Integration of multi-scale defects for optimizing thermoelectric properties of n-type Cu1−xCdxFeS2 (x = 0–0.1)

Abstract

The performance of thermoelectric (TE) materials is strongly influenced by multi-scale defects. Some defects can improve the TE performance but some are unfavorable. Therefore, the multi-scale defects need to be integrated rationally to enhance the TE properties. Here, the defects including atomic-scale point defects, high-density grain boundaries and nano-precipitates were integrated into CuFeS2, an n-type and Earth-abundant TE material. Primitively, a Cd dopant with high scattering factor was introduced to form Image ID:c9nr04693c-t1.gif point defects in Cu1−xCdxFeS2 (x = 0–0.1) according to the calculated scattering parameters. Furthermore, the processes of quenching, annealing, high-energy ball milling (QAH) and sintering were carried out to integrate the multi-scale defects into Cu1−xCdxFeS2. The results suggested that Image ID:c9nr04693c-t2.gif point defects and Image ID:c9nr04693c-t3.gif antisite defects were achieved and the unfavorable Cd′Fe defects were suppressed effectively, leading to a higher electrical conductivity. Moreover, the CdS nano-precipitates played a vital role in carrier filtering to increase the Seebeck coefficient. Meanwhile, the high-density grain boundaries suppressed the lattice thermal conductivity. As a result, a peak ZT value of 0.39 at 723 K was obtained in Cu0.92Cd0.08FeS2, which is the highest value reported so far in the CuFeS2 family.

Graphical abstract: Integration of multi-scale defects for optimizing thermoelectric properties of n-type Cu1−xCdxFeS2 (x = 0–0.1)

Supplementary files

Article information

Article type
Paper
Submitted
03 jun 2019
Accepted
20 ago 2019
First published
20 ago 2019

Nanoscale, 2019,11, 17340-17349

Integration of multi-scale defects for optimizing thermoelectric properties of n-type Cu1−xCdxFeS2 (x = 0–0.1)

B. Ge, J. Hu, Z. Shi, H. Wang, H. Xia and G. Qiao, Nanoscale, 2019, 11, 17340 DOI: 10.1039/C9NR04693C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements