Mohamed Sherif El-Eskandarany*,
Mohammad Banyan and
Fahad Al-Ajmi
Nanotechnology and Advanced Materials Program, Energy and Building Research Center, Kuwait Institute for Scientific Research, Safat 13109, Kuwait. E-mail: msherif@kisr.edu.kw
First published on 14th September 2018
Formation of a new metastable fcc-MgH2 nanocrystalline phase upon mechanically-induced plastic deformation of MgH2 powders is reported. Our results have shown that cold rolling of mechanically reacted MgH2 powders for 200 passes introduced severe plastic deformation of the powders and led to formation of micro-lathes consisting of γ- and β-MgH2 phases. The cold rolled powders were subjected to different types of defects, exemplified by dislocations, stacking faults, and twinning upon high-energy ball milling. Long term ball milling (50 hours) destabilized β-MgH2 (the most stable phase) and γ-MgH2 (the metastable phase), leading to the formation of a new phase of face centered cubic structure (fcc). The lattice parameter of fcc-MgH2 phase was calculated and found to be 0.4436 nm. This discovered phase possessed high hydrogen storage capacity (6.6 wt%) and revealed excellent desorption kinetics (7 min) at 275 °C. We also demonstrated a cyclic-phase-transformation conducted between these three phases upon changing the ball milling time to 200 hours.
Apart from doping MgH2 powders with catalysts, it has been experimentally demonstrated by some authors that changing the crystal structure of stable β-tetragonal MgH2 phase to a less stable phase of γ-orthorhombic MgH2 led to improve the gas uptake/release kinetics and decrease the hydrogenation temperature without drastic decreasing of the storage capacity.23–26 The β-to-γ phase transformations can be attained via severe plastic deformation (SPD)27 at ambient temperature by different approaches such as high-energy ball milling (HEBM),28 cold rolling (CRing),29 equal channel angular pressing (ECAP),30 and high pressure torsion (HPT).22,31 A common result of these employed techniques is the formation of nanocrystalline phase along with introducing high intensity defects, leading to increase of grain boundaries density. Presence of these defects in the lattice leads to create nucleation points for hydrogenation, where existence of large number of grain boundaries assists fast diffusion pathways for hydrogen.
The present work has been addressed in part to study the effect of HEBM on the structure and decomposition properties of CRed MgH2 powders. Moreover, we aimed to investigate experimentally the possibility of formation a new metastable MgH2 phase rather than the reported g-phase and theoretically calculated δ and ε phases32 upon long term of milling.
For the purpose of the present study, 5 g Mg (∼80 μm, 99.8 wt%) powder was balanced inside a He gas atmosphere-glove box and sealed together with fifty hardened steel-balls (11 mm in diameter), using ball-to-powder weight ratio as 40:
1. The vial was then evacuated to the level of 10−3 bar and then filled with 50 bar of H2. The RBM process was carried out at room temperature, using planetary-type HEBM. After 25 hours (h) of RBM, the vial was open inside the glove box to discharge the powders. The powders were charged and sealed in a stainless steel (SUS304) tube (0.8 cm diameter and 20 cm length) inside the glove box. The tube contained MgH2 powders were severely CRed for different number of passes (1 to 200 passes), using two-drum type manual cold roller (11 cm wide × 5.5 cm rollers diameter). The as-CRed powders for 200 passes were then HEBMed under hydrogen gas for different milling time, in the range between 3 h to 50 h. All the samples were characterized by means of X-ray diffraction (XRD) with Cu radiation, field-emission high-resolution transmission electron microscope (FE-HRTEM) equipped with energy-dispersive X-ray spectroscopy (EDS), field emission scanning electron microscope (FE-SEM)/EDS, and differential scanning calorimeter (DSC). The absorption/desorption kinetics were investigated via Sievert's method in different temperatures under hydrogen gas pressure in the range between 200 mbar to 8 bar.
The XRD patterns of MgH2 powders obtained after 25 h of RBM is shown in Fig. 1a. Bragg peaks corresponding to starting hcp-Mg powders were hardly seen and replaced by sharp diffracted lines related to γ- and β-MgH2 phases, as elucidated in Fig. 1a. The SEM observations indicated the powders tendency to agglomerate, forming large aggregates upon CRing for 25 passes (Fig. 2a). Increasing the CRing passes to 200 times led to grain refinement, as implied by the broadening in the Bragg-peaks presented in Fig. 1b. At this stage, micro-bands with thickness of 143 μm were developed as a result of cold working generated during CRing process, as shown in Fig. 2b. The FE-HRTEM image of as-CRed powders for 200 passes indicated the development of lattice imperfections (e.g. stacking faults and deformation twins). This is implying the mechanically-induced SPD, as elucidated in ESI, Fig. S1.†
![]() | ||
Fig. 1 XRD patterns of MgH2 powders obtained after 25 h of RBMing (a), and then CRed for 200 passes (b). XRD pattern of CRed powders for 200 passes and then HEBMEd for 50 h is presented in (c). |
![]() | ||
Fig. 2 FE-SEM micrographs taken at accelerated voltage of 1 kV of MgH2 powders obtained after 25 h of RBMing and then CRed for (a) 25, and (b) 200 passes. |
In order to study the effect of HEBM on the stability of cold-rolled MgH2 aggregates, the powders were charged into tool steel vial and ball milled under 50 bar of H2 for different milling time. The XRD pattern of CRed MgH2 powders obtained after 200 CR passes and then HEBMed for 50 h is displayed in Fig. 1c. Obviously, the Bragg peaks corresponding to γ- and β-MgH2 phases were completely vanished and replaced by new Bragg peaks of unreported phase, appeared at scattering angles (2θ) of, 35.034, 40.584, 58.758, 70.115, and 73.868 (Fig. 1c). XRD analysis indicated that this discovered MgH2 phase has face centered cubic structure (fcc) of space group, Fmm(225). The lattice parameter (ao) of this phase, calculated from (111) was 0.44361 nm. The as-synthesized fcc-MgH2 powders had fine spherical particles with sizes distributed in the range between 0.25 μm to 1 μm, as displayed in Fig. 3.
![]() | ||
Fig. 3 FE-SEM micrograph of MgH2 powders obtained after 25 h of RBM, CRed for 200 passes and finally HEBMed for 50 h. |
Table 1 presents some of structural parameters related to this new phase, indexed by the interplanar spacing for the corresponding Miller indexes (h,k,l) and 2θ.
Peak position, 2θ (degree) | Interplanar spacing, d (nm) | Miller indexes (h,k,l) | Lattice parameter, ao (nm) |
---|---|---|---|
35.034 | 0.25612 | 111 | 0.44361 |
40.584 | 0.22229 | 200 | 0.44458 |
58.758 | 0.15713 | 220 | 0.44443 |
70.115 | 0.13421 | 311 | 0.44512 |
73.868 | 0.12829 | 222 | 0.44441 |
The FE-HRTEM image of the as-CRed powders for 200 passes and then HEBMed for 50 h is shown in Fig. 4. The image revealed Moiré fringe image for 3 intimated nanograins. Filtered-fringe images corresponding to Zone I is presented in Fig. 4a. The d-spacing related to fcc-MgH2 (111) was calculated and found to be 0.2559 nm, where the corresponding ao was calculated and found to be 0.4433 nm. These values matches well with the XRD analysis (Table 1). The FFT image, which is displayed in Fig. 4c, was taken from Zone I and oriented to [001] axis, where the corresponding FFT showed spot-electron diffraction pattern related to fcc-MgH2 (111).
![]() | ||
Fig. 4 (a) FE-HRTEM image, (b) filtered atomic resolution image of Zone I, and (c) FFT image of MgH2 powders obtained after 25 h of RBM, consequently CRed for 200 passes and finally HEBMed for 50 h. |
Fig. 5 presents DSC thermograms of MgH2 powders obtained after 25 h of RBM, consequently cold-rolled for 200 passes and then HEBM for different times, as indexed in Fig. 5. The DSC curves for the powders obtained after 25 h of RBM and then cold-rolled only without milling for different passes are shown together in ESI (Fig. S2†).
The decomposition temperature of the powders obtained after 25 h of RBM (before applying CRing process) was 415 °C (Fig. S2†), and tended to decrease sharply to 361 °C upon powders CRing for 200 passes, as displayed in Fig. S2.† This significant decreasing on the decomposition temperature upon increasing the number of CRing passes was attributed to destabilization of MgH2, yielded from introducing severe plastic deformation to the powders.
The XRD pattern for MgH2 powders obtained after 200 CRing passes and then heated in DSC up to 500 °C showed the presence of a single hcp-Mg phase (Fig. S3†). The as-HEBMed of the powders CRed for 200 passes revealed single endothermic events related to the decomposition reaction (Fig. 5).
Obviously, the peak temperature of the samples obtained after different milling times shifted monotonically to the low temperature side with increasing the HEBMing time (Fig. 5). After 50 h of milling (single metastable fcc-MgH2 phase), the decomposition temperature was reordered to be 222 °C (Fig. 5). This temperature was far below the corresponding decomposition temperature (361 °C, Fig. S3†) corresponding to as-CRed powders (γ- + β-MgH2 phases) obtained after 200 passes (Fig. S3†).
The powders obtained after 50 h of HEBM was annealed in the DSC at 220 °C (just beyond decomposition onset temperature) and at 375 °C (well above the onset decomposition temperature) for 7 min. XRD pattern of the first sample annealed at 220 °C indicated metastable fcc-MgH2-to-stable β-MgH2 phase transformation, as implied by disappearance of fcc-Bragg peaks and the presence of pronounced sharp Bragg lines corresponding to β-MgH2 coexisted with small volume fraction of γ-MgH2 (Fig. 6a).
![]() | ||
Fig. 6 XRD patterns of the samples obtained after 50 h and then annealed in the DSC for 7 min at (a) 220 °C, and (b) 375 °C for 7 min. |
FE-HRTEM (Fig. 7a) and NBD (Fig. 7b) analysis of the annealed sample at 220 °C confirmed the presence of γ- and β-MgH2 phases and a complete disappearance of metastable fcc-MgH2, as displayed in Fig. 7a and b, respectively. In contrast, XRD pattern of the sample annealed at 375 °C showed the Bragg peaks of hcp-Mg coexisted with small volume fraction of undecomposed β-MgH2 crystals (Fig. 6b). It can be concluded from the structural and thermal analysis that γ- and β-MgH2 phases tended to transform to a new metastable phase upon CRing for 200 passes followed by HEBMing for 50 h. The obtained metastable fcc-MgH2 phase transformed into more stable phases of γ- and β-MgH2 phases when annealed at 220 °C for 7 min. A complete phase transformation to hcp-Mg was attained upon annealing fcc-MgH2 at 375 °C.
![]() | ||
Fig. 7 (a) FE-HRTEM, and (b) NBDP of the sample milled for 50 h and then annealed in the DSC at 220 °C for 7 min. |
Further experiments were conducted to examine the stability of fcc-MgH2 phase against the mechanical deformation generated by HEBMing. The powders obtained after 50 h were continuously milled for 100 h, 150 h, and 200 h. The XRD pattern of the milled powders for 100 h indicated the disappearance of Bragg peaks related fcc-MgH2 phase, which were replaced by diffracted lines related to γ- and β-MgH2 phases as shown in Fig. 8a. This implies the disability of fcc-MgH2 phase to withstand against the shear and impact forces generated by the milling media. Surprisingly, increasing the HEBMing to 150 h led to clear γ- , β-MgH2 to fcc-MgH2 (less stable phase) phase transformation (Fig. 8b). This is indicated by the presence of Bragg peaks related to fcc-MgH2 phase and the disappearance of the diffracted lines corresponding to the MgH2 phases, as displayed in Fig. 8b.
![]() | ||
Fig. 8 XRD patterns of as-CRed MgH2 powders for 200 passes and then HEBMed for (a) 100 h, (b) 150 h, and (c) 200 h. |
Fig. 9 presents a schematic illustration of free energy changes of β-γ-fcc MgH2 phases upon increasing HEBM time. Based on the results motivated of the present study, mechanically-induced fcc-MgH2 to γ- and β-MgH2 phase transformation (point 3-to-points 2 + 3) was achieved upon increasing the milling time to 100 h. Introducing severe lattice imperfections to the fcc-phase is proposed to be responsible to insist this metastable phase to gain free energy and hence transformed into a more stable phase, as illustrated in Fig. 9. This phase transformation can be taken place upon annealing the powders via thermally induced phase transformation, as indexed by point 3-to-points 2 + 1 (Fig. 9).
![]() | ||
Fig. 9 Schematic presentation of free energy changes conducted upon HEBMing CRed MgH2 powders for long term of milling. |
The obtained γ- and β-MgH2 composite phases were subjected plastic deformation and defects, leading to lose free energy and transformed to the same metastable fcc-MgH2 phase with further milling time (150 h), as denoted by points 1 + 2 to point 3 (Fig. 9). Further increasing the milling time (200 h) led fcc-MgH2 to gain energy and failed into more stable phases of γ- and β-MgH2.
Since high-energy ball milling process introduces intensive vacancies, lattice defects, grain boundaries and surfaces, the ball-milled powders can store a large amount of mechanical-strain energy.33,34 Introducing such defects to the crystalline lattice destroys the periodical structure of the stable tetragonal-MgH2 phase, leading to the formation of a less stable phase (fcc-MgH2). Moreover, the present result suggests that the formation enthalpy of the metastable fcc-MgH2 phase is comparable to the γ- and β-MgH2 phases and the energy barrier between these three phases is probably rather low to allow such cyclic-phase transformations. We should emphases that all the results obtained from XRD analysis were used to determine the weight percentage of each phase, using the approaches described by Guan et al.,35 Ma et al.,36 Yu et al.,37 and Cheng et al.38
Fig. 10 displays the dehydrogenation kinetics behaviors of the CRed powder obtained after 200 passes and then HEBMed for 50 h (fcc-MgH2 phase). The measurements were conducted in the temperature range of 175 °C to 275 °C under 200 mbar.
In order to maintain the crystal structure of the powders (fcc-MgH2 phase) obtained after this stage of milling, the desorption kinetics measurements measured without activation for 5 individual samples (Fig. 10a). All samples were successfully desorbed their hydrogen storage with different time scale. Generally, the fcc-MgH2 powders showed advanced dehydrogenation characteristics over γ- and β-MgH2 phases. At 175 °C, the sample desorbed ∼4 wt% H2 within 40 min (Fig. 10a). However, the powders desorbed about 6.5 wt% H2 within 22 min at 200 °C (Fig. 6a). Increasing the applied temperature to 225 °C and 250 °C, improved the dehydrogenation kinetics of fcc-MgH2, indicated by the short time required to desorb 6.6 wt% H2 in 17 min and 10 min, respectively (Fig. 10a).
Outstanding desorption kinetics was conducted at 275 °C, when the sample desorbed 6.6 wt% H2 within 7 min, as elucidated in Fig. 10a. We should emphases that the XRD patterns for the examined samples at temperature range laid between 175 °C to 225 °C revealed presence of Bragg peaks corresponding to γ- and β-MgH2 phases. However, the XRD pattern for those samples examined at higher temperatures (250 °C and 275 °C) revealed diffracted lines of hcp-Mg phase.
Fig. 10b displays the dehydrogenation kinetics conducted for the same samples shown in 10a, however, they were activated firstly at 300 °C (far above the transformation temperature of fcc-MgH2 to γ- and β-MgH2 phases) under 25 bar H2. Based on this activation step condition, all the samples lost their fcc-structure and completely transformed into γ- and β-MgH2 phases. This led to a significant deduction of dehydrogenation kinetics that become very slow when compared with the same samples shown in Fig. 10a. For example, the sample examined at 175 °C required more than 650 min to desorb less than 5.5 wt% H2 (Fig. 10b). The two samples examined at 200 °C and 225 °C desorbed about 6.4 and 6.6 wt% H2 within 600 and 390 min, respectively (Fig. 10b). Comparing the necessary desorption time (100 min) for the sample examined at 275 °C to release 6.6 wt% H2 (Fig. 10b) with that time required (7 min) for fcc-MgH2 sample (Fig. 10a) to desorb same hydrogen amount at the same temperature, we can realize that the kinetics desorption of fcc-MgH2 phase is 14 time faster than γ- and β-MgH2 phases.
Footnote |
† Electronic supplementary information (ESI) available. See DOI: 10.1039/c8ra07068g |
This journal is © The Royal Society of Chemistry 2018 |