Understanding and unlocking the role of V in boosting the reversible hydrogen storage performance of MgH2

Abstract

Although MgH2 is widely regarded as one of the most promising solid-state hydrogen storage materials, the high operating temperature and sluggish kinetics of hydrogenation and dehydrogenation are major challenges for its practical application. Herein, V6O13 nanobelts with a thickness of 11 nm are fabricated to promote the reversible hydrogen storage performance of MgH2. The favorable interaction between V6O13 nanobelts and MgH2 leads to in situ homogeneous formation of metallic V during the initial dehydrogenation of MgH2. Induced by the catalysis of metallic V, which results in weaker structural stability and higher surface states of MgH2 attributed to the strong bonding interactions between V and H, the energy required for H2 desorption from MgH2 is decreased to 49.5 kJ mol−1, 10.9 kJ mol−1 lower than that of pristine MgH2. Moreover, during the reversible hydrogenation process, the catalysis of metallic V lowers the energy for H2 adsorption and dissociation on Mg down to −5.904 and 0.023 eV, respectively, while those values reach −0.086 and 1.103 eV for pristine Mg. As a result, with the introduction of V6O13 nanobelts with an ultralow content of 3 wt%, a systematic hydrogen storage capacity of 6.8 wt% could be retained at 250 °C after 10 cycles.

Graphical abstract: Understanding and unlocking the role of V in boosting the reversible hydrogen storage performance of MgH2

Supplementary files

Article information

Article type
Communication
Submitted
28 رجب 1444
Accepted
21 رمضان 1444
First published
21 رمضان 1444

J. Mater. Chem. A, 2023,11, 9762-9771

Understanding and unlocking the role of V in boosting the reversible hydrogen storage performance of MgH2

Y. Meng, J. Zhang, S. Ju, Y. Yang, Z. Li, F. Fang, D. Sun, G. Xia, H. Pan and X. Yu, J. Mater. Chem. A, 2023, 11, 9762 DOI: 10.1039/D3TA01029E

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements