Xiangnan Liabc,
Zhaoxia Caoabc,
Hongyu Dongabc,
Zhenpu Shiabc,
Huishuang Zhangabc,
Junyi Liabc,
Shuaijia Yangabc and
Shuting Yang*abc
aSchool of Physics, School of Chemistry and Chemical Engineering, Henan Normal University, Xinxiang, Henan 453007, China. E-mail: shutingyang@foxmail.com; Tel: +86-373-3323366
bNational and Local Joint Engineering Laboratory of Motive Power and Key Materials, Xinxiang, Henan 453007, China
cCollaborative Innovation Center of Henan Province for Motive Power and Key Materials, Xinxiang, Henan 453007, China
First published on 17th January 2020
Constructing uniform nanoceramic coating layers is a well-known challenge in the field of coating materials. Herein, Al2O3-coated Li[Li0.13Ni0.305Mn0.565]O2 (LLNM) Li-rich cathode materials are successfully prepared through a dry prilling coating (DPC) method. The structures and electrochemical performances of the Al2O3-coated products are systematically examined. Typically, the cycling stability is enhanced and voltage degradation upon cycling is reduced, benefiting from the unique and controllable nano-sized Al2O3 coating layer. Moreover, metal ion dissolution is avoided when using the DPC method, which is eco-friendly and suitable for large scale production.
Wet chemical synthesis is a common method that is used to form a coating layer on cathode particles. Wang et al.29 reported a freeze-drying method for coating with Al2O3, and the long-term cycling performance was enhanced and capacity decay was effectively suppressed in the meantime. Zhang et al.33 reported TiO2(B)-coated Li[Li0.2Mn0.54Co0.13Ni0.13]O2 composites obtained via a hydrothermal method, and these showed higher reversible capacity and better cycling stability and rate capabilities. Yang et al.34 synthesized Al2O3/SiO2-coated Li1.2Mn0.54Ni0.13Co0.13O2 via a sol–gel method, and the initial coulombic efficiency and capacity retention were improved, while voltage decay was suppressed effectively during charge/discharge cycling. Zheng et al.35 used MgO and TiO2 to coat 0.5Li2MnO3·0.5LiNi0.5Co0.2Mn0.3O2 cathode materials. The results showed that the surface coating materials could improve the discharge voltage retention, decrease the Li2CO3 content on the surface of the materials, and suppress side reactions. However, non-uniform coating and metal-ion leaching were observed during the wet chemical synthesis process. Also, the thickness of the coating layer is usually more than 100 nm, which hinders the diffusion of Li ions. Moreover, water pollution caused by wet chemical reactions is also a signification problem that is concerning.
Physical deposition methods, including atomic layer deposition (ALD) and magnetron sputtering, are considered ideal surface coating techniques. Uniformity and atomic-level control of films can be achieved using these techniques, making them useful for a wide range of applications. Dannehl et al.36 prepared an Al2O3-coated Li1.2Mn0.55Ni0.15Co0.1O2 material via an ALD method. The results showed that the capacity retention was improved and the initial capacity was increased. Xia et al.37 fabricated ZnO-modified 0.3Li2MnO3·0.7LiNi5/21Co5/21Mn11/21O2 cathode materials via reactive magnetron sputtering. The experimental data clearly exhibited a much higher initial discharge capacity and coulombic efficiency. Unfortunately, these physical deposition methods rely heavily on sophisticated equipment, and they are not suitable for large-scale industrial production at present.
The dry prilling coating (DPC) method is a facile strategy for material surface modification. As a kind of excellent surface treatment technology, DPC can form uniform coating layers on materials and the thickness of the coating layer can be expediently controlled at the nanoscale. Meanwhile, the procedure is simple and eco-friendly and does not require the use of water, and the cost of production is cheap. The DPC method can satisfactorily meet the demands of whole-scale industrialization, and it has been widely recognized and applied for obtaining powder materials in recent years. Nowadays, it is becoming a prospective strategy for constructing uniform thin films, especially in cases where high reproducibility and excellent conformity are required.
As far as we know, the surface coating of Li-rich cathode materials using DPC has been barely reported previously. This work will validate a novel and simple method for Li-rich cathode materials and provide further understanding of Al2O3 coatings obtained with DPC technology. Herein, Li[Li0.13Ni0.305Mn0.565]O2 (LLNM) Li-rich cathode materials with an Al2O3 coating are successfully prepared through a dry prilling coating method. The optimized coated samples obtained via DPC coating are investigated. The effects of Al2O3 coating via DPC on the surface morphology before and after cycling, the discharge capacity, the voltage decay, the cycling stability, and Mn/Ni ion dissolution are systematically investigated. The results indicate that appropriate Al2O3 coating dosages could effectively improve the electrochemical cycling stability and decrease capacity fading.
Fig. 1 Graphical illustration of the coating process via DPC (a). XRD patterns of the prepared cathode materials (b). |
Sample | Lattice parameters | |||
---|---|---|---|---|
a (Å) | c (Å) | c/a | I(003)/I(004) | |
LLNM-A0 | 2.8579 | 14.2215 | 4.9762 | 1.3271 |
LLNM-A5 | 2.8568 | 14.2187 | 4.9771 | 1.4270 |
LLNM-A10 | 2.8575 | 14.2213 | 4.9768 | 1.4435 |
LLNM-A15 | 2.8580 | 14.2226 | 4.9764 | 1.4255 |
The morphologies of Al2O3, a pristine sample, and the series of Al2O3-coated samples were confirmed via FESEM (Fig. S1† and 2). Both the pristine and coated materials contain fine and uniform particles ranging from 8 to 12 μm in diameter. The surfaces of the pristine spherical particles are smooth, with slight extensions resulting from primary particles (Fig. 2a, e and i); this is very different from the coated samples. The surfaces of LLNM samples coated with nanoscale Al2O3 particles via DPC are fuzzy. In particular, with an increase in the Al2O3 content, the roughness of the coated samples increased significantly. When the Al2O3 content is increased to 1.5 wt%, the LLNM sample is totally covered and the surface is rougher than the other Al2O3-coated samples, which may imply that the amount of Al2O3 exceeds requirements.
Fig. 2 FESEM images of samples: LLNM-A0 (a, e and i); LLNM-A5 (b, f and j); LLNM-A10 (c, g and k); and LLNM-A15 (d, h and l). |
Similarly, SEM images and elemental mapping of an LLNM-A10 sample are also provided (Fig. S2†). Mn, Ni and trace Al elements exist on the particles of LLNM. The uniform distribution of Mn, Ni and Al clearly illustrates that their distribution is similar to what is seen in Fig. S2a.† This also verifies the homogeneous nature of the LLNM-A10 particles. Combining the elemental distribution mapping and SEM images, it can be proved that Al2O3 successfully coated the obtained materials.
Fig. 3 shows HRTEM images of LLNM-A0 and LLNM-A10. The images clearly show the bulk particles of the pristine and coated samples. The pristine material LLNM-A0 displays smooth boundaries without any coating layer on the surface (Fig. 3a and b). For the coated sample of LLNM-A10 (Fig. 3c), some Al2O3 nanoparticles are distributed on the LLNM material; the thickness of the coating layer is 28 nm (Fig. 3d), which illustrates that a coating layer has been obtained. Fig. 3e and f further demonstrate the presence of Al2O3 (Fig. 3e and f show partial enlargements of Fig. 3d and e). As displayed in Fig. 3f, the interplanar spacing of 0.35 nm corresponds to the (210) plane of Al2O3.28 A uniform modification layer is helpful to suppress the dissolution of transition metal ions and maintain structural stability during the charge–discharge process. The Al2O3 coating layer is further probed via Ni, Mn, O, and Al elemental mapping using HRTEM (Fig. S3†). The Al elements are uniformly distributed in the LLNM-A10 sample, which shows that Al2O3 has coated the obtained materials successfully.
Fig. 3 TEM images (a and c) and HRTEM (b and d) images of LLNM-A0 and LLNM-A10, respectively. (e) An enlargement of the red rectangle area in (d). (f) An enlargement of the red rectangle area in (e). |
X-ray photoelectron spectroscopy (XPS) analysis was performed in order to confirm the oxidation states of Ni, Mn and Al. The C 1s peak (284.4 eV) is used to calibrate the binding energy (BE). The elements Ni, Mn and Al in LLNM-A0 and LLNM-A10 are detected in the survey spectrum, as shown in Fig. 4a. The XPS spectra of Ni 2p, Mn 2p and Al 2p species are further illustrated in Fig. 4b–d, respectively. In the Ni 2p spectra, the peak located at 872.3 eV with a satellite peak at 879.1 eV is attributed to Ni 2p1/2. The Ni 2p3/2 peaks in the spectra located at 854.1 and 855.4 eV, with a satellite peak at 861.0 eV, are assigned to Ni2+ and Ni3+, respectively. Ni exists as a mixture of +2 and +3 valence states.40,41 The Mn 2p1/2 and Mn 2p3/2 XPS peaks are located at about 653.9 eV and 642.1 eV, respectively, which demonstrates that the main valence state of Mn is +4.20,40 The peak at 73.8 eV in the Al 2p spectrum is assigned to Al3+ in Al2O3.42 Moreover, the Al 2p spectrum of the DPC derived sample is in accordance with previously reported results from Al2O3 coatings.28 The XPS results indicate that Al2O3 is successfully coated on the surface of LLNM.
Fig. 4 XPS survey spectra (a), Ni 2p spectra (b), and Mn 2p spectra (c) of LLNM-A0 and LLNM-A10 and the Al 2p spectrum (d) of LLNM-A10. |
Fig. 5 and S4–S8 (ESI†) present the cycling performance and charge–discharge curves of the pristine and coated materials at 0.1C (activated for an initial three cycles, 1C = 300 mA g−1) and 1C at room temperature. The LLNM-A0 sample manifests excellent discharge capacities (254.4 mA h g−1 and 186.5 mA h g−1 for the first cycle at 0.1C and 1C, respectively). Al2O3 is inactive during the charge–discharge process, which results in distinct initial polarization and specific capacity loss being shown by the coated samples. This can probably be attributed to increases in the contact resistance and charge transfer resistance. However, the Al2O3-coated samples present more stable long-term cycling performance than the pristine sample. As the cycling goes on, the LLNM-A0 sample capacity retention is approximately level with the LLNM-A10 sample after 200 cycles at 1C. And after 500 cycles, LLNM-A10 displays a higher capacity retention ratio (85.87%) than the pristine sample (72.92%). Appropriate coating with Al2O3 could effectively decrease polarization, which is beneficial for decreasing capacity fading and improving cycling stability performance.
Fig. 5 The long-term cycling performance (a), and charge–discharge curves after the 1st (b), 4th (c), 200th (d), 300th (e) and 500th (f) cycle at 0.1C and 1C of pristine and coated samples. |
To better describe and understand the effects of Al2O3 coating via DPC on the electrochemical performance, Fig. 6 shows the discharge behaviors of pristine and Al2O3-coated samples at 1C. Obviously, there are remarkable differences between the discharge voltage plateaus of LLNM-A0 and LLNM-A10. The voltage decay of the discharge plateaus is suppressed by the Al2O3 coating layer. Upon cycling, the discharge capacity of LLNM-A0 (Fig. 6a) decreases at a faster rate than LLNM-A10 (Fig. 6b). It can be found that the LLNM-A0 sample undergoes rapid voltage decay (0.31 V) from the 4th to the 500th cycle at 1C, which is much higher than that undergone by LLNM-A10 (0.22 V). Benefiting from the effective coating technology and synergistic effects arising from the Al2O3 coating thickness, using the DPC method to coat LLNM could restrain discharge voltage fading upon cycling. As illustrated in Fig. 6, the Al2O3 coating layer plays a central role in slowing voltage fading polarization. These results indicate that this coating strategy may suppress interfacial reactions between the cathode material and the electrolyte, reducing interfacial resistance.
Fig. 6 Discharge curves of LLNM-A0 (a) and LLNM-A10 (b) at 25 °C at 1C. The dissolution of transition metal ions from LLNM-A0 and LLNM-A10 samples (c). |
To demonstrate the suppression of transition metal ion dissolution by the Al2O3 coating layer on the LLNM material, ICP analyses of electrodes were carried out after 500 cycles. Fig. 6c illustrates that transition metal ion dissolution levels in the LLNM-A10 sample were obviously less than in the LLNM-A0 sample. This is a result of the appropriate Al2O3 coating strategy. This indicates that Al2O3 coating via DPC technology could stabilize the framework and decrease Mn/Ni ion dissolution from the LLNM cathode material, improving the structural stability over numerous battery cycles.
FESEM and EDS analysis of typical pristine and Al2O3-coated samples after 500 cycles was carried out in order to further figure out how Al2O3 coating via DPC technology affected the cycling stability. LLNM-A0 and LLNM-A10 electrode samples were soaked and washed after 500 charge–discharge cycles before observations were made. As shown in Fig. 7a–c, the images manifest that a number of cracks appeared and the structure deteriorated in the case of LLNM-A0. By contrast, these phenomena are not found in the case of LLNM-A10. Also, the Al2O3 coating layer maintains its morphological and structural completeness, indicating reduced volume change (Fig. 7d–f). The homogeneous distribution of Mn, Ni and Al elements on the surface of LLNM, as shown in the element mapping in Fig. S9,† reveals that the coating layer remains nearly intact after 500 cycles, thus effectively protecting LLNM from HF attack.43
Electrochemical impedance spectra (EIS) from LLNM-A0 and LLNM-A10 before and after different numbers of cycles and the corresponding equivalent circuit diagram are shown in Fig. 8. The Nyquist plots are formed from a semicircle in the high frequency region and an oblique line in the low frequency region. The large intercept with the real axis demonstrates the large ohmic resistance of the cell.21 In addition, the depressed semicircle is caused by reaction processes at the electrolyte/electrode interface.7 The oblique line in the lower frequency range is attributed to Warburg impedance, which was associated with lithium ion diffusion through the cathode electrode.
Fig. 8 AC impedance spectra from LLNM-A0 and LLNM-A10 samples before cycling (a), after 300 cycles (b), and after 500 cycles (c), and the equivalent circuit diagram (d). |
The LLNM-A0 sample manifests excellent Rct and ZW values before cycling. However, as the number of cycles increases, it is obviously seen that the Rct and ZW values of LLNM-A0 are visibly increased compared with LLNM-A10. It is indicated that this is consistent with the battery discharge capacities of LLNM-A0 and LLNM-A10. Furthermore, the Rct and ZW values of LLNM-A0 and LLNM-A10 are increased, but the RΩ values remain approximately similar. It can be inferred that the use of the same conductive agent is the primary cause. The results indicate that the coating dosage maintains a compromise between impedance and polarization: the surface Al2O3 coating slows down the Li mobility in LLNM-A10, while it is beneficial for improving the structural stability of the active material and decreasing polarization.
Footnote |
† Electronic supplementary information (ESI) available. See DOI: 10.1039/c9ra09206d |