Crumpled thin sheets exhibit extraordinary characteristics such as a high strength combined with a low volume ratio. This review focuses on the physics of crumpled thin sheets, including the crumpling mechanics, crumpling methods, and the mechanical behavior of crumpled thin sheets. Most of the physical and mechanical properties of crumpled thin sheets change with the compaction ratio, which creates the opportunity to obtain the properties that are needed for a specific application simply by changing the compaction ratio. This also enables obtaining unusual combinations of material properties, which cannot be easily found in nature. Furthermore, crumpling starts from a flat surface, which could first be decorated with (nano-) patterns or functionalized through other surface treatment techniques, many of which are only applicable to flat surfaces. Ultimately, the crumpling of thin sheets could be used for creating disordered mechanical metamaterials, which are less sensitive to geometric imperfections compared to ordered designs of mechanical metamaterials that are based, for example, on origami or lattice structures.
In this paper, we review the existing literature on the crumpling of planar materials with the aim of exploring the possibilities and providing strategies for fabrication of 3D porous materials. In the first section, we describe the methods that could be used to create crumpling-based 3D materials. Then, the different factors influencing the folding mechanics are described. The relationships between the applied forces and deformations as well as the morphological characteristics (e.g. density, porosity, surface curvature, etc.) and the related folding networks are discussed as well. Furthermore, the relationships between the mechanical properties of crumpled structures such as stiffness, strength, and relaxation and the underlying physics are addressed. Finally, a range of potential applications and strategies for designing advanced metamaterials are proposed.
![]() | ||
Fig. 1 Crumpling methods with (a) crumpling by hand, (b) crumpling with the use of a net of wires evenly distributed over the surface of the ball, and (c) crumpling in a cylindrical die with axial compression. (d) Isotropic compaction of aluminum crumpled balls using ambient pressure.29 (e) Numerical simulation of crumpling in a spherical shell.34 |
The method most similar to hand-crumpling is perhaps crumpling in a 3D sphere, which could change in radius. This method is often used in simulations and numerical models of the crumpling of thin sheets (Fig. 1e).13,30–34 However, this method is much more difficult to apply in practice.
Habibi et al.6 and Mirzaali et al.17 used a net of wires distributed equally over the surface of a loosely crumpled ball (Fig. 1b). The wires go all through a hole in the bottom plate and are connected to a weight, which causes the wires to tighten equally and decrease the radius of the sphere they create.
Lin et al.29 used ambient pressure on a loosely crumpled ball to compress it further (Fig. 1d). They found that the force that was needed to crumple aluminum and high-density polyethylene (HDPE) sheets with ambient pressure was much higher than in crumpling by hand. In addition, a much lower crumpling ratio can be reached with crumpling by ambient pressure as compared to crumpling by hand.29 In the most confined state, the crumpled ball they created contained only 7% body fraction, while this could be up to 25% in hand-crumpled specimens.
Another approach to crumple a sheet within a sphere is to keep the sphere the same size while enlarging the thin sheet. Aharoni and Sharon10 used temperature-responsive elastic sheets in a glass sphere filled with water in which the swelling of the sheets could be controlled by controlling the temperature of the water. This technique could only be applied to specific materials. Spherical crumpling of thin sheets is challenging in practice, which is why it has not been widely used.
A frequently used crumpling technique is application of a cylindrical die (Fig. 1c),7,11,23,35–37 which is known to be well reproducible.36,37 Cambou and Menon35 compressed polydimethylsiloxane (PDMS) sheets either radially, by decreasing the radius of the cylindrical die, or axially, by reducing the height within the cylindrical die with a flat piston. They showed that using a cylindrical die to crumple a sheet causes vertical alignment near the top and bottom plate regardless of the confinement method (axially or radially). Cottrino et al.36 observed similar behavior when crumpling aluminum sheets in a cylindrical die through axial confinement. This alignment is much stronger in cylindrical confinement as compared to spherical confinement.35 The cylindrical die is also used to prepare the samples such that they could undergo compression tests.36,37
To combine the strengths of several methods and minimize the limitations, the methods are sometimes combined. An example is hand-crumpling combined with compression by a piston38 or squeezing by a tip-tweezer,8 where a loose ball is formed by hand and further compression is accomplished using the other technique.
Apart from the method used to crumple a thin sheet, the crumpling rate seems to influence the characteristics of final structure. In aluminum foils, it has been shown that the stress–strain behavior depends on the loading rate38 particularly when compressed in a simple compression test.36 Simulations of a rectangular, elastic sheet crumpled in a spherical shell show that configurations with low elastic energy are more likely to appear during slow deformation.34 Tallinen et al.34 discovered that when frictionless elastic sheets are crumpled slowly, two different final modes could be achieved: a highly random crumpled ball with high deformation energy and entropy or a crumpled ball with symmetric folds showing a low entropy and deformation energy. Both modes were found to appear equally frequently, implying that there is a competition amongst states of low energy and high entropy.34
Additionally, simulations on graphyne nano sheets crumpled in a spherical shell32 exhibit the importance of the crumpling rate as well. At slow crumpling rates, high symmetry is usually detected in the folding, while high crumpling rates result in a much more random folding pattern and show an approximately constant increase of potential energy during the confinement.32 This indicates that higher stress levels are reached within the sheet when crumpled under a higher crumpling rate.32 Moreover, Becton et al.32 discovered that the temperature and the initial shape of the graphyne nano-sheet affect the geometry of the crumpled structure. At low temperatures, the packing of graphene is more rigid and it shows a higher tendency to unfold when the confinement pressure is released.32 However, the overall behavior does not differ significantly. In general, the only difference is an increase in flexibility with temperature, initiating a higher propensity for abnormal crumpling modes.32 The geometry of the graphyne nano sheet particularly affects the initial crumpling behavior.32 A circular sheet will first form a horn before self-adhesion causes the sheet to roll up, while in a square sheet the corners will fold towards the diagonal opposite corners and then buckle in the middle until self-adhesion occurs and the sheet will form an indeterminately folded sheet.32 In a triangular sheet, two corners will fold in the same direction, while the third corner will fold in the opposite direction.32 Notwithstanding those differences within the initial crumpling, the hardness and the bulk modulus of the triangular and square sheets were found to be within 10% of the hardness and the bulk modulus of the circular sheets, suggesting that the final crumpled structures of all three geometries are similar.32
![]() | ||
Fig. 2 (a–c) Hand-crumpled paper balls with a compaction ratio (D/D0) of 0.35, 0.25, and 0.15 respectively. (d) Dimensionless crumpling force (F/Eh2) as a function of compaction ratio (D/D0) in crumpled sheets of PDMS (green), aluminum (red), paper (blue) and mylar (yellow), fitted by eqn (2) with β is 6.0, 5.9, 4.5 and 3.9 for PDMS, mylar, printing paper and aluminum respectively.6 (e–g) Cross sections of the crumpled paper balls shown in (a–c), showing the layers created during the crumpling process. (h) Number of layers (N) as a function of compaction ratio (D/D0) for crumpled PDMS (green), aluminum (red) and paper (blue), based on findings of Habibi et al.6 and Deboeuf et al.,7 fitted by eqn (5) with γ is 1.2, 1.7 and 2 for aluminum, PDMS and paper respectively. (i–k) Unfolded crumpled paper balls with compaction ratios (D/D0) corresponding to the crumpled balls in (a–c), revealing the ridge network created during crumpling. (l) Correlation between average ridge length (lmean) and compaction ratio (D/D0) in crumpled paper, based on the results of Balankin et al.,39 showing the mean length of ridges scales with the initial size of the sheet and the compaction ratio (D/D0). |
Crumpling of aluminum foils and high-density polyethylene (HDPE) films under ambient pressure has shown a power-law correlation between the compaction force (F) and the final ball size (R).29 This relationship could be expressed as:29
R ∝ R0νF−α | (1) |
Similar power laws relating the compaction ratio to the compaction force have been found in other studies.6–11 Habibi et al.6 crumpled polydimethylsiloxane (PDMS) (thickness t = 1 mm), Mylar (t = 75, 36, 23 and 19 μm), regular printing paper (t = 100 μm), and aluminum foils (t = 20 and 8 μm) using a net of wires, distributed homogeneously over the external area of a loosely crumpled material (Fig. 1b). All materials showed a power-law behavior (Fig. 2d) which could be expressed as:
![]() | (2) |
Simulation results indicate similar power-law relationships between the compaction force and the dimensions of the compacted geometry. In particular, Vliegenthart and Gompper30 studied the confinement of a 2D sheet in a 3D sphere through simulations. They found that when the compaction force exceeds a certain threshold, the correlation between the radius of the crumpled material and the compaction force obeys a power-law function, which could be expressed as:30
![]() | (3) |
At higher levels of compaction, the resistance of crumpled materials increases drastically,29,40 which is referred to as the locking state and corresponds to an exponential function.29 The critical force which leads to this state is determined by the thickness of the sheet and the type of material.29
t/LC = 4 × 10−5 | (4) |
Another interesting phenomenon that occurs during crumpling is the formation of various layers.6,7,9,29,41 Research in aluminum sheets crumpled by hand41 as well as aluminum and HDPE sheets crumpled under ambient pressure29 show that many layers are created in the initial steps of the crumpling process. This is most likely due to the high degree of freedom in space, allowing the material to form new layers.29,41 However, when the material becomes denser, the possibility to form new layers becomes limited, resulting in a lower amount of newly formed layers.29,41 Even further confinement only enables the material to buckle and surge, as there is no space left to form new layers.29,41 Fig. 2e–g show the cross-sections of the corresponding hand-crumpled paper balls in Fig. 2a–c, illustrating that the number of layers increases with increasing compaction.
The correlation between the number of layers and the number of vertices in crumpling aluminum foil and HDPE sheets under ambient pressure has been also studied.29 It shows that as the number of vertices increases, the number of layers decreases.29
Additionally, Habibi et al.6 found a power-law relationship between the size of the crumpled ball and the number of layers (N) in spherically crumpled PDMS, Mylar, paper, and aluminum foils:
N ∝ (D/D0)−γ | (5) |
The layers that originated during the crumpling process have the tendency to stack.9 Research in hand-crumpled aluminum sheets with a volume fraction of 8.5%9 shows more stacking in the outer layers of the crumpled ball as compared to the center of the ball. Additionally, higher numbers of layers are more often found in crumpled balls with a higher compaction, starting from the outer side and developing towards the core with growing compaction.9 This corresponds to the findings of Lin et al.41 demonstrating the mass tends to accrue at the crust of the ball in loose compacted aluminum balls. However, they state that the mass distribution becomes more homogeneous when the compaction grows denser. In crumpled aluminum samples compressed in a cylindrical die, the volume fraction is homogeneously distributed over the height but is nonhomogeneous over the diameter.36 Interestingly, the density decreases near the edges in those samples36 in contrast to hand-crumpled paper balls. Cottrino et al.36 found that the layers formed in crumpled aluminum foils tend to orient in a direction perpendicular to the compaction force. Furthermore, they found an increase in the number of contact points with the degree of compaction.36 The stacking behavior in crumpled structures therefore seems to depend on the crumpling technique.
Simulation of self-avoidant and phantom sheets crumpled in a three-dimensional sphere show that the differences between self-avoidant and phantom sheets are mainly caused by self-contacts.30 In loose compacted balls, only a few line-like contacts are present. The number of line-like contacts, however, grows with the compaction ratio as well with the two-dimensional contact area.30 The number of two-dimensional contact regions expands with further compaction and in highly compacted crumpled balls, the contacts mainly consist of two-dimensional contact regions rather than line-like contacts.30 Interestingly, ridges compressing on flat areas are rarely found.30 Another study, simulating a crumpled ball in one dimension, has also shown numerous self-contacts in high confinement.40
In hand-crumpled paper balls compressed by a constant force, the size and mass of the ball have been found to be correlated according to a fractal scaling law:24,25
M ∝ RD | (6) |
A laser and a CCD camera were used in another work to study ridge networks in flattened hand-crumpled paper balls.14 In this approach, the intersection of the vertical laser beam with the surface of de-crumpled paper is captured. Using this technique, it was found that loose compaction results in the formation of large ridges. After further compaction, those large ridges are randomly split into smaller ridges of various length. Blair and Kudrolli14 found that the distribution of the ridge lengths match a log-normal distribution. The same has been suggested by Wood31 and is supported by the statistical study of Sultan and Boudaoud40 on a minimal 1D model of a crumpled paper. Furthermore, Deboeuf et al.7 de-crumpled paper balls, after they were cut in half, to evaluate the number of layers. They scanned the de-crumpled paper to detect the ridge network and compared the obtained data on ridge lengths with a log-normal and a gamma distribution. They concluded that the gamma distribution overestimated the probability at small ridge lengths whereas the log-normal distribution showed a better fit. The log-normal distribution suggests the ridges will form in a hierarchical order.7 This is in line with the findings of Blair and Kudrolli14 according to which the ridges will randomly split during confinement, forming smaller ridges. Andresen and Hansen12 found that for the lower ridge lengths, the log-normal distribution fits well, supporting the findings of Blair and Kudrolli,14 Deboeuf et al.,7 and Sultan and Boudaoud.40 However, the distribution of the higher ridge lengths is better captured by a power-law function.12 Simulations of confining flexible flat sheets in a three-dimensional sphere30 support the finding that the distribution of ridge length could be described either by a log-normal or an exponential distribution.
Several theoretical studies state ridges always intersect at vertices.33,46,47 Research in hand-crumpled paper12 confirmed this statement. Andresen et al.12 observed that the maximum probability of the number of ridges intersecting at a vertex, also known as the node degree, was at the median, implying a Gaussian distribution. Only the tail of the distribution was better fitted by a log-normal distribution.12 Surprisingly, Blair and Kudrolli14 noticed that not all ridges are connected in flattened hand-crumpled paper. They investigated the number of neighbors at the end of a ridge and found that some ridges are without any neighbors. They provided two possible explanations for these findings. According to one of those explanations, this could be a consequence of the research method, as the ridges are examined after flattening the crumpled sheet of paper, which causes the recovery of elastic deformations. The alternative explanation is that the paper is capable of absorbing the forces producing the ridges, causing the ridges to dissipate near the ends due to the thickness of the sheet. During their study, they also discovered that a vertex with four ridges intersecting is the most common. Therefore, they looked at the angular distribution in a vertex where four ridges intersect. They found the angles are broadly distributed between 0° and 180° with predominant peaks at 20°, 60°, and 110°, which indicates that the d-cone geometry is dominant in a vertex where four ridges meet.14
Using the concept of node degree, Andresen and Hansen12 investigated the connectivity of different nodes and found that small-degree nodes tend to make a connection with large-degree nodes rather than other small-degree nodes. This is known as a disassortative network,12,48 which is found in nearly all technological and biological networks.48 The clustering coefficients that Andresen and Hansen12 found in their flattened hand-crumpled paper are in the range 0.13–0.23, indicating that the network is planar. In comparison with the clustering coefficient of a planar Delaunay network with similar spatial layout of the nodes, which describes the maximum possible clustering, the clustering coefficient in the crumpled paper is considerably lower. This shows that the ridge network in hand-crumpled paper does not develop highly interconnected sets of vertices.12
The vertices and ridges enclose a small area of the sheet called a facet.12,13 The number of ridges and vertices that enclose such a facet differ. In hand-crumpled paper, the facets were most often connected to three vertices12 and, thus, to three ridges. Furthermore, the distribution of the number of vertices per facet was best fitted by a log-normal function.12 Additionally, the facet sizes were found to match a log-normal distribution.12 Simulations on spherically crumpled elastoplastic sheets show a log-normal distribution of facet sizes.13 Tallinen et al.13 suggested that the average ridge length should scale with the size of a facet. Vliegenthart and Gompper30 simulated the crumpling of a flexible flat sheet in a sphere and found a log-normal distribution of the ridge length, corresponding well to the log-normal function found by Tallinen13 et al. for the distribution of the facet area. However, Blair and Kudrolli14 found a slightly wider ridge length distribution in hand-crumpled paper. This could be due to the fact that one facet is surrounded by multiple ridges of various lengths.13 Interestingly, Tallinen et al.13 found that the distribution of facet area in elastic sheets was slightly better fitted by a gamma distribution, which was also observed for the ridge length distribution in a one-dimensional simulations of crumpling.40 The difference in facet size distribution in elastic and elastoplastic sheets could be explained by the difference in forming layers during crumpling, as elastic sheets show much stronger layering.13
Another interesting feature in crumpled materials is curvature. In crumpled materials, the facets contain low curvature, while the network of ridges contains high curvatures.9 Research on aluminum sheets crumpled in a cylindrical die has revealed that the curvature of ridges increases with the compaction ratio.36 Cambou and Menon9 studied the distribution of the radius of curvature in hand-crumpled aluminum and found that the radius of curvature at the peak of the histogram is much higher than what is required to initiate plastic folds in aluminum. This suggests that there is a limiting value of curvature at which new features are created by the crumpling process rather than increasing the curvature in the existing ridges. They also found a homogeneous distribution of radii of curvatures throughout the structure without any preference to originate at the confining walls. This is in contrast with what is found for crumpling in two dimensions by pulling a sheet through a hole and only look at the cross section, where the radii of curvature are different in the bulk of the material as compared to its boundaries.9,49
![]() | (7) |
![]() | (8) |
This approach was previously suggested by Lobovsky et al.50 in their simulations of crumpling elastic sheets in an impenetrable sphere. Tallinen et al.13 used a similar approach in their models of a rectangular elastic or elastoplastic sheet crumpled in a spherical shell. To find an expression for the total energy stored in a crumpled structure, they used an approximation for the number of ridges (NX):
![]() | (9) |
![]() | (10) |
For elastic sheets they found α ≈ 1.65 for where R0 is the initial shell radius and β = 1/3,13 corresponding to the previous statement. From this expression, a scaling relationship could be derived:
EelT ∝ R−2.76 | (11) |
This scaling relationship for elastic sheets is equivalent to the findings of Vliegenthart et al.30 In elastoplastic sheets, ridges appear very early in the process because of plastic deformations. In the later phases of the crumpling process, the scaling of energy is similar to the elastic sheet. The scaling parameters are therefore similar as well.13
Another commonly used approach to determine the total energy stored in a crumpled sheet is to divide it into different energy contributions. Early research already suggested that the sum of stretching and bending energies is equal to the total energy.50–52 Chaïeb and Melo51 crumpled deoxidized high phosphorus (DHP) copper sheets in a cylindrical die and assumed the stretching energy to be constant, as the creases are self-similar and the stretching energy does not depend on the ridge length or the panel radius. Therefore, the only variable was the bending energy, which depends on the ridge length, rigidity, and the compaction ratio. Wood31 argued that the stretching energy is not constant, but that the ratio between the stretching and bending energy at the energetic minimum is equal to five. Vliegenthart and Gompper30 did simulations on a single ridge to predict the contributions of stretching and bending energy. They found a similar ratio of the stretching and bending energy on a single ridge when all sides of the sheets were fixed. However, when they fixed only one edge, the ratio was equal to twelve, which is probably caused by the relaxation of the elastic energy in the sheet.
Vliegenthart and Gompper30 state that in a flexible sheet, the Föppl-von Kármán number characterizes the elastic properties. They found an expression for the total energy (ET) in a crumpled sheet by integrating the force in eqn (3) with respect to the final radius:
![]() | (12) |
Eb = γαηβ | (13) |
Furthermore, crumpled membranes are known to dilate after the compressing load is removed, quickly at first followed by a slow expansion.36,53 This is known as stress relaxation and is caused by the relaxation of the ridge network, which is created during the process of crumpling.36 This property could be very interesting in potential applications and will therefore be discussed at the end of this section.
![]() | (14) |
![]() | ||
Fig. 3 Mechanical behavior of a crumpled thin sheet. (a) The correlation between the initial relative modulus (E0/ES) and the initial relative density (ρ0/ρS) for crumpled aluminum sheets (red), 20 μm thick, compressed at a compression rate of 0.17 mm s−1, fitted by eqn (14)37 and crumpled paper sheets (blue), 24, 39 and 68 μm thick, compressed at a compression rate of 0.1 mm s−1, which all could be fitted by eqn (15).4 (b) The yield stress (σy) as a function of the initial relative density (ρ0/ρS) for aluminum with thickness t = 20 μm compressed in closed die conditions at compression rate of 0.1 mm s−1 (red diamonds), fitted by eqn (16),37 as well as aluminum with thickness t = 22 μm compressed in a simple compression test at 1 (red crosses) and 10 mm s−1 (red circles) both fitted by eqn (17).38 (c) Stress–strain curves of crumpled aluminum samples with different initial relative densities, uniaxially loaded in a closed cylindrical die.37 |
This result supports the conclusion of Balankin and Huerta4 that the relative Young's modulus of a crumpled material is related to its relative density through a power-law relationship. However, they found slightly different scaling parameters in their study in crumpled hyperelastic latex rubber and elastoplastic paper balls under axial compression using a simple compression test:
![]() | (15) |
This difference could be caused by the differences in material or testing conditions. It has been shown that differences in the conditions of the compression tests will affect the strength of the crumpled material, as the required force to achieve a certain strain was higher in a compression test using closed die conditions than in a simple compression test.36 Research on crumpled graphene oxide (GO) presents a similar correlation between the relative density and the relative Young's modulus regardless of the fact that graphene structures could be bonded by van der Waals bonds or even be covalently bonded.54 This power-law relationship suggests that crumpled materials could be considered as a special class of cellular materials, as the same power-law dependence has been universally observed for cellular materials such as foams.36,54–57
In cellular materials, the yield stress (σy) is also dependent on the relative density through a power-law function.54–56 The same has been observed for crumpled materials (Fig. 3b).37,54 Bouaziz et al.37 found that the yield stress (σy) in hand-crumpled aluminum compressed under closed-die conditions scales as:
![]() | (16) |
This suggests that the ridges and thin walls start to deform plastically.37 The yield stresses uncovered in simple compression tests of hand-crumpled aluminum are slightly lower than the ones found in a compression test under closed-die conditions38 and could be described by:
![]() | (17) |
The transition from elastic to plastic behavior is clearly marked (Fig. 3c), as is the case in foams.37 However, when the yield stress (σy) is reached, the stress (σ) within the material keeps increasing in contrast to foams that show a flat line.37 The plastic behavior after the yield stress is reached causes energy dissipation, leading to changes in the microstructure and hardening of the crumpled material.36–38 Strain hardening has been found in crumpled graphene oxide (GO) as well, and the hardening causes the material to become highly resistant towards further compaction both in dry conditions and solutions.54 Bouaziz et al.37 showed that in hand-crumpled aluminum, the increase in the stress (σ) after the yield stress has been reached, scales with densification:
![]() | (18) |
This relationship has been also found to hold for entangled materials.37 The values of the scaling parameter (p) are, however, lower in hand-crumpled aluminum (1.5 ≤ p ≤ 1.7) as compared to entangled materials (3 ≤ p ≤ 5).37
Cyclic loading at low strains shows a small hysteresis (Fig. 3c)36–38 with nonlinear recovery after unloading. However, the starting and finishing points of an unload-reload loop are very close and, once the loop is finished, the loading curve will continue along the initial monotonous loading curve.37 This small hysteresis indicates that the energy dissipation and internal friction are little,36,38 which is different from entangled wires.36 Possible explanations are a lower motility within the crumpled structure, more interlocking, and a limited topological rearrangement.36,37
The mechanical behavior does not solely depend on the internal properties such as the relative density of the crumpled material but may be also affected by a number of external factors such as the strain rate.36 It has been shown that crumpling aluminum foils in a cylindrical die using a high strain rate creates a material that exhibits lower stress values and, thus, lower strengths as compared to a sheet crumpled under a low strain rate.36 However, this effect was only observed in simple compression, while the effects of the strain rate were negligible in closed-die conditions.36 Additionally, the same study showed a decrease in the stiffness and strength when the aluminum foil was folded into two, four, or eight plies before crumpling, most likely because pre-folding causes the foil to organize and therefore decreases the internal friction in the crumpled structure.36 It was even shown that the conditions during the compression affected the strength of the crumpled material, as the required force to achieve a certain strain was higher in a compression test using closed-die conditions than in a simple compression test.36 Furthermore, Cottrino et al.36 studied the impact of several processing techniques on the strength and stiffness of crumpled aluminum. In the first group, a Gleeble machine was used to create bonding after crumpling the aluminum by applying an electric current, while the second group of samples were annealed after crumpling by keeping them in a salt-bath at 425 °C for 7 minutes. The samples of the last group were covered with a thin layer of epoxy glue at one side of the sheet before crumpling. Annealing the samples, group two, does not strengthen the crumpled material. However, the material is not substantially weakened by this procedure either, which indicates that the stiffness depends on the yield stress.36 The samples bonded using a Gleeble machine showed a minor increase in the stiffness and the strength of the crumpled aluminum.36 The glued samples show the highest increase in the mechanical behavior in crumpled aluminum due to the strong bonds that arise from the procedure.36
νe = −ε⊥/ε∥ | (19) |
λ⊥ = λ∥−ν | (20) |
![]() | ||
Fig. 4 (a) Lateral expansion ratio (λ⊥) as a function of axial compression ratio (λ∥) for crumpled aluminium sheets (red diamonds) of initial size 500 × 500 mm, fitted by eqn (20) with ν = 0.22 (red dashed line) and eqn (19) with νe = 0.34 (red dash-dot line), and for crumpled paper sheets (blue symbols) of initial size 500 × 500 mm (open symbols) and 250 × 250 mm (closed symbols), fitted by eqn (20) with ν = 0.17 (blue dashed line). (b) Lateral strains (−ε⊥) versus axial strains (ε∥) for crumpled aluminum sheets (red diamonds) of thickness t = 20 μm and initial size 500 × 500 mm and 200 × 200 mm, approximated by eqn (19) with νe = 0.33 (red dashed line).27 (c) The correlation between the Poisson ratio (νe) and the relative density in crumpled aluminum sheets of thickness t = 20 μm and different initial sizes to create different relative densities, fitted by νe = 0.33 − exp(−200(ρ0/ρS)3).37 |
Gomes et al.58 found that, in crumpled aluminum foils, the Poisson's indices depend on the foil thicknesses. However, Balankin et al.27 showed that the Poisson's effect in crumpled aluminum foil could be captured by a universal Poisson's index of ν = 0.25 ± 0.04, although a universal linear relationship (Fig. 4a and b) with a Poisson's ratio of νe = 0.33 ± 0.02 showed even a better approximation. The difference in the dependence of the Poisson's effect for plastic and elastoplastic sheets suggests that they belong to different universality classes.27
Bouaziz et al.37 evaluated the transverse compression Poisson's ratio upon unloading as well. Those observations showed the Poisson's ratio varies with the relative density (ρ0/ρS) of the crumpled material.37 Fig. 4c shows that below a relative density of 0.15, in the transverse process of compression, the Poisson's ratio is negative,37 which signifies that the material is auxetic.27 This kind of auxetic behavior could make crumpling an even more interesting basis for creating mechanical metamaterials, as the auxetic behavior59 is one of the most sought after behaviors when designing mechanical metamaterials.
F(t) = F(0)exp[−(t/τ)β] | (21) |
![]() | ||
Fig. 5 (a) Stress relaxation after loading a crumpled aluminum sheet of thickness t = 14 μm and initial size 280 × 280 mm, strained at 2 × 10−2 s−1 (dashed line) and 4 × 10−2 s−1(solid line).36 (b) Relaxation after loading by keeping the load constant (200 g) and observing the change in height (h − h0) in tissue paper (Kimwipes®: one-ply white wipers 381 × 431 mm),11 aluminized mylar sheets, circular with D = 340 mm and t = 12.5 μm, fitted by h − h0 = −0.14![]() |
Instead of keeping the displacement constant, the compression force could be kept constant to study the creep behavior of crumpled sheets. This method was used by Matan et al.11 as they placed a mass on the piston that compressed aluminized Mylar in a cylindrical die. They studied the changes in the height during a couple of weeks and observed that the asymptotic height was not reached even after three weeks. They found a logarithmic dependence of the height on time:
h = a − b![]() | (22) |
When measuring the relaxation after the discharge of the confinement load, the increase in ball diameter is usually measured. Huerta et al.53 found that, during a ten days period, the increase in the ball diameter of elastoplastic sheets scales as:
R(t) = R(0) + ν(R/L)ln(t/τε) | (23) |
![]() | ||
Fig. 6 An overview of potential applications for crumpled-based materials. (a) Robust sensation of strain and pressure using crumped sheets of graphene oxide.60 (b) Encapsulation of Si nano-particles using graphene micro-meter sized graphene sheets through the evaporation process of liquid droplets to improve the performance of lithium ion batteries.61 (c) Reduction of friction coefficient of lubricants using crumpled graphene balls.62 (d) Dynamic control of surface wettability based on crumpled patterns of molybdenum disulfide (MoS2) on a polystyrene (PS) substrate achieved via shrinkage of PS layer.63 (e) Super flexibility achieved based on a simple chemical treatment of natural wood.66 The micro structure of super flexible wood might be mimicked artificially based on crumpling of planar materials. (f) The surface of crumpled-based scaffolds can be functionalized to adjust the pattern of cell adhesion.69 (g) Surface curvature can adjust the cytoskeletal tensions.77 |
Crumpled graphene may be promising for creating new ways to store energy with applications in sensors, actuators, and solar cells.54 Crumpled graphene oxide (GO) has been used to create strain and pressure sensors with extremely high pressure sensing capability at ultra-small strains (Fig. 6a).60 Moreover, microscale graphene oxide (GO) sheets have been used to encapsulate Si nano-particles based on capillary forces during evaporation of aerosol droplets (Fig. 6b).61 Composite capsules of GO/Si can greatly improve the performance of lithium ion batteries. Miniaturized crumpled graphene balls have been shown to be highly influential in reduction of friction and wear while used as additives in lubricant-based oils (Fig. 6c).62 The 2D crumpling of molybdenum disulfide (MoS2), based on shrinkage of a polystyrene (PS) substrate, has been shown as a dynamic way to tune the level of wettability (Fig. 6d).63 Furthermore, crumpled materials have been shown to combine the mechanical behaviors of foams, a clearly marked elastic to plastic transition, and entangled fibrous materials, strain hardening after the yield stress is reached,37,64 which makes them a suitable candidate for numerous engineering applications such as lightweight sandwich panels, shock absorbers, or as a mechanical metamaterial for mechanical cloaking.6,36,38 Additionally, crumpled materials are a feasible alternative to more expensive engineering materials such as cellular metals due to their relatively easy production process. While maintaining robust mechanical properties17,36,54,65 they may provide super flexibility due to their cellular design (Fig. 6e).66
Crumpled materials could also be of interest for medical applications.54 Given their rich physics and the unusual combination of properties that they offer, crumpled sheets could be also used as a basis for creating advanced functionalities.59 For example, Bouaziz et al.37 showed that the crumpled material could be designed in such a way to exhibit auxetic behavior, meaning that the material would expand in the lateral direction when it is stretched, instead of contracting.59 Auxetic behavior has been found in several natural systems such as cancellous bone, tendons, living cow skin, certain zeolites, and some minerals.59 In addition to the unusual mechanical response of auxetic materials, the possibility to attain unusually high values of other material properties such as hardness, fracture toughness, indentation resistance, and energy absorption makes them very interesting.59 Auxetic materials could therefore be appealing for creating stents and smart bandages.59 Furthermore, they are highly interesting for orthopedic implants, as they could be designed to mimic cancellous bone and to fabricate meta-implants59 that lead to a longer implant longevity.
With the use of surface treatment techniques, crumpled structures could be also used to improve tissue regeneration within the context of what is referred to as meta-biomaterials17 in the literature. Most conventional techniques for surface enhancement are only applicable to flat surfaces and are therefore not useful for three-dimensional scaffolds.18–20 As a crumpled material initially starts from a two-dimensional state, the entire surface area is accessible and could be functionalized using conventional techniques, thereby allowing for fabrication of meta-biomaterials that combine complex three-dimensional shapes with surface-related functionalities.20,67 It has been shown that chemical and/or topological cues at the surface could significantly influence the behavior of cells and regulate cell orientation, cell morphology, cell proliferation, and cell differentiation (Fig. 6f and g).68–72 Additionally, the same type of surface-related cues, e.g. surface nanopatterns, could also affect the growth of bacteria73 by preventing bacteria from attaching to the surface of biomaterials and forming a biofilm,68 which may be an alternative for conventional antimicrobial agents or disinfectants, leaving toxic residue.74 Another advantage of starting from a flat surface is the possibility to incorporate drug delivery vehicles, which could then be used to deliver therapeutic agents to a specific part of the body.22,75,76
After surface functionalization, a three-dimensional structure could be obtained through crumpling. There are other techniques known for transforming a two-dimensional structure into a three-dimensional one including origami-based techniques.21,22 Most of those techniques result in an ordered origami arrangement, which are susceptible to defects.17,54 Relatively small imperfections could substantially affect the mechanical properties of the ordered three-dimensional construct.17,54 However, crumpling results in a disordered arrangement, which is less sensitive to imperfections.17 To use the crumpled structure for tissue regeneration, the structure should be porous to ensure cell nutrition, oxygenation and migration.17 In addition, the complex morphological design of crumpled-based materials can be beneficial to adjust the attachment of cells to the crumpled substrate (Fig. 6g), cell migration and differentiation of stem cells based on the patterns of forces acting on their nucleus.77 Mirzaali et al.17 studied the effects of circular holes created in crumpled Mylar sheets and concluded that the crumpling behavior is generally similar to that of sheets without holes. However, the crumpling exponents were somewhat higher, indicating that the rate of increase in the crumpling force is higher for porous sheets, which was explained by the fact that the edges of the holes could interlock. An important factor for the increase of the crumpling exponents was the fraction of surface occupied by the holes: the higher this fraction, the higher the increase of the crumpling exponent.17
In conclusion, crumpled structures are promising candidates for applications in multiple fields, due to the unusual mechanical properties of crumpled matter and the possibility to tune those properties. The fact that crumpling starts from a flat sheet increase the possibilities even further particularly in the areas where surface-related functionalities are of interest.