Jump to main content
Jump to site search

Cellulose nanocrystal-reinforced poly(5-triethoxysilyl-2-norbornene) composites

Author affiliations


We demonstrate the reinforcement of a previously inaccessible norbornene-silane with a stiff, bio-based nanofiller. Poly(5-triethoxysilyl-2-norbornene) (PTESN), a glassy and thermally stable polymer, was combined with cellulose nanocrystals (CNCs) and solvent cast from toluene to form reinforced materials. Composite films showed excellent translucency and no visible aggregation, which was supported by scanning electron micrographs that showed no signs of CNC aggregation within the polymer matrix. Reinforcement was evident at the moderate loading of 5 wt% CNC, showing a statistically significant enhancement for Young's modulus and even greater reinforcement for 20 wt% CNC loading for Young's modulus (540 MPa vs. 970 MPa) and storage modulus at 25 °C (400 MPa vs. 1200 MPa). We suspect that there is a strong interaction between the polymer and CNC filler based upon the increase of thermal degradation temperature of the CNCs increasing, for example from 278 °C to 295 °C at 10 wt% CNCs. These interactions were probed via solid-state NMR, which suggests that no covalent bonding occurs between the triethoxylsilyl substituents of the polymer and the CNCs. We therefore hypothesize that hydrogen bonding interactions between PTESN and CNCs are responsible for the increased thermal stability and reinforcement of the polymer material.

Graphical abstract: Cellulose nanocrystal-reinforced poly(5-triethoxysilyl-2-norbornene) composites

Back to tab navigation

Supplementary files

Publication details

The article was received on 30 Jun 2019, accepted on 16 Sep 2019 and first published on 18 Sep 2019

Article type: Paper
DOI: 10.1039/C9PY00963A
Polym. Chem., 2020, Advance Article

  •   Request permissions

    Cellulose nanocrystal-reinforced poly(5-triethoxysilyl-2-norbornene) composites

    K. D. Hendren, M. A. Higgins, B. K. Long and E. J. Foster, Polym. Chem., 2020, Advance Article , DOI: 10.1039/C9PY00963A