Highly efficient near-UV-excitable Ca2YHf2Al3O12:Ce3+,Tb3+ green-emitting garnet phosphors with potential application in high color rendering warm-white LEDs

Abstract

Inorganic phosphors with broadband near-ultraviolet (near-UV) excitation and efficient visible emission are highly important for fabricating high-performance near-UV-pumped white light-emitting diodes (LEDs). Herein, we report on novel efficient near-UV-excitable Ce3+/Tb3+ ion co-activated Ca2YHf2Al3O12 (CYHA) green-emitting garnet phosphors, which were successfully prepared through a high-temperature solid-state reaction process. X-ray diffraction, field-emission scanning electron microscopy, energy-dispersive X-ray spectroscopy, elemental mapping, photoluminescence, CIE color coordinates, the internal and external quantum efficiency, and temperature-dependent emission spectra were used to characterize the samples. Interestingly, due to the efficient energy transfer from Ce3+ to Tb3+ ions in CYHA, the CYHA:Ce3+,Tb3+ samples presented a wide excitation band in the 370–470 nm region peaking around 408 nm owing to the 4f–5d transition of Ce3+ ions, and under 408 nm excitation they showed intense characteristic sharp green emission around 543 nm corresponding to the 5D47F0–6 transitions of Tb3+ ions. The energy transfer mechanism from Ce3+ to Tb3+ ions was ascribed to the quadruple–quadruple interaction, and the energy transfer efficiency reached as high as 93.2%. Notably, the composition-optimized CYHA:0.03Ce3+,0.6Tb3+ sample exhibited a high internal quantum efficiency (IQE) of 78.5% and external quantum efficiency (EQE) of 56%, which were much higher than those of the Tb3+ singly-activated CYHA:0.6Tb3+ sample (IQE = 8%, EQE = 2.2%). Finally, a prototype white LED device was made by combining a 400 nm near-UV-emitting LED chip with a phosphor blend of the as-prepared CYHA:0.03Ce3+,0.6Tb3+ green phosphors, commercial BaMgAl10O17:Eu2+ blue phosphors and commercial CaAlSiN3:Eu2+ red phosphors, which emitted bright warm-white light with good CIE chromaticity coordinates of (0.391, 0.356), a low correlated color temperature of 3528 K and a high color rendering index of 92.3 under 120 mA driving current. This work opens up new opportunities for the development of efficient color converters toward near-UV-pumped warm-white LEDs with high color rendering index.

Graphical abstract: Highly efficient near-UV-excitable Ca2YHf2Al3O12:Ce3+,Tb3+ green-emitting garnet phosphors with potential application in high color rendering warm-white LEDs

Supplementary files

Article information

Article type
Paper
Submitted
09 ⵉⵏⵏ 2020
Accepted
14 ⴱⵕⴰ 2020
First published
14 ⴱⵕⴰ 2020

J. Mater. Chem. C, 2020,8, 4408-4420

Highly efficient near-UV-excitable Ca2YHf2Al3O12:Ce3+,Tb3+ green-emitting garnet phosphors with potential application in high color rendering warm-white LEDs

S. Wang, B. Devakumar, Q. Sun, J. Liang, L. Sun and X. Huang, J. Mater. Chem. C, 2020, 8, 4408 DOI: 10.1039/D0TC00130A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements