Characterization of layered silicate HUS-5 and formation of novel nanoporous silica through transformation of HUS-5 ion-exchanged with alkylammonium cations

Abstract

Hiroshima University Silicate-1 (HUS-1) and its precursor (HUS-5), whose crystal structure was similar to that of β-HLS layered silicate, were prepared. The interlayer distance of HUS-5 was 0.4 nm; both Na+ cations and hydrated water were present in the interlayer. The interlayer distance of HUS-5 was expanded by ion-exchanging with several bulky organic cations such as dodecyltrimethylammonium, hexadecyltrimethylammonium, and benzyltrimethylammonium. The HUS-5 variants that were ion-exchanged with alkylammonium exhibited high catalytic activities base catalysts in a Knoevenagel condensation reaction. In particular, the HUS-5 that was ion-exchanged with hexadecyltrimethylammonium cations was converted to novel nanoporous silica by acetic acid treatment and subsequent calcination and was named HUS-6. The BET surface area and average pore diameter were 983 m2 g−1 and 1.6 nm, respectively. Formation of nanopores in HUS-6 was clearly confirmed by TEM. Nanopores (ca. 1.6 nm) of HUS-6 present a unique adsorption space; there was an intermediate state between micropores (ca. 0.6 nm) of silicalite-1 and mesopores (ca. 2.9 nm) of MCM-41.

Graphical abstract: Characterization of layered silicate HUS-5 and formation of novel nanoporous silica through transformation of HUS-5 ion-exchanged with alkylammonium cations

Supplementary files

Article information

Article type
Paper
Submitted
19 mai 2013
Accepted
25 juin 2013
First published
26 juin 2013

J. Mater. Chem. A, 2013,1, 9680-9688

Characterization of layered silicate HUS-5 and formation of novel nanoporous silica through transformation of HUS-5 ion-exchanged with alkylammonium cations

N. Tsunoji, M. Fukuda, K. Yoshida, Y. Sasaki, T. Ikeda, Y. Ide, M. Sadakane and T. Sano, J. Mater. Chem. A, 2013, 1, 9680 DOI: 10.1039/C3TA11971H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements