Fe3O4 hard templating to assemble highly wrinkled graphene sheets into hierarchical porous film for compact capacitive energy storage

Abstract

Highly wrinkled graphene film (HWGF) with high packing density was synthesized by combining an electrostatically self-assembling process, a vacuum filtration-induced film assembling process and capillary compression. Fe3O4 nanoparticles were used as a low-cost and environment-friendly hard template. Hierarchical porosity and high packing density were achieved with the aid of capillary compression in the presence of Fe3O4 nanoparticles. This strategy enables integration of highly wrinkled graphene sheets to form highly compact carbon electrodes with a continuous ion transport network. The generated HWGF exhibited a high packing density of 1.53 g cm−3, a high specific surface area of 383 m2 g−1 and a hierarchically porous structure. The HWGF delivered a high capacitance of 242 F g−1 and 370 F cm−3 at 0.2 A g−1 in 6 M KOH aqueous electrolyte system with excellent rate capability (202 F g−1 and 309 F cm−3 retained at 20 A g−1). The capacity retention rate reached 97% after 10 000 cycles at 1 A g−1. The HWGF-based supercapacitor exhibited a high energy density of 17 W h kg−1 at the power density of 49 W kg−1. Such high capacitive performances could be attributed to the highly dense but porous graphene assemblies composed of highly wrinkled graphene sheets.

Graphical abstract: Fe3O4 hard templating to assemble highly wrinkled graphene sheets into hierarchical porous film for compact capacitive energy storage

  • This article is part of the themed collection: Graphene

Supplementary files

Article information

Article type
Paper
Submitted
20 3月 2019
Accepted
17 6月 2019
First published
27 6月 2019
This article is Open Access
Creative Commons BY license

RSC Adv., 2019,9, 20107-20112

Fe3O4 hard templating to assemble highly wrinkled graphene sheets into hierarchical porous film for compact capacitive energy storage

H. Fang, F. Meng, J. Yan, G. Chen, L. Zhang, S. Wu, S. Zhang, L. Wang and Y. Zhang, RSC Adv., 2019, 9, 20107 DOI: 10.1039/C9RA02132A

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements