Abstract

The stability of encapsulated planar-structured CH3NH3PbI3 (MAPbI3) perovskite solar cells (PSCs) was investigated under various simulated environmental conditions. The tests were performed under approximately one sun (100 mW cm−2) illumination, varying temperature (up to 85 °C cell temperature) and humidity (up to 80%). The application of advanced sealing techniques improved the device stability, but all devices showed significant degradation after prolonged aging at high temperature and humidity. The degradation mechanism was studied by post-mortem analysis of the disassembled cells using SEM and XRD. This revealed that the degradation was mainly due to the decomposition of MAPbI3, as a result of reaction with H2O, and the subsequent reaction of hydroiodic acid, formed during MAPbI3 decomposition, with the silver back contact electrode layer.

Graphical abstract: Degradation observations of encapsulated planar CH3NH3PbI3 perovskite solar cells at high temperatures and humidity

Article information

Article type
Paper
Submitted
16 janv. 2015
Accepted
05 mars 2015
First published
09 mars 2015

J. Mater. Chem. A, 2015,3, 8139-8147

Degradation observations of encapsulated planar CH3NH3PbI3 perovskite solar cells at high temperatures and humidity

Y. Han, S. Meyer, Y. Dkhissi, K. Weber, J. M. Pringle, U. Bach, L. Spiccia and Y. Cheng, J. Mater. Chem. A, 2015, 3, 8139 DOI: 10.1039/C5TA00358J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements