Study on the long time aging behavior of MAPbI3: from experiment to first-principles simulation

Yan Li *ae, Yu-Jing Dongbc, Hong Hea, Xue-Lian Chena, Hao Jianga and Yu Jia*bd
aSchool of Materials Science and Engineering, Xi'an Shiyou University, Xi'an, 710065, China. E-mail: yli@xsyu.edu.cn
bKey Laboratory for Special Functional Materials of Ministry of Education, School of Materials, Center for Topological Functional Materials, School of Physics and Electronic, Henan University, Kaifeng 475001, China. E-mail: jiayu@henu.edu.cn
cSchool of Science and Technology, Xinyang College, Xinyang 464000, China
dInternational Laboratory for Quantum Functional Materials of Henan, School of Physics, Zhengzhou University, Zhengzhou 450001, China
eState Key Laboratory for Mechanical Behavior of Materials, Xi'an Jiaotong University, Xi'an, 710065, China

Received 27th August 2022 , Accepted 2nd November 2022

First published on 16th November 2022


Abstract

As the core functional layer of perovskite solar cells, the serious issues of the CH3NH3PbI3 film related to the long-term stability and its rapid degradation when exposed to the environment should be investigated deeply. In this study, the variation of phase construction, light absorption ability and fluorescence quenching ability during the long time aging process have been monitored. The results show that the degradation process is composed of the original serious fluorescence quenching and the lag behind phase decomposition. Then, the intrinsic physical mechanism has been obtained by the first-principles simulation of defect properties, which shows that the original serious fluorescence emission quenching is attributed to the deep level defects with low formation energies (such as VPb and IPb); meanwhile, the lag behind phase decomposition is caused by the easy ionic diffusion; for example, the diffusion activation energy of the iodine ion is 0.286 eV. The results illustrate that both the defect passivation and prevention of the ion diffusion are necessary for achieving a stable perovskite film.


1. Introduction

CH3NH3PbI3 (MAPbI3) based perovskite solar cells are one of the earliest and classical perovskite solar cell (PSC) types. The MAPbI3 material is responsible for harvesting light, converting light into excitons and transporting excitons under sunlight. It shows the ability of broadband light absorption range, low exciton binding energy, long carrier diffusion length and high charge carrier mobility,1–3 which boost the conversion efficiency of PSCs to almost 20% in the first few years. Nowadays, to prolong the lifetime of the PSCs, the systematic investigation of the phase decomposition, defect properties and ionic diffusion of the MAPbI3 materials becomes increasingly significant.

In the beginning, the researchers found that the MAPbI3 material is composed of an inorganic Pb–I octahedron and organic CH3NH3+, and the organic and inorganic parts are brought together by van der Waals force, which leads to the easy breakdown of the perovskite structure under an external environment.4–6 Common conclusions have shown that moisture, oxygen and light soaking are all the main reasons for the degradation of the perovskite materials. It is confirmed that the failure processes of MAPbI3 under moisture should be the CH3NH3+ being deprotonated by water, and then forming methylamine, hydrated HI and PbI2.7 The failure process of MAPbI3 being exposed to oxygen and light soaking is because of the reaction of superoxide (O2) between the photo-generated electrons and O2, yielding methylamine, PbI2 and I2 as products.8,9 At this research stage, in order to detect the reaction products accurately, the failure behavior can be traced by some kinds of a precision testing equipment; for example, Yang et al.10 used in situ absorption spectroscopy and in situ grazing incidence X-ray diffraction to monitor chemical changes, and found that the formation of a hydrated intermediate containing isolated PbI64− octahedra was the first step of the degradation processes. Shi et al.11 used gas chromatography-mass spectrometry to verify the gas compositions during the degradation of the multi-cation perovskite precursors, and they identified the decomposition products as CH3I, NH3, and so on.

As the research investigation moved forward, researchers found that before the van der Waals bond was broken down under the environment, defect properties and ion diffusion must be considered. Considering original defect properties and ionic diffusion are hard to detect by equipment, first principles study has usually been proposed to uncover the changes in crystal structures. The first principles studies show 12 intrinsic point defects in the MAPbI3 materials, including vacancies (VMA, VPb, and VI), interstitials (MAI, PbI, and II) and antisites (MAPb, PbMA, MAI, PbI, IMA, and IPb).12 The calculation results also show that most vacancies produce shallow trap states near the band edge, but deep level defects (such as interstitial and antisite defects) may exist at the surface and grain boundaries of the perovskite films. In detail, it is considered that the defect densities on the surface are five orders of magnitude larger than that in the interior.13,14 The defects will cause nonradiative recombination and affect the ionic diffusion.15,16 As to the correlation between the phase decomposition, defect property and ion diffusion, Yuan et al.17 applied simultaneous luminescence and electron microscopy on the perovskite to monitor in situ morphology evolution and optical properties, and they pointed out that during the degradation process, the defects were created in the perovskite first, and then, the directional ion diffusion would be driven by these defects, which altered the fluorescence intensity and changed the chemical composition finally. Zhang et al.18 studied the role of iodine in the degradation of MAPbI3 by ab initio simulation, and they thought that excess electrons or holes would enhance I radical adsorption and its reaction with MAPbI3 surfaces. Wang et al.19 emphasized that the diffusion and accumulation of charged ions directly lead to significant changes in the doping concentration of the perovskite film and the built-in electric field, which were the key factors affecting the stability of PSCs. It can be seen that the defect property and ion diffusion play an important role in the degradation process of the MAPbI3 films.

In this study, MAPbI3 films of uniform quality have been prepared, and the long time aging behaviors, including the variation of phase construction, light absorption ability and fluorescence quenching ability of the perovskite films, under series conditions have been monitored by fluorescence emission spectrometry, UV-visible absorption spectrometry and X-ray diffraction spectrometry. Subsequently, the trap properties and the ion diffusion have been used to explain the initial serious fluorescence quenching and the lag behind phase decomposition. Lastly, the degradation process of the MAPbI3 film has been explained by the formation of deep level trap states and the ion diffusion.

2. Experiment

2.1 Chemicals

Lead iodide (PbI2) and methylammonium (CH3NH3I, MAI) purchased from p-OLED Co. (China) were used as solutes. N,N-Dimethylformamide (DMF) purchased from Adamas-beta (China) was used as the solvent. All the chemicals were of reagent grade and used without further purification. Transparent fluorine-doped tin oxide (FTO, TEC-15, LOF) conductive glasses (20 mm × 20 mm) were employed as substrates. Before the film deposition, the substrates were cleaned successively in deionized water and alcohol, and dried with N2 flow.

2.2 Preparation of the MAPbI3 film

For MAPbI3 film preparation, first, PbI2 and MAI are dissolved in the DMF solvent with a concentration of 460 mg ml−1, and then kept at 70 °C for 30 min by using a laboratory type magnetic stirrer. Second, the prepared MAPbI3 precursor solution was dropped on the surface of the FTO substrate, and subsequently, the substrate was spin-coated at 3000 rpm for 10 s and then was dried under a gas pumping pressure of 3000 Pa, which was controlled automatically by the equipment control unit.20–22 Finally, the MAPbI3 film was prepared. All the processes were carried out in air without inert gas protection, and the laboratory temperature was kept below 20 °C during the film preparation.

2.3 Long time aging test of the MAPbI3 film

The full spectrum light source was provided by a solar simulator (Newport, Class AAA) with a 100 mW cm−2 xenon lamp (Sol3A, Oriel), and the UV source was proved by a monochromatic UV lamp with a wavelength of 365 nm and intensity of 20 mW cm−2 (S-939, Saibao). The aging test proceeded under full spectrum light and under an atmosphere, indicating with sunlight with air, coded as Air-AM 1.5. The aging test proceeded under full spectrum light in a N2 glove box, indicating with sunlight without air, coded as N2-AM 1.5. The aging test proceeded under UV irradiation and under an atmosphere, indicating with UV with air, coded as Air-UV.

During the long time aging process, the phase construction of the perovskite films was measured using an X-ray diffractometer with Cu Kα radiation (XRD, Bruker, Germany). The absorption ability of the perovskite films was quantitatively analyzed using a UV-visible spectrophotometer (UV-vis., Shimadzu U-2700, Japan). The fluorescence quenching ability is measured using a high sensitivity spectrometer (PL, Maya2000Pro, Ocean Optics, China) at an excitation wavelength of 560 nm. The morphology of the MAPbI3 film was characterized using a scanning electron microscope (TSCAN, The Czech Republic).

2.4 Calculation methods and models

All the calculations are accomplished by density functional theory (DFT) using the generalized gradient approximation (GGA) within the Perdew–Burke–Ernzerhof (PBE)23 level and the plane-wave pseudopotential approach as implemented in the Vienna ab initio simulation package (VASP).24 A kinetic energy cutoff of 400 eV is used for the plane-wave basis set and geometries are relaxed until a residual force less than 0.02 eV per Å per atom. The supercell containing 2 × 2 unit cells is employed to make sure enough distance (>12 Å) and avoid the interaction between defects. It is important to determine the number of layers of the surface structure. Because the surface energy changes little with the atomic layer thickness larger than three layers, the thickness of four atomic layers was selected to calculate the surface defect properties, and the bottom fixed two layers were chosen as the bulk properties in the further calculation. The total energy of a charged system was not considered due to the electrostatic repulsion between slabs.25 The DFT simulations also include van der Waals correction of Grimme and coworkers26,27 to treat the weak interaction of organic–inorganic perovskites. The activation energy of iodine vacancy-assisted ion diffusion was obtained by the climbing image nudged elastic band (CI-NEB) method.28

3. Results and discussion

3.1 Microstructures of the MAPbI3 films

The architecture of the prepared MAPbI3 sample is presented in Fig. 1a. It is composed of a rough FTO substrate and a ∼400 nm MAPbI3 film, and the detailed morphology information was discussed in the previous literature.29 The appearance of the MAPbI3 film by the naked eyes is shown in Fig. 1b and c, and all the samples show a uniform dark brown color and mirror like surface. The surface microstructure of the perovskite film is shown in Fig. 1d and e, as can be seen there is a uniform full coverage surface and condensed grains without pinholes in low magnification, and the grain size is less than 500 nm in high magnification.
image file: d2ra05378k-f1.tif
Fig. 1 The MAPbI3 film deposited on the substrate: (a) schematic diagram, (b) and (c) photograph appearance, and (d) and (e) scanning electron microscope images under high and low resolutions.

Furthermore, the MAPbI3 films are divided into three groups, which individually undergo a long time aging test for 6 h under an air atmosphere with AM1.5 illumination, under a N2 atmosphere with AM1.5 illumination, and under an air atmosphere with UV 365 nm irradiation. The samples are coded as Air-AM1.5, N2-AM1.5 and Air-UV correspondingly.

3.2 The long time aging behaviors of the MAPbI3 film

The PL, UV-vis and XRD data have been characterized each hour. The original data are added in the ESI, as shown in Fig. S1 (Air-AM1.5), S2 (N2-AM1.5) and S3 (Air-UV), and the relative intensity trends of the three conditions are listed in Fig. 2. To summarize the results in Fig. 2, the reference wavelength of the PL is chosen as 770 nm, and the reference wavelength of UV-vis is chosen as 500 nm, and also, the reference 2θ degree of XRD is chosen as 12.7°. The PL, UV-vis and XRD data at 0 h are defined as 100%.
image file: d2ra05378k-f2.tif
Fig. 2 The long time aging behaviors of the MAPbI3 under the series conditions: (a) under an air atmosphere with AM1.5 illumination (Air-AM1.5), (b) under a N2 atmosphere with AM1.5 illumination (N2-AM1.5) and (c) under an air atmosphere with UV illumination (Air-UV). The original data are listed in Fig. S1 to S3. To reach Fig. 2, the reference wavelength of the PL is chosen as 770 nm, and the reference wavelength of UV-vis is chosen as 500 nm, and also the reference 2θ degree of XRD is chosen as 12.7°. The PL, UV-vis and XRD data at 0 h are defined as 100%.

As can be seen in Fig. 2, the absorption ability and fluorescence quenching ability of the MAPbI3 film under the three conditions, Air-AM1.5, N2-AM1.5 and Air-UV, all decline obviously at the original aging time; however, the XRD results coming from the (001) plane of PbI2 appear when the aging test reaches a certain time; for example, the PbI2 appears at the aging time of 1 h, 3 h and 3 h for Air-AM1.5, N2-AM1.5 and Air-UV based on Fig. S1(a), S2(a) and S3(a), respectively. In addition, a faster failure rate under Air-AM1.5 compared with both of N2-AM1.5 and Air-UV is found in this experiment.

Compared with the PL and XRD data, we found that the fluorescence quenching seems more sensitive to the aging process compared with phase decomposition. As can be seen in Fig. 2a, the fluorescence quenching ability decreased ∼60%; however, the PbI2 phase only increased ∼5% when the aging time went on to 1 h under the Air-AM1.5 condition. The fluorescence quenching ability decreased to 80%, and only ∼20% increase of PbI2 was characterized when the aging time went on to 4 h. The relative intensities show the same tendency under N2-AM1.5 and Air-UV conditions, indicating that there is a serious PL quenching at first, and the phase decomposition of the MAPbI3 film lags behind the fluorescence quenching. Considering that both the defect properties and ion diffusion play an important role in the degradation process of the MAPbI3 films, we use the first-principles simulation to establish the fundamental physics interpretation from the original fluorescence quenching and the subsequent phase decomposition in the following.

3.3 The initial serious PL quenching of the MAPbI3 film

The defect states in the MAPbI3 film have been simulated. The as-prepared MAPbI3 crystal film is a tetragonal structure with the parameters of a = b = 8.91 Å and c = 13.14 Å, which is in agreement with the previous XRD results (a = b = 8.97 Å, c = 13.16 Å).29 When it is cut parallel to the (110) panel, the possible surface forms of the MAPbI3 crystal are listed in Fig. 3. The surface energies of the stoichiometric atom ratio and the nonstoichiometric atom ratio of MAPbI3 surfaces are calculated based on eqn (1) and eqn (2), separately. All the calculated surface energies are shown in Table 1, which shows that the surface energy of MAI-termination with a nonstoichiometric atom ratio of MAPbI3 (MAI-non) is the lowest compared to those of the other three surfaces, which is chosen and considered in the following investigation.
 
image file: d2ra05378k-t1.tif(1)
 
image file: d2ra05378k-t2.tif(2)
where n refers to the number of atoms in the unit cell, and μ refers to the total energy of MAI or PbI2.

image file: d2ra05378k-f3.tif
Fig. 3 The four possible surfaces of the MAPbI3 crystal are stoichiometric atom ratio with MAI-termination (a) and with PbI2-termination (b), and nonstoichiometric atom ratio with MAI-termination (c) and with PbI2-termination (d).
Table 1 The surface energies of the four MAPbI3 surfaces (meV Å−2)
  PbI2-termination MAI-termination
Stoichiometric atom ratio 26.42 20.24
Nonstoichiometric atom ratio 31.38 17.72


In order to determine the easily formed defect types, we calculated the phase diagram of MAPbI3, and the stable MAPbI3 phase is shown in Fig. S4, which will provide the chemical potential for the following defect formation energy calculation. The defect types in the MAPbI3 crystal and corresponding defect formation energies under both I-poor and I-rich chemical conditions are shown in Table 2. In general, the MAPbI3 film prepared by the one-step solution method always produces a Pb-poor/I-rich component in the film,30,31 and then, the corresponding defect energy level positions for the I-rich component are calculated and listed in Fig. 4. Based on Table 2 and Fig. 4, the defects of VPb and IPb not only show the lowest formation energy (negative data) but also are the deep level defect types, indicating their easy formation and easy to be non-radiation recombination centers.

Table 2 Considered types of surface defects and their formation energy (in eV) under different conditions; the types of surface defects include vacancies (VMA, VPb, and VI), interstitials (MAi, Pbi, and Ii) and anti-site substitutions (MAI, IMA, PbI, IPb, MAPb, PbMA, and AB means A on B site)
MAI-non I-poor I-rich
VMA 2.638 0.880
VI 0.423 2.180
VPb 2.226 −1.289
MAi 0.011 1.769
Pbi 2.028 5.543
Ii 1.835 0.077
IMA 3.700 0.185
MAI 0.961 4.476
IPb 4.160 −1.112
PbI 2.106 7.379
MAPb 0.683 −1.075
PbMA 2.104 3.861



image file: d2ra05378k-f4.tif
Fig. 4 The various defect types in MAPbI3 crystals and the corresponding energy level positions.

In fact, in order to reach the uniform and full-coverage morphology, the rapid crystallization process is always chosen to prepare the perovskite film, for example the low pressure gap pumping method used in this research, and it usually results in a large amount of surface defects. At the same time, the external stimuli will also stimulate a large amount of defects under the long-time aging process. Based on these reasons, the large amount of defects, particularly the deep level defects VPb and IPb with low formation energies, will form non-radiation recombination centers and capture carriers, which may induce a serious fluorescence quenching at the early aging time.

3.4 The lag behind phase degradation of the MAPbI3 film

Then, the lag behind phase decomposition of the MAPbI3 has also been analyzed. Previous results have proved that the abundant surface defects, mainly shallow-level defect halide vacancies, will act as ion diffusion channels, which will enlarge open circuit voltage loss, and hinder device advancements.32 In the working environment, the formation of shallow-level defects is promoted through the influence of light and electricity, resulting in enhanced ion diffusion. In addition, the chemical bond is easy to break down under light, heat and other conditions. Taking the Pb–I bond as an example, the diffusion energy of I in MAPbI3 crystals has been calculated and is shown in Fig. 5. The energy barrier for I diffusion is 0.286 eV.
image file: d2ra05378k-f5.tif
Fig. 5 The diffusion energy of I in the MAPbI3 surface. The inset figure is the diffusion path of I when I vacancy defects exist.

Previous results not only proved that the ionic diffusion can recover when the trigger was removed,33 but also pointed that the more easy the diffusion of ions, for example I, the more easy the escape of CH3NH3+ from being bound by the I–Pb octahedra,34 which would induce the collapse of the octahedron structure in the long time aging process. Therefore, the phase decomposition lags behind the fluorescence quenching, can be illustrated that, more and more defects appear with proceeding the light irradiation, and the ion diffusion is not only enhanced, but also be irreversible, therefore both the continuous decrease of the fluorescence quenching and a lag behind phase decomposition are two important effect factors for the high performance and stability MAPbI3 film.

4. Conclusion

In this study, fluorescence quenching and phase decomposition, both important for identifying the quality of the perovskite film, have been investigated through a long time aging analysis. Based on the experimental results, it can be noticed that there is a serious PL quenching in the first stage, followed by a lag behind phase degradation. Combined with the first-principles simulation to analyze the defect properties and ion diffusion, there are deep level defect types with low formation energies, including VPb and IPb in the MAPbI3 film, and the diffusion energy barrier of the I in the MAPbI3 film is 0.286 eV. Therefore, it can be concluded that the degradation process is composed of two periods, the original fluorescence quenching and the subsequent phase decomposition. At the early aging stage, the easily formed deep level defects are responsible for the decrease of the fluorescence quenching. With the proceeding of the aging time, the irreversible ion diffusion will lead to the phase decomposition. The degradation processes gained from this study are important for designing stable perovskite films, and it proves that both the defect passivation and preventing the ion diffusion are necessary for achieving a stable perovskite film.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

All the authors acknowledge financial support from State Key Laboratory for Mechanical Behavior of Materials and National Natural Science Foundation of China (Grant No. 62104191).

References

  1. J. Xiao and H. L. Zhang, Recent progress in organic–inorganic hybrid perovskite materials for luminescence applications, Acta Phys.-Chim. Sin., 2016, 32, 1894–1912 CAS.
  2. F. Li, C. Ma, H. Wang, W. Hu, W. Yu, A. D. Sheikh and T. Wu, Ambipolar solution-processed hybrid perovskite phototransistors, Nat. Commun., 2015, 6, 8238 CrossRef PubMed.
  3. D. Shi, V. Adinolfi, R. Comin, M. J. Yuan, E. Alarousu, A. Buin, Y. Chen, S. Hoogland, A. Rothenberger, K. Katsiev, Y. Losovyj, X. Zhang, P. A. Dowben, O. F. Mohammed, E. H. Sargent and O. M. Bakr, Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals, Science, 2015, 347, 519–522 CrossRef CAS PubMed.
  4. N. Li, X. Niu, Q. Chen and H. Zhou, Towards commercialization: the operational stability of perovskite solar cells, Chem. Soc. Rev., 2020, 49, 8235–8286 RSC.
  5. Q. Guo, J. X. Zhao, K. Zhou, B. Y. Xing, X. J. Wang, F. Y. Tian, X. He and L. Zhang, High-throughput computational material screening of the cycloalkane-based two-dimensional Dion-Jacobson halide perovskites for optoelectronics, Chin. Phys. B, 2022, 31, 37104 CrossRef.
  6. J. Xin, P. Z. Yang, J. P. Wang and S. H. Wei, Theoretical investigation of halide perovskites for solar cell and optoelectronic applications, Chin. Phys. B, 2020, 29, 108401 CrossRef.
  7. J. A. Christians, P. A. Miranda Herrera and P. V. Kamat, Transformation of the excited state and photovoltaic efficiency of CH3NH3PbI3 perovskite upon controlled exposure to humidified air, J. Am. Chem. Soc., 2015, 137, 1530–1538 CrossRef CAS PubMed.
  8. N. Aristidou, I. Sanchez-Molina, T. Chotchuangchutchaval, M. Brown, L. Martinez, T. Rath and S. A. Haque, The role of oxygen in the degradation of methylammonium lead trihalide perovskite photoactive layers, Angew. Chem., Int. Ed., 2015, 54, 8208–8212 CrossRef CAS PubMed.
  9. G. Niu, W. Li, F. Meng, L. Wang, H. Dong and Y. Qiu, Study on the stability of CH3NH3PbI3 films and the effect of post-modification by aluminum oxide in all-solid-state hybrid solar cells, J. Mater. Chem. A, 2014, 2, 705–710 RSC.
  10. J. L. Yang, B. D. Siempelkamp, D. Y. Liu and T. L. Kelly, Investigation of CH3NH3PbI3 degradation rates and mechanisms in controlled humidity environments using in situ techniques, ACS Nano, 2015, 9, 1955–1963 CrossRef CAS PubMed.
  11. L. Shi, M. P. Bucknall, T. L. Young, M. Zhang, L. Hu, J. M. Bing, D. S. Lee, J. Kim, T. Wu, N. Takamure, D. R. McKenzie, S. J. Huang, M. A. Green and A. W. Y. Ho-Baillie, Gas chromatography-mass spectrometry analyses of encapsulated stable perovskite solar cells, Science, 2020, 368, 1328 Search PubMed.
  12. Y. Yin, L. Li and W. J. Yin, Theoretical and computational study on defects of solar cell materials, Acta Phys. Sin., 2020, 69, 177101 CrossRef.
  13. A. Hassan, Z. J. Wang, H. A. Yeong, M. Azam, A. A. Khan, U. Farooq, M. Zubair and Y. Cao, Recent defect passivation drifts and role of additive engineering in perovskite photovoltaics, Nano Energy, 2022, 101, 107579 CrossRef CAS.
  14. Z. Y. Ni, C. X. Bao, Y. Liu, Q. Jiang, W. Q. Wu, S. S. Chen, X. Z. Dai, B. Chen, B. Hartweg, Z. S. Yu, Z. Holman and J. S. Huang, Resolving spatial and energetic distributions of trap states in metal halide perovskite solar cells, Science, 2020, 367, 1352–1358 CrossRef CAS PubMed.
  15. J. M. Ball and A. Petrozza, Defects in perovskite-halides and their effects in solar cells, Nat. Energy, 2016, 1, 1–13 Search PubMed.
  16. D. Luo, R. Su, W. Zhang, Q. Gong and R. J. Zhu, Minimizing non-radiative recombination losses in perovskite solar cells, Nat. Rev. Mater., 2020, 5, 44–60 CrossRef CAS.
  17. H. Yuan, E. Debroye, K. Janssen, H. Naiki and M. B. J. Roeffaers, Degradation of methylammonium lead iodide perovskite structures through light and electron beam driven ion diffusion, J. Phys. Chem. Lett., 2016, 7, 566 Search PubMed.
  18. L. Zhang and H. L. Sit, Ab initio study of the role of iodine in the degradation of CH3NH3PbI3, J. Mater. Chem. A, 2017, 5, 23976 RSC.
  19. J. F. Wang, D. X. Lin and Y. B. Yuan, Recent progress of ion migration in organometal halide perovskite, Acta Phys. Sin., 2019, 68, 21 Search PubMed.
  20. B. Ding, L. Gao, L. Liang, Q. Chu, X. Song, Y. Li, G. Yang, B. Fan, M. Wang and C. Li, Facile and scalable fabrication of highly efficient lead iodide perovskite thin-film solar cells in air using gas pump method, ACS Appl. Mater. Interfaces, 2016, 8, 20067 CrossRef CAS PubMed.
  21. Y. Li, X. L. He, B. Ding, L. L. Gao, G. J. Yang, C. X. Li and C. J. Li, Realizing full coverage of perovskite film on substrate surface during solution processing: Characterization and elimination of uncovered surface, J. Power Sources, 2016, 320, 204–211 CrossRef CAS.
  22. G. J. Yang, B. Ding, Y. Li, S. Y. Huang, Q. Q. Chu, C. Li and C. Li, Material nucleation/growth competition tuning towards highly reproducible planar perovskite solar cells with efficiency exceeding 20%, J. Mater. Chem. A, 2017, 5, 6840–6848 RSC.
  23. J. P. Perdew, K. Burke and M. Ernzerh, Generalized gradient approximation made simple, Phys. Rev. Lett., 1996, 77, 3865 CrossRef CAS PubMed.
  24. G. Kresse and D. Joubert, From ultrasoft pseudopotentials to the projector augmented-wave method, Phys. Rev. B: Condens. Matter Mater. Phys., 1999, 59, 1758–1775 CrossRef CAS.
  25. H. Uratani and K. Yamashita, Charge carrier trapping at surface defects of perovskite solar cell absorbers: a first-principles study, J. Phys. Chem. Lett., 2017, 8, 742–746 CrossRef CAS PubMed.
  26. S. Grimme, J. Comput. Chem., 2006, 27, 1787–1799 CrossRef CAS PubMed.
  27. V. Barone, M. Casarin, D. Forrer, M. Pavone, M. Sambi and A. Vittadini, Role and effective treatment of dispersive forces in materials: polyethylene and graphite crystals as test cases, J. Comput. Chem., 2009, 30, 934–939 CrossRef CAS PubMed.
  28. G. Henkelman and H. Jonsson, Improved tangent estimate in the nudged elastic band method for finding minimum energy paths and saddle points, J. Chem. Phys., 2000, 113, 9978–9985 CrossRef CAS.
  29. Y. Li, R. L. Z. Hoye, H. H. Gao, L. H. Yan, X. Y. Zhang, Y. Zhou, J. L. MacManus-Driscoll and J. Gan, Over 20% efficiency in methylammonium lead iodide perovskite solar cells with enhanced stability viain situ solidification” of the TiO2 compact layer, ACS Appl. Mater. Interfaces, 2020, 12, 7135–7143 CrossRef CAS PubMed.
  30. X. C. Qiu, Y. Liu, W. W. Li and Y. Y. Hu, Traps in metal halide perovskites: characterization and passivation, Nanoscale, 2020, 12, 22425–22451 RSC.
  31. Y. Huang, W. J. Yin and Y. He, Intrinsic point defects in inorganic cesium lead iodide perovskite CsPbI3, J. Phys. Chem. C, 2018, 122, 1345–1350 CrossRef CAS.
  32. R. Partha, P. Sil, D. Sayantan, S. Arka and D. Dirtha, Investigation of ion-mediated charge transport in methylammonium lead iodide perovskite, J. Phys. Chem. C, 2017, 121, 5515–5522 Search PubMed.
  33. W. Nie, J. C. Blancon, A. J. Neukirch, K. Appavoo, H. Tsai, M. Chhowalla, M. A. Alam, M. Y. Sfeir, C. Katan, J. Even, S. Tretiak, J. J. Crochet, G. Gupta and A. D. Mohite, Light-activated photocurrent degradation and self-healing in perovskite solar cells, Nat. Commun., 2016, 7, 11574 CrossRef CAS PubMed.
  34. T. A. Berhe, W. N. Su, C. H. Chen, C. J. Pan, J. H. Cheng, H. M. Chen, M. C. Tsai, L. Y. Chen, A. A. Dubale and B. J. Hwang, Organometal halide perovskite solar cells: degradation and stability, Energy Environ. Sci., 2016, 9, 323–356 RSC.

Footnotes

Electronic supplementary information (ESI) available. See DOI: https://doi.org/10.1039/d2ra05378k
The first two authors contribute equally to this research.