J-aggregation and photodimerisation behaviour of cinnamoyloxy side chains of hyper-branched polymers determined by higher-order derivative spectra

Abstract

Hyper-branched polyester polyols (HBPs) comprised of 2,2-dimethyolpropionic acid (DMPA) were treated with cinnamoyl chloride to give the corresponding polycinnamates (DCi20, DCi30 and DCi40) in order to compare their spectroscopic and photochemical properties with those of poly(vinyl cinnamate) (PVCi) as a linear counterpart, as well as low-mass cinnamates. λmax of the cinnamate residues of DCi20, DCi30 and DCi40 suffered from marked red-shifting when compared with those of PVCi and the model compounds in solution. Fourth as well as eighth-order derivative spectra revealed that DCi20, DCi30 and DCi40 give rise to a new sub-peak ascribable to a J-aggregate at ca. 320 nm, causing the red-shifting of λmax in the absorption spectra. On the other hand, higher-order derivative spectra of PVCi consisted solely of the sub-peaks which are close to those of the low-mass compounds in dilute solution, indicating that PVCi does not form any aggregate at all. The new sub-peak due to the J-aggregate was more distinctly observed in the fourth-order derivative spectra for a film of DCi40, while a PVCi film shows again no sub-peak ascribable to aggregation. Photoirradiation of a DCi40 film with 313 nm light resulted in the rapid and thorough disappearance of the sub-peak due to the J-aggregate as a result of exclusive photodimerisation, when compared with that of the sub-peaks due to monomeric cinnamate, which displays both photoisomerisation and photodimerisation. It is assumed that dicinnamated DMPA residues attached densely to the branched side chains of HBPs form dendritic units that are prone to head–tail stacking to give the J-aggregate.

Graphical abstract: J-aggregation and photodimerisation behaviour of cinnamoyloxy side chains of hyper-branched polymers determined by higher-order derivative spectra

Supplementary files

Article information

Article type
Paper
Submitted
13 Sep 2013
Accepted
19 Oct 2013
First published
23 Oct 2013

J. Mater. Chem. C, 2014,2, 641-650

J-aggregation and photodimerisation behaviour of cinnamoyloxy side chains of hyper-branched polymers determined by higher-order derivative spectra

K. Ichimura, J. Mater. Chem. C, 2014, 2, 641 DOI: 10.1039/C3TC31820F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements