Sebastián
Alberti
*a,
Sonja
Schmidt
b,
Simone
Hageneder
c,
Paula C.
Angelomé
e,
Galo J. A. A.
Soler-lllia
d,
Philipp
Vana
b,
Jakub
Dostalek
cf,
Omar
Azzaroni
a and
Wolfgang
Knoll
cg
aInstituto de Investigaciones Fisicoquimicas Teoricas y Aplicadas (INIFTA), Departamento de Quimica, Facultad de Ciencias Exactas, Universidad Nacional de La Plata-CONICET, CC. 16 Suc. 4, La Plata, 1900, Argentina. E-mail: sebastian.alberti@uit.no
bGeorg-August-University Göttingen, Institute of Physical Chemistry, Tammannstr. 6, 37077 Göttingen, Germany
cBiosensor Technologies, AIT-Austrian Institute of Technology, Konrad Lorenz Straße 24, 3430 Tulln, Austria
dInstituto de Nanosistemas, Universidad Nacional de General San Martín-CONICET, San Martín, 1650, Argentina
eInstituto de Nanociencia y Nanotecnología & Gerencia Química – Centro Atómico Constituyentes, CNEA-CONICET, Av. Gral. Paz 1499, 1650, San Martín, Buenos Aires, Argentina
fFZU-Institute of Physics, Czech Academy of Sciences, Na Slovance 2, Prague 182 21, Czech Republic
gDanube Private University, Steiner Landstrasse 124, 3500 Krems, Austria
First published on 13th July 2023
Nanopores have been applied in the development of artificial biocatalytic systems, controlled drug delivery, and solid-state sensing devices. The interaction of biomacromolecules with surfaces show a dependence on the nanopore diameter, crucial in their ability to infiltrate porous materials. In this context, ordered mesoporous materials obtained by evaporation-induced self-assembly are model materials to test pore-biomolecule interactions. Nevertheless, these materials are generally restricted to pore diameters within the 2–10 nm range, therefore, new polymers as templating agents hold potential to provide an easy reproducible route for the synthesis of mesoporous silica thin films (MTF) with pore diameters above 10 nm without the use of swelling or additional structuring agents. Here, we present a novel and simple approach towards large pore MTF through the combination of supramolecular templating and phase separation with tailor-made block co-polymers. Accurate tuning of the oxide pore size distribution (with small mesopores between 13–18 nm diameter) is achieved by controlling the length and the nature of the hydrophilic polymer block used as a template through a simple reversible addition-fragmentation chain transfer (RAFT) polymerization approach. The importance of these features is highlighted by showing the capability that these new materials offer for biomolecule infiltration benchmarked against the widespread MTF prepared using pluronic F127 as a template. Effect of protein to pore diameter ratio, protein location and effect of pH and ionic strength is briefly tested and discussed.
In particular, its application in nanopore-based biotechnologies is highly sensitive to pore diameter, due to conformation of biomacromolecules and surface interaction in confinement.8 Optimal nanopore diameters have been reported for enhancing the stability of the folded structures,9–11 and inhibit irreversible aggregation despite being under protein crowding conditions.12–14 Furthermore, the knowledge of protein location and assembly within a material will contribute to design programmable or multifunctional bio-composite systems inside nanopores and to make nanopore based sensing of protein structures more accurate.15,16
Mesoporous oxide thin films (MTF) provide a sound platform for the creation of ordered arrays of monodisperse cavities. Nowadays, they can precisely designed and produced in reproducible fashion.17,18 Indeed, the synthesis of MTF by combination of soft chemistry, self-assembly of supramolecular templates (Fig. 2), and surface modification permits to create hybrid interfacial nanoarchitectures where chemical functions can be precisely located in space.19–23 Nevertheless, the most common polymers used as porogenic agents limit the preparation of MTF to pore sizes below 10 nm in diameter and rather narrow connecting necks below 5 nm in diameter.24 In this regard, most reports rely on commercial templating agents such as CTAB, the diblock co-polymer Brij family, and the triblock co-polymer pluronic family.25 Among them, pluronic F127 gives rise to the biggest pore sizes, with up to 7–8 nm pore diameter and necks below 4 nm.17 These limited pore sizes can be subsequently further reduced by post-grafting procedures leading to a loss in porous volume, monodispersity and eventually to pore blocking.26–28 In applications that require coupling delicate macromolecules, such as enzymes, to the inorganic material, the narrow pore size imposes a severe drawback. In particular, immobilization of biomolecules has appeared as a promising field for applications such as catalysis, sensing or soil remediation.29–31 In this regard, preparing structures with enlarged pore diameters up to 40 nm represents a step forward, since they can accommodate macromolecules without losing the key confinement effects.8,32 However, expanding mesopores sizes beyond 10 nm diameter while ensuring a high pore volume in an easy and reproducible way without the use of toxic solvents remains a big challenge.
In search of increasing the pore size in mesoporous structures, different groups have approached the problem with several strategies based on the development of specific templating agents, the addition of swelling agents, or the use of nanoparticles as templates.33,34 The evaporation induced self-assembly (EISA) method is a very flexible and well developed synthesis route,35 yet so far, large pores using a single templating agent have only been attained in ultrathin oxide films (pore monolayers or bilayers, or even arranged craters) with very dilute precursor concentrations.36–38 Furthermore, new commercial polymers as porogenic agents are usually limited to polyethylenoxide (PEO) as the hydrophilic block and only very few alternatives have been proposed.32 These new polymers normally require the use of expensive or toxic solvents that complicate scaling up of the production.39 The introduction of swelling agents presents an alternative strategy and has been successfully used in several materials, but this strategy adds complexity to the solution composition.38 Other limitations like thermal treatments, aging time, layer thickness and lack of monodispersity are to be considered when this approach is used.38 A third approach to widening pore diameters through sol–gel chemistry has been based on the use of nanoparticles as templates, as is the case for latex nanoparticles. This approach mainly leads to macroporous structures (pore diameter above 50 nm) and interconnectivity between the pores may be limited.34 Despite all these efforts, pore sizes between 15–40 nm have not been achieved in a standard and reproducible manner and a new facile route for pore design within this scale is still needed.40
In this regard, novel co-polymers prepared by controlled radical polymerization (CRP) procedures can be used as templates, taking advantage of incorporating a broad spectrum of radically (co)polymerizable monomers.41 Controlled polymerization strategies (i.e. atom transfer radical polymerization (ATRP), nitroxide mediated radical polymerization (NMP) and reversible addition-fragmentation chain transfer polymerization (RAFT)) allow to obtain polymers with low molar mass polydispersity without the need of further purification.32,42 Furthermore, this technique enables the use of less stringent conditions as those required for anionic polymerization.43 These procedures allow for the design of a straightforward route for block copolymer synthesis, as polymerization can be stopped and restarted in the presence of a new monomer without the need of further purification. Within CRP, RAFT polymerization provides an easy protocol for block copolymer synthesis with an outstanding control over the length and monodispersity of each block, compatible with commercial monomers (acrylates, methacrylates and styrene).44 This diversity of functional groups enables the synthesis of tailor-made polymers. Interestingly, these polymers can be used as template agents but also as precursors to functionalize the inner pores.45
In this work, we will briefly discuss the design and the synthesis of new triblock co-polymers, soluble in ethanol, to be used as templates for mesoporous silica thin films synthesis through sol–gel chemistry. The ratio of the hydrophobic block volume to the hydrophilic block volume will be tuned by changing the hydrophobic polymer length. In addition, the degree of hydrophobicity will be studied by changing the nature of the respective polymer block. This study gives us the opportunity to find the configuration that will define the pore size and pore volume of the porous films and guarantee a reproducibility that is currently not achievable with the available commercial polymers. These new mesoporous thin films will be compared to a widely known pluronic F127 based MTF. Finally, to demonstrate the possible applications of the obtained materials, we will report a systematic study on biologically relevant proteins infiltration, taking advantage of the wide MTF pore size here synthesized. The effect of pore size, protein molecular weight, protein isoelectric point and solution ionic strength on protein infiltration will also be analyzed, in search of the limiting conditions for infiltration. The design of such material is highlighted as a step forward for the clever design of hybrid materials arising from the integration of entities coming from supramolecular chemistry, macromolecular chemistry, biochemistry and material science.
As a final product three N-Isopropylacrylamide (NIPAM)-tbutylacrylate-NIPAM co-polymers (named PN-PB-12, PN-PB-24 and PN-PB-48) and other three PNIPAM-polystyrene-PNIPAM co-polymer (named PN-PS-12, PN-PB-24 and PN-PS-48) were obtained (see molecular structures in Fig. 1). Table S1 (ESI†) summarizes the block length and the molecular weight of the obtained polymers.
The prepared triblock co-polymers were analyzed by thermogravimetric analysis (TGA) and compared to the commercial polymer Pluronic F127 (Fig. S2, ESI†). Pluronic F127 burns completely at 230 °C while PN-PB start to decompose at 270 °C and PN-PB at 340 °C. The residue amount decreases even further towards higher temperatures, burning completely at temperatures close to 500 °C.
Each new block co-polymer was used as a templating agent to produce mesoporous SiO2 thin films. To this end, polymers were added to ethanol solutions of prehydrolized TEOS, ethanol and hydrochloric acid. Sols showed a colorless clear appearance in all cases. Nevertheless, it should be noted that high molecular weight hydrophobic blocks (polymers PN-PB-48 and PN-PS-48) presented limited solubility under the tested conditions. The increase in the hydrophobic-block molecular weight lowers polymer solubility and therefore the amount of template dissolved limits the pore volume, as will be discussed later.
The sols were spun onto glass substrates and thermally treated to obtain the mesoporous oxides (Fig. 2). The thermal treatment was chosen according to TGA results. Although the polymers are completely decomposed above 500 °C, when they are used as templating agents, the effect on the oxide structure should be taken into account. Due to their curvature and thin wall thickness, mesoporous materials are sensitive to temperature, and sintering occurs approaching 500 °C, affecting the porous structure (see Fig. S3, ESI†). Therefore, a temperature above 370 °C (burning temperature of PN-PS and the second drop in mass for PN-PB) and below 500 °C was chosen for calcination. Calcination was done at 400 °C for two hours, the total amount of residues left was below 25% and 10% for PN-PB and PN-PS respectively.
The surface of the thin films obtained was analyzed by Scanning Electron Microscopy (SEM). SEM images, presented in Fig. 2, show a great variety of pore morphology ranging from low to high polydispersity and well-defined and shapeless pores. The information is summarized in the histograms in Fig. 2. Statistical analysis of the SEM images was performed to estimate pore distribution and mean pore size of each sample. Additionally, thin films were studied through ellipsometry at 0 and 100% humidity to estimate the pore volume accessible to water vapor.
The two different PN-PB templates (Fig. 2c and d, respectively) allowed for the creation of a MTF with highly monodisperse porosity, with a pore diameter that increased with the molecular weight. The template PN-PB 48 presents a larger hydrophobic block compared to PN-PB 24, while both PN-PB-24 and PN-PB-48 were designed to achieve a 2–3 fold higher molecular weight compared to PN-PB-12 (see Fig. S4 and Table S1, ESI†). This increment in polymer weight was reflected in an increase of the pore size and porous volume, leading to a 16 nm mean pore size in the case of PN-PB-24 and 24 nm pore diameter for PN-PB-48. In this latter case, the length of the hydrophilic block was two times the hydrophobic block length and thus the film presented a limited pore volume due to poor interconnectivity. This was attributed to a decrease in solubility as the hydrophobic chain increases, limiting the pore size attainable by this strategy. In the case of PN-PS polymers, well defined pores were obtained for the MTF based on PN-PS-12 with the smallest molecular weight, with general features similar to those of PN-PB-24 (both with similar molecular weight and tail to head ratio), a pore volume of 31% and a pore diameter of 15 nm. PN-PS-24 MTF, with a higher hydrophobic: hydrophilic block ratio, presented a sponge-like structure with poorly defined pores and wide pore size distribution. For this case, undefined micelles are responsible for the pore structure, and undefined aggregates act as molecular spacers. The increase of the hydrophobic block decreases solubility dramatically, and the hydrophobic–hydrophilic balance reaches its solubility limits, preventing any pore structure formation for PN-PS-48.
This variety on pore morphology accounts for several aspects regarding hydrophobicity, solubility, block molecular volumes, and micelle surface area, as described briefly by Israelachivili.47 A quantitative study would need a meticulous analysis on each of these variables and the dynamic aspect such as the mesostructure organization, inorganic condensation, and the thermal treatments. However, a qualitative analysis can be done taking into account thermodynamic, geometric and kinetic aspects. From a kinetic point of view, small molecules organize swiftly, giving rise to more organized structures and therefore less polydispersity. In contrast, bigger molecules need more time to self-assemble, in an extreme case working as molecular spacers. On the other hand, from a thermodynamic point of view, the hydrophobic/hydrophilic balance is crucial for the phase separation process. Solubility on ethanol of the high molecular weight hydrophobic blocks significantly limits the chances of creating homogenous thin films with high pore interconnection and with high pore volume. Low solubility entails low amounts of template molecules and compromises the mesoporous thin films formation, giving rise to spread-out pores and poor connectivity as seen in the case of PN-PB-48. In the worst-case scenario, no pores are found for the final films as for PN-PS-48. In a more detailed analysis, geometrical parameters should be considered, as well. The molecular volume of both the tail (hydrophobic) and the head (hydrophilic) of the synthesized polymers are one of the main features that define micelle size and mesophase morphology and are computed into a parameter known as compact factor. As the ratio of hydrophobic to hydrophilic volume increases pore size, eventually, globular, cylindrical, and lamellar mesophases could be formed.35
Fig. 3 SEM analysis of the films surface for MTF-F127 (a) and MTF-PB-PB-24 (b) samples. EEP isotherm (b) and pore distribution analysis (c) for MTF-PN-PB-24 (green) and MTF-F127 (blue) |
As can be seen from the SEM images, pores sizes for films obtained using PN-PB-24 are much wider than the ones obtained with Pluronic F127, a mean diameter size of 17 nm is obtained in contrast to a mean size of 7 nm for the commercial polymer; this results matches perfectly with pore size distribution measured by EEP and relate to a surface area of 380 m2 g−1 and 270 m2 g−1 measured following BET model. XRR measurements (Fig. 4a and b) show well-defined Kiessig fringes for both films exhibiting smooth surfaces and thickness was calculated to be approximately 200 nm and 300 nm for MTF-F127 and MTF-PN-PB-24, respectively. XRR measurements performed at 0% RH and 100% RH confirm a porous volume accessible to water above of 50% for MTF-PN-PB-24 sample. These results are in agreement with the data acquire by EEP measurements which shows a porous volume of 53% and 45% for MTF-PN-PB-24 and MTF-F127, respectively. Additionally, interplanar distance of 7 nm along the Z-axis could be calculated from XRR for MTF-F127 sample. Data from MTF-PN-PB-24 samples show a much less clearly defined interplanar distance along the Z-axis of 15 nm.
Finally, GI-SAXS measurements (Fig. 4c and d) confirm a more ordered structure for the F127 templated sample. This sample presents a uniaxially contracted body centered cubic Im3m mesostructure, as reported elsewhere.48 The MTF-PN-PB-24 sample, on the other hand, shows a local order but not an as well-defined structure as the F127 based ones, in agreement with XRR measurements. Nevertheless, these measurements allow to calculate interplanar distances within the X-Y-plane for both systems, being 26,6 nm and 12,2 nm for PN-PB-24 and F127, respectively. It is worth noting that interplanar distances within X-Y plane are much larger (around 70% larger) than those perpendicular to the Z axis due to contraction in Z direction after thermal treatments, typical of mesoporous thin films (Fig. S5, ESI†).48
Infiltration of macromolecules has been described previously by several authors55–57 by indirect methods to assess general adsorbed protein, such as Fourier-transform infrared spectroscopy and activity assays or depletion from solution. However, the limitation of these methods to distinguish spatial protein arrangement within the pores and the outer surface compromise future applications. In particular, Caruso's and Jiskoot's groups studied infiltration of proteins in mesoporous particles,33 nevertheless their study based on silica particles has spatial resolution limitations. MTF open the door to specific characterization techniques able to discriminate between the deposition of molecules inside the pores from the deposition on the top surface of the film through widely available techniques such as ellipsometry, XRR or optical waveguide spectroscopy (OWS).
In this work, infiltration of biomolecules within MTF was carried out to analyze the potentialities of the new wide pores. For this purpose, a concise infiltration study was performed in MTF-PN-PB-24, and similar studies were done on MTF-F127 for comparison purposes. Multi-mode OWS, through a careful study of the changes of the guided modes in the thin film, allows us to distinguish infiltration of proteins to the outer interface due to the refractive index change in distinct layers (examples and more details are provided in Fig. S6 and S7, ESI†).58 Thus, OWS is the technique of choice for a systematic study on the infiltration of biologically relevant proteins in mesoporous thin layers.
Five proteins of different molecular weights with isoelectric points above 5 were selected to test the infiltration: adenosine deaminase, neutravidin, glutaminase, amino acid oxidase, and urease. The influence of ionic strength and isoelectric point was taken into account to determine the best conditions for infiltration (see Table S2, ESI†). The isoelectric point was carefully selected to be above the working pH, since this will determine a positive protein charge and avoid charge exclusion to hinder any protein infiltration. Lactalbumin is used to test the importance of the isoelectric point in the infiltration: at Ph = 7 lactalbuminis negatively charged and, despite its small size, is not able to infiltrate.
Additionally, we prove that an increase in ionic strength may favor protein infiltration (Table 1 and Table S2, ESI†), in agreement with work reported by Lazzara et al. and Caruso's group.58,59 The results are summarized in Table 1 for the system MTF-PN-PB-24 and Table 2 for system MTF-F127. It is worth noticing that for MTF-F127 the smallest enzymes were studied (lysozyme, lactalbumin and neutravidin) as no infiltration occurs for larger molecules.
Protein | Molecular weight (kDa) | Isoelectric point | pH | Buffer | ΔRefractive index | ΔThickness (nm) | Diameter range (nm) |
---|---|---|---|---|---|---|---|
Lysozyme | 14 | 10 | 5 | PBS | 0.061 (27% pore filling) | 5 | 3–5 |
Neutravidin | 66 | 6.3 | 4.5 | PBS | 0.023 (10% pore filling) | 10 | 4–6 |
Glutaminase | 110 | 5.4 | 4.5 | PBS | 0.024 (10% pore filling) | 6 | 6–10 |
Amino acid oxidase | 110 | 6.3 | 4.5 | PBS | 0.026 (11% pore filling) | 7 | 5–11 |
Urease | 440 | 5.2 | 4.5 | PBS | 0.008 | 23.3 | 14–20 |
Protein | Molecular weight (kDa) | Isoelectric point | pH | Buffer | ΔRefractive index | ΔThickness (nm) | Diameter range (nm) |
---|---|---|---|---|---|---|---|
Lysozyme | 14 | 10 | 5 | PBS | 0.012 (7% pore filling) | 23 | 3–5 |
Lysozyme | 14 | 10 | 5 | PBSx 10−1 | −0.01 | 10 | 3–5 |
Lactalbumin | 14 | 4 | 7 | PBS | −0.003 | 0 | 2–4 |
Neutravidin | 66 | 6.3 | 4.5 | PBS | −0.009 | 5 | 4–6 |
The results show that proteins above 110 kDa are not able to infiltrate MTF-PN-PB-24 porous matrix. In contrast, all proteins are adsorbed on top of the MTF layer, with a layer thickness that increases as the molecular weight becomes larger. This tendency is disrupted by neutravidin, for this protein the overlayer thickness doubles the molecule size. Although the model parameters (refractive index of the porous layer and thickness of the overlayer) is limited to the number of guided modes (TM0 and TE0) and no gradient can be modeled, this anomalous result may account for some protein infiltration in the pores close to the surface, before a complete pore blocking. This results are in agreement with recent publication on myoglobin infiltration and condensation at pores entrance.13,60 Results of infiltration of glutaminase and amino acid oxidase show an increased overlayer deposition close to the enzyme diameter. In case of urase the infiltration into the structure seems to be hindered and an overlayer thickness similar in value to the enzyme diameter was measured.
Infiltration of proteins through MTF-F127 layers is only feasible for low molecular weight proteins. Lysozyme does not infiltrate the whole pore structure (pore filling 7%) as could be seen for MTF-PN-PB-24 (pore filling 27%), nevertheless, the protein layer thickness triples the enzyme mean diameter value. Therefore, we can argue that the enzyme infiltrates the first layer of pores before a complete blockage. In the same way as described for neutravidin in the MTF-PN-PB-24 system, here we are in the presence of a limiting case where infiltration is hindered partially and limited to the superficial pores. Therefore, bigger proteins are not be able to infiltrate the structure. This assumption is supported by the inability of neutravidin to infiltrate. These results clearly demonstrate that the preparation of mesoporous thin films with wider pores give rise to more accessible materials for macromolecules and biomolecules incorporation, as exemplified here with protein infiltration.
Neutravidin was obtained from Thermo scientific, glutaminase (40%) from Sorachim, D-amino acid oxidase (90%) from Calzyme, and Urease from Canavalia ensiformis (Jack Bean) type IX (50000–100000 units per g), lactalbumin form bovine milk (85%) and Lysozyme (98%) were provided by Sigma-Aldrich.
MTF were synthesized by spin coating the corresponding sol at 1500 rpm for 1 minute over glass substrates. After deposition, the films were subject to a thermal treatment as follows: 60 °C for 30 minutes, 130 °C for another 30 minutes and finally at 400 °C for 2 hours, achieved with a temperature ramp of 3 °C per minute.
Measurements were performed using a home-built optical instrument relying on Kretschmann configuration utilizing attenuated total reflection (ATR) configuration. It relies on the resonant optical excitation of surface plasmons (SPs) and dielectric OW modes at the sensor surface. Shortly, linearly polarized monochromatic light from a He–Ne laser (PL610P, Polytec, Germany, power 2 mW, wavelength λ = 632.8 nm) was made passing through a chopper (Princeton Applied Research, USA) and a polarizer, and was coupled to a LASFN9 prism. Onto the prism base, a LASFN9 glass substrate with a 2 nm layer of Cr and 50 nm thick layer of Au was optically matched using immersion oil (Cargile, USA). A flow-cell consisting of a rubber o-ring and a glass substrate with drilled inlet and outlet ports was pressed against the MTF surface to form a chamber with approximately 250 μl volume.
The intensity of the light beam reflected at the prism base was measured using a photodetector and a lock-in amplifier (Model 5210, Princeton Applied Research, USA). The angle of incidence of the light beam was controlled using a rotation stage (Hans Huber AG, Germany). Thereby, the intensity of the light was recorded as a function of the angle of incidence in order to monitor changes in the excitation of surface plasmons (SPs) and optical waveguides modes (OWMs). These modes can be seen as dips in the recorded spectrum in transverse magnetic (TM) polarization for SPs, set by the polarizer, and in both, transverse electric (TE) or transverse magnetic (TM) polarization for OWMs. The readout signal was recorded using Winspall software developed at the Max Planck Institute for Polymer Research, Mainz, Germany.
The results presented in this work should be taken into account for the future design of porous scaffolds for sensors,63 catalysis,64 fuel cells50 and soil remedation31 that required enzyme, protein or other macromolecule infiltration. In particular, the information presented is highly relevant for both, encapsulation and sieving purposes of porous silica coatings. Although activity of the enzymes studied has not been tested in this work, the presented results provide the foundation for understanding the relation between infiltration and enzymatic activity, as has been exemplified in a recent work.54
In summary, this work is an example of rational design implemented in the synthesis of new porous materials and bio-hybrid materials starting from the template design to the infiltration of macromolecules for potential applications. Two different pathways for functionalizing pores can be ascertained from this work. In the first case we expanded the strategies for custom made block co-polymers to be used for tailor made functionalization of hybrid thin films.65 In the second, after template removal, infiltration of macromolecules provides the functionalization required.
Footnote |
† Electronic supplementary information (ESI) available. See DOI: https://doi.org/10.1039/d3qm00378g |
This journal is © the Partner Organisations 2023 |