Solution growth of Ta-doped hematite nanorods for efficient photoelectrochemical water splitting: a tradeoff between electronic structure and nanostructure evolution

Abstract

Ta-doped hematite (α-Fe2O3) nanorod array films were successfully prepared on fluorine-doped tin dioxide (FTO) coated glass substrates via a facile solution growth process with TaCl5 as a Ta doping precursor. Under 1 sun illumination and at an applied potential of 1.0 V vs. Ag/AgCl, the Ta-doped α-Fe2O3 photoanode with optimized dopant concentration showed a photocurrent density as high as 0.53 mA cm−2, which was about 3.5 times higher than that of the undoped sample. As demonstrated by Mott–Schottky and X-ray absorption spectroscopy measurements, considerable increase in photoelectrochemical (PEC) performance achieved for Ta-doped α-Fe2O3 nanorod films should be mainly attributed to the increased electron donor density induced by Ta doping. However, with superfluous Ta doping, the [110]-oriented nanorod structure was destroyed, which caused greatly restrained photoinduced holes transferring to the surface and retarded surface water oxidation reaction, leading to decreased PEC water splitting activity. This study clearly demonstrated that doping could be effective to enhance the PEC activity of α-Fe2O3 nanorods as photoanodes, while it is of great necessity to balance the trade-off between the electronic structure and nanostructure evolution by optimizing the dopant concentration, for increased donor density and meanwhile with the nanorod nanostructure well preserved for directed charge transfer.

Graphical abstract: Solution growth of Ta-doped hematite nanorods for efficient photoelectrochemical water splitting: a tradeoff between electronic structure and nanostructure evolution

Supplementary files

Article information

Article type
Paper
Submitted
04 十二月 2015
Accepted
04 一月 2016
First published
05 一月 2016

Phys. Chem. Chem. Phys., 2016,18, 3846-3853

Solution growth of Ta-doped hematite nanorods for efficient photoelectrochemical water splitting: a tradeoff between electronic structure and nanostructure evolution

Y. Fu, C. Dong, Z. Zhou, W. Lee, J. Chen, P. Guo, L. Zhao and S. Shen, Phys. Chem. Chem. Phys., 2016, 18, 3846 DOI: 10.1039/C5CP07479G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements