Direct immobilization of an atomically dispersed Pt catalyst by suppressing heterogeneous nucleation at −40 °C

Abstract

Direct deposition of isolated metal atoms onto substrates has been recognized as a simple route to obtain high performance supported atomically dispersed metals (SACs), however, the agglomeration driven by high surface energy is difficult to avoid. Herein, we demonstrate a one-pot solution synthesis to obtain atomically dispersed platinum (Pt) supported on nitrogen (N)-doped mesoporous carbon (NMC) substrates (Pt/NMC-LT) by conducting the whole synthesis at −40 °C, owing to the sluggish nucleation kinetics. We obtained the Pt/NMC-LT catalyst with superior electrochemical hydrogen evolution reaction (HER) activity and stability, in comparison with the NMC supported dominant Pt sub-nanometer cluster catalyst from solution synthesis at RT ∼ 25 °C (Pt/NMC-RT) and commercial carbon supported Pt nanoparticle catalysts (Pt/C). Lower over-potential values (only 17.0 and 49.8 mV) are needed for high HER current densities (10 and 100 mA cm−2, respectively), and no obvious degradation is observed after an accelerated durability test (ADT) for 5000 CV cycles.

Graphical abstract: Direct immobilization of an atomically dispersed Pt catalyst by suppressing heterogeneous nucleation at −40 °C

Supplementary files

Article information

Article type
Communication
Submitted
11 7月 2019
Accepted
08 9月 2019
First published
09 9月 2019

J. Mater. Chem. A, 2019,7, 25779-25784

Direct immobilization of an atomically dispersed Pt catalyst by suppressing heterogeneous nucleation at −40 °C

K. Huang, R. Wang, H. Wu, H. Wang, X. He, H. Wei, S. Wang, R. Zhang, M. Lei, W. Guo, B. Ge and H. Wu, J. Mater. Chem. A, 2019, 7, 25779 DOI: 10.1039/C9TA07469D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements