RSC Adv., 2018,
8, 35157-35161
Alleviate the J–V hysteresis of carbon-based perovskite solar cells via introducing additional methylammonium chloride into MAPbI3 precursor†
Received
22nd May 2018
, Accepted 3rd October 2018
First published on 15th October 2018
Abstract
The hysteretic phenomenon commonly exists in the J–V curves of perovskite solar cells with different structures, especially for carbon-based mesoscopic perovskite solar cells without hole-conductor (carbon-based PSCs). By adding moderate amounts of methylammonium chloride (MACl) into MAPbI3 perovskite precursor, we found the J–V hysteresis of carbon-based PSCs could be significantly alleviated and the crystallinity of MAPbI3 perovskite could also be influenced. With the increasing amount of MACl, MAPbI3 perovskite showed better and better crystallinity until the MACl came to 0.45 M. The champion device with 0.45 M of additional MACl exhibited a preferable PCE of 14.27% for reverse-scan (RS) and 14.50% for forward-scan (FS), significantly higher than that of the pristine device (8.74% for RS and 4.80% for FS). What's more, the J–V hysteretic index of the device gradually decreased along with the increasing amount of MACl, and kept at low value even when the crystallinity of MAPbI3 perovskite became poor. Through XRD and PL analysis, we demonstrated that the recombination rate of the accumulated charges at the perovskite/TiO2 interface is the main reason for photocurrent hysteresis in carbon-based PSCs. High quality of perovskite crystals is an important contributing factor for high-performance PSCs with low hysteresis, but there is no necessary correlation between low hysteresis and good crystallinity. This research presents an effective way to fabricate carbon-based PSCs with low-hysteresis, and at the same time, provides evidence for investigating the origin of J–V hysteresis of PSCs.
Introduction
In the past few years, the organic–inorganic hybrid lead halide perovskite materials (e.g. methylammonium lead iodide, MAPbI3) have caught world-wide attention for their excellent photo- and electrical-properties such as high absorption coefficient, long charge diffusion length and high carrier mobility.1–5 Solar cells based on these perovskite light absorbers (perovskite solar cells, PSCs) have shown tremendous application potential due to their easy fabrication procedures and high power conversion efficiency (PCE). Up to now, the world champion PCE of PSCs has reached 22.7%, far exceeding that of the other emerging photovoltaic technologies such as dye-sensitized solar cells (DSSCs) and organic photovoltaics (OPV).6 For most kinds of the PSCs, they still need Au or Ag as their counter electrodes, which are commonly deposited by thermal evaporation. However, the usage of noble metals, together with high vacuum facilities in the fabrication procedures, is unfavourable for achieving a low cost of PSCs. In this regard, carbon-based PSCs,7 which employ carbon as counter electrode, has significant research value for low-cost PSCs. What's more, the carbon-based PSCs can be fabricated via fully-printing procedures, which is propitious for scaling-up the devices. Since firstly be reported in 2013, carbon-based PSCs have been studied by many research groups in aspect of materials, interface engineering, solvent engineering and long-term stability.8–15 However, like other types of PSCs, carbon-based PSCs suffer from the current density–voltage (J–V) hysteresis as well. The J–V hysteresis influences the PCE of a solar cell device and occurs as a result of the large discrepancy between the forward and reverse scans. Though researchers haven't come to an agreement on the origin of this anomalous hysteretic behaviour in PSCs, most of them considered that ion migration,16,17 ferroelectricity,18,19 a photo-induced capacitive effect20,21 and charge trapping/detrapping22,23 could be the reasons. For optimum PCE, several strategies8,12,14,15 have been applied on the carbon-based PSCs. These strategies can also alleviate the hysteretic behaviour of the device, and most of the researchers believe that poor crystallinity of perovskite should be the culprit of hysteresis in carbon-based PSCs.
In this work, we mainly focused on the J–V hysteretic behaviour of the carbon-based PSCs and investigated the reason for J–V hysteresis. By adding extra methylammonium chloride (MACl) into MAPbI3 perovskite precursor, we found that the J–V hysteresis of the device disappeared gradually as the increasing amount of MACl. For dug reason, the X-ray diffraction (XRD) and steady-state photoluminescence (PL) measurements were performed on the devices. The XRD results showed that the crystallinity of MAPbI3 perovskite can be improved by certain amount of MACl, and better crystallinity also brings higher PCE to the device. The champion device exhibited a reverse-scan (RS) PCE of 14.27% and forward-scan (RS) PCE of 14.50%, which was significantly higher than that of the pristine device (8.74% for RS and 4.80% for FS). Furthermore, with continuous increasing the amount of MACl, the crystallinity of MAPbI3 perovskite got worse and worse. However, the J–V hysteresis of the devices still kept at low level. PL results revealed that the recombination rate of the accumulated charges at the perovskite/TiO2 interface is the main reason for photocurrent hysteresis. Hence, to fabricate hysteresis-free carbon-based PSCs with high performance, optimizing the perovskite/TiO2 interface should be the priority concern.
Experimental
Materials and precursor preparation
MAI, PbI2, MACl and FACl were purchased from Xi'an p-OLED Corp. N,N-Dimethyl formamide (DMF) were purchased from Sigma-Aldrich. TiO2 paste was purchased from NJUKII. ZrO2 and carbon paste were prepared as former reports.7
The pristine perovskite precursor was prepared by dissolving the mixture composed of 461.01 mg PbI2 and 158.97 mg MAI in 1 mL DMF to achieve 1 M MAPbI3 precursor solution.
The MACl-incorporated perovskite precursor was prepared via adding x mmol MACl (x = 0.15, 0.3, 0.45, 0.6, 0.75, 0.9, 1.05) into 1 mL pristine perovskite precursor to achieve MAPbI3 with x M MACl precursor solution.
Device fabrication
FTO glass was etched by a laser machine (Universal Laser Systems, VLS2.30), and followed by ultrasonic cleaning with detergent solution, pure water and ethyl alcohol for 20 min, respectively. A compact TiO2 layer was deposited on FTO glass by spray pyrolysis deposition at 450 °C with a 2-propanol solution involving titanium diisopropoxide bis(acetylacetonate) solution. A 1 μm mesoscopic TiO2 layer (NJU-30NR-D) was screen-printed on top of the compact layer and then sintered at 500 °C for 30 min. After that, a 1.6 μm ZrO2 and a 11 μm carbon layer were subsequently screen-printed above the TiO2 mesoscopic layer. The ZrO2 layer and carbon layer ware sintered at 500 °C and 400 °C for 30 min, respectively. After cooling down to room temperature, the triple layer was infiltrated with 5 μL perovskite solution via drop casting on top of the carbon counter electrode and then annealed at 100 °C for 20 min. All the above procedures were accomplished in air atmosphere.
Characterization
The XRD spectra were recorded on a Bruker D8 Advance X-ray diffractometer with Cu Kα radiation (λ = 1.5418 Å). The UV-visible spectra of perovskite films deposited on glass were measured by PerkinElmer lambda 750S spectrophotometer. The cross-sectional structure and elemental distribution of the perovskite solar cells were investigated with field-emission scanning electron microscopy (FE-SEM, Zeiss Ultra Plus) equipped with an EDS detector. Steady-state photoluminescence spectra were measured by a PL microscopic spectrometer (Flex One, Zolix, China) with an excitation wavelength of 532 nm. Photocurrent density–voltage (J–V) characteristics and steady-state output of photocurrent density were tested by a solar simulator (Oriel 94023A, 300 W) and a Keithley 2400 source meter under AM 1.5 G (100 mW cm−2). The light intensity was calibrated by a standard Si solar cell (Oriel, VLSI standards). All the devices were tested under AM 1.5 G sun light (100 mW cm−2) using a black mask with an aperture area of 0.1475 cm2 at a scan rate of 0.1 V s−1. EQE measurements were performed by an internal establishment system with monochromatic light and white bias light (∼0.1 sun). The photodiode used for the calibration of EQE measurements has been calibrated by Newport.
Results and discussion
Carbon-based PSCs were fabricated by the procedures reported previously.7 Briefly, via screen printing technique, mesoporous TiO2, ZrO2 and carbon films were successively deposited on the FTO substrates, which have been coated with compact TiO2 beforehand. Afterwards, MAPbI3 perovskite light absorber was loaded by filtrate the precursor solution into the mesoporous carbon/ZrO2/TiO2 layers (shown in Fig. 1a). The microstructure of the as-prepared device was observed by SEM measurement from the cross-section, and we can find each layer has well-defined boundaries and uniform thickness (see Fig. 1b). To investigate how the MACl additive influences the performance of the device, we added different amount of MACl (0.15, 0.3, 0.45, 0.6, 0.75, 0.9, 1.05 M) into the standard 1 M MAPbI3 precursor.
![image file: c8ra04347g-f1.tif](/image/article/2018/RA/c8ra04347g/c8ra04347g-f1.gif) |
| Fig. 1 (a) The schematic structure of the carbon-based PSCs; (b) SEM images from the cross section of the carbon-based PSCs. | |
Photocurrent density–voltage (J–V) characteristics (measured under AM 1.5 G irradiation at 100 mW cm−2 with a scan rate of 10 mV s−1) of the devices assembled by using these precursors are shown in Fig. 2 and the detail parameters are summarized in Table S1.† Interestingly, with the adding of MACl from 0 to 0.3 M, the J–V hysteretic behaviour alleviated gradually (see Fig. 2a–c). When the amount of MACl came to 0.45 M, no obvious hysteresis can be found from the J–V curve (see Fig. 2d) and the PCE of the device reached maximum value.
![image file: c8ra04347g-f2.tif](/image/article/2018/RA/c8ra04347g/c8ra04347g-f2.gif) |
| Fig. 2 J–V curves of MAPbI3-based PSCs with different amount of MACl. | |
Fig. 3 presents the J–V parameters of the corresponding champion carbon-based PSCs. The carbon-based PSCs with pristine MAPbI3 perovskite showed poor PCE and obvious J–V hysteresis (8.74% for RS and 4.80% for FS). However, by adding 0.45 M MACl into MAPbI3 perovskite precursor, the champion device achieved a PCE of 14.27% with low J–V hysteresis (IPCE spectra and long-term stability are shown in Fig. S1 and S2†). To ensure the improvement of MACl on the performance of PSCs device is repeatable, two batches of devices (each consist of 15 devices) were fabricated by MAPbI3 perovskite and MAPbI3/0.45MACl, respectively. The devices with pure MAPbI3 possessed an average PCE of 7.09% and the ones with MAPbI3/0.45MACl exhibited an average PCE of 13.36% (see Table S2 and S3†).
![image file: c8ra04347g-f3.tif](/image/article/2018/RA/c8ra04347g/c8ra04347g-f3.gif) |
| Fig. 3 J–V curves of champion MAPbI3-based PSCs with 0 and 0.45 M MACl. | |
As the continuous increasing of MACl, the corresponding devices showed a tendency of lower PCE (see Fig. 2e–h). Note that, though with poorer PCEs, the J–V hysteresis of devices still kept at low level. To make clear how MACl influence the J–V hysteresis of the device, XRD measurement was utilized to investigate the crystallinity of MAPbI3 perovskite prepared by different precursors.
As shown in Fig. 4, all of the perovskite samples exhibit similar diffraction peaks at 2θ values of 13.91°, 28.20° and 31.69°, corresponding to the (110), (220) and (310) crystal planes of tetragonal MAPbI3 perovskite. With the adding of additional MACl from 0.15 M to 0.45 M, the peak at 2θ value of 13.91° gradually increased its intensity, indicating better and better crystallinity of MAPbI3 perovskite. Obviously, the good crystallinity of perovskite in the mesoporous films is the prerequisite of high PCE. When we continue increased the amount of MACl (from 0.6 M to 1.05 M), the crystallinity of MAPbI3 became worse again. Moreover, no obvious MAPbCl3 peaks can be found in these patterns, indicating most of the chloride was released in the annealing procedure or the chloride only exist in the boundaries of MAPbI3 crystals. To confirm this, energy dispersive X-ray spectroscopy (EDS) measurement was performed on the device with champion PCE.
![image file: c8ra04347g-f4.tif](/image/article/2018/RA/c8ra04347g/c8ra04347g-f4.gif) |
| Fig. 4 XRD patterns of MAPbI3 with different amount of MACl on FTO substrates. | |
From the cross-section of the sample (Fig. 5a), we can clearly find the elements of carbon (Fig. 5b), zirconium (Zr, Fig. 5c) and titanium (Ti, Fig. 5d) distribute homogeneously in the top, middle and bottom area, respectively. Oxygen (Fig. 5b) is mainly exists in the ZrO2, TiO2 and FTO substrate. For perovskite, elements of lead (Pb) together with iodine (I) and chlorine (Cl) have a uniform distribution in carbon/ZrO2/TiO2 layers. However, the atom ratio of Pb, I and Cl is around 1
:
2.56
:
0.12, indicating only a few Cl exist in MAPbI3 perovskite. Thus, we deduced that most of the Cl elements were removed in the form of MACl gas24 by annealing. Meanwhile, the crystallinity of MAPbI3 perovskite changed as the release of MACl. To further study the different J–V hysteresis behaviour of MACl-incorporated MAPbI3 perovskite, steady-state photoluminescence (PL) spectra measurements were carried out on the glass/ZrO2/perovskite and FTO/TiO2/perovskite samples.
![image file: c8ra04347g-f5.tif](/image/article/2018/RA/c8ra04347g/c8ra04347g-f5.gif) |
| Fig. 5 EDS mapping of the carbon-based PSCs form cross-section. | |
As illustrated by Fig. 6, the steady-state PL spectra of MAPbI3 perovskite films with different amount of MACl displayed a PL emission peak at ∼780 nm. The MAPbI3 with 0.45 M MACl film on the glass/ZrO2 substrate showed the strongest PL intensity, indicating fewer traps and defects within the perovskite crystal (Fig. 6a). These results correspond well with the XRD results. In addition, we also performed the steady-state PL test on the perovskite samples with FTO/TiO2 substrate (Fig. 6b). All of the MAPbI3 perovskite film with MACl exceeding 0.3 M possessed a dramatically higher degree of PL quenching in comparison with other samples with lower amount of MACl. Generally, this PL quenching is attributed to originate from efficient electron extraction across the interface.25 Hence, we can conclude that the charge carrier extraction at the perovskite/TiO2 interface could be enhanced by introducing sufficient MACl into MAPbI3. And J–V hysteresis in carbon-based PSCs is mainly depends on the charge carrier extraction speed rather than the crystallinity of perovskite.
![image file: c8ra04347g-f6.tif](/image/article/2018/RA/c8ra04347g/c8ra04347g-f6.gif) |
| Fig. 6 The steady-state photoluminescence spectra of MAPbI3 with different amount MACl on (a) glass/ZrO2, (b) FTO/TiO2. | |
Conclusions
In summary, we demonstrated a facile method to alleviate the J–V hysteresis of carbon-based PSCs by introducing moderate MACl into MAPbI3 precursor. We adjusted the amount of MACl (from 0 M to 1.05 M) in MAPbI3 precursor and found that the crystallinity of MAPbI3 appeared regularly change along with the amount of MACl. The champion device with the best crystallinity (MAPbI3 with additional 0.45 M MACl in the precursor) achieved a PCE of 14.27% with low J–V hysteresis, which is much higher than that of the pristine one (8.74%). EDS results showed there was only a small amount of chloride residues in the MAPbI3 perovskite after annealing. We deduced that most of the chloride were removed in the form of MACl gas in the annealing procedure and thus, changed the crystallinity of MAPbI3 perovskite. Moreover, the steady-state PL measurements manifested that, with sufficient MACl in the MAPbI3 precursor, the charge carrier extraction at the perovskite/TiO2 interface could be enhanced. Note that, for the carbon-based PSCs, there is no significant relationship between the interfacial charge extraction and the crystal quality of perovskite. These results would provide evidence for further investigating the origin of J–V hysteresis in PSCs and solutions for fabricating high-performance carbon-based PSCs.
Conflicts of interest
There are no conflict to declare.
Acknowledgements
The authors acknowledge the financial support by National Natural Science Foundation of China (NSFC 51702243, 51402115, 51672202), Hubei Provincial Natural Science Foundation of China (2016CFB464), the Technological Innovation Key Project of Hubei Province (2018AAA048), the Fundamental Research Funds for the Central Universities (WUT: 2016IVA093, 2016IVA089, 2016IVA085, 2016III030, 2017III022) and Hubei Key Laboratory of Low Dimensional Optoelectronic Material and Devices (HLOM151001).
Notes and references
- A. Kojima, K. Teshima, Y. Shirai and T. Miyasaka, J. Am. Chem. Soc., 2009, 131, 6050–6051 CrossRef CAS PubMed.
- M. M. Lee, J. Teuscher, T. Miyasaka, T. N. Murakami and H. J. Snaith, Science, 2012, 338, 643–647 CrossRef CAS PubMed.
- H. S. Kim, C. R. Lee, J. H. Im, K. B. Lee, T. Moehl, A. Marchioro, S. J. Moon, R. Humphry-Baker, J. H. Yum, J. E. Moser, M. Gratzel and N. G. Park, Sci. Rep., 2012, 2, 591 CrossRef PubMed.
- C. Wehrenfennig, G. E. Eperon, M. B. Johnston, H. J. Snaith and L. M. Herz, Adv. Mater., 2014, 26, 1584–1589 CrossRef CAS PubMed.
- G. C. Xing, N. Mathews, S. Y. Sun, S. S. Lim, Y. M. Lam, M. Gratzel, S. Mhaisalkar and T. C. Sum, Science, 2013, 342, 344–347 CrossRef CAS PubMed.
- N. R. E. L. N. Best Research Cell_Efficiencies, https://www.nrel.gov/pv/assets/images/efficiency-chart.png, October, 2017.
- Z. L. Ku, Y. G. Rong, M. Xu, T. F. Liu and H. W. Han, Sci. Rep., 2013, 3, 3132 CrossRef PubMed.
- A. Mei, X. Li, L. Liu, Z. Ku, T. Liu, Y. Rong, M. Xu, M. Hu, J. Chen, Y. Yang, M. Gratzel and H. Han, Science, 2014, 345, 295–298 CrossRef CAS PubMed.
- G. Grancini, C. Roldán-Carmona, I. Zimmermann, E. Mosconi, X. Lee, D. Martineau, S. Narbey, F. Oswald, F. De Angelis, M. Graetzel and M. K. Nazeeruddin, Nat. Commun., 2017, 8, 15684 CrossRef CAS PubMed.
- M. Wang, W.-L. Yim, P. Liao and Y. Shen, ChemistrySelect, 2017, 2, 4469–4477 CrossRef CAS.
- A. K. Baranwal, S. Kanaya, T. A. Peiris, G. Mizuta, T. Nishina, H. Kanda, T. Miyasaka, H. Segawa and S. Ito, ChemSusChem, 2016, 9, 2604–2608 CrossRef CAS PubMed.
- Y. Rong, X. Hou, Y. Hu, A. Mei, L. Liu, P. Wang and H. Han, Nat. Commun., 2017, 8, 14555 CrossRef PubMed.
- X. Li, M. Tschumi, H. Han, S. S. Babkair, R. A. Alzubaydi, A. A. Ansari, S. S. Habib, M. K. Nazeeruddin, S. M. Zakeeruddin and M. Grätzel, Energy Technol., 2015, 3, 551–555 CrossRef CAS.
- C.-M. Tsai, G.-W. Wu, S. Narra, H.-M. Chang, N. Mohanta, H.-P. Wu, C.-L. Wang and E. W.-G. Diau, J. Mater. Chem. A, 2017, 5, 739–747 RSC.
- S. G. Hashmi, D. Martineau, M. I. Dar, T. T. T. Myllymaki, T. Sarikka, V. Ulla, S. M. Zakeeruddin and M. Gratzel, J. Mater. Chem. A, 2017, 5, 12060–12067 RSC.
- Z. Xiao, Y. Yuan, Y. Shao, Q. Wang, Q. Dong, C. Bi, P. Sharma, A. Gruverman and J. Huang, Nat. Mater., 2015, 14, 193–198 CrossRef CAS PubMed.
- D.-Y. Son, J.-W. Lee, Y. J. Choi, I.-H. Jang, S. Lee, P. J. Yoo, H. Shin, N. Ahn, M. Choi, D. Kim and N.-G. Park, Nat. Energy, 2016, 1, 16081 CrossRef CAS.
- Z. Fan, J. Xiao, K. Sun, L. Chen, Y. Hu, J. Ouyang, K. P. Ong, K. Zeng and J. Wang, J. Phys. Chem. Lett., 2015, 6, 1155–1161 CrossRef CAS PubMed.
- H.-S. Kim, S. K. Kim, B. J. Kim, K.-S. Shin, M. K. Gupta, H. S. Jung, S.-W. Kim and N.-G. Park, J. Phys. Chem. Lett., 2015, 6, 1729–1735 CrossRef CAS PubMed.
- H.-S. Kim and N.-G. Park, J. Phys. Chem. Lett., 2014, 5, 2927–2934 CrossRef CAS PubMed.
- B. Chen, M. Yang, X. Zheng, C. Wu, W. Li, Y. Yan, J. Bisquert, G. Garcia-Belmonte, K. Zhu and S. Priya, J. Phys. Chem. Lett., 2015, 6, 4693–4700 CrossRef CAS PubMed.
- Y. Shao, Z. Xiao, C. Bi, Y. Yuan and J. Huang, Nat. Commun., 2014, 5, 5784 CrossRef CAS PubMed.
- J. Xu, A. Buin, A. H. Ip, W. Li, O. Voznyy, R. Comin, M. Yuan, S. Jeon, Z. Ning, J. J. McDowell, P. Kanjanaboos, J.-P. Sun, X. Lan, L. N. Quan, D. H. Kim, I. G. Hill, P. Maksymovych and E. H. Sargent, Nat. Commun., 2015, 6, 7081 CrossRef CAS PubMed.
- H. Yu, F. Wang, F. Xie, W. Li, J. Chen and N. Zhao, Adv. Funct. Mater., 2014, 24, 7102–7108 CAS.
- Y. Sheng, A. Mei, S. Liu, M. Duan, P. Jiang, C. Tian, Y. Xiong, Y. Rong, H. Han and Y. Hu, J. Mater. Chem. A, 2018, 6, 2360–2364 RSC.
Footnote |
† Electronic supplementary information (ESI) available: IPCE spectra of the champion devices. See DOI: 10.1039/c8ra04347g |
|
This journal is © The Royal Society of Chemistry 2018 |