Open Access Article
This Open Access Article is licensed under a Creative Commons Attribution-Non Commercial 3.0 Unported Licence

Enhanced fungicidal efficacy on Ganoderma boninense by simultaneous co-delivery of hexaconazole and dazomet from their chitosan nanoparticles

Farhatun Najat Maluina, Mohd Zobir Hussein*a, Nor Azah Yusofab, Sharida Fakurazic, Idris Abu Semand, Nur Hailini Zainol Hilmid and Leona Daniela Jeffery Daime
aInstitute of Advanced Technology, Universiti Putra Malaysia, 43400 UPM, Serdang, Selangor, Malaysia. E-mail: mzobir@upm.edu.my; Tel: +603 8946 8092
bDepartment of Chemistry, Faculty of Science, Universiti Putra Malaysia, 43400 UPM, Serdang, Selangor, Malaysia
cDepartment of Human Anatomy, Faculty of Medicine and Health Sciences, Universiti Putra Malaysia, 43400 UPM, Serdang, Selangor, Malaysia
dMalaysian Palm Oil Board (MPOB), 6, Persiaran Institusi, Bandar Baru Bangi, 43000, Kajang, Selangor, Malaysia
eSime Darby Technology Centre Sdn. Bhd., UPM-MTDC Technology Centre III, Universiti Putra Malaysia, Lebuh Silikon, 1st Floor, Block B, 43400 Serdang, Selangor, Malaysia

Received 15th July 2019 , Accepted 14th August 2019

First published on 28th August 2019


Abstract

The excessive use of fungicides may be of environmental and health concerns. Hence, to overcome this problem, chitosan as a controlled release matrix was used in this work to encapsulate the fungicide for the development of enhanced fungicide nanodelivery system. In this proposed study, dual-loaded fungicides (hexaconazole and dazomet) were simultaneously encapsulated into chitosan nanoparticles as an antifungal agent on Ganoderma boninense (G. boninense). In this work, we report the synthesis and characterization of the nanoparticles prepared using various concentrations of the crosslinking agent of sodium tripolyphosphate (TPP); 2.5, 5, 10, and 20 mg mL−1, which resulted in the nanoparticles of CHDEN2.5, CHDEN5, CHDEN10, and CHDEN20, respectively. The effect of TPP on the synthesized nanoparticle size revealed that an increase of TPP resulted in smaller particles, which in turn play a crucial role in controlling G. boninense growth. CHDEN20 shows the highest antifungal efficacy with the lowest half-maximal effective concentration (EC50) on G. boninense. The formulated nanocarrier system of fungicide aims to enhance the efficient delivery of the active ingredients to the target site, able to sustain in it for a longer time, and consequently improve the fungicide efficacy in combating the basal stem rot disease in oil palm.


Introduction

Palm oil emerges as the most profitable and efficient vegetable oilseed versus other world leading oilseeds, such as sunflower, coconut, rapeseed, and soybean. This is due to the high yield of oil palm where a hectare can produce up to ten times the oil compared to other oilseeds.1 In respect to that, Indonesia and Malaysia are the leading countries in oil palm production.2,3 However, oil palm cultivation is threatened by the most devastating disease, the basal stem rot (BSR) disease caused by Ganoderma boninense (G. boninense) and has subsequently become the major concern in the oil palm industry.4–6

Previous studies have shown that fungicidal treatments of hexaconazole7,8 and dazomet9 were effective against the Ganoderma disease in oil palms. Hexaconazole is classified under the triazole group, widely used on cereal and ornamental plants to control fungi, particularly Ascomycetes and Basidiomycetes.10–12 It has systemic demethylation inhibitors (DMI) that act mainly on the vegetative stage of fungi by blocking the mycelial growth either inside or on the surface of the host plant.13 In addition, dazomet is a soil fumigant that releases methyl isothiocyanate (MITC) when it comes into contact with water.14,15 This MITC has been reportedly used in a broad spectrum of activities, such as inhibiting the activity of pathogenic fungi.16–18

However, it is also reported that the application of fungicides has caused environmental and health concerns, hence are a threat to both terrestrial and aquatic life as it is dissipated and leached.19,20 Thus, to address this issue, the fungicide was encapsulated in a nanocarrier of chitosan to develop an effective formulation nanodelivery system. The nanodelivery system aims to improve the solubility and stability, minimize volatilization, and enhance uptake with controlled release properties to give a high efficiency as the fungicide active ingredient can reach the target fungus, G. boninense, more effectively.21–24

Numerous studies have been conducted on the use of chitosan in plant protection, but only limited studies have been reported in the use of chitosan in agronanoparticles.25 Apart from non-toxicity, biodegradability, biocompatibility, and antimicrobial and antioxidant activity, chitosans are known for their ability to control or reduce the spreading of disease in the plant by inhibiting pathogens and enhance the plant defense mechanism.26,27 In addition, dual encapsulation had been proven to increase the drug release and bioavailability, but the formulation might be challenging due to the drugs incompatibility that could give rise to complications.28

This study aims to synthesize and characterize the host–guest type nanoparticles by combining the chitosan with fungicide molecules through chemical reactions, hoping that the resulting nanoparticles have a slow-release capability, low toxicity, and high antifungal activity against G. boninense. The chitosan nanoparticles were embedded simultaneously with hexaconazole and dazomet (CHDEN) using an ionic gelation method by adding several concentrations of the crosslinking agent, sodium tripolyphosphate (TPP). The effect of TPP on the formation of chitosan–hexaconazole–dazomet nanoparticles was investigated, namely the particle size distribution, loading capacity, and encapsulation efficiency of the fungicides. In addition, the relationship between the particle size of the synthesized chitosan–hexaconazole–dazomet nanoparticles and in vitro antifungal activity against G. boninense also was investigated. The co-release profiles of both hexaconazole and dazomet from the synthesized nanoparticles were also studied.

An encapsulation mechanism of both hexaconazole and dazomet in the chitosan matrix is proposed in Fig. 1. The fungicides were embedded first by separately mixing hexaconazole and dazomet with the chitosan solution. Then, both solutions were mixed together before adding the Tween-80 and TPP solution, prior to the formation of the nanoparticles. The nanoparticles were formed through the electrostatic interaction between the embedded fungicides in the positively charged amine group of chitosan and the negatively charged crosslinker of TPP using an ionic gelation method. Tween-80 was added as a stabilizing agent for the formation of nanoparticles. Moreover, TPP has also been reported to be used in controlling nanoparticles size and drug loading.27,28


image file: c9ra05417k-f1.tif
Fig. 1 Proposed mechanism for the formation of chitosan–hexaconazole–dazomet nanoparticles.

Material and methods

Materials

Hexaconazole (C14H17Cl2N3O, molecular weight 314.21 g mol−1) and dazomet (C5H10N2S2, molecular weight 162.269 g mol−1) were purchased from Changzhou Aiteng with 95% purity and were used as received. Chitosan (medium molecular weight, 190[thin space (1/6-em)]000–310[thin space (1/6-em)]000 degree of acetylation), Tween-80 and sodium tripolyphosphate (TPP) were purchased from Sigma-Aldrich [St. Louis, MO, USA]. Hydrochloric acid (37%) and N,N-dimethylformamide (DMF) were purchased from Friendemann Schmidt [Parkwood, Australia] and Merck [Kenilworth, NJ, USA], respectively. All the other reagents used were of analytical grade. The G. boninense culture was provided by the Malaysian Palm Oil Board (MPOB), Bangi, Malaysia, and maintained in potato dextrose agar (PDA) media purchased from Oxoid, Thermo Scientific (pH 5.5) [Waltham, MA, USA] incubated at 28 ± 2 °C.

Preparation of chitosan–hexaconazole–dazomet nanoparticles

Hexaconazole–dazomet-loaded chitosan nanoparticles were prepared using ionic gelation method.29,30 Briefly, 5 mg mL−1 of chitosan was prepared in 100 mL of a 1.0% (v/v) acetic acid solution and, in a different flask, 10 mg mL−1 of hexaconazole and dazomet were prepared in 100 mL of DMF separately. Then, all the solutions were mixed together under stirring until a homogeneous solution was obtained. Then, 2% v/v Tween-80 was added as a stabilizer to prevent particle aggregation.31,32 Various concentrations of sodium TPP ranging from 2.5, 5, 10, and 20 mg mL−1 were used and the resulting nanoparticles labeled as CHDEN2.5, CHDEN5, CHDEN10, and CHDEN20, respectively. The nanoparticles were formed spontaneously upon the addition of 40 mL sodium TPP solution added dropwise using a burette while stirring. The final TPP-to-chitosan ratio achieved was 1[thin space (1/6-em)]:[thin space (1/6-em)]2.5 (v/v). The mixture was then centrifuged at 40[thin space (1/6-em)]000 rpm for 10 min and the supernatant was discarded. The chitosan–hexaconazole–dazomet nanoparticle pellet was then freeze-dried overnight before further analysis.

Reaction yield, fungicide loading, and encapsulation efficiency

The reaction yield of the synthesized chitosan–hexaconazole–dazomet nanoparticles was calculated using eqn (1).29,30
 
RY = [produced nanoparticle (mg)/(used chitosan (mg) + used dazomet (mg) + used hexaconazole (mg))] × 100 (1)

The hexaconazole and dazomet loading content (LC) and encapsulation efficiency (EE) were determined using the high-performance liquid chromatography (HPLC) technique. Briefly, 5.0 mg of the synthesized nanoparticles were dissolved in 10.0 mL of methanol and hydrochloric acid (0.5% v/v) under sonication, and a clear solution was obtained prior to the HPLC analysis. The nanoparticles were ensured to be completely dissolved, thus releasing 100% of the hexaconazole and dazomet content. The mobile phase of the HPLC used was methanol/water (30[thin space (1/6-em)]:[thin space (1/6-em)]70, v/v), the flow rate was 1.0 mL min−1 at 25 °C, and the wavelength was set at 235 and 280 nm for hexaconazole and dazomet, respectively. The retention time obtained was 1.8 and 2.5 min for hexaconazole and dazomet, respectively. The LC and EE of the hexaconazole and dazomet were calculated according to the following equations:

 
LC (%) = [weight of fungicide in nanoparticles/weight of nanoparticles] × 100 (2)
 
EE (%) = [weight of fungicide in nanoparticles/initial amount of fungicide in the system] × 100 (3)

Fungicide release studies

The hexaconazole and dazomet release profile from the nanoparticles was investigated using HPLC. Briefly, 30.0 mg of the synthesized nanoparticles were dispersed in 30 mL of the medium and shaken in incubator shaker (27 °C; 100 rpm) in a phosphate-buffered saline solution (PBS), pH 5.5. The buffer solution of pH 5.5 was chosen in this experiment in order to imitate the release of fungicide in the potato dextrose agar (PDA) media. At predetermined intervals time, 1 mL of the solution was isolated by centrifugation and replaced with the same amount of the fresh medium. The concentrations of the released hexaconazole and dazomet were determined by HPLC as described above.

Characterizations

Fourier transform infrared spectra (FTIR), powder X-ray diffraction (PXRD) and thermogravimetric and differential thermogravimetric analysis (TGA/DTG) techniques were used to characterize the structure of the synthesized nanoparticles.27,28 The FTIR study was carried out with a Thermo Nicolet Nexus spectrometer with a Smart Orbit, in the range 400–4000 cm−1 (Waltham, MA, USA). The phase and purity studies were performed with an XRD technique using a Bruker D8 Advance powder XRD using CuKα radiation (λ = 0.15406 nm) at 40 kV and 40 mA (Billerica, MA, USA). The thermal stability and decomposition were done by a thermal gravimetric analyzer, a Mettler-Toledo 851e, at a heating rate of 10 °C min−1 in 150 μL alumina crucibles over the range 30–900 °C (Columbus, OH, USA).

The hydrodynamics particle size was determined by a dynamic light scattering (DLS) method using a particle size analyzer (Nano Series Nano-ZS, Malvern Panalytical Ltd., Malvern, UK). The internal morphology and particle size diameter were studied using a high-resolution transmission electron microscope (HRTEM), FEI Tecnai G2 F20 S-TWIN (Hillsboro, OR, USA). The surface morphology analysis was conducted using field-emission scanning electron microscopy (FESEM), JSM-7500F JEOL, Tokyo, Japan.

The amount of fungicide loading and release was measured using a high-performance liquid chromatography (HPLC) Waters Alliance 2695 separation module (Waters, Milford, MA, USA). HPLC assays were conducted at room temperature (23 °C) with a diode array detector Waters 2996. The mobile phase of a 30[thin space (1/6-em)]:[thin space (1/6-em)]70 (v/v) methanol[thin space (1/6-em)]:[thin space (1/6-em)]water solution and a C18 column (5 μm, 4.6 × 150 mm) was employed.27

In vitro antifungal activity efficacy studies

The in vitro antifungal activity of the synthesized nanoparticles was evaluated against G. boninense using a poisoned medium technique with potato dextrose agar (PDA) as the medium. The PDA was amended in seven different conditions (pure hexaconazole, pure dazomet, chitosan, and the synthesized nanoparticles, CHDEN2.5, CHDEN5, CHDEN10 and CHDEN20) at several concentrations (0.1, 0.5, 1, 5, 10, 50, 100, 500 and 1000 ppb of active ingredient), which were prepared in acetone and 0.5% (v/v) HCl. Mycelia plated on the PDA with the solvent only served as a control. A 5 mm mycelial disc from the margins of the actively growing culture of G. boninense was placed at the center of amended PDA as well as in the non-amended PDA. The radial growth of the mycelia was measured for 7 days of inoculation by incubating the Petri plates at 28 ± 2 °C (n = 5). Mycelial growth was recorded every day. The percentage inhibition of the radial growth (PIRG) by the fungicide was then calculated.

Statistical analysis

Data are presented as mean ± standard deviation and the statistical difference of the parameters was analyzed using ANOVA and Tukey's test (p ≤ 0.05) using SPSS software. The half-maximal effective concentration (EC50) of chitosan–hexaconazole–dazomet nanoparticles at various concentrations of TPP were determined using the sigma plot analysis of Sigma Plot 10.0.

Results and discussions

Reaction yield, fungicide loading, and encapsulation efficiency

As listed in Table 1, there is no significant difference in the loading content and encapsulation efficiency of both hexaconazole and dazomet in the synthesized nanoparticles prepared at various concentrations of TPP. This suggests that there is no effect of TPP concentration on the loading content of both hexaconazole and dazomet in the preparation of chitosan–hexaconazole–dazomet nanoparticles. On the other hand, the amount of dazomet in the synthesized nanoparticles exhibited a higher loading content and encapsulation efficiency compared to the amount of hexaconazole, thus suggesting that dazomet has a higher capability to be encapsulated into the chitosan matrix, compared to the hexaconazole. This behavior is also supported by our previous work on a single loaded system of chitosan–hexaconazole nanoparticles29 and chitosan–dazomet nanoparticles.30 This might be due to the smaller molecular structure of dazomet compared to hexaconazole (Fig. 2), hence making it much easier to form hydrogen bonding with the chitosan. Moreover, the reaction yield of the hexaconazole–dazomet-loaded chitosan reached an optimum at 5 mg mL−1, where the increase of TPP at 10 and 20 mg mL−1 no longer affected the yield.
Table 1 Loading content and encapsulation efficiency of fungicide in the synthesized nanoparticles
Synthesized nanoparticles Loading content (%) Encapsulation efficiency (%) Reaction yield (%)
Hexaconazole Dazomet Hexaconazole Dazomet
CHDEN2.5 7.4 ± 2.0 9.7 ± 2.5 64.8 ± 4.0 69.4 ± 2.5 58.5 ± 3.0
CHDEN5 7.5 ± 2.5 9.4 ± 2.0 64.9 ± 2.0 68.7 ± 3.0 69.0 ± 2.0
CHDEN10 7.6 ± 1.5 9.5 ± 1.0 65.3 ± 4.5 68.9 ± 3.5 70.0 ± 3.5
CHDEN20 6.7 ± 3.0 7.0 ± 3.0 63.4 ± 3.5 63.9 ± 4.0 72.0 ± 2.0



image file: c9ra05417k-f2.tif
Fig. 2 Chemical structures of hexaconazole and dazomet.

Powder X-ray diffraction

As shown in Fig. 3, pure dazomet and pure hexaconazole showed a sharp peak suggesting that they are highly crystalline in nature. Meanwhile, chitosan showed a broad peak showing it is an amorphous type of material. For the nanoparticles, CHDEN2.5, CHDEN5, CHDEN10 and CHDEN20, broad peaks of an amorphous type are observed, suggesting a high content of the chitosan phase, in which the crystalline peaks of dazomet and hexaconazole were buried when they were encapsulated within the chitosan nanoparticles. The broad peak at diffraction angles (2θ) of 16.1, 19.2, 20.8, 22.7, 29.1, and 36.0° matched with the peak pattern of pure dazomet, while diffraction angles (2θ) of 8.4, 10.4, 11.7, 13.9, 16.0, 20.2, and 24.0° matched the peak pattern of pure hexaconazole, thus inferring the encapsulation of both dazomet and hexaconazole into the chitosan matrix.
image file: c9ra05417k-f3.tif
Fig. 3 PXRD patterns of (A) pure dazomet, (B) pure hexaconazole, (C) chitosan, and chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP (D) 2.5 mg mL−1, (E) 5 mg mL−1, (F) 10 mg mL−1 and (G) 20 mg mL−1.

FTIR spectroscopy

As shown in Fig. 4, broad bands at 2870 cm−1 and 3288 cm−1 were due to the C–H bond and NH2 stretching of the chitosan, respectively.33 Chitosan also showed characteristic broad bands at 1022, 1588, and 1647 cm−1, which indicated the stretching of the C–O–C moiety, NH2 group bending, and CO–NH2 group stretching, respectively.33 Besides, all the synthesized nanoparticles showed the characteristic peak of chitosan with a slight shifting of NH2 peak at 1536 cm−1. The shifting might be due to the presence of N–H bending from the dazomet, which is at 1513 cm−1 34. Moreover, additional bands of dazomet for the synthesized nanoparticles have also been observed at 1176 and 657 cm−1, which can be attributed to the C[double bond, length as m-dash]S stretching and C–H bending, respectively, of a 1,3,5-trisubstituted aromatic alkane.34,35 Apart from that, additional bands of hexaconazole can also be seen for the synthesized nanoparticles at 1384, 890, 806 and 657 cm−1, which can be attributed to C–N stretching, C[double bond, length as m-dash]C bending and C–Cl stretching, respectively,36 and thus strongly support the encapsulation of both hexaconazole and dazomet into the host, chitosan, in all the CHDEN2.5, CHDEN5, CHDEN10, and CHDEN20.
image file: c9ra05417k-f4.tif
Fig. 4 FTIR spectrum of (A) pure hexaconazole, (B) pure dazomet, (C) chitosan, and chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP (D) 2.5 mg mL−1, (E) 5 mg mL−1, (F) 10 mg mL−1 and (G) 20 mg mL−1.

Thermal analysis

Thermal stability of the synthesized nanoparticles was studied using a thermal analyzer, and the TGA/DTG thermograms and the data obtained are shown in Fig. 5. Chitosan showed two stages of weight loss at 65 °C and 309 °C, which are attributed to the release of the physical adsorption of the water molecules and decomposition of chitosan (loss of hydrogen bonding), respectively. In addition, at the end of the analysis, nearly 30% of the sample remained as a residue indicating a higher thermal stability of chitosan. Moreover, 100% weight loss was obtained at 282 °C and 194 °C for pure hexaconazole and pure dazomet, respectively, which indicates the total decomposition of hexaconazole and dazomet. Hence, showing a higher thermal stability for pure hexaconazole compared to that of pure dazomet. This is presumably due to the more complex and bigger molecular structure of hexaconazole compared to dazomet (Fig. 2).
image file: c9ra05417k-f5.tif
Fig. 5 TGA-DTG thermogram of (A) chitosan, (B) pure dazomet, (C) pure hexaconazole and chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP (D) 2.5 mg mL−1, (E) 5 mg mL−1, (F) 10 mg mL−1 and (G) 20 mg mL−1.

The synthesized nanoparticles showed four stages of weight loss. In the first stage, weight losses of approximately 14.0, 15.8, 12.6 and 18.5%, respectively, for CHDEN2.5, CHDEN5, CHDEN10, and CHDEN20 occurred due to the release of water molecules. The second stage at around 245–255 °C was attributed to the decomposition of chitosan. While at the third stage, the synthesized nanoparticles of CHDEN2.5, CHDEN5, CHDEN10, and CHDEN20 showed a third weight loss at 344, 346, 346 and 340 °C, respectively, attributed to a combination of dazomet and hexaconazole thermal decomposition. This shows the higher thermal stability of hexaconazole and dazomet in the synthesized nanoparticles compared to the bare fungicide, hexaconazole and dazomet. For the last stage at around 800 °C, the weight loss is attributed to char from the decomposition of chitosan.

Morphology and particle size distribution

The morphological and particle size distribution of CHDEN2.5, CHDEN5, CHDEN10, and CHDEN20 were studied by FESEM (Fig. 6) and HRTEM (Fig. 7A–H), and their size distribution was measured via ImageJ software (Fig. 7I–L). The agglomeration of sphere shape can be seen in the FESEM image. Moreover, the internal morphology of the HRTEM images clearly shows the spherical shape of all the synthesized nanoparticles. The loaded of the fungicides inside the chitosan nanoparticles matrix can also be seen clearly for CHDEN2.5, CHDEN5, and CHDEN10 in the HRTEM image at a high magnification of 39[thin space (1/6-em)]000×. The image is not clear for CHDEN20 since its size is too small. In addition, the results reveal the higher size range of the particle size distribution for the synthesized nanoparticles at the lowest concentration of TPP (CHDEN2.5) with a mean particle size of 156.5 nm. The increased TPP concentration resulted in smaller particle sizes of the synthesized nanoparticles which follows the order: CHDEN5 > CHDEN10 > CHDEN20, with mean particle size of 57.9, 30.7 and 5.3 nm, respectively.
image file: c9ra05417k-f6.tif
Fig. 6 FESEM image of chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP (A) 2.5 mg mL−1, (B) 5 mg mL−1, (C) 10 mg mL−1 and (D) 20 mg mL−1.

image file: c9ra05417k-f7.tif
Fig. 7 HRTEM image at 4,500× magnification (A–D) and 39,000× magnification (E–H) of the chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP (A and E) 2.5 mg mL−1, (B and F) 5 mg mL−1, (C and G) 10 mg mL−1 and (D and H) 20 mg mL−1 and the particle size distribution of the chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP (I) 2.5 mg mL−1, (J) 5 mg mL−1, (K) 10 mg mL−1 and (L) 20 mg mL−1.

Furthermore, the hydrodynamic size measured via dynamic light scattering (DLS) of the synthesized chitosan nanoparticles simultaneously loaded with both hexaconazole and dazomet, CHDEN2.5, CHDEN5, CHDEN10, and CHDEN20, are shown in Fig. 8. The findings of both methods indicate that the use of a higher concentration of TPP resulted in a smaller particles size of the synthesized nanoparticles. The presence of oppositely charged ions in the deionized water (solvent medium) leading to adsorption might be the reason for this phenomenon. The interaction between –NH3+ of chitosan (protonated under acid conditions) with the multivalent anion, TPP, results in the formation of CS-TPP. Thus, a higher concentration of TPP means a higher number of anions, and hence more inter- and intramolecular cross-linking between the chitosan and TPP. Consequently, this leads to the formation of smaller particle sizes.37


image file: c9ra05417k-f8.tif
Fig. 8 Cumulative and relative particles size distributions (PSD) of chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP (A) 2.5 mg mL−1, (B) 5 mg mL−1, (C) 10 mg mL−1 and (D) 20 mg mL−1.

Fungicide release studies

To investigate the delivery of hexaconazole and dazomet in response to time, the synthesized nanoparticles prepared at 5 mg mL−1 TPP and 20 mg mL−1 TPP, i.e. CHDEN5 and CHDEN20, respectively, were incubated in a phosphate buffer saline solution at pH 5.5. As shown in Fig. 9 and 10, a small burst effect can be observed in the first 11 hours for both release profiles of hexaconazole and dazomet in both CHDEN5 and CHDEN20. This may be because the fungicides were located close to the surface of the nanoparticles. In addition, a faster release of both hexaconazole and dazomet in CHDEN20 can be seen in the first 80 and 40 hours, respectively. However, surprisingly, the sustained releases of hexaconazole and dazomet in CHDEN20 were much longer with 130 hours (93.6% cumulative release) and 50 hours (76.4% cumulative release), respectively. In contrast, the sustained releases of hexaconazole and dazomet in CHDEN5 were achieved up to 118 hours (93.7% cumulative release) and 42 hours (75.3% cumulative release), respectively. This suggests a minimal effect of particle size in the dual release of hexaconazole and dazomet. However, it is worth noting that the release of both fungicides was a bit faster in the smaller particle size, but at the same time prolonged the fungicides release. This is due to the higher surface area of the smaller nanoparticle size.
image file: c9ra05417k-f9.tif
Fig. 9 Cumulative release profiles of (A) hexaconazole from CHDEN5 and CHDEN20 at pH 5.5 and (B–F) the fitting of the data using five different mathematical models at pH 5.5.

image file: c9ra05417k-f10.tif
Fig. 10 Cumulative release profiles of (A) dazomet from CHDEN5 and CHDEN20 at pH 5.5 and (B–F) the fitting of the data using five different mathematical models at pH 5.5.

By fitting the data of the hexaconazole and dazomet release from the nanoparticles into the five different kinetics and mathematical models, the linear fits of the model are presented in Fig. 9B–F and 10B–F, respectively. The linear form in the first-order kinetics model is given in eqn (4), where qe and qt are the quantities of fungicides released at equilibrium and at any time (t), respectively, and K1 is the rate constant for the pseudo-first-order release kinetics. The linear form in the second-order kinetics model can be represented by eqn (5), where K2 is the rate constant of the pseudo-second-order release kinetics. The Higuchi model (eqn (6)) describes the increased release of the fungicides from the nanoparticles with an increasing square root of time, where KH is the Higuchi rate constant. The Hixson–Crowell model (eqn (7)) provides a relationship between the cube root of the dazomet that remains in the nanoparticles as a function of time, where KHC is the Hixson–Crowell rate constant, Mo is the initial quantity of the fungicides in the nanoparticles and qt is the quantity released at time t. The Korsmeyer–Peppas (eqn (8)) model provides a relationship between the log of the percentage of the fungicides released and the log of time, where q is the release at infinite time and n is the release exponent.

 
ln(qeqt) = ln[thin space (1/6-em)]qeK1t (4)
 
t/qt = 1/K2qe2 + t/qe (5)
 
qt = KHt (6)
 
image file: c9ra05417k-t1.tif(7)
 
qt/q = Ktn (8)

The calculated correlation coefficient (R2), the rate constant (K) and t1/2 values (Table 2) of the release data reveal that the release kinetics of both CHDEN5 and CHDEN20 fitted well to the pseudo-second-order kinetics for both fungicides compared to the other models used in this work. Hence indicating that the overall reactions are dependent upon the ion exchange between the fungicide molecules and the release medium at the time of release and at the equilibrium.38,39 On the other hand, the results revealed the ability of hexaconazole to sustain for a longer time when encapsulated in chitosan, compared to the dazomet. This finding is also in an agreement with previous studies done by our group on the single-loaded systems of chitosan–hexaconazole nanoparticles (CHEN)29 and chitosan–dazomet nanoparticles (CDEN).30 Moreover, in contrast with the single encapsulation of CHEN and CDEN, the dual encapsulation of CHDEN showed a prolonged release of fungicides for up to twice the release time.

Table 2 Correlation coefficient, rate constant and half-life obtained by fitting the release data of hexaconazole and dazomet from CHDEN5 in phosphate buffer solution at pH 5.5 using five different kinetic mathematical models
Fungicides Nanoparticle Correlation coefficient, R2 Rate constant of pseudo-second order, k (mg h−1) t1/2 of pseudo-second order (h)
Pseudo-first order Pseudo-second order Higuchi model Hixson–Crowell model Korsmeyer–Peppas model
Hexaconazole CHDEN5 0.8095 0.9977 0.7919 0.4395 0.8677 0.0108 53
CHDEN20 0.6775 0.9998 0.7919 0.3576 0.8677 0.0108 66
Dazomet CHDEN5 0.4697 0.9997 0.8068 0.2787 0.8712 0.0132 15
CHDEN20 0.2183 0.9997 0.8068 0.1126 0.8712 0.0132 19


In vitro antifungal activity assay in the inhibition on G. boninense

The in vitro antifungal studies were done under several conditions: a control, where the mycelia were plated on the PDA with only solvent and the host (chitosan), the guests (pure hexaconazole and pure dazomet), and the synthesized nanoparticles; CHDEN2.5, CHDEN5, CHDEN10, and CHDEN20. The inhibitory effect of the pure fungicides and the synthesized nanoparticles on G. boninense was evaluated based on the inhibition rate and the calculated EC50 value. A higher inhibition rate showed better antifungal activity against G. boninense. On the contrary, the lower the EC50 value, the more effective the fungicide is in combating the Ganoderma disease.

The antifungal activity was analyzed using the mycelia growth method. As shown in Fig. 11, at 10 ppb, similar to the control, chitosan showed a negligible inhibitory effect as the maximum mycelial growth was achieved (radius of 40.0 mm), while pure dazomet showed a low inhibitory effect (38.8 mm). However, pure hexaconazole showed a better inhibition with 29.0 mm mycelial growth. On the other hand, significant inhibitory effects could be seen for the synthesized nanoparticles. The significant inhibitory effects for the synthesized nanoparticles followed the order CHDEN2.5 > CHDEN5 > CHDEN10 > CHDEN20 as the mycelial growth was much lower compared to the others (26.6, 23.5, 9.8 and 8.1 mm, respectively).


image file: c9ra05417k-f11.tif
Fig. 11 Anti-fungal effect on G. boninense of the control (A), 10 ppb of chitosan (B), 10 ppb of pure hexaconazole (C), 10 ppb of pure dazomet (D), 10 ppb of chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP (E) 2.5 mg L−1, (F) 5 mg mL−1, (G) 10 mg mL−1 and (H) 20 mg mL−1, 7 days after incubation at 28 ± 2 °C.

These results also indicate that hexaconazole has a higher antifungal activity against G. boninense compared to dazomet. The hexaconazole mode of action is by blocking the ergosterol biosynthesis pathway which leads to the toxic sterol accumulation, and consequently results in fungal cell death.40 On the other hand, the dazomet mode of action is by the releasing of poisonous MITC gas which can inhibit the activity of the pathogenic fungi.41 This is presumably the reason why the antifungal activity of hexaconazole is higher because dazomet is only effective when it is in the gas form.

To obtain a better understanding, the mycelial mean radial growth was plotted against duration (day) (Fig. 12) and the percentages inhibition of radial growth (PIRG) at day 7 was calculated (Fig. 13). The pure hexaconazole showed a significant inhibitory effect starting from 5 ppb (1.3% PIRG) with complete inhibition (100%) achieved at 500 ppb. Meanwhile, the pure dazomet showed significant inhibitory effects from 10 ppb (2.8% PIRG) and 100% inhibition at 1000 ppb. Moreover, remarkable inhibitory effects of the synthesized chitosan–hexaconazole–dazomet nanoparticles were achieved. CHDEN10 and CHDEN20 started to show inhibition on G. boninense growth at a very low concentration of 0.1 and 0.5 ppb. Meanwhile, CHDEN2.5 and CHDEN5 begin to show their inhibition on G. boninense at 1 ppb. In addition, a complete inhibition (100%) was achieved at 100 ppb for all the synthesized chitosan–hexaconazole–dazomet nanoparticles.


image file: c9ra05417k-f12.tif
Fig. 12 Growth curves of G. boninense incubated in pure hexaconazole (A), pure dazomet (B), and chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP (C) 2.5 mg L−1, (D) 5 mg mL−1, (E) 10 mg mL−1 and (F) 20 mg mL−1 at 28 ± 2 °C and at increasing concentrations of 0–1000 ppb at day 1 until 7. Black arrows represent the increasing of the total fungicide concentration and the error bars represent standard deviation of the mean.

image file: c9ra05417k-f13.tif
Fig. 13 Percentage inhibition of radial growth on G. boninense against concentration at day 7 incubation at 28 ± 2 °C of chitosan, pure dazomet, pure hexaconazole and chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP where *P < 0.01 (significant) and **P > 0.5 (not significant); the error bars represent standard deviation of the mean.

Moreover, the EC50 of the fungicides are presented in Table 3. Chitosan showed the highest EC50 value with 1534.5 ppb, followed by pure dazomet and pure hexaconazole with values of 152.2 and 21.4 ppb, respectively. Besides, the synthesized nanoparticles showed a remarkably better antifungal activity on G. boninense with lower EC50 values. In general, in all the systems, parallel to the effect of TPP on the particle size, the smaller particle sizes of the chitosan–fungicide nanoparticles resulted in lower EC50 values in which there was higher antifungal activity on G. boninense, which follows the order: CHDEN2.5 > CHDEN5 > CHDEN10 > CHDEN20 with 16.3, 13.3, 5.6, and 3.5 ppb, respectively.

Table 3 Calculated EC50 of chitosan, pure hexaconazole, pure dazomet and chitosan–hexaconazole–dazomet nanoparticles prepared at various concentrations of TPP on G. boninense at day 7 incubation at 28 ± 2 °C
Parameter Type of fungicides and nanoparticles
Chitosan Hexaconazole Dazomet CHDEN2.5 CHDEN5 CHDEN10 CHDEN20
EC50 (ppb) 1534.5 21.4 152.2 16.3 13.3 5.6 3.5
Fiducial limit (ppb) (lower–upper) 494.0–13[thin space (1/6-em)]280.4 16.7–27.3 73.2–565.8 7.3–46.3 6.6–33.3 3.0–18.0 2.5–5.0


Furthermore, the relationship between the particle size of the synthesized chitosan–hexaconazole–dazomet nanoparticles and EC50 value as well as the percentage of inhibition of mean mycelial growth of G. boninense was plotted (Fig. 14). Both methods confirmed that the decrease in particle size logarithmically decreased the EC50 value (Fig. 14A), and increased the inhibition percentage (Fig. 14B). This shows that the smaller particle size of the synthesized chitosan–hexaconazole–dazomet nanoparticles had a better antifungal activity against G. boninense which is due to the larger surface area that can be contacted with the fungus cell.42


image file: c9ra05417k-f14.tif
Fig. 14 The relationship between the hydrodynamic mean particle size distribution and HRTEM mean particle size distribution of the synthesized chitosan–hexaconazole–dazomet nanoparticles to (A) their percentage inhibition at 50 ppb and (B) the calculated EC50 (ppb) value on G. boninense.

In comparison to our earlier work on single loaded systems of hexaconazole29 and dazomet30 into the chitosan nanoparticles, the results revealed a synergistic effect in the co-delivery of hexaconazole and dazomet in the inhibition of G. boninense growth. The lowest EC50 values achieved for single loaded hexaconazole and dazomet in chitosan nanoparticles at 20 mg mL−1 of TPP were 4.6 ± 1.6 and 13.7 ± 1.8 ppb, respectively. Meanwhile, the dual loading of fungicides managed to enhance its fungicidal effect by up to four times.

Conclusions

In summary, four types of chitosan–hexaconazole–dazomet nanoparticles were successfully synthesized at four different sizes: 155, 56, 27, and 5 nm. The particle size of the agronanoparticles can be modified by varying the sodium TPP concentrations, where the increase of sodium TPP resulted in a smaller particle size. In addition, the synthesized agronanoparticles showed better thermal stability compared to their counterparts, pure dazomet, and pure hexaconazole. Moreover, the co-delivery of fungicide showed a sustained release with the release time of hexaconazole and dazomet up to 118 and 42 hours, respectively. Furthermore, the plot of the relationship between the particle size of the synthesized chitosan–hexaconazole–dazomet nanoparticles and EC50 value as well as the percentage of inhibition of the mean mycelial growth of G. boninense revealed a synergistic effect of dual-loaded fungicides, where the decrease in particle size logarithmically decreased the EC50 value as well as increased the inhibition percentage of mean mycelial growth of G. boninense. The proposed agronanoparticles were able to give a longer efficiency time and had a low toxicity but a high antifungal activity against G. boninense, which make them a promising candidate to be applied in the control and treatment of basal stem rot disease in oil palms.

Conflicts of interest

The authors declare no conflicts of interest.

Acknowledgements

The research was funded by Universiti Putra Malaysia (UPM) and the Ministry of Higher Education of Malaysia under the LRGS-NanoMITe program, vote no. 9443100 and 5526300 and GP-IPS, vote no. 9647400. F. N. M. would like to thank UPM for a graduate research fellowship (GRF) and the Sime Darby Foundation for a scholarship. Thanks to the Malaysian Palm Oil Board (MPOB) for the G. boninense culture and laboratory facilities for the in vitro analysis studies.

References

  1. S. D. Plantation, Sime Darby Plantation, 2014 Search PubMed.
  2. T. C. Hai, The palm oil industry in Malaysia, WWF, Malaysia, 2002 Search PubMed.
  3. C. Carter, W. Finley, J. Fry, D. Jackson and L. Willis, Eur. J. Lipid Sci. Technol., 2007, 109, 307–314 CrossRef CAS.
  4. R. Paterson, Crop Protect., 2007, 26, 1369–1376 CrossRef.
  5. D. Ariffin, A. Idris and G. Singh, Ganoderma Dis. Perenn. Crop., 2000, pp. 49–68 Search PubMed.
  6. A. Idris, A. Kushairi, S. Ismail and D. Ariffin, J. Oil Palm Res., 2004, 16, 12–18 Search PubMed.
  7. A. Idris, R. Arifurrahman and A. dan Kushairi, MPOB TS Inf. Ser., 2010 Search PubMed.
  8. A. Idris, R. Arifurrahman and D. Kushairi, PIPOC (Agriculture, Biotechnology and Sustainability), Malaysia, 2009 Search PubMed.
  9. A. Idris and S. Maizatul, MPOB TS Inf. Ser., 2012, vol. 107 Search PubMed.
  10. J. Zhou, J. Li, J. Li, G. Ren, Y. Ren and H. Ma, Chem. Res. Chin. Univ., 2017, 1–5 Search PubMed.
  11. J. T. i. Blasco, T. Grote, M. Scherer, R. Stierl, S. Strathmann and U. Schofl, US Pat., US20070066629A1, 2007.
  12. L. Huang, D. Lu, P. Zhang, J. Diao and Z. Zhou, Chirality, 2012, 24, 610–614 CrossRef CAS PubMed.
  13. S. Khalfallah, U. Menkissoglu-Spiroudi and H. A. Constantinidou, J. Agric. Food Chem., 1998, 46, 1614–1617 CrossRef CAS.
  14. M. Austerweil, B. Steiner and A. Gamliel, Phytoparasitica, 2006, 34, 491–501 CrossRef.
  15. D. Wang, S. W. Fraedrich, J. Juzwik, K. Spokas, Y. Zhang and W. C. Koskinen, Pest Manage. Sci., 2006, 62, 263–273 CrossRef CAS.
  16. F. I. Taylor, D. Kenyon and S. Rosser, Plant Soil, 2014, 382, 281–289 CrossRef CAS.
  17. R. Troncoso, C. Espinoza, A. Sánchez-Estrada, M. Tiznado and H. S. García, Food Res. Int., 2005, 38, 701–708 CrossRef CAS.
  18. T. Degenkolb and A. Vilcinskas, Appl. Microbiol. Biotechnol., 2016, 100, 3799–3812 CrossRef CAS PubMed.
  19. Z. Maznah, M. Halimah, S. Ismail and A. S. Idris, Environ. Sci. Pollut. Res., 2015, 22, 19648–19657 CrossRef CAS PubMed.
  20. P. M. White, T. L. Potter and A. K. Culbreath, Sci. Total Environ., 2010, 408, 1393–1402 CrossRef CAS PubMed.
  21. L. F. Fraceto, R. Grillo, G. A. de Medeiros, V. Scognamiglio, G. Rea and C. Bartolucci, Front. Environ. Sci., 2016, 4, 20 Search PubMed.
  22. A. Ditta, M. Arshad and M. Ibrahim, in Nanotechnology and plant sciences, Springer, 2015, pp. 55–75 Search PubMed.
  23. M. Sharon, A. K. Choudhary and R. Kumar, J. Phytol., 2010, 2, 83–92 Search PubMed.
  24. A. Ditta, Adv. Nat. Sci.: Nanosci. Nanotechnol., 2012, 3, 033002 Search PubMed.
  25. A. J. Anderson, Res. Plant Dis., 2018, 24, 99–112 Search PubMed.
  26. S. M. Ouda, Res. J. Microbiol., 2014, 9, 34–42 CrossRef CAS.
  27. A. El Hadrami, L. R. Adam, I. El Hadrami and F. Daayf, Mar. Drugs, 2010, 8, 968–987 CrossRef CAS PubMed.
  28. V. Sharma, S. Anandhakumar and M. Sasidharan, Mater. Sci. Eng., C, 2015, 56, 393–400 CrossRef CAS PubMed.
  29. F. N. Maluin, M. Z. Hussein, N. A. Yusof, S. Fakurazi, A. S. Idris, N. H. Zainol Hilmi and L. D. Jeffery Daim, Molecules, 2019, 24, 2498 CrossRef PubMed.
  30. F. N. Maluin, M. Z. Hussein, N. A. Yusof, S. Fakurazi, A. S. Idris, N. H. Z. Hilmi and L. D. Jeffery Daim, Int. J. Mol. Sci., 2019, 20, 2247 CrossRef PubMed.
  31. A. S. Hanafy, R. M. Farid and S. S. ElGamal, Drug Dev. Ind. Pharm., 2015, 41, 2055–2068 CrossRef CAS PubMed.
  32. R. Subbiah, P. Ramalingam, S. Ramasundaram, K. Park, M. K. Ramasamy and K. J. Choi, Carbohydr. Polym., 2012, 89, 1289–1297 CrossRef CAS PubMed.
  33. S. H. Hussein-Al-Ali, A. Kura, M. Z. Hussein and S. Fakurazi, Polym. Compos., 2018, 39, 544–552 CrossRef CAS.
  34. S. Mohan, N. Sundaraganesan and J. Mink, Spectrochim. Acta, Part A, 1991, 47, 1111–1115 CrossRef.
  35. I. F. Mustafa, M. Z. Hussein, I. A. Seman, N. H. Z. Hilmi and S. Fakurazi, ACS Sustainable Chem. Eng., 2018, 6, 16064–16072 CrossRef CAS.
  36. I. F. Mustafa, M. Z. Hussein, B. Saifullah, A. S. Idris, N. H. Z. Hilmi and S. Fakurazi, J. Agric. Food Chem., 2018, 66, 806–813 CrossRef CAS PubMed.
  37. B. Hu, C. Pan, Y. Sun, Z. Hou, H. Ye, B. Hu and X. Zeng, J. Agric. Food Chem., 2008, 56, 7451–7458 CrossRef CAS PubMed.
  38. Y. Ho and G. McKay, Process Saf. Environ. Prot., 1998, 76, 332–340 CrossRef CAS.
  39. J. M. Tan, G. Karthivashan, S. A. Gani, S. Fakurazi and M. Z. Hussein, J. Mater. Sci.: Mater. Med., 2016, 27, 26 CrossRef PubMed.
  40. W. Köllerm, Encyclopedia of Agrochemicals, 2003 Search PubMed.
  41. P. P. Reddy, in Recent advances in crop protection, Springer, 2012, pp. 37–60 Search PubMed.
  42. F. Raimondi, G. G. Scherer, R. Kötz and A. Wokaun, Angew. Chem., Int. Ed., 2005, 44, 2190–2209 CrossRef CAS PubMed.

This journal is © The Royal Society of Chemistry 2019