Injectable polyoxazoline grafted hyaluronic acid thermoresponsive hydrogels for biomedical applications

Abstract

Injectable thermosensitive hydrogels based on hyaluronic acid (HA) grafted with lower critical solution temperature (LCST) polyoxazoline (copolymers of poly(isopropyl-co-butyl oxazoline)) or P(iPrOx-co-BuOx) have been elaborated with tunable solution/gel temperature transitions and gel state elastic modulus. A suitable HA-g-P(iPrOx-co-BuOx-67/33)-0.10 sample with an iPrOx/BuOx ratio of 67/33, a polymerization degree (DP) of 25, a substitution degree (DS) of 10%, and displaying thermally induced gelling character with elastic (G′) and viscous (G′′) moduli crossover points at 25 °C and a G′ at 37 °C around 80 Pa has been chosen for medical application. Hydrogels obtained with HA-g-P(iPrOx-co-BuOx-67/33)-0.10 exhibited high stability at 37 °C and excellent injectability properties with full and quick reversibility. The incorporation of a secondary network (HA), until 35 wt%, into the thermosensitive hydrogel also demonstrated very good stability and injectability.

Graphical abstract: Injectable polyoxazoline grafted hyaluronic acid thermoresponsive hydrogels for biomedical applications

Supplementary files

Article information

Article type
Paper
Submitted
10 Вер 2023
Accepted
14 Лют 2024
First published
15 Лют 2024

J. Mater. Chem. B, 2024,12, 2807-2817

Injectable polyoxazoline grafted hyaluronic acid thermoresponsive hydrogels for biomedical applications

M. Morel, M. Madau, D. Le Cerf, V. Dulong, A. Groo, A. Malzert-Fréon and L. Picton, J. Mater. Chem. B, 2024, 12, 2807 DOI: 10.1039/D3TB02108D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements