Abstract

The effect of the particle's shape of Gd0.1Ce0.9O2−d (GDC) nanopowders on the electrochemical performance of La0.6Sr0.4CoO3−δ (LSC)–GDC composite cathodes was experimentally studied by electrochemical impedance spectroscopy (EIS). Composites were made of nanostructured LSC perovskite (average crystallite size D = 30 nm) mixed with nanostructured GDC powder (D = 8 nm) of irregular particle shape or with spherical particles of 200 nm diameter. Symmetrical cells (cathode/electrolyte/cathode) with different weight ratios of LSC:GDC (100 : 0, 75 : 25, 50 : 50 and 25 : 75 wt%) thick cathodes were fabricated by the screen-printing method and tested by EIS in the temperature range of 500–700 °C under a synthetic air flow of 100 mL min−1. These nanostructured composite materials exhibited excellent performance (area-specific resistance – ASR – values in the range of 0.019–0.032 Ω cm2 for an operating temperature of 700 °C). The best performance was achieved at a weight ratio of 75 : 25 wt% (LSC : GDC) when nanostructured GDC spheres were employed. This enhanced performance can be attributed to GDC morphology along with GDC anionic conduction, which prevent the blocking of LSC electrochemical reaction sites on surface, keeping them active by depleting its surface of adsorbed and reduced oxygen. The limiting processes were determined to take place on the LSC surface. New insight on cobalt's speciation under working-like conditions, determined by in situ X-ray Absorption Spectroscopy (XAS) experiments, suggests that the ease of cobalt atoms for changing their oxidation state is the key feature that rules the electrochemical activity of LSC and an atomistic model that explains it is proposed.

Graphical abstract: Improvement on the electrochemical performance by morphology control of nanostructured La0.6Sr0.4CoO3−δ-Gd0.1Ce0.9O1.95 cathodes for IT-SOFC

Supplementary files

Article information

Article type
Paper
Submitted
09 noy 2021
Accepted
19 apr 2022
First published
20 apr 2022
This article is Open Access
Creative Commons BY-NC license

Energy Adv., 2022,1, 344-356

Improvement on the electrochemical performance by morphology control of nanostructured La0.6Sr0.4CoO3−δ-Gd0.1Ce0.9O1.95 cathodes for IT-SOFC

L. M. Acuña, M. D. Cabezas and R. O. Fuentes, Energy Adv., 2022, 1, 344 DOI: 10.1039/D2YA00085G

This article is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported Licence. You can use material from this article in other publications, without requesting further permission from the RSC, provided that the correct acknowledgement is given and it is not used for commercial purposes.

To request permission to reproduce material from this article in a commercial publication, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party commercial publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements