles, lipids significantly enhance cellular uptake mechanisms. The fluidic nature of the lipid bilayer, driven by van der Waals forces among the acyl chains of fatty acids, facilitates lateral and transverse diffusion of lipid molecules and associated bioactive compounds across the membrane.11,12 This intrinsic property is harnessed in biomedical applications, wherein lipid-based nanocarriers, such as liposomes and lipid nanoparticles, are employed to encapsulate and deliver therapeutic agents—including small molecule drugs, nucleic acids, and proteins—into cells with high efficiency.13 Lipids enable the encapsulation of hydrophilic molecules within their aqueous core and hydrophobic molecules within the lipid bilayer, thus protecting the cargo from enzymatic degradation and improving its bioavailability. By combining biocompatibility with effective cellular internalization, lipids play an indispensable role in advancing targeted drug delivery systems and enhancing therapeutic outcomes.14,15
Cationic-surface L-SPIOs (superparamagnetic iron oxide nanoparticles) with an average size of 46 nm were found to exhibit enhanced cellular uptake in HeLa, PC-3, and Neuro-2a cells. In vivo imaging in Balb/c mice injected with CT-26 tumor cells loaded with SPIOs allowed for tracking of tumor growth using optical and MR images.16 A study exploring lipid–polymer hybrid nanoparticles composed of PLGA coated with DOTMA and loaded with mRNA-mCherry demonstrated their significantly higher transfection efficiency (80%) compared to chitosan-PLGA NPs (5%) in vitro. Translation of mCherry protein within DCs was evaluated.17 In other research, silica nanoparticles were double coated with PG and DOPC and were compared to uncoated nanoparticles for cellular uptake and adsorption on hybrid bilayer membranes. The lipid-coated nanoparticles showed reduced aggregation, leading to smaller structures compared to uncoated nanoparticles.18 Further, cationic magneto liposomes with iron oxide cores and enveloped in a bilayer containing cationic lipids were studied for toxicity. Higher doses of cationic lipid were found to potentially limit uptake efficiency due to increased electrostatic attraction to the cell membrane.19
In recent times, the drug delivery community has shown significant interest in green synthesis of nanoparticles because they are biocompatible and environmentally friendly. The mango leaf quantum dots have been used in bioimaging and drug delivery while exhibiting low cytotoxicity compared to heavy metal QDs.1,20 In addition, the mango leaf has antioxidant and anti-inflammatory properties which provided added benefits in quantum dots.21 Surface modifying the lipid-coated nanoparticles due to their outstanding biocompatibility, effective permeation enhancement, and scalability allows a broad range of applications. However, the uptake of cationic lipid-coated nanoparticles is influenced by various factors, including the lipid's properties, surface decoration, size, and physicochemical attributes of liposome formulations. These elements collectively impact the potential release of cationic lipids from the nanoparticle and its subsequent movement toward the cell plasma membrane.19,22
In our study, we introduce novel red-emitting carbon dots, mQDs, derived from mango leaves, with an emission wavelength of 670 nm and a size of 10.1 nm. These mQDs were decorated with a small cationic lipid, N-[1-(2,3-dioleyloxy)propyl]-N,N,N-trimethylammonium chloride (DOTMA), forming a bioconjugate, mQDs:
DOTMA, which exhibited enhanced fluorescence intensity, photostability, and reduced cytotoxicity compared to standalone mQDs and DOTMA. Our findings highlight the bioconjugate's potential for bioimaging, offering brighter signals and improved biocompatibility for precise cellular imaging in in vitro studies. Cellular internalization assays and viability assessments revealed decreased uptake in cancer (SUM159A) and increased uptake in retinal pigment epithelial (RPE-1) cells, demonstrating the bioconjugate's promising utility in cellular imaging and potential therapeutic applications (Fig. 1).
For AFM sample preparation mica sheets were peeled freshly and 5 μL of samples (1:
0.25–1
:
10) having a concentration of 100 μg mL−1 were dropped. The sheet containing samples were then placed in a desiccator for drying overnight. Finally, the AFM imaging was done in tapping mode using a Bruker AFM instrument.
FTIR spectra of all the concentrations of mQD:
DOTMA were recorded from 450 cm−1 to 4000 cm−1 using a Spectrum Two spectrometer from PerkinElmer in ATR mode. Further, analysis of the powder was done to obtain the XRD diffraction pattern using a Bruker-D8 Discover with a speed of 0.2 min−1 from 5° to 90°.
A Malvern Panalytical Zetasizer Nano ZS was utilized to conduct Dynamic Light Scattering (DLS) for the solution-based size characterization of mQDs and mQDs:
DOTMA. Subsequently, the obtained data was plotted using a Gaussian fit in the OriginPro software.
The photostability of mQDs was analysed by incubating the samples for a duration of 10 days. Fluorescence intensity readings at 670 nm were taken every day following excitation with 400 nm light. The relative fluorescence intensity was plotted by normalizing each fluorescence intensity measurement against the maximum fluorescence intensity recorded.
These mQDs and mQD:
DOTMA conjugates were then dissolved in the serum free media to assess the cellular uptake and cellular uptake of these particles in a breast cancer cell line (SUM-159A) and healthy cells (RPE-1).
Cell viability (%) = Absorbance of the sample/Absorbance of the control × 100.
The mQDs thus formed have an inherent negative charge, which prompted us to conjugate it electrostatically with the positively charged small lipid molecule N-[1-(2,3-dioleyloxy)propyl]-N,N,N-trimethylammonium chloride (DOTMA). The mQDs and DOTMA were mixed in the following ratios: 1:
0.25, 1
:
0.5, 1
:
1, 1
:
2, 1
:
5 and 1
:
10, with water as the solvent. Next, characterization studies were carried out for the mQDs and the bioconjugates.
To characterize the quantum dots thus formed the optical properties were analyzed using UV spectra and fluorescence spectra. In UV spectra, for DOTMA there were no peaks observed, whereas peaks were observed in case of mQDs at 206 nm (–OH group) and 260 nm (flavonoids), and the mQD:
DOTMA conjugate displayed both the peaks of mQDs and another peak at 327 nm as shown in Fig. 3(A). Further, for fluorescence spectra the 400 nm wavelength was chosen as it gave the maximum intensity. Fluorescence spectra of DOTMA showed a peak at 460 nm, and both mQDs and the mQD
:
DOTMA conjugate displayed peaks at 460 nm, 495 nm, 549 nm and 679 nm upon excitation at 400 nm as shown in Fig. 3(B). As the DOTMA concentration increased the fluorescence intensity of the sample increased (Fig. 3(B)). Hence, we observed the presence of DOTMA not only enhanced the fluorescence of mQDs but also increased the photostability of mQDs (ESI Fig. 1†). Next to understand the functional groups present on our quantum dots we performed FTIR, and the spectra show the presence of different functional groups present on the surface of mQDs: 2923 cm−1 for alkanes and acidic groups; 2850 cm−1 for aldehyde, alkanes, and acidic groups; 1560 cm−1 for nitro compounds; 1188 cm−1 for anhydride (acyl), amines, alcohol (alkoxy), and esters; and 938 cm−1 for alkenes (sp2 C–H), as shown in Fig. 3(C).
To analyze the size and morphology of the quantum dots Atomic Force Microscopy (AFM) and Dynamic Light Scattering (DLS) were performed for both mQDs and mQD:
DOTMA conjugates. The quasi-spherical morphology and topography of mQDs and DOTMA were observed with a size of about 30 nm and 179 nm, respectively (Fig. 3(D,E,G and H)). The ring-like structure of the DOTMA coating around the mQD can be observed in case of the conjugate and was about 580 nm (Fig. 3(F) and (I)).
mQDs and DOTMA were mixed in water as a solvent and the following ratios were made: 1:
0.25, 1
:
0.5, 1
:
0.75, 1
:
1, 1
:
2, 1
:
5, 1
:
10. The hydrodynamic size and zeta potential were assessed following the conjugation of mQDs with DOTMA as shown in Fig. 4(A–I). The hydrodynamic size of mQDs and DOTMA alone in water as solvent was measured to be 10.1 nm and 142 nm, respectively. The hydrodynamic radius of mQDs
:
DOTMA (1
:
0.25, 1
:
0.5, 1
:
0.75, 1
:
1, 1
:
2, 1
:
5, 1
:
10) in water was measured to be 122 nm, 122 nm, 122 nm, 122 nm, 164 nm, 190 nm, and 190 nm respectively. The size of the conjugates 1
:
0.25, 1
:
0.5, 1
:
0.75 and 1
:
1 showed a similar size as the mQD surface is not yet saturated with the lipid layer of DOTMA and the lipid layer/coating is still forming. As the concentration increases further the size of the bioconjugate increases with an increase in concentration of DOTMA as a new lipid layer is formed. A similar trend is observed in 1
:
2, 1
:
5 and 1
:
10 ratios where the size of the bioconjugate is approximately 164 nm, 190 nm and 190 nm as the surface gets saturated with DOTMA. Another saturation is observed in ratios 1
:
5 and 1
:
10, as even on increasing the concentration to double the amount the hydrodynamic radius remains the same. The zeta potential of our negatively charged mQD molecule is −0.99 mV and that of positively charged DOTMA is 21.1 mV. We can observe an increase in the positive charge in the conjugates as the concentration of DOTMA increases as shown in Fig. 4(J).
The SUM-159A cells with mQDs alone at concentrations of 100, 200, and 300 μg mL−1 showed cell viability of 12%, 16%, and 33% respectively. For SUM-159A cells with DOTMA alone at concentrations of 100, 200, and 300 μg mL−1 the corresponding values were 18%, 8%, and 8% respectively. This established that in SUM-159 cells mQDs alone and DOTMA alone are toxic to the cells and hence the cell viability has decreased significantly. For ratios 1:
0.5, 1
:
1, 1
:
2, 1
:
5 and 1
:
10 concentrations 100, 200 and 300 μg mL−1 were taken. The cell viability for ratio 1
:
0.5 is 38%, 104%, and 104% respectively. The cell viability for ratio 1
:
1 is 64%, 53%, and 68% respectively. The cell viability for 1
:
2 is 23%, 47%, and 68% respectively. The cell viability for 1
:
5 is 26%, 30%, and 27% respectively. And for ratio 1
:
10 cell viability is 38%, 22%, and 21% respectively. Hence, we can see that the 1
:
0.5 ratio of mQD
:
DOTMA at 200 and 300 μg mL−1 concentrations is not toxic to the cell and can be further explored as a potential molecule for bioimaging purposes.
Further with respect to RPE cells, mQDs alone at 100, 200, and 300 μg mL−1 showed cell viability of 71%, 80%, and 60%. For DOTMA alone the cell viability is 33%, 37%, and 42%. These findings suggest that DOTMA when given alone to the cells is toxic. For ratios 1:
0.5, 1
:
1, 1
:
2, 1
:
5 and 1
:
10 concentrations 100, 200 and 300 μg mL−1 were taken. The cell viability for ratio 1
:
0.5 is 150%, 252%, and 292% respectively. The cell viability for ratio 1
:
1 is 226%, 284%, and 370% respectively. The cell viability for 1
:
2 is 227%, 315%, and 353% respectively. The cell viability for 1
:
5 is 83%, 111%, and 164% respectively. And for ratio 1
:
10 cell viability is 123%, 139%, and 92% respectively. We can see that when mQDs are conjugated with DOTMA they quench the cytotoxic effect and further lead to cell proliferation as seen in Fig. 5.
In the case of both cancer cells and epithelial cells, there was an increase in uptake at concentrations of 100 and 200 μg mL−1 of mQDs compared to 50 μg mL−1 and control. Thus, the cellular uptake studies were performed with 100 μg mL−1 and 200 μg mL−1 concentrations as shown in Fig. 6.
Further uptake studies for mQD:
DOTMA conjugates were done both in SUM-159 and RPE-1 cells using concentrations of 100 μg mL−1 and 200 μg mL−1. The uptake of bioconjugates as compared to mQDs when provided alone was less in both the cell lines. This could be due to the highly positive charge on the conjugates and the increase in size, which might lead to a decrease in the uptake. Upon comparing the ratios in SUM-159A cancerous cells, we can observe that in case of 100 μg mL−1 concentration, a 1
:
2 ratio has relatively higher uptake as compared to others as shown in Fig. 7. A similar trend was observed in case of 200 μg mL−1 where the mQD
:
DOTMA bioconjugate's fluorescence intensity was lower indicating lower uptake of the molecule in the cytoplasm as shown in ESI Fig. S2.† Comparing the ratios, we found comparably higher uptake of both 1
:
2 and 1
:
10 ratios.
In the case of non-cancerous epithelial cells RPE-1, the uptake of the mQD:
DOTMA conjugate is relatively lower than only mQDs which can be due to the increase in size and positive charge on the bioconjugate. When the cells are treated with 100 μg mL−1 concentration of mQD
:
DOTMA, there was an increase in fluorescence intensity in 1
:
5 and 1
:
10 which indicates an increase in cellular uptake as shown in Fig. 8. And when the cells were treated with 200 μg mL−1 concentration of mQD
:
DOTMA, similar results were obtained (ESI Fig. S3†).
Next, we studied the effect of this biconjugate in vitro in cancerous cells (SUM-159A) and epithelial cells (RPE-1). Interestingly, our cellular uptake studies using fluorescence microscopy demonstrated that the uptake of the mQDs:
DOTMA bioconjugate in SUM-159 (cancerous cells) was lower than that of mQDs alone (Fig. 7 and ESI Fig. S2†). This reduced uptake can be attributed to the increased size and zeta potential of the bioconjugates, which may hinder their cellular internalization23 (Fig. 9). However, mQD
:
DOTMA bioconjugates with specific ratios showed higher uptake in RPE-1 cells, suggesting a potential dose-dependent effect on cellular internalization. Upon comparing different ratios of mQD
:
DOTMA, we found that in SUM-159A, the 1
:
2 and 1
:
10 ratios exhibited relatively higher uptake compared to others at both the concentrations of 100 and 200 μg mL−1, as depicted in Fig. 7. Similarly, for RPE-1 the fluorescence intensity of the mQD
:
DOTMA conjugates of ratios 1
:
5 and 1
:
10 is higher than that of mQDs at both the concentrations of 100 and 200 μg mL−1, indicating increased cytoplasmic uptake, as illustrated in Fig. 8 and ESI Fig. S2.†
![]() | ||
Fig. 9 Decreased cellular uptake of the mQD–DOTMA bioconjugate in cancer cells as compared to non-cancer cells due to increased size and zeta potential of the bioconjugate. |
Furthermore, cytotoxicity assays revealed that while both mQDs and DOTMA alone exhibited toxicity across all tested concentrations (100, 200, and 300 μg mL−1) in SUM-159A and RPE-1 cells,24 some ratios of the mQD:
DOTMA bioconjugate showed quenching of cytotoxicity of individual molecules and maintained high cell viability. In SUM-159A 1
:
0.5 at concentrations of 200 and 300 μg mL−1 showed cell viability of 104% and 104% respectively. In RPE cells these bioconjugates have increased the cell viability. The maximum cell viability was observed in 1
:
2 at 100 μg mL−1 (cell viability 227%), 1
:
2 at 200 μg mL−1 (cell viability 315%) and 1
:
1 at 300 μg mL−1 (cell viability 370%). This indicates the potential of these bioconjugates to mitigate cytotoxic effects which can be further explored in bioimaging and potential therapeutics (Fig. 5).
The versatility of mQD:
DOTMA bioconjugates opens up numerous possibilities for biomedical applications, including targeted drug delivery, cellular imaging, and therapeutics. The enhanced fluorescence intensity and photostability make them ideal candidates for sensitive and prolonged imaging of cellular processes. Furthermore, the ability to modulate cytotoxicity through ratio optimization underscores their potential as safe and effective drug delivery systems.
In conclusion, the mQD:
DOTMA bioconjugates represent a promising platform for a wide range of biomedical applications, offering enhanced fluorescence properties, tunable cytotoxicity, and potential therapeutic benefits. Future studies should focus on further optimizing the bioconjugate ratios, investigating their efficacy in vivo, and exploring additional characterization techniques to fully realize their translational potential in biomedical research and clinical practice. This shows that the bioconjugate is not toxic and can be used in therapeutics.
Footnotes |
† Electronic supplementary information (ESI) available. See DOI: https://doi.org/10.1039/d4na00306c |
‡ These authors contributed equally. |
This journal is © The Royal Society of Chemistry 2024 |