Solution synthesis of GeS and GeSe nanosheets for high-sensitivity photodetectors

Author affiliations

Abstract

We report the synthesis of 2D nanosheets of GeS and GeSe by facile solution based approaches. The synthesized nanosheets are single-crystalline in nature with lateral dimensions in micrometers. Band structures calculated from DFT calculations predicted a direct bandgap value of 1.67 and 1.37 eV for GeS and GeSe, respectively. The experimental bandgap values (GeS, Eg = 1.6 eV and GeSe, Eg = 1.2 eV) determined from optical measurements are slightly smaller than the predicted ones. Photoresponse measurements of GeS and GeSe nanosheets revealed that the nanosheets are extremely photoresponsive toward the incident light and exhibit a high photoresponsivity of up to 173 and 870 A W−1 under a 405 nm laser diode, respectively. These values are several orders of magnitude higher than those of previous reports for graphene and many other metal chalcogenide nanosheet photodetectors. In addition, the photodetectors show a fast photoresponse time and a specific detectivity on the order of 1013 Jones. These results show that both the GeS and GeSe nanosheets are promising narrow bandgap semiconductors for high performance photodetectors.

Graphical abstract: Solution synthesis of GeS and GeSe nanosheets for high-sensitivity photodetectors

Back to tab navigation

Supplementary files

Publication details

The article was received on 05 Nov 2015, accepted on 01 Dec 2015 and first published on 01 Dec 2015


Article type: Paper
DOI: 10.1039/C5TC03667D
Author version
available:
Download author version (PDF)
J. Mater. Chem. C, 2016,4, 479-485

  •   Request permissions

    Solution synthesis of GeS and GeSe nanosheets for high-sensitivity photodetectors

    P. Ramasamy, D. Kwak, D. Lim, H. Ra and J. Lee, J. Mater. Chem. C, 2016, 4, 479
    DOI: 10.1039/C5TC03667D

Search articles by author

Spotlight

Advertisements