A novel degradation mechanism of the elastic modulus of wet polymer substrates under nanoindentation

Author affiliations

Abstract

We demonstrated that the formation and solidification of a continuous confined water film played a very important role in changing the elastic modulus of the wet polymer substrate in a nanoindentation process by a coarse-grained molecular dynamics simulation of this process. It was found that as the water content increased, the elastic modulus of the wet polymer substrate showed a non-monotonic change. Relative to the dry polymer substrate, the elastic modulus of the wet polymer first decreased. This is because the appearance of a confined water film caused the force between the polymer substrate and the indenter to change from repulsion to attraction. Subsequently, as the confined water film gradually solidified and then weakened, the elastic modulus of the wet polymer slowly increased and then rapidly increased due to a large number of interstitial water molecules gradually penetrating the polymer substrate. Therefore, it is unreasonable to explain the wet polymer degradation during nanoindentation only from the plasticization and anti-plasticization effects based on the hydrogen bond breaking and formation during stretching. The above-mentioned results will help to more comprehensively understand the degradation mechanism of the polymers’ encounter with water, thus promoting further practical applications for polymers.

Graphical abstract: A novel degradation mechanism of the elastic modulus of wet polymer substrates under nanoindentation

Back to tab navigation

Supplementary files

Article information


Submitted
11 Apr 2020
Accepted
04 May 2020
First published
05 May 2020

Soft Matter, 2020, Advance Article
Article type
Paper

A novel degradation mechanism of the elastic modulus of wet polymer substrates under nanoindentation

R. Chen, Z. Wang, S. Li and H. Du, Soft Matter, 2020, Advance Article , DOI: 10.1039/D0SM00645A