Tuning porous nanostructures of MnCo2O4 for application in supercapacitors and catalysis

Abstract

It is shown that spinel type MnCo2O4 can be used as a pure negative electrode in supercapacitors. The electrochemical response can be significantly tuned by forming and modulating the mesoporous structures of these materials. With varying formation temperature, the nature of particle growth mechanism moves from Oswald ripening type to digestive ripening. This leads to increased surface area, porosity and charged states on the particles surface. Thus, making this material useful from application ranging from supercapacitors to catalysis. As a function of changing porosity, specific capacitance could be tuned in the range ∼290 F g−1. Added functionality of the material could be established by proving its excellent catalytic response for reducing p-nitrophenol, a common pollutant found in industrial waste streams. The sample calcined at 800 °C reduced p-nitrophenol in 8 min at 1 mg mL−1 catalyst concentration, while the sample obtained at 400 °C could complete the task only after 16 min. The superior catalytic response have been explained by analyzing the change in zeta potential, which develops on the surface of different porous structures.

Graphical abstract: Tuning porous nanostructures of MnCo2O4 for application in supercapacitors and catalysis

Supplementary files

Article information

Article type
Paper
Submitted
05 ذو القعدة 1437
Accepted
01 محرم 1438
First published
02 محرم 1438

RSC Adv., 2016,6, 96296-96305

Tuning porous nanostructures of MnCo2O4 for application in supercapacitors and catalysis

Md. A. Akhtar, V. Sharma, S. Biswas and A. Chandra, RSC Adv., 2016, 6, 96296 DOI: 10.1039/C6RA20004D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements