Fabrication of reactive pigment composite particles for blue-light curable inkjet printing of textiles

Chenglong Wanga, Lili Wangac, Yi Huanga, Yiding Menga, Guangdong Suna, Qinguo Fanab and Jianzhong Shao*a
aEngineering Research Center for Eco-Dyeing and Finishing of Textiles, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China. E-mail: jshao@zstu.edu.cn; Fax: +86-571-86843666; Tel: +86-571-86843625
bDepartment of Bioengineering, University of Massachusetts Dartmouth, North Dartmouth, MA 02747, USA
cSaintyear Holding Group Co., Ltd., Hangzhou 311221, China

Received 24th April 2017 , Accepted 13th July 2017

First published on 20th July 2017


Abstract

The reactive pigment composite particles were fabricated by a two-step method. Phthalocyanine Blue (PB) was encapsulated with silica through a Sol–Gel method in the first step, and the encapsulation conditions were optimized. 3-(Trimethoxysilyl)propyl methacrylate was then grafted onto the silica encapsulated organic pigment (EPB) in the second step, and the FT-IR analysis indicated that the relevant functional groups had been introduced onto the EPB. The particle size, hydrophilicity and the color characteristics of the Reactive Phthalocyanine Blue (RPB) changed little in comparison with PB. The photo-polymerization performance of the RPB-based ink showed a certain increase, and the fastness toward crocking of the printed fabrics was coordinately improved.


1 Introduction

Textile digital printing is considered one of the most promising methods for the printing of textile fabrics.1,2 Compared with dye-based inks, pigment-based inks have become more and more popular due to shorter printing processes, lower water and energy consumption and their applicability to all types of textile fabric substrates.3,4 However, pigment-based inks usually suffer from nozzle clogging problems. In order to overcome a nozzle clogging problem, light curable inks are proposed by substituting oligomers and monomers for the polymeric binder.5 Blue-light curable digital inkjet printing of textiles employs oligomers and monomers instead of the polymeric binder used in conventional pigment inks to ensure a sufficient fluidity during the ink-jet process and to solve the nozzle clogging problem. After injection, the oligomers and monomers polymerize and form a tough film on the fabric surface under blue-LED irradiation, achieving an expected colorfastness.6–8 However, in view of the inherent characterizations of pigment printing, pigment particles are physically covered in the film. Consequently, there are few firm forces between pigment particles and polymer film, resulting in a difficulty to achieve high-level colorfastness.

In order to improve the colorfastness of pigment-based ink-jet printing, many studies have been reported.9–14 Fu et al.15 considered that the most promising method to improve the quality of pigment-based inks was encapsulating latex particles onto surface of organic pigment. Recently, several methods have been reported for the encapsulation of pigment particles such as emulsion or mini-emulsion polymerization,16,17 phase separation,18,19 layer by-layer assembly,20 and sol–gel method.21,22 Nevertheless, the encapsulated pigments by these methods were still lack of firm forces in the crosslinking film. In our previous work,23 reactive organic pigment complex was prepared by the absorption-encapsulation of 3-(trimethoxysilyl)propyl methacrylate (MPS) onto the surface of organic pigment. However, the surface of PB was lack of reactive groups, so that the distribution of MPS onto PB was difficult to be controlled effectively. Thus, the hydrophilicity of reactive organic pigment complex were slightly increased, resulting in the increase of the particle size in ink. Silica was considered to be a good candidate of the transition layer, because it was convenient to coat on organic pigment and easy to be functionalized.24–26 After encapsulation of silica, hydroxyl group can be induced onto the surface of PB, which has good reactivity with various coupling agents.27,28 Based on the above idea, two-step method was proposed to prepare reactive pigment composite particles.

In this paper, silica encapsulated organic pigment (EPB) was firstly prepared by Sol–gel method, and the Reactive Phthalocyanine Blue (RPB) was then prepared by grafting MPS onto the surface of EPB. The double bonds existed in RPB can participate in the copolymerization of oligomers and monomers to realize the firm anchorage of pigment particles in the polymer cross-linked network structure via covalent bonds. The optimum process to prepare EPB was investigated. The particle size, color performance and hydrophilicity of RPB were studied. The application of the RPB in blue light curable inks was carried out and the colorfastness toward crocking of the printed fabric was investigated.

2 Experimental sections

2.1 Materials

Poly(diallyldimethylammonium chloride) (PDADMAC, Mw < 200[thin space (1/6-em)]000), 2-hydroxyethylacrylate (HEA) and 3-(trimethoxysilyl)propyl methacrylate (MPS) were obtained from Aladdin Industrial Corporation. Ammonia (NH3) and absolute ethanol were purchased from Hangzhou Gaojing Fine Chemical Co. Ltd. Poly(sodium 4-styrenesulfonate) (PSS, Mw = 70[thin space (1/6-em)]000) was obtained from Shanghai Macklin Biochemical Co. Ltd. Polyvinylpyrrolidone (PVP) was obtained from Tianjin Kemiou Chemical Reagent Co. Ltd. Camphorquinone (CQ), ethyl-4-dimethylaminobenzoate (EDMAB) and tetraethyl orthosilicate (TEOS) were obtained from Sigma-Aldrich Co. LLC. Phthalocyanine Blue was provided from Clariant Chemical Co. Ltd. A commercial oligomer SM6202 was supplied by Jiangsu Sanmu Group Corporation.

2.2 Preparation of EPB composite particles

1 g Phthalocyanine Blue pigment was added into 0.5 g L−1 PSS solution. The mixture was milled by the planetary ball mill (PM400, Germany) with 6 mm stainless steel ball and dispersed for 1 h at 300 rpm, centrifugal washing to remove the residual PSS. Then, the above organic pigment was added to 1 g L−1 PDADMAC solution (containing 0.3 mol L−1 NaCl). After adsorption for 30 min, centrifugal washing to remove the residual PDADMAC. The organic pigment with positive charges was redispersed into a certain amount of deionized water and 200 mL ethanol. 0.2 g PVP was sequentially added and pH was adjusted. A certain amount of TEOS and 40 mL ethanol were dropped into the organic pigment dispersion solution within 1 h. After that, the reactant was stirred for 20 h at 25 °C. Finally, centrifugal washing and dried. The preparation route of EPB was shown in Scheme 1.
image file: c7ra04576j-s1.tif
Scheme 1 Schematic diagram for the preparation of EPB composite particles.

2.3 Preparation of reactive pigment composite particles

Reactive pigment composite particles were achieved by the following procedure: 1 g EPB was dispersed into 100 mL solution of ethanol/water (2/8, v/v). The dispersion was ultrasonically dispersed for 30 min, then a solution of 0.1 g MPS in 20 mL solution of ethanol/water (2/8, v/v) was added into the above dispersion. And the mixture was stirred for 3 h further at 75 °C. The obtained sample was rinsed twice with deionized water and dried at 40 °C for 24 h. The schematic mechanism of preparation of reactive pigment composite particles was shown in Scheme 2.
image file: c7ra04576j-s2.tif
Scheme 2 Mechanism for preparation of RPB.

2.4 Preparation of the blue light curable inks

A blue light curable ink was composed of 1 wt% CQ/EDMAB combination as photoinitiators, a commercial oligomer/HEA/IBOA combination as medium, 1.0 wt% as-prepared reactive pigment or PB. The mixture was dispersed by a covered ultrasonic oscillator (250 W, 40 kHz, Kunshan Ultrasound Co., Ltd).

2.5 Photo-differential scanning calorimetry measurement

The photo-polymerization behavior of as-prepared blue light curable ink was examined by photo-DSC analysis. Photo-DSC measurements were performed using a differential scanning calorimeter (Q2000, TA Instruments, USA) equipped with a photo-calorimetric accessory (PCA OmniCure S2000, Canada).

2.6 BET analysis

Nitrogen adsorption/desorption isotherms were measured using a Micromeritics ASAP 2020HD88. The Brunauer–Emmett–Teller (BET) method was used to analyze the specific surface areas of the samples.

2.7 FT-IR analysis

Fourier transform infrared (FT-IR) spectra of the samples was recorded on a FT-IR spectrometer (Nicolet 5700, USA) at a resolution of 4 cm−1 in the range from 4000 to 600 cm−1.

2.8 TEM analysis

The morphologies of PB, EPB and RPB were taken using a JSM-2100 transmission electron microscope (JEOL, Japan) at an acceleration voltage of 200 kV.

2.9 Particle size analysis

The samples of PB and EPB were prepared respectively by mixing pigment (0.01 g) and deionized water (10 g), which were subjected to ultrasonic treatment for 30 min, and then diluted in same times. The particle sizes of the samples were determined by a Malvern laser particle sizes analyzer (Nano-S, England).

The samples of PB and RPB were prepared respectively by mixing organic pigment (0.01 g) and HEA (10 g), which were subjected to ultrasonic treatment for 30 min, and then diluted in same times. The particle sizes of the samples were determined by a Malvern laser particle sizes analyzer (Nano-S, England).

2.10 Dispersion stability

The samples of PB and RPB were prepared respectively by mixing pigment (0.01 g) and HEA (10 g), which were subjected to ultrasonic treatment for 30 min. After standing for a week, the digital photographs were taken by digital camera (Sony).

2.11 Surface tension

The surface tension of inks was measured by using a contact-angle system (DSA-20, Germany) at ambient temperature and saturated humidity.

2.12 Thermogravimetric analyses (TGA)

EPB and PB were analyzed for their thermal behavior using a Perkinelmer Pyris 1 TGA thermal analysis instrument. The samples were heated from 25 to 700 °C at a heating rate of 20 °C min−1 under N2 atmosphere.

2.13 UV-vis spectrophotometer

The reflection of PB and RPB was detected on a UV-vis spectrophotometer (UV-2600, Japan) using the diffuse reflectance mode.

2.14 Digital printing of cotton fabrics

A digital printing trial using the as-prepared blue light curable ink was carried out on a plain woven cotton fabric with fluid dispensing equipment (TenSun TS-500B, China) at 20 mm s−1 moving speed with 140 kPa nitrogen pressures. After printing, the printed fabrics were cured under a self-assembled blue light emitting diode (LED) lamp in nitrogen atmosphere for 5 min.

2.15 Measurement of rubbing color-fastness

The dry and wet rubbing color-fastness of the printed cotton fabrics was measured by employing a rubbing tester (680MD, UK) according to AATCC 8-2007 test method.

2.16 Mechanical properties

The cured films were prepared by blue light curable ink. The elongation at break and breaking strength of cured films were tested by Instron 3367 material testing machine according to ASTM D638-2014 standard.

2.17 Handle analysis

The handle of printed fabric was tested by intelligent fabric style instrument (YG821LPhabrOmeterfabric, China), and the samples were cut into circle with diameter of 12 cm.

3 Results and discussion

3.1 Preparation of EPB

The effective encapsulation of organic pigment with silica was beneficial for the preparation of RPB. The encapsulation of organic pigment via sol–gel process of TEOS was carried out in ethanol at room temperature. The effects of deionized water, pH and TEOS on the preparation of EPB were investigated.
3.1.1 Effect of deionized water on the preparation of EPB. The influences of deionized water on the encapsulation of organic pigment with silica are shown in Table 1. The particle size and PDI of PB had the biggest value. After silica encapsulation, the particle size and PDI of EPB decreased. This was probably because organic pigment was encapsulated by silica, so that the hydrophilicity and the dispersion stability of EPB were improved. The particle size and PDI of EPB increased with increasing of deionized water. It might be that high water content could result in fast hydrolysis and condensation of TEOS, accompanied by the strong tendency to self-nucleation. Therefore, the optimum dosage of deionized water was 1[thin space (1/6-em)]:[thin space (1/6-em)]16 (Vwater/Vethanol).
Table 1 Particle size and PDI of PB and EPB with different water concentration
  PB 1[thin space (1/6-em)]:[thin space (1/6-em)]20 1[thin space (1/6-em)]:[thin space (1/6-em)]16 1[thin space (1/6-em)]:[thin space (1/6-em)]12 1[thin space (1/6-em)]:[thin space (1/6-em)]10
Z-Aver 404.8 253.0 222.0 278.8 301.2
PDI 0.419 0.208 0.209 0.269 0.327


3.1.2 Effect of pH on the preparation of EPB. Table 2 displays the effects of pH on the encapsulation of organic pigment with silica. In Table 2, when pH values were 11 and 12, the particle sizes and PDI were obviously increased. It might be attributed to high pH value, leading to the fast hydrolysis and condensation of TEOS.
Table 2 Particle size and PDI of EPB with different pH
  9 10 11 12
Z-Aver 261.2 222.0 333.8 374.5
PDI 0.296 0.209 0.320 0.376


The specific surface areas of the PB particles and EPB with different pH were determined by BET and Langmuir method and listed in Table 3. It could be found that the specific surface area of EPB had little change at pH value 9 and 10. However, at pH 11 and 12, the specific surface of EPB were obviously increased. In Fig. 1, it also demonstrated that the N2 adsorption/desorption isotherms of EPB were similar to that of the PB particles at pH 9 and 10. When relative pressure P/P0 was more than 0.75, a slight separation of the adsorption isotherms and desorption isotherms of EPB was also observed at pH 11 and 12, which should be the evidence of a small quantity of micropores existed on the organic pigment surfaces, due to the generation of SiO2 nanoparticles on the surface of organic pigment.21 As a result, the optimum pH value was 10.

Table 3 The specific surface areas of PB and EPB with different pH
Sample BET surface area (m2 g−1) Langmuir surface area (m2 g−1)
PB 50.57 81.15
pH = 9 51.56 82.17
pH = 10 55.45 89.28
pH = 11 73.83 118.11
pH = 12 68.82 109.76



image file: c7ra04576j-f1.tif
Fig. 1 Nitrogen adsorption/desorption isotherm of EPB with different pH value (a: PB, b: pH = 9, c: pH = 10, d: pH = 11, e: pH = 12).
3.1.3 Effect of TEOS on the preparation of EPB. Table 4 shows the effect of TEOS dosage on the encapsulation of organic pigment. When the concentration of TEOS changed, the particle size and PDI of EPB had little change. Furthermore, the amount of silica, which was encapsulated on the surface of organic pigment, was characterized by TGA, shown in Fig. 2. As TEOS increased, the amount of silica encapsulate on the surface of organic pigment increased. It also implied that the content of silica encapsulated on the surface of organic pigment could be easily modulated with various TEOS dosage. Fig. 2 shows the thermogravimetric results of the PB and EPB and Fig. 3 gives the differential of the TGA curves in Fig. 2. It was found that the PB had two stages of weight loss while EPB had three stages. It demonstrated that the thermostability of EPB was improved after silica encapsulation. Above all, the optimum TEOS dosage was 0.8[thin space (1/6-em)]:[thin space (1/6-em)]1 (mass ratio of TEOS to PB).
Table 4 Particle size and PDI of EPB with different TEOS
  0.6[thin space (1/6-em)]:[thin space (1/6-em)]1 0.8[thin space (1/6-em)]:[thin space (1/6-em)]1 1[thin space (1/6-em)]:[thin space (1/6-em)]1 1.2[thin space (1/6-em)]:[thin space (1/6-em)]1
Z-Aver 209.6 196.1 222.0 226.7
PDI 0.222 0.201 0.209 0.314



image file: c7ra04576j-f2.tif
Fig. 2 TGA curves of PB and EPB with different TEOS.

image file: c7ra04576j-f3.tif
Fig. 3 Differential of the TGA cures in Fig. 2.

3.2 FT-IR analysis

After encapsulated silica, the EPB was easy to be functionalized by silane coupling agent, therefore, the reactive pigment composite particles could be easily prepared by grafting MPS onto EPB.27,28 The FT-IR spectra of PB, EPB and RPB were presented in Fig. 4 to confirm the successful modification of Phthalocyanine Blue by silica and MPS. As seen in Fig. 4(b) and (c), the characteristic peaks at 813 cm−1 corresponded to the Si–O–Si stretching vibration absorption peak. In comparison with the spectra of the PB and EPB, the absorption peaks at 1717 and 1636 cm−1 appeared in the spectra of the RPB, which referred to C[double bond, length as m-dash]O and the C[double bond, length as m-dash]C stretching vibration absorption peak, respectively. Therefore, silica and C[double bond, length as m-dash]C group were introduced onto the surface of PB.
image file: c7ra04576j-f4.tif
Fig. 4 FT-IR spectra of organic pigment (a: PB, b: EPB, c: RPB).

3.3 TEM and EDS analyses

The morphologies of PB, EPB and RPB were characterized by TEM microscopy as shown in Fig. 5. Compared with the PB (Fig. 5a), the relatively much darker surfaces could be observed in the EPB and RPB, which indicated that the surfaces of organic pigment were encapsulated with silica.21 The presence of silica could be further confirmed by the following EDS analysis.
image file: c7ra04576j-f5.tif
Fig. 5 TEM images of organic pigment (a: PB, b: EPB, c: RPB).

Fig. 6 showed the atomic compositions of PB, EPB and RPB. It could be seen that, from Fig. 6, there was no presence of atomic silica on the PB, while obvious presence of atomic silica on both the EPB and RPB, indicated by the peaks at 1.8 keV on Fig. 6(b) and (c).


image file: c7ra04576j-f6.tif
Fig. 6 The atomic compositions of PB, EPB and RPB (a: PB, b: EPB, c: RPB).

Further observation of TEM images, it seems that there were no SiO2 particles presented on the pigment surface on Fig. 5(b) and (c) though EDS analysis has confirmed the presence of silica element. This might be explained by the formation of silica film on the pigment surface during the sol–gel treatment, rather than the formation of SiO2 particles.

3.4 Contact angle of organic pigment

The wetting of water on the solid is dependent on the relationship between the interfacial tensions. The contact angle (θ) between the water droplet and the given surface can be used to represent the hydrophobicity–hydrophobicity. The influences of modification on the water contact angle of organic pigment are shown in Fig. 7. With regard to Fig. 7(a), it was observed that the water contact angle of PB was 115.95°. However, the water contact angle of EPB was 51.16°, it implied that the hydrophilic of EPB was improved due to the silica encapsulated on the surface of organic pigment. The water contact angle of RPB was increased after grafting MPS. The reaction between MPS and –OH on the surface of EPB was occurred, and C[double bond, length as m-dash]C groups replaced –OH groups. As a result, the hydrophobicity of RPB was close to the PB.
image file: c7ra04576j-f7.tif
Fig. 7 Contact angles of water droplets on the surface of organic pigment (a: PB, b: EPB, c: RPB).

3.5 Color performance of modified organic pigment particles

Fig. 8 displays the influences of modification on the color characteristic of the organic pigment. The color characteristic of the organic pigment was evaluated by examining the changes of the visible diffuse reflectance spectra. In the spectra, the peak locations of PB, EPB and corresponding RPB were almost the same. The RPB kept similar hues to the PB, which could be proved by the appearance of the pigments, as shown in Fig. 8. Therefore, there had little influence of modification on the color performance of the organic pigments.
image file: c7ra04576j-f8.tif
Fig. 8 Reflection spectra of organic pigment.

3.6 Particle size and dispersion stability analysis

The particle size distribution of PB and RPB were analyzed by a Nano Particle Analyzer. The results were plotted in Fig. 9. The particle size distribution of RPB was similar to PB. It implied that the average particle size of RPB had little change. The reasons might be that a thin and homogeneous film was formed on the surfaces of the organic pigment particles, and the encapsulation and grafting had little influence on the particle size. Fig. 10 shows the dispersion stability of PB and RPB in HEA. After one week standing, significant stratification was found in the PB dispersion. In contrast, there was almost no stratification phenomenon appeared in the RPB dispersion, which indicated that the dispersion stability was improved after modification. The reason was that an outward extension of the organic chain was formed on the surface of RPB which acted as a steric hindrance.
image file: c7ra04576j-f9.tif
Fig. 9 The particle size of PB and RPB.

image file: c7ra04576j-f10.tif
Fig. 10 The dispersion stability of PB and RPB in HEA.

3.7 The surface tension of inks analysis

Surface tension is defined as the force per unit length that acts across any line in a surface, tending to pull the surface closed. Surface tension is calculated using the forces experienced by the balance as the probe interacts with the surface of the liquid. Fig. 11 showed the tensions of different inks. It was found that the surface tension of inks had little change after the addition of PB and RPB. Furthermore, the surface tensions of inks with PB and RPB were almost the same. It suggested that the modification of organic pigment had little effect on the surface tension of inks.
image file: c7ra04576j-f11.tif
Fig. 11 Surface tensions of inks (a: ink without pigment, b: ink with PB, c: ink with RPB).

3.8 Photo-polymerization performance of blue light cured inks

Photo-polymerization performances of blue light cured inks are presented in Fig. 12. Compared to the blank polymerization system, the photo-polymerization performance of the blue light cured inks declined after the addition of PB or RPB, resulting from the physical shielding effect of pigment particle. The blue light cured ink with RPB had better performances than ink with PB. The reason was that the concentration of double bonds in inks increased after modified. Therefore, the photo-polymerization performance of the blue light cured ink with RPB was improved.
image file: c7ra04576j-f12.tif
Fig. 12 The polymerization rate of the blue light curable inks.

3.9 Printing performance

Table 5 shows the crock fastness of the printed fabrics. It was clearly seen that the crock colorfastness of the printed fabric with RPB was improved. This was probably because the double bonds existed in RPB. The double bonds could participate in the copolymerization of oligomers and monomers, achieving a firm anchorage of pigment particles in the cross-linked polymer network. Fig. 13 showed the stress–strain curves of the cured films. It was found that the elongation at break and breaking strength of cured films were declined after the addition of organic pigment. However, the elongation at break and breaking strength of cured films with RPB were better than PB, which implied that the double bonds introduced in RPB had taken part in the copolymerization of oligomers and monomers.
Table 5 Colorfastness to crocking of the printed fabrics with PB or RPB
  Dry fastness Wet fastness
PB 3 3.5
RPB 4 4.5



image file: c7ra04576j-f13.tif
Fig. 13 Stress–strain curves of the cured films.

Table 6 displayed the handle of unprinted and printed fabric. The handle of fabric includes stiffness, smoothness and softness tested by PhabrOmeter fabric style instrument. The lower the stiffness value is, the greater the smoothness and softness value are, the better the hand feeling. Table 6 showed the stiffness, smoothness and softness of unprinted and printed fabric had little change. It indicated that blue-light curable digital inkjet printing of textiles using RPB had little negative effect on the handle of fabric.

Table 6 The handle of the printed fabrics with PB and RPB
  Stiffness score Softness score Smoothness score
Blank sample 57.74 71.08 84.35
PB 58.31 68.82 84.69
RPB 58.84 68.46 84.74


4 Conclusions

EPB was obtained by silica encapsulation via sol–gel methods, and the optimized encapsulation conditions were as follows: the dosage of deionized water was 1[thin space (1/6-em)]:[thin space (1/6-em)]16 (Vwater/Vethanol), the pH value was 10 and the TEOS dosage was 0.8[thin space (1/6-em)]:[thin space (1/6-em)]1 (mass ratio of TEOS to PB). The RPB was prepared by grafting 3-(trimethoxysilyl)propyl methacrylate onto EPB. TEM analysis showed that the surfaces of organic pigment were encapsulated with silica, and FTIR analysis indicated that MPS was grafted on the EPB surface as expected. The particle size and hydrophilicity of RPB were similar to those of the PB. For the application properties of blue light curable pigment inks prepared using RPB, Photo-DSC analysis showed a markedly increased polymerization rate, and physical property measurements of printed fabrics showed an improved colorfastness toward crocking, and little negative influence on fabric handle as well.

Acknowledgements

This work was financially supported by the National Natural Science Foundation of China (grant number 51273180), and Zhejiang Provincial Top Key Academic Discipline of Chemical Engineering and Technology of Zhejiang Sci-Tech University (grant number CETT2015003).

References

  1. D. J. Tyler, Textile Digital Printing Technologies, Text. Prog., 2005, 37(4), 1–65 CrossRef.
  2. S. Leelajariyakul, H. Noguchi and S. Kiatkamjornwong, Surface-modified and micro-encapsulated pigmented inks for ink jet printing on textile fabrics, Prog. Org. Coat., 2008, 62(2), 145–161 CrossRef CAS.
  3. M. M. Marie, Y. H. El-Hamaky and D. Maamoun, et al., Pigment Ink Formulation for Inkjet Printing of Different Textile Materials, Int. J. Innovation Appl. Stud., 2013, 4(1), 239–247 CAS.
  4. S. Mhetre and W. C. P. Radhakrishnaiah, On the relationship between ink-jet printing quality of pigment ink and the spreading behavior of ink drops, J. Text. Inst., 2010, 101(5), 423–430 CrossRef CAS.
  5. B. Neral, S. Šostar-Turk and B. Vončina, Properties of UV-cured pigment prints on textile fabric, Dyes Pigm., 2006, 68(2–3), 143–150 CrossRef CAS.
  6. J. Shao, Y. Huang and Q. Fan, Visible light initiating systems for photopolymerization: status, development and challenges, Polym. Chem., 2014, 5(14), 4195–4210 RSC.
  7. Y. Huang, B. Cao and C. Xu, et al., Synthesis process control and property evaluation of a low-viscosity urethane acrylate oligomer for blue light curable ink of textile digital printing, Text. Res. J., 2014, 85(7), 759–767 CrossRef.
  8. Y. Huang, H. Zhang and Y. Meng, et al., Study on Flexible Polymerization System of Blue Light Curing Ink for Textile Digital Inkjet Printing, Journal of Zhejiang Sci-Tech University, 2016, 35(1), 9–16 Search PubMed.
  9. X. Zhou, J. Zhang and X. Li, et al., Synthesis of core-shell acrylic-polyurethane hybrid latex as binder of aqueous pigment inks for digital inkjet printing, Prog. Nat. Sci., 2012, 22(1), 71–78 CrossRef.
  10. S. Fu, L. Zhang and A. Tian, et al., Preparation of a Novel Colorant with Branched Poly(styrene-alt-maleic anhydride) for Textile Printing, Ind. Eng. Chem. Res., 2014, 53(24), 10007–10014 CrossRef CAS.
  11. C. Fang, X. Zhou and Q. Yu, et al., Synthesis and characterization of low crystalline waterborne polyurethane for potential application in water-based ink binder, Prog. Org. Coat., 2014, 77(1), 61–71 CrossRef CAS.
  12. Y. Guan, B. Tawiah and L. Zhang, et al., Preparation of UV-cured pigment/latex dispersion for textile inkjet printing, Colloids Surf., A, 2014, 462, 90–98 CrossRef CAS.
  13. O. A. Hakeim, A. A. Arafa and M. K. Zahran, et al., UV-curable encapsulation of surface—Modified organic pigments for inkjet printing of textiles, Colloids Surf., A, 2014, 447(447), 172–182 CrossRef CAS.
  14. C. H. Xue, M. M. Shi and H. Z. Chen, et al., Preparation and application of nanoscale microemulsion as binder for fabric inkjet printing, Colloids Surf., A, 2006, 287(1–3), 147–152 CrossRef CAS.
  15. S. Fu, D. Wang and C. Du, et al., Improve color fastness of inkjet printing textiles using pigment ink, J. Text. Res., 2015, 36(02), 141–147 Search PubMed.
  16. S. Fu, C. Du and M. Zhang, et al., Preparation and properties of polymer-encapsulated phthalocyanine blue pigment via emulsion polymerization, Prog. Org. Coat., 2012, 73(2), 149–154 CrossRef CAS.
  17. O. A. Hakeim, Q. Fan and Y. K. Kim, Encapsulation of Pigment Red 122 into UV-curable resins via a mini-emulsion technique, Pigm. Resin Technol., 2010, 39(1), 3–8 CrossRef CAS.
  18. S. Fu and K. Fang, Properties of waterborne nanoscale pigment red 122 dispersion prepared by phase separation method, J. Appl. Polym. Sci., 2008, 108(6), 3968–3972 CrossRef CAS.
  19. A. A. Haroun, H. A. Diab and O. A. Hakeim, Cellulosic fabrics printing with multifunctional encapsulated phthalocyanine pigment blue using phase separation method, Carbohydr. Polym., 2016, 146, 102–108 CrossRef CAS PubMed.
  20. J. Yuan, W. Xing and G. Gu, et al., The properties of organic pigment encapsulated with nano-silica via layer-by-layer assembly technique, Dyes Pigm., 2008, 76(2), 463–469 CrossRef CAS.
  21. J. Yuan, S. Zhou and G. Gu, et al., Encapsulation of organic pigment particles with silica via sol-gel process, J. Sol-Gel Sci. Technol., 2005, 36(3), 265–274 CrossRef CAS.
  22. B. Xiao, H. Wu and S. Guo, Regulating the properties of C.I. Pigment Red 170 by surface modification via, hydrous alumina, Dyes Pigm., 2016, 127, 87–93 CrossRef CAS.
  23. C. Wang, L. Wang and Y. Huang, et al., Preparation and characterization of Phthalocyanine Blue encapsulated with silane coupling agent for blue light curable inkjet printing of textiles, Dyes Pigm., 2017, 139, 453–459 CrossRef CAS.
  24. J. Yuan, S. Zhou, B. You and L. Wu, Organic pigment particles coated with colloidal Nano-Silica particles via layer-by-layer assembly, Chem. Mater., 2005, 17, 3587–3594 CrossRef CAS.
  25. B. Zhang, Z. Zhang and X. Fei, et al., Preparation and properties of C.I. Pigment Red 170 modified with silica fume, Pigm. Resin Technol., 2016, 45(3), 141–148 CrossRef.
  26. S. Kango, S. Kalia and A. Celli, et al., Surface modification of inorganic nanoparticles for development of organic–inorganic nanocomposites—A review, Prog. Polym. Sci., 2013, 38(8), 1232–1261 CrossRef CAS.
  27. Z. Wen, Y. Feng and X. Li, et al., Surface modification of organic pigment particles for microencapsulated electrophoretic displays, Dyes Pigm., 2012, 92(1), 554–562 CrossRef CAS.
  28. Y. Li, Q. Guo and Z. Wang, et al., Fabrication of tri-layer structured CdS/SiO2/sulfonated PS composite sphere and its photocatalytic behavior, Colloids Surf., A, 2015, 486, 106–113 CrossRef CAS.

This journal is © The Royal Society of Chemistry 2017