Open Access Article
This Open Access Article is licensed under a Creative Commons Attribution-Non Commercial 3.0 Unported Licence

A review of biomass materials for advanced lithium–sulfur batteries

Huadong Yuan , Tiefeng Liu , Yujing Liu , Jianwei Nai , Yao Wang , Wenkui Zhang and Xinyong Tao *
Department of Materials Science and Engineering, Zhejiang University of Technology, Hangzhou 310014, China. E-mail: tao@zjut.edu.cn

Received 5th June 2019 , Accepted 12th July 2019

First published on 15th July 2019


Abstract

High energy density and low cost make lithium–sulfur (Li–S) batteries famous in the field of energy storage systems. However, the advancement of Li–S batteries is evidently hindered by the notorious shuttle effect and other issues that occur in sulfur cathodes during cycles. Among various strategies applied in Li–S batteries, using biomass-derived materials is more promising due to their outstanding advantages including strong physical and chemical adsorptions as well as abundant sources, low cost, and environmental friendliness. This review summarizes the recent progress of biomass-derived materials in Li–S batteries. By focusing on the aspects of carbon hosts, separator materials, bio-polymer binders, and all-solid-state electrolytes, the authors aim to shed light on the rational design and utilization of biomass-derived materials in Li–S batteries with high energy density and long cycle lifespan. Perspectives regarding future research opportunities in biomass-derived materials for Li–S batteries are also discussed.


image file: c9sc02743b-p1.tif

Huadong Yuan

Huadong Yuan received his BS in Materials Science and Engineering from Northeast Forestry University in 2013. He is currently a Ph.D. candidate in the Professor Xinyong Tao group at the Zhejiang University of Technology. His research is now focused on advanced electrode materials for energy storage such as lithium–sulfur batteries, lithium metal anodes, and lithium ion batteries.

image file: c9sc02743b-p2.tif

Tiefeng Liu

Tiefeng Liu received his Ph.D. degree from the Harbin Institute of Technology in 2017 and went to work as a postdoctoral researcher at the Guangdong University of Technology. In 2019, he became a member of the Tao Group. His main research interests are focused on green design of lithium/sodium ion batteries.

image file: c9sc02743b-p3.tif

Yujing Liu

Yujing Liu received his bachelor's degree in polymer science in 2011 and Ph.D. degree in polymer science and engineering in 2016 from Zhejiang University, China. He is currently an associate professor in the College of Materials Science and Engineering at the Zhejiang University of Technology. His research interests focus on bioinspired strategies for regulating metallic crystallization for energy storage, such as lithium metal anodes and lithium-ion batteries.

image file: c9sc02743b-p4.tif

Jianwei Nai

Jianwei Nai received his Ph.D. degree in Materials Science and Engineering in 2014 from Beihang University. Then he conducted his postdoctoral research at Beihang University, The University of Chicago, and Nanyang Technological University until July 2018. He is currently a professor in the College of Materials Science and Engineering at the Zhejiang University of Technology. His research interests focus on controllable synthesis and assembly of transition metal-based nanomaterials for energy storage and conversion.

image file: c9sc02743b-p5.tif

Yao Wang

Yao Wang received his Bachelor of Science degree from the Department of Physics in 2011 and Ph.D. degree in Materials Science and Engineering in 2018 from Zhejiang University. In 2019, he joined the College of Materials Science and Engineering at the Zhejiang University of Technology. His interests include 2D materials, ferroelectrics and lithium metal anodes.

image file: c9sc02743b-p6.tif

Wenkui Zhang

Wenkui Zhang is a professor in the College of Materials Science and Engineering at the Zhejiang University of Technology. He received his Ph.D. degree in 1997 from Zhejiang University. His research interests focus on advanced secondary batteries and energy storage/conversion materials such as lithium-ion batteries, lithium–sulfur batteries, fuel cells, and supercapacitors.

image file: c9sc02743b-p7.tif

Xinyong Tao

Xinyong Tao received his Ph.D. from the School of Materials Science and Engineering at Zhejiang University (2007). He is now a Professor in the College of Materials Science and Engineering at the Zhejiang University of Technology. His main research interest is focused on the design and synthesis of green materials for energy storage such as lithium–sulfur batteries, lithium metal anodes, and lithium-ion batteries.


1 Introduction

The demand for energy storage technologies continues to increase due to their future applications in electric vehicles and smart grids. Lithium-ion batteries (LIBs) based on an intercalation mechanism feature the highest energy density among commercially viable energy storage technologies, but are approaching the limitation of theoretical energy density.1–5 Therefore, a new energy storage system with higher energy density is urgently required. Lithium–sulfur (Li–S) batteries, coupled with a sulfur cathode and a lithium metal anode, have attracted increasing attention due to their high energy density (around 2600 W h kg−1). The practically viable energy density of Li–S batteries is still 2–3 times higher than that of the state-of-the-art commercial LIBs.6–10 Unfortunately, the real-world applications of Li–S batteries are restricted by the low conductivity of sulfur and discharge products (Li2S/Li2S2), high volume expansion of sulfur during cycles, serious shuttle effect originating from the dissolved lithium polysulfides (LiPSs) in the electrolyte, and irreversible Li2S/Li2S2 deposition and phase conversion.9,11–13

So far, these challenges have driven intensive research on potential solutions including novel strategies and materials. Strategies to suppress polysulfide shuttling and stabilize cycle life can be divided into constructing polar sulfur hosts,14–19 developing multifunctional separators,20–22 introducing all-solid-state electrolytes,23–25etc.26–29 Accordingly, corresponding materials such as graphene, MXenes, nanotubes, functional polymers, porous carbon, metal oxides, sulfides and carbides have been massively developed.30–36 Among them, bio-materials have a great possibility of enabling commercially viable Li–S batteries due to their advantages of strong physical and chemical adsorptions, low-cost, environmental friendliness, and easy accessibility. Furthermore, naturally moulded biomass-based materials have various morphologies. Hence, the exploration of bio-materials to construct key components for Li–S batteries would be worthwhile considering the potential scale of electrochemical applications.37–45

This review aims to provide a comprehensive summary of the recent progress of bio-derived materials for Li–S batteries.38,46,47 We highlight the representative applications of bio-derived materials in Li–S batteries as the following four parts: carbon hosts, separator materials, bio-polymer binders, and all-solid-state electrolytes. Structural and chemical characterization of bio-materials is briefly surveyed. Finally, we conclude by presenting our perspective and suggestions on the further development of bio-derived materials in Li–S batteries.

2 Carbon hosts derived from biomass for storing sulfur

Due to their inherited specific structures, carbon materials derived from biomass (CDB) have attracted great attention as a promising host for storing sulfur.48,49 Furthermore, the richness of biomass in nature allows a variety of CDBs to be obtained. In this section, the progress of the representative CDBs as a carbon host for sulfur will be summarized and discussed.

Fibrous biomass such as kapok, cotton, and bacterial cellulose with a 3D cross-linked and porous structure is a promising carbon precursor candidate for carbon hosts. Benefitting from the inherited network structure, the resultant carbon host can enable high sulfur loading and fast electron transfer in a sulfur cathode. Employing low-cost and high-yield kapok fibers (KFs) as a carbon precursor, Tao and co-workers developed carbon nanoflakes modified with metal oxides (MxOy/C, M = Al, Ce, La, Mg, or Ca) via a simple carbonization step.12 A schematic of the fabrication of MxOy/C is illustrated in Fig. 2a. With the help of capillarity, the solution containing a certain metal nitrate is infiltrated into the KFs. Subsequently, scalable carbon nanoflakes decorated with (MxOy/C) nanoparticles are readily synthesized through a carbonization process. Due to the high surface area of the materials and high capability of metal oxides for trapping polysulfides, the sulfur cathodes can deliver high sulfur utilization and stable cycling performance (Fig. 1).12


image file: c9sc02743b-f1.tif
Fig. 1 The schematic diagram of bio-derived materials applied in the Li–S battery system.

An additional demonstration of a carbon host for sulfur is carbon cotton, which was applied in Li–S batteries by Manthiram and co-workers.50Fig. 2b shows the fabrication procedures of the flexible carbon-cotton cathode, which was synthesized through a simple carbonization step at 900 °C for 6 h under an Ar atmosphere.50 The obtained carbon cotton has a high surface area (805 m2 g−1), good porous structure, excellent mechanical strength, and cross-linked conductive network (Fig. 2c). Therefore, an ultrahigh sulfur loading ranging from 30.7 to 61.4 mg cm−2 is successfully achieved via a thermal diffusion method.50 Besides KFs and cotton, other fibrous biomass materials, such as bacterial cellulose, cotton cloth, silk and cobweb, are also considered for carbon hosts.51,52 These web-like biomass materials with a high surface area are conducive to integrating with sulfur and converting to carbon materials with high conductivity. Furthermore, silk and cobweb can form nitrogen dopants in the obtained carbon materials during the carbonization process, which is favorable for trapping polysulfides and improving sulfur utilization for Li–S batteries.53


image file: c9sc02743b-f2.tif
Fig. 2 (a) Fabrication diagram of MxOy/C composites. Reproduced with permission.12 Copyright 2016, Nature publishing group. (b) Schematic of the fabrication process of carbonized cotton. (c) Digital and SEM images of cotton and carbonized cotton. Reproduced with permission.50 Copyright 2016, American Chemical Society. (d) Schematic illustration of PRC. Reproduced with permission.54 Copyright 2017, Wiley-VCH.

Multiporous carbon materials derived from biomass are other promising candidates for storing sulfur due to their high surface area and superior physical adsorption for polysulfides. Rice, a staple food for people, is made up of starch. Inspired by the fabrication process of popcorn, Xia et al. developed a puffed rice carbon (PRC) material as a sulfur host via a one-pot and facile method.54 As shown in Fig. 2d, the resultant PRC exhibits a 3D microcellular architecture consisting of numerous interconnected carbon nanoflakes with a thickness of 500 nm. In addition, an effective strategy by using NiCl2 as the etching agent is used to improve the electrical conductivity and surface area of the carbon host. Rapid puffing fabrication allows Ni nanoparticles to be in situ embedded into PRC and the formation of a highly porous structure in PRC/Ni composites. Taking advantage of such a microcellular structure and good distribution of Ni nanoparticles both in the interior and on the surface, the sulfur cathode based on PRC/Ni composites exhibits a high reversible capacity of 1257 mA h g−1 and stable cycling performance at 0.2C.

In addition to the microcellular structure of PRC, the 3D aligned microchannels of wood for water transportation is also an ideal structure for sulfur loading. The vast space of the aligned microchannels in wood provides internal room for high sulfur loading. Hu and co-workers synthesized a 3D aligned porous carbon matrix using carbonized wood as the framework and reduced graphene oxide (rGO) as the filler (Fig. 3a and b).55 The rGO is filled inside the microchannels to promote the construction of multiporous and anti-deformation structures in wood channels, which can effectively improve the sulfur mass loading and the electron transport. The shuttling of polysulfides can also be suppressed due to the rich oxygen functional groups on the surface of rGO inside the wood channels. Employing this design, the sulfur cathode with a high sulfur loading of 7.8 mg cm−2 exhibits a high areal capacity of 6.7 mA h cm−2 at a current density of 1.56 mA cm−2.


image file: c9sc02743b-f3.tif
Fig. 3 (a) Schematic illustration of the fabrication process and structure of the S@C-wood composite. (b) Morphological characterization of the C-wood matrix. (a and b) Reproduced with permission.55 Copyright 2017, American Chemical Society. (c) Binding energy and related adsorption experiments between TiO2/carbon and polysulfides. (d) A model of a biological cell. (e) Biomimetic microcapsules. (f) The fabrication procedure of the biomimetic microcapsule confined sulfur cathodes (SDC@TiO2/S). (c–f) Reproduced with permission.57 Copyright 2018, Wiley-VCH.

In addition, wood microfibers with hierarchical and mesoporous structures are other good host materials applied in Li–S batteries,56 achieving a high sulfur loading of 76 wt%. Besides wood, bacteria, derived from the wastes of the pharmaceutical industry, are other promising precursors for the fabrication of hierarchically porous carbon. The mesoporous structure of the obtained carbon materials increases the utilization of active sulfur materials. For example, Zhang et al. developed a kind of uniformly porous carbon using Staphylococcus aureus as the precursor.57 The obtained carbon materials fully inherit the sphere morphology and multiporous structure of Staphylococcus aureus (Fig. 3c and d). In addition, modified TiO2 (Fig. 3e) and N dopants derived from protein after carbonization (Fig. 3f) can be employed for Li–S batteries. As a result, the as-prepared cathodes delivered ultra-stable cycling performance with 0.05% capacity decay per cycle after 1500 cycles at a current density of 1.5 A.

Although multiporous structures are advantageous for storing sulfur, most of the biomass materials have only a few macropore structures. Fortunately, such an issue can be addressed by a simple method at high temperature in an inert atmosphere using activation agents such as KOH, K2CO3, and ZnCl2. Manoj et al. reported micro/mesoporous coconut shell carbon with high specific surface areas as a carbon host for Li–S batteries.62 In addition, Table 1 shows the characterization of other carbon materials obtained from biomass.58–62 The adjustable structures, eco-friendly fabrication processes, and rich surface chemical groups offer a lot of possibilities for suppressing the shuttle effect and improving sulfur utilization, which crossed the threshold into a new depth of Li–S battery commercialization.

Table 1 Categories, fabrication methods, structures and characteristics of other carbon materials derived from biomass
Source Representative SEM/TEM image Fabrication method Surface chemical group
Coconut shell63,64 image file: c9sc02743b-u1.tif KOH activation Hydroxyl groups
Wood waste65 image file: c9sc02743b-u2.tif K2CO3 activation N dopants
Walnut shell66 image file: c9sc02743b-u3.tif KOH activation Hydroxyl groups
Pomelo peel67 image file: c9sc02743b-u4.tif KOH activation Hydroxyl groups
Rapeseed shell68 image file: c9sc02743b-u5.tif KOH activation Hydroxyl groups
Seaweed69 image file: c9sc02743b-u6.tif NaCl activation N dopants
Coffee waste70 image file: c9sc02743b-u7.tif ZnCl2 activation O and N dopants
Cherry pits71 image file: c9sc02743b-u8.tif H3PO4 activation Hydroxyl groups
Bamboo72 image file: c9sc02743b-u9.tif KOH activation Hydroxyl groups
Cyclosorus 73 image file: c9sc02743b-u10.tif KHCO3 activation S and O dopants
Jellyfish61 image file: c9sc02743b-u11.tif NH4H2PO4 activation N and P dopants
Peanut shell53 image file: c9sc02743b-u12.tif KOH activation Hydroxyl groups


3 Bio-derived materials used as separators for preventing the shuttle effect

Besides the wide application of biomass-derived carbon hosts in Li–S batteries, constructing multifunctional separators is considered as another effective method. Not only can the internal charge-transfer resistance of the Li–S cells be reduced, but also the utilization of active materials can be improved. This section will discuss the application of bio-interlayers in Li–S batteries. The reported strategies can be divided into two categories: porous carbon film coating of a commercial separator and freestanding carbon interlayer insertion between the cathode and separator. In general, any bio-derived carbon material can be employed as an active material to coat the commercial separator after the carbonization step. But for freestanding interlayer fabrication, fiber-shaped materials may be more adaptive. In addition, benefitting from the 3D cross-linked structures, the obtained freestanding interlayer is favourable for fast electron transportation in sulfur cathodes. Both porous carbon coated separators and cross-linked interlayers play an important role in preventing the shuttling of polysulfides.

The combination of biomass-derived carbon and a commercialized separator is a simple but effective method to enable a synergistic effect for chemically and physically trapping polysulfides. As illustrated in Fig. 4a, a nitrogen-doped micro-/mesoporous carbon (N-MIMEC) was fabricated using crab shell waste as the source by Huang et al.74 The obtained carbon materials with a channel-like structure possess a large surface area and abundant N dopants, which are often demonstrated for suppressing polysulfide shuttling. And hence, the obtained N-MIMEC-coated separator (Fig. 4b) exhibited many advantages during discharge/charge processes: (i) the micro-/mesopores and rich N-dopants in N-MIMEC provided strong physical and chemical adsorption for polysulfides. (ii) The mesopores in N-MIMEC promote the electrolyte penetration to enable fast diffusion of Li ions. (iii) The as-prepared N-MIMEC layer acts as an upper current collector to improve the electrical conductivity of the electrode. Therefore, enhanced cyclability of Li–S batteries with N-MIMCEC-coated separators is readily achieved with a high reversible capacity of 971.3 mA h g−1 at 0.1C. Other studies have also succeeded in fabricating various porous carbon materials from biomass, such as shrimp shell and sea grass. These carbon materials as adsorption layers are coated on commercial separators, suppressing the shuttle effect of polysulfides. To further block the polysulfides, polar group such as SiO2 modified bio-carbon materials were fabricated on a commercial separator surface.75 With the assistance of strong adsorption between the polar group and polysulfides, high sulfur utilization and stable cycling performance are achieved.


image file: c9sc02743b-f4.tif
Fig. 4 (a) Fabrication of N-MIMEC using crab shells and the detailed polysulfide suppression mechanisms of the N-MIMEC-coated separator. (b) The digital picture of the N-MIMEC-coated separator. (a and b) Reproduced with permission.74 Copyright 2017, Royal Society of Chemistry. (c) The LiPS-trapping mechanisms of the BCF@SiO2 interlayer. (c) Reproduced with permission.80 Copyright 2018, Elsevier. (d) The procedure for fabricating the freestanding CBC interlayer. (e) Schematic of the working mechanism for Li–S batteries using the CBC interlayer. (d and e) Reproduced with permission.78 Copyright 2015, Royal Society of Chemistry.

3D network bio-fiber materials are other promising interlayer precursor candidates due to their cross-linked framework and rich –OH groups.76,77 Such a 3D network structure is often made of bacterial cellulose (BC), which naturally consists of interconnected cellulose nanofibers.78 As shown in Fig. 4d, the fabrication of the BC interlayer was developed by Sun et al.78 Because of the unique interlinked network, the obtained BC interlayer endowed the composites with superior conductivity and a robust framework. More importantly, with the help of the BC interlayer inserted between the sulfur cathode and separator, not only can the excessive accumulation of sulfur be relieved, but also the shuttle effect of polysulfides in the electrolyte can be reduced through a new “guiding” strategy (Fig. 4e).76–78 The sulfur cathode exhibits a high discharge capacity of 1134 mA h g−1 at a current density of 200 mA g−1 after 400 cycles.78

Similarly, Rezan Demir-Cakan et al. proposed to synthesize freestanding pyrolyzed BC interlayers for suppressing dissolved polysulfides in the electrolyte.79 During the growth of bacterial cellulose (Fig. 5a), SnO2 particles were added into the medium of bacteria, leading to the formation of cellulose fibers modified with SnO2. Hence, an intimate contact between SnO2 and bacterial cellulose can be obtained (Fig. 5b). The sulfur cathodes employing the as-prepared SnO2@BC interlayer displayed a more stable cycle life than that containing bare pyrolyzed BC as well as without an interlayer.79


image file: c9sc02743b-f5.tif
Fig. 5 (a) Fabrication process of SnO2-containing pyrolyzed bacterial cellulose (SnO2-PBC). (b) Schematic cell configuration of the Li–S battery with the SnO2-PSC interlayer. (a and b) Reproduced with permission.79 Copyright 2018, Elsevier. (c) The fabrication of BCF. (d) Schematic illustration of the mechanism of the PGCF/Ni/S and BCF/S cycling processes. (c and d) Reproduced with permission.82 Copyright 2018, American Chemical Society. (e) The synthesis of the SMPC interlayer used in Li–S batteries. (f) Schematic cell configuration of the Li–S battery with the SMPC interlayer. (e and f) Reproduced with permission.83 Copyright 2016, Royal Society of Chemistry.

Besides bacterial cellulose, other cellulose fibers derived from wood and cotton are also investigated as interlayer materials. Cost-effective carbonized cellulose paper (CCP) is a potential interlayer for Li–S batteries.81 When inserted between the sulfur cathode and separator, the interlayer significantly improved sulfur utilization and rate performance due to the highly conductive CCP interlayer. Tu and co-workers developed a Ni-embedded porous carbon fiber (PGCF/Ni) interlayer for Li–S batteries through a facile delignification step from bamboo in alkaline solution (Fig. 5c).82 Metallic Ni nanoparticles are modified to improve the adsorption ability for polysulfides. Due to its attractive properties such as a large surface area, 3D porous structure, and high electrical conductivity, the Li–S batteries employing the functional PGCF/Ni interlayer exhibited improved electrochemical performances (Fig. 5d).

Other biomass with abundant heteroatom dopants after carbonization is another good precursor for interlayer fabrication. Low-cost Luffa sponge with abundant sources is the most representative due to the high content of sulfur and oxygen elements. As shown in Fig. 5e, Zhou's group developed a sulfur-doped microporous carbon (SMPC) material via a simple step of carbonization at high temperature.83 Unlike the aforementioned fiber-like materials, the obtained SMPC powder was rolled into a film using a twin roller and was punched into SMPC interlayers. The SMPC interlayer can prevent the shuttling of polysulfides toward the lithium metal anode. Such an interlayer opened up electron pathways to enable the reutilization of dissolved active materials during repeated discharge/charge processes (Fig. 5f).83 Various interlayers derived from biomass for Li–S batteries have been compared and summarized in Table 2. Benefitting from the inherited cross-linked structures, rich heteroatom dopants, and simple fabrication processes of these bio-interlayers, the electrochemical performance of Li–S batteries has been significantly improved.

Table 2 Categories, fabrication methods, structures and characteristics of interlayers derived from biomass
Source Representative SEM/TEM image Fabrication method Surface chemical group
Bacterial cellulose78 image file: c9sc02743b-u13.tif Carbonization Rich hydroxy
Cellulose paper81 image file: c9sc02743b-u14.tif Carbonization Rich hydroxy
Bacterial cellulose79 image file: c9sc02743b-u15.tif Carbonization SnO2 modification
Crab shell74 image file: c9sc02743b-u16.tif KOH activation Rich hydroxy
Cotton52 image file: c9sc02743b-u17.tif Carbonization Rich hydroxy
Lignin fibers85 image file: c9sc02743b-u18.tif Carbonization Rich hydroxy
Luffa 83 image file: c9sc02743b-u19.tif Carbonization Sulfur dopants


4 Binders derived from biomass for sulfur

The binder is a key component to keep electrode film integrity during the charge/discharge process. As a conventional binder, polyvinylidene fluoride (PVDF) has been widely applied in the state-of-the-art LIBs. However, the high volume expansion of sulfur and the notorious shuttle effect challenge the effectiveness of PVDF in Li–S batteries. In addition, the requirement of using toxic and volatile N-methyl-2-pyrrolidone (NMP) as solvent for PVDF is also a concerning issue. Recently, several bio-polymers have been often reported derived from biomass for Li–S batteries with improved cycling stability.84 Furthermore, the solvent for these bio-binders is water, having the merits of nontoxicity and low cost. In this section, the progress of bio-binders in Li–S batteries will be summarized.

Gum arabic (GA), a natural polymer derived from Acacia senegal, is mainly composed of highly branched polysaccharides, consisting of a galactan backbone chain with rich branched galactose, arabinose, rhamnose, and hydroxyproline side chains.26 Due to the rich hydroxyl, carboxyl, and ether functional groups, the binding interaction between the polysulfides and GA can be effectively strengthened, which offers powerful assistance for improving sulfur utilization and cycle stabilization. Li et al. reported the application of GA as a binder for Li–S batteries.26 The molecular structure of GA is revealed by Fourier transform infrared (FTIR) spectroscopy (Fig. 6a and b). The X-ray absorption spectroscopy (XAS) results (Fig. 6c) suggest that CA could chemically bond with polysulfides with no additional treatment, providing the direct mechanism for GA to suppress polysulfide dissolution in organic electrolytes. The sulfur cathode using the GA binder delivers a high initial capacity of 1157 mA h g−1 and a stable cycle life of more than 500 cycles at a current density of 0.2C.


image file: c9sc02743b-f6.tif
Fig. 6 (a) Chemical structure of GA with the background of Acacia senegal. (b) FTIR spectra of GA. (c) FTIR spectroscopy of a mixture of GA–polysulfide composites. (a–c) Reproduced with permission.26 Copyright 2015, Wiley-VCH. (d) FTIR spectroscopy spectra of (1) Na-alginate and (2) Na-alginate sulfur electrodes. (e) SEM images of the Na-alginate sulfur cathode. (d and e) Reproduced with permission.86 Copyright 2013. Elsevier.

Sodium-alginate (SA), a by-product derived from kelp or seaweed, has been widely used as a binder for LIBs due to its good adhesion and electrochemical stability. Zhang et al. reported on the preparation of sulfur cathodes using SA as the binder and water as the solvent for the first time.86 As illustrated by FTIR spectroscopy (Fig. 6e), the decreased intensity of pyranose-ring deformation vibration peaks indicates strong chemical interaction between SA and sulfur powder. Such a resultant bonding is a critical factor that can stabilize the sulfur cathodes during cycling. In addition, compared with the PVDF binder, the SA binder endows the sulfur cathode with a much more porous structure (Fig. 6f and g), which was favourable for electrolyte permeation and thus fast lithium ion transfer. More importantly, the volume expansion of sulfur cathodes during the charge/discharge process could be effectively buffered due to the formation of porous-like sulfur cathodes.

Gelatin macromolecules were adopted as a typical water-soluble binder for Li–S batteries.87 Biological gelatin has evident advantages in the preparation of sulfur cathodes. Firstly, as bio-polysulfides extracted from animal protein, rich ionizable groups such as COOH and NH2 provide gelatin with great hydrophilic capability for trapping dissolved polysulfides. The substantial insolvability of gelatin in organic electrolytes (such as carbonic acid and ether) can keep the resultant sulfur cathodes integrated on the current collector. Secondly, as a widely used agent in the food, photographic and pharmaceutical industries, gelatin is easily scaled up. Huang et al. successfully employed gelatin as a binder in the design and development of Li–S batteries.87,88 Due to its high adhesion, strong dispersion, and stable electrochemistry, the sulfur cathodes using gelatin as the binder achieved a stable cycle life. Even at a high current density of 1600 mA g−1, the sulfur cathodes based on the gelatin binder still display an evident discharge plateau, indicating that the sulfur in the cathode is converted to polysulfides.

Soy protein (SP) has abundant polar groups, such as amines and carboxyl groups, providing rich active sites for trapping dissolved polysulfides, which has been evidenced by density functional theory (DFT) calculation.89 Meanwhile, the superior conductivity of SP promotes electrochemical reactions in sulfur cathodes. Zhong et al. reported a SP–PAA binder instead of the PVDF binder for sulfur cathodes, buffering their large volume change (Fig. 7a). The stable cycle lifespan of the high-loading sulfur cathode is attributed to high mechanical strength, strong adsorption for polysulfides, and good ionic conductivity (Fig. 7b). In addition, the SP–PAA binder could effectively adjust the uniformity, the porous structure, and the interface in the resulting sulfur cathodes, which is beneficial for improving the coulombic efficiency. This strategy provides a facile method for stabilizing the cycle life of sulfur cathodes via using natural materials, indicating the great potential of biomass in Li–S batteries.


image file: c9sc02743b-f7.tif
Fig. 7 (a) The schematic illustration of a robust and multi-functional binder (SP–PAA) via the incorporation of two bio-derived materials. (b) The structural changes of the obtained bio-derived binder in sulfur cathodes during discharge/charge processes. (a and b) Reproduced with permission.89 Copyright 2019, Royal Society of Chemistry. (c) Chemical structures of bio-derived GG and XG. (d and e) Schematic of the chemical binding effect between GG and XG. (f) FTIR spectra of GG, XG and N-GG-XG. (c–f) Reproduced with permission,90 Copyright 2017, Royal Society of Chemistry.

Exploring biopolymer binders should not be confined to the area of single biopolymers. Incorporation of various biopolymers offers a greater possibility. Well-designed sulfur cathodes with a 3D network binder are beneficial for dramatically improving the cycling stability of Li–S batteries. Liu et al. developed an adaptable binder for Li–S batteries using the intermolecular binding effect between guar gum (GG) and xanthan gum (XG) (Fig. 7c–e), which are, respectively, extracted from the endosperm of Cyamopsis tetragonolobus seeds and the bacterium Xanthomonas campestris.90 Both GG and XG biopolymers are low-cost, non-toxic, and sustainable natural products (Fig. 7c). Due to the intermolecular binding effect between GG and XG (Fig. 7f), a binder network with rich oxygenous functional groups was obtained, providing strong adsorption for trapping dissolved polysulfides and realizing an ultrahigh areal specific capacity of 26.4 mA h cm−2. These results confirmed that high-energy-density Li–S batteries can be easily obtained using a biomass binder.

5 All-solid-state electrolyte derived from biomass for Li–S batteries

All-solid-state Li–S batteries with high energy density and high safety are a promising solution for next-generation energy storage systems.23 However, the application of most reported all-solid-state electrolytes is limited by complicated procedures and high-cost chemicals. Hence, safer, cheaper and more sustainable solid-state electrolyte materials should be developed.80

Starch, a form of energy storage in plants, is composed of repeated glucose monomers with glycosidic linkages, which would allow reversible ion transfer. Hence, starch is used as an all-solid-state electrolyte for Li–S batteries. To enhance the stretchable properties of the electrolyte film, γ-(2,3-epoxypropoxy)propyltrimethoxysilane (KH560) was employed to cross-link with the obtained corn starch.91 As shown in Fig. 8a, the peak related to the chemical reaction between –OH groups from starch and –Si–(OCH3)3 is observed (Fig. 8b). A possible structure of starch is composed of repeated glucose monomers joined by glycosidic linkages, which are described in detail in Fig. 8c and d. The highest ionic conductivity is achieved using 40 wt% bistrifluoromethanesulfonimide lithium salt (LiTFSI) and a 60 wt% starch-based biopolymer, whose optimized ratio of the obtained electrolyte film between starch and KH560 is 1[thin space (1/6-em)]:[thin space (1/6-em)]1. In addition, confirmed by a related electrochemical test, the as-prepared starch-based electrolyte can be compatible with high-voltage and high-capacity cathodes. The electrolyte is more economically and environmentally advantageous compared with other solid polymer electrolytes developed so far.


image file: c9sc02743b-f8.tif
Fig. 8 (a) Schematic diagram of starch host synthesis. (b) The digital image of starch host solution using DMSO as solvent and the corresponding GPC result. (c) Solid state Si NMR spectrum of the starch host after vaporizing DMSO at 60 °C for 10 h. (d) The digital image of the transparent and flexible electrolyte film and a suggested structure of the starch host. (a–d) Reproduced with permission.91 Copyright 2016, Royal Society of Chemistry.

Table 3 displays the categories, structures, and characteristics of bio-derived polymers as binders or all-solid-state electrolytes for Li–S batteries. Different from the traditional PVDF binder using toxic NMP as the solvent, the bio-derived binders are more environment-friendly and cost-effective, and use water as the solvent. More importantly, due to the rich oxygen-containing groups such as –OH, –COOH, and C[double bond, length as m-dash]O, these bio-derived polymers exhibit high adsorption ability for trapping polysulfides, which is beneficial for improving active sulfur utilization and stabilizing cycle life.

Table 3 The categories, structures and characteristics of bio-derived polymers as binders for Li–S batteries
Categories Source Chemical structure Solvent
Gum arabic92 Acacia senegal Rich –OH Water
Na-alginate86 Sea grass Rich –OH and –COOH Water
Gelatin87 Animal protein Rich –COOH and –NH2 Water
Caboxymethylcellulose93 Cellulose Rich –OH and –COOH Water
Guar gum and xanthan gum90 Endosperm and Xanthomonas Rich –OH and C[double bond, length as m-dash]O Water
Soy protein and poly(acrylic acid)89 Soya Rich –COOH and –NH2 Water


6 Conclusions and outlook

The past few years have witnessed the fast development of bio-derived materials for Li–S batteries due to their inherited structures and sustainability of chemical properties. In this review, we provided an overview of green biomass materials for Li–S batteries, highlighting various aspects toward the design and fabrication of sulfur hosts, separator membranes, binders, and all-solid-state electrolytes. A rich variety of carbon materials as sulfur hosts with various structures have been developed from various biomass materials using different fabrication strategies (Table 1), which provide plenty of building blocks for further development of Li–S battery commercialization.

Besides the application of biomass with specific structures, the activation step using KOH (or KHCO3, or NaCl, or ZnCl2, or KCO3, or H3PO4) is a flexible and applicable method for most biomass materials. A variety of bio-derived fiber materials such as BC, cellulose and cotton are built by simple methods to meet the specific applications as interlayer films in Li–S batteries (Table 2). With the help of rich oxygen-containing groups on the surface of bio-materials, the suppression of the shuttle effect can be achieved with minimal cost. More importantly, instead of toxic NMP solvent, using water as the solvent for the bio-derived binder in Li–S batteries is more environmentally friendly and conducive to large-scale fabrication. Besides the successful development of biomass for a sulfur host and interlayer, bio-polymers extracted from biomass have also been applied in Li–S batteries as a binder (Table 3) or all-solid-state electrolyte. With the application of these natural bio-polymers, the employment of toxic and volatile organic solvents is under effective control.

Although the applications of bio-derived materials in Li–S batteries have obtained great progress, there are still several challenges for their commercialization in practical battery systems. At the end of this review, we attempt to propose several potential solutions to address these issues:

(1) The diversity of biomass ingredients endows the bio-derived sulfur host materials with chemical adsorption for trapping polysulfides, which is important for the improvement of sulfur utilization and cycle life. However, just relying on biomass itself will not satisfy the increasing requirement of high sulfur loading. The surface and interface modification using polar groups (e.g., metal oxides, sulfides, and advanced polysulfides) for bio-derived sulfur hosts can be a promising strategy.

(2) Because of the microscopic size of most fiber-like bio-materials, the prepared interlayers show signs of weakness for trapping polysulfides in high sulfur loading cathodes. The whole size of the interlayer in sulfur cathodes is also not beneficial for promoting fast ion transfer. Therefore, developing an advanced bio-synthesis method is still urgently important, which can make bio-derived materials meet the ever-increasing demand for Li–S batteries. For example, the strategy of fabricating nanocellulose can reduce the size of micro-cellulose to the nanoscale, which can significantly improve its capability for trapping polysulfides.

(3) Low-cost bio-polymers as binders and electrolytes in sulfur cathodes made a great contribution to environmental protection. However, the extraction of some bio-polymers from biomass is very difficult, which raises the production cost. It is still hard to carry out large-scale fabrication of these bio-polymers with high quality and uniformity. Learning from the behavior of biomass, developing a bionic method may be a candidate approach to overcome this challenge. In summary, biomaterials are sustainable, earth abundant, low cost, biodegradable, and chemically accessible for modification. Due to these remarkable merits, the materials derived from biomass have been widely applied in Li–S batteries and achieved great progress. While various applications have been demonstrated, there are still some challenges such as large-scale fabrication in fundamental research and understanding to promote biomaterials toward commercial reality, especially for emerging applications, such as lithium metal anodes, catalysis, etc. In addition, in-depth research that can significantly improve the added value of biomaterials is also an area of concern. With a worldwide effort, new developments in Li–S batteries using biomaterials elaborated in this review will provide emerging technologies affecting our everyday life.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

H. Yuan and T. Liu contributed equally to this work. The authors acknowledge financial support by the National Natural Science Foundation of China (Grant no. 51722210, 51572240, U1802254, 51871201, and 51677170), and the Natural Science Foundation of Zhejiang Province (Grant no. LY16E070004 and LD18E020003).

Notes and references

  1. P. G. Bruce, S. A. Freunberger, L. J. Hardwick and J. M. Tarascon, Nat. Mater., 2011, 11, 19–29 CrossRef PubMed.
  2. X. Ji, K. T. Lee and L. F. Nazar, Nat. Mater., 2009, 8, 500–506 CrossRef CAS PubMed.
  3. A. Manthiram, S. H. Chung and C. Zu, Adv. Mater., 2015, 27, 1980–2006 CrossRef CAS PubMed.
  4. X. Liu, J. Q. Huang, Q. Zhang and L. Mai, Adv. Mater., 2017, 29, 1601759 CrossRef PubMed.
  5. H. Yuan, M. Wu, J. Zheng, Z. G. Chen, W. Zhang, J. Luo, C. Jin, O. Sheng, C. Liang, Y. Gan, Y. Xia, J. Zhang, H. Huang, Y. Liu, J. Nai and X. Tao, Adv. Funct. Mater., 2019, 29, 1809051 CrossRef.
  6. Z. W. Seh, Y. Sun, Q. Zhang and Y. Cui, Chem. Soc. Rev., 2016, 45, 5605–5634 RSC.
  7. O. Ogoke, G. Wu, X. Wang, A. Casimir, L. Ma, T. Wu and J. Lu, J. Mater. Chem. A, 2017, 5, 448–469 RSC.
  8. D.-W. Wang, Q. Zeng, G. Zhou, L. Yin, F. Li, H.-M. Cheng, I. R. Gentle and G. Q. M. Lu, J. Mater. Chem. A, 2013, 1, 9382–9395 RSC.
  9. H.-J. Peng, J.-Q. Huang, X.-B. Cheng and Q. Zhang, Adv. Energy Mater., 2017, 7, 1700260 CrossRef.
  10. R. Fang, S. Zhao, Z. Sun, D. W. Wang, H. M. Cheng and F. Li, Adv. Mater., 2017, 29, 1606823 CrossRef.
  11. Z. Li, J. Zhang, B. Guan, D. Wang, L. M. Liu and X. W. Lou, Nat. Commun., 2016, 7, 13065–13076 CrossRef CAS PubMed.
  12. X. Tao, J. Wang, C. Liu, H. Wang, H. Yao, G. Zheng, Z. W. Seh, Q. Cai, W. Li, G. Zhou, C. Zu and Y. Cui, Nat. Commun., 2016, 7, 11203–11212 CrossRef CAS.
  13. Z. W. Seh, J. H. Yu, W. Li, P. C. Hsu, H. Wang, Y. Sun, H. Yao, Q. Zhang and Y. Cui, Nat. Commun., 2014, 5, 5017 CrossRef CAS PubMed.
  14. G. Zhou, E. Paek, G. S. Hwang and A. Manthiram, Adv. Energy Mater., 2016, 6, 1501355 CrossRef.
  15. Q. Pang, J. Tang, H. Huang, X. Liang, C. Hart, K. C. Tam and L. F. Nazar, Adv. Mater., 2015, 27, 6021–6028 CrossRef CAS PubMed.
  16. G. Zhou, E. Paek, G. S. Hwang and A. Manthiram, Nat. Commun., 2015, 6, 7760 CrossRef CAS PubMed.
  17. L. Sun, D. Wang, Y. Luo, K. Wang, W. Kong, Y. Wu, L. Zhang, K. Jiang, Q. Li, Y. Zhang, J. Wang and S. Fan, ACS Nano, 2016, 10, 1300–1308 CrossRef CAS.
  18. S. Wang, H. Chen, J. Liao, Q. Sun, F. Zhao, J. Luo, X. Lin, X. Niu, M. Wu, R. Li and X. Sun, ACS Energy Lett., 2019, 4, 755–762 CrossRef CAS.
  19. H. Yao, G. Zheng, W. Li, M. T. McDowell, Z. Seh, N. Liu, Z. Lu and Y. Cui, Nano Lett., 2013, 13, 3385–3390 CrossRef CAS PubMed.
  20. J. Yoo, S. J. Cho, G. Y. Jung, S. H. Kim, K. H. Choi, J. H. Kim, C. K. Lee, S. K. Kwak and S. Y. Lee, Nano Lett., 2016, 16, 3292–3300 CrossRef CAS.
  21. D. Fang, Y. Wang, X. Liu, J. Yu, C. Qian, S. Chen, X. Wang and S. Zhang, ACS Nano, 2019, 13, 1563–1573 CrossRef CAS PubMed.
  22. Y. Dong, S. Zheng, J. Qin, X. Zhao, H. Shi, X. Wang, J. Chen and Z. S. Wu, ACS Nano, 2018, 12, 2381–2388 CrossRef CAS PubMed.
  23. X. Tao, Y. Liu, W. Liu, G. Zhou, J. Zhao, D. Lin, C. Zu, O. Sheng, W. Zhang, H. W. Lee and Y. Cui, Nano Lett., 2017, 17, 2967–2972 CrossRef CAS PubMed.
  24. S. Wang, Y. Ding, G. Zhou, G. Yu and A. Manthiram, ACS Energy Lett., 2016, 1, 1080–1085 CrossRef CAS.
  25. D. Dong, B. Zhou, Y. Sun, H. Zhang, G. Zhong, Q. Dong, F. Fu, H. Qian, Z. Lin, D. Lu, Y. Shen, J. Wu, L. Chen and H. Chen, Nano Lett., 2019, 19, 2343–2349 CrossRef CAS PubMed.
  26. G. Li, M. Ling, Y. Ye, Z. Li, J. Guo, Y. Yao, J. Zhu, Z. Lin and S. Zhang, Adv. Energy Mater., 2015, 5, 1500878 CrossRef.
  27. Z. Yang, R. Li and Z. Deng, ACS Appl. Mater. Interfaces, 2018, 10, 13519–13527 CrossRef CAS.
  28. X. Yu, G. Zhou and Y. Cui, ACS Appl. Mater. Interfaces, 2019, 11, 3080–3086 CrossRef CAS.
  29. Z. W. Seh, H. Wang, P.-C. Hsu, Q. Zhang, W. Li, G. Zheng, H. Yao and Y. Cui, Energy Environ. Sci., 2014, 7, 672 RSC.
  30. G. Zhou, L.-C. Yin, D.-W. Wang, L. Li, S. Pei, I. R. Gentle, F. Li and H.-M. Cheng, ACS Nano, 2013, 7, 5367–5375 CrossRef CAS PubMed.
  31. G. Zheng, Q. Zhang, J. J. Cha, Y. Yang, W. Li, Z. W. Seh and Y. Cui, Nano Lett., 2013, 13, 1265–1270 CrossRef CAS PubMed.
  32. R. Chen, T. Zhao, J. Lu, F. Wu, L. Li, J. Chen, G. Tan, Y. Ye and K. Amine, Nano Lett., 2013, 13, 4642–4649 CrossRef CAS.
  33. H. J. Peng, J. Q. Huang and Q. Zhang, Chem. Soc. Rev., 2017, 46, 5237–5288 RSC.
  34. J. Zhang, Y. Shi, Y. Ding, W. Zhang and G. Yu, Nano Lett., 2016, 16, 7276–7281 CrossRef CAS PubMed.
  35. X. Tao, J. Wang, Z. Ying, Q. Cai, G. Zheng, Y. Gan, H. Huang, Y. Xia, C. Liang, W. Zhang and Y. Cui, Nano Lett., 2014, 14, 5288–5294 CrossRef CAS PubMed.
  36. H. Yuan, X. Chen, G. Zhou, W. Zhang, J. Luo, H. Huang, Y. Gan, C. Liang, Y. Xia, J. Zhang, J. Wang and X. Tao, ACS Energy Lett., 2017, 2, 1711–1719 CrossRef CAS.
  37. Y. Cheng, S. Ji, X. Xu and J. Liu, RSC Adv., 2015, 5, 100089–100096 RSC.
  38. J. Deng, M. Li and Y. Wang, Green Chem., 2016, 18, 4824–4854 RSC.
  39. Y.-P. Gao, Z.-B. Zhai, K.-J. Huang and Y.-Y. Zhang, New J. Chem., 2017, 41, 11456–11470 RSC.
  40. D. Liu, Q. Li, J. Hou and H. Zhao, Sustainable Energy Fuels, 2018, 2, 2197–2205 RSC.
  41. M. K. Rybarczyk, H.-J. Peng, C. Tang, M. Lieder, Q. Zhang and M.-M. Titirici, Green Chem., 2016, 18, 5169–5179 RSC.
  42. J. Wang, P. Nie, B. Ding, S. Dong, X. Hao, H. Dou and X. Zhang, J. Mater. Chem. A, 2017, 5, 2411–2428 RSC.
  43. X. Yuan, B. Liu, J. Xu, X. Yang, K. Zeinu, X. He, L. Wu, J. Hu, J. Yang and J. Xie, RSC Adv., 2017, 7, 13595–13603 RSC.
  44. L. Zhang, Y. Wang, B. Peng, W. Yu, H. Wang, T. Wang, B. Deng, L. Chai, K. Zhang and J. Wang, Green Chem., 2014, 16, 3926–3935 RSC.
  45. J. Xu, K. Zhou, F. Chen, W. Chen, X. Wei, X.-W. Liu and J. Liu, ACS Sustainable Chem. Eng., 2016, 4, 666–670 CrossRef CAS.
  46. M. Wang, X. Xia, Y. Zhong, J. Wu, R. Xu, Z. Yao, D. Wang, W. Tang, X. Wang and J. Tu, Chem, 2019, 25, 3710–3725 CrossRef CAS PubMed.
  47. J. Zhang, Y. Cai, Q. Zhong, D. Lai and J. Yao, Nanoscale, 2015, 7, 17791–17797 RSC.
  48. Y. Xia, R. Fang, Z. Xiao, H. Huang, Y. Gan, R. Yan, X. Lu, C. Liang, J. Zhang, X. Tao and W. Zhang, ACS Appl. Mater. Interfaces, 2017, 9, 23782–23791 CrossRef CAS PubMed.
  49. L. Xia, Y. Zhou, J. Ren, H. Wu, D. Lin, F. Xie, W. Jie, K. H. Lam, C. Xu and Q. Zheng, Energy Fuels, 2018, 32, 9997–10007 CrossRef CAS.
  50. S. H. Chung, C. H. Chang and A. Manthiram, ACS Nano, 2016, 10, 10462–10470 CrossRef CAS PubMed.
  51. X. Tao, J. Zhang, Y. Xia, H. Huang, J. Du, H. Xiao, W. Zhang and Y. Gan, J. Mater. Chem. A, 2014, 2, 2290–2296 RSC.
  52. B. Zheng, N. Li, J. Yang and J. Xi, Chem. Commun., 2019, 55, 2289–2292 RSC.
  53. J. Zhou, Y. Guo, C. Liang, J. Yang, J. Wang and Y. Nuli, Electrochim. Acta, 2018, 273, 127–135 CrossRef CAS.
  54. Y. Zhong, X. Xia, S. Deng, J. Zhan, R. Fang, Y. Xia, X. Wang, Q. Zhang and J. Tu, Adv. Energy Mater., 2018, 8, 1701110 CrossRef.
  55. Y. Li, K. K. Fu, C. Chen, W. Luo, T. Gao, S. Xu, J. Dai, G. Pastel, Y. Wang, B. Liu, J. Song, Y. Chen, C. Yang and L. Hu, ACS Nano, 2017, 11, 4801–4807 CrossRef CAS PubMed.
  56. C. Luo, H. Zhu, W. Luo, F. Shen, X. Fan, J. Dai, Y. Liang, C. Wang and L. Hu, ACS Appl. Mater. Interfaces, 2017, 9, 14801–14807 CrossRef CAS PubMed.
  57. W. Wu, J. Pu, J. Wang, Z. Shen, H. Tang, Z. Deng, X. Tao, F. Pan and H. Zhang, Adv. Energy Mater., 2018, 8, 1702373 CrossRef.
  58. J. Qu, S. Lv, X. Peng, S. Tian, J. Wang and F. Gao, J. Alloys Compd., 2016, 671, 17–23 CrossRef CAS.
  59. J. Li, F. Qin, L. Zhang, K. Zhang, Q. Li, Y. Lai, Z. Zhang and J. Fang, J. Mater. Chem. A, 2014, 2, 13916 RSC.
  60. Y. Xia, H. Zhong, R. Fang, C. Liang, Z. Xiao, H. Huang, Y. Gan, J. Zhang, X. Tao and W. Zhang, J. Power Sources, 2018, 378, 73–80 CrossRef CAS.
  61. J. Han, X. Chen, B. Xi, H. Mao, J. Feng and S. Xiong, ChemistrySelect, 2018, 3, 10175–10181 CrossRef CAS.
  62. M. Manoj, C. Muhamed Ashraf, M. Jasna, K. M. Anilkumar, B. Jinisha, V. S. Pradeep and S. Jayalekshmi, J. Colloid Interface Sci., 2019, 535, 287–299 CrossRef CAS.
  63. S. Zhang, M. Zheng, Z. Lin, N. Li, Y. Liu, B. Zhao, H. Pang, J. Cao, P. He and Y. Shi, J. Mater. Chem. A, 2014, 2, 15889–15896 RSC.
  64. Z. H. Chen, X. L. Du, J. B. He, F. Li, Y. Wang, Y. L. Li, B. Li and S. Xin, ACS Appl. Mater. Interfaces, 2017, 9, 33855–33862 CrossRef CAS PubMed.
  65. C. Schneidermann, C. Kensy, P. Otto, S. Oswald, L. Giebeler, D. Leistenschneider, S. Gratz, S. Dorfler, S. Kaskel and L. Borchardt, ChemSusChem, 2019, 12, 310–319 CrossRef CAS.
  66. J. Liu, B. Liu, C. Wang, Z. Huang, L. Hu, X. Ke, L. Liu, Z. Shi and Z. Guo, J. Alloys Compd., 2017, 718, 373–378 CrossRef CAS.
  67. J. Zhang, J. Xiang, Z. Dong, Y. Liu, Y. Wu, C. Xu and G. Du, Electrochim. Acta, 2014, 116, 146–151 CrossRef CAS.
  68. M. Zheng, Q. Hu, S. Zhang, H. Tang, L. Li and H. Pang, Appl. Sci., 2017, 7, 1036–1047 CrossRef.
  69. L. Hencz, X. Gu, X. Zhou, W. Martens and S. Zhang, J. Mater. Sci., 2017, 52, 12336–12347 CrossRef CAS.
  70. Y. Zhao, L. Wang, L. Huang, M. Y. Maximov, M. Jin, Y. Zhang, X. Wang and G. Zhou, Nanomaterials, 2017, 7, 402–412 CrossRef PubMed.
  71. C. Hernández-Rentero, R. Córdoba, N. Moreno, A. Caballero, J. Morales, M. Olivares-Marín and V. Gómez-Serrano, Nano Res., 2017, 11, 89–100 CrossRef.
  72. Y. Yan, M. Shi, Y. Wei, C. Zhao, M. Carnie, R. Yang and Y. Xu, J. Alloys Compd., 2018, 738, 16–24 CrossRef CAS.
  73. X.-l. You, L.-j. Liu, M.-y. Zhang, M. D. Walle, Y. Li and Y.-N. Liu, Mater. Lett., 2018, 217, 167–170 CrossRef CAS.
  74. H. Shao, F. Ai, W. Wang, H. Zhang, A. Wang, W. Feng and Y. Huang, J. Mater. Chem. A, 2017, 5, 19892–19900 RSC.
  75. T. Liu, X. Sun, S. Sun, Q. Niu, H. Liu, W. Song, F. Cao, X. Li, T. Ohsaka and J. Wu, Electrochim. Acta, 2019, 295, 684–692 CrossRef CAS.
  76. Y. Huang, Z. Lin, M. Zheng, T. Wang, J. Yang, F. Yuan, X. Lu, L. Liu and D. Sun, J. Power Sources, 2016, 307, 649–656 CrossRef CAS.
  77. S. Li, T. Mou, G. Ren, J. Warzywoda, Z. Wei, B. Wang and Z. Fan, J. Mater. Chem. A, 2017, 5, 1650–1657 RSC.
  78. Y. Huang, M. Zheng, Z. Lin, B. Zhao, S. Zhang, J. Yang, C. Zhu, H. Zhang, D. Sun and Y. Shi, J. Mater. Chem. A, 2015, 3, 10910–10918 RSC.
  79. K. B. Celik, E. C. Cengiz, T. Sar, B. Dursun, O. Ozturk, M. Y. Akbas and R. Demir-Cakan, J. Colloid Interface Sci., 2018, 530, 137–145 CrossRef CAS PubMed.
  80. A. Song, Y. Huang, X. Zhong, H. Cao, B. Liu, Y. Lin, M. Wang and X. Li, J. Membr. Sci., 2018, 556, 203–213 CrossRef CAS.
  81. S. Li, G. Ren, M. N. F. Hoque, Z. Dong, J. Warzywoda and Z. Fan, Appl. Surf. Sci., 2017, 396, 637–643 CrossRef CAS.
  82. X. Zhang, Y. Zhong, X. Xia, Y. Xia, D. Wang, C. Zhou, W. Tang, X. Wang, J. B. Wu and J. Tu, ACS Appl. Mater. Interfaces, 2018, 10, 13598–13605 CrossRef CAS PubMed.
  83. J. Yang, F. Chen, C. Li, T. Bai, B. Long and X. Zhou, J. Mater. Chem. A, 2016, 4, 14324–14333 RSC.
  84. A. Ghosh, S. Shukla, G. S. Khosla, B. Lochab and S. Mitra, Sci. Rep., 2016, 6, 25207–25220 CrossRef CAS.
  85. T. Liu, S. Sun, W. Song, X. Sun, Q. Niu, H. Liu, T. Ohsaka and J. Wu, J. Mater. Chem. A, 2018, 6, 23486–23494 RSC.
  86. W. Bao, Z. Zhang, Y. Gan, X. Wang and J. Lia, J. Energy Chem., 2013, 22, 790–794 CrossRef CAS.
  87. Q. Wang, W. Wang, Y. Huang, F. Wang, H. Zhang, Z. Yu, A. Wang and K. Yuan, J. Electrochem. Soc., 2011, 158, A775–A779 CrossRef CAS.
  88. J. Sun, Y. Huang, W. Wang, Z. Yu, A. Wang and K. Yuan, Electrochim. Acta, 2008, 53, 7084–7088 CrossRef CAS.
  89. X. Fu, L. Scudiero and W.-H. Zhong, J. Mater. Chem. A, 2019, 7, 1835–1848 RSC.
  90. J. Liu, D. G. D. Galpaya, L. Yan, M. Sun, Z. Lin, C. Yan, C. Liang and S. Zhang, Energy Environ. Sci., 2017, 10, 750–755 RSC.
  91. Y. Lin, J. Li, K. Liu, Y. Liu, J. Liu and X. Wang, Green Chem., 2016, 18, 3796–3803 RSC.
  92. S. Tu, X. Chen, X. Zhao, M. Cheng, P. Xiong, Y. He, Q. Zhang and Y. Xu, Adv. Mater., 2018, 30, e1804581 CrossRef PubMed.
  93. L. Luo, S. H. Chung, H. Yaghoobnejad Asl and A. Manthiram, Adv. Mater., 2018, 30, e1804149 CrossRef PubMed.

Footnote

These authors contributed equally to this work.

This journal is © The Royal Society of Chemistry 2019