Importance of small loops within PIM-1 topology on gas separation selectivity in thin film composite membranes

Abstract

Studies of blends of topologically distinct samples of the polymer of intrinsic microporosity PIM-1 demonstrate, for the CO2/N2 gas pair, the ability to vary dramatically the selectivity and aging behaviour of thin film composite (TFC) membranes. Polymerizations carried out in the absence of nitrogen gas produced polymers with higher degrees of branching, which formed further into loops and at higher temperatures into significant amounts of colloidal network PIM-1 (<100 nm). In contrast, polymerizations carried out with excessive nitrogen purging produced high molar mass, di-substituted PIM-1 polymer chains. Blending of these diverse samples and testing as TFC membranes, prepared with a 2 μm active layer by kiss-coating directly on a polyacrylonitrile support, identified small loops as a topological component within di-substituted polymer chains that is required to obtain above average gas separation. A refined polymerization process produced a topologically rich sample, best described on average as a multi-loop polymeric structure (with 3 small loops) containing very few chain ends (0–1 max), which when used in TFC membranes exhibited good long-term aging (120 days) performance: CO2 permeance of 671 GPU and ideal CO2/N2 selectivity of 27. To put the level of optimization in context, a self-standing film (40 μm thickness) exhibited initial CO2 permeability of 4835 barrer (121 GPU) and ideal CO2/N2 selectivity of 55.5. This work presents a new approach to delivering polymeric materials for use in thin film membranes, which is based on multi-loop polymeric structures that aid both permeance and selectivity performance.

Graphical abstract: Importance of small loops within PIM-1 topology on gas separation selectivity in thin film composite membranes

Supplementary files

Article information

Article type
Paper
Submitted
03 Тра 2021
Accepted
02 Вер 2021
First published
13 Вер 2021

J. Mater. Chem. A, 2021,9, 21807-21823

Importance of small loops within PIM-1 topology on gas separation selectivity in thin film composite membranes

A. B. Foster, J. L. Beal, M. Tamaddondar, J. M. Luque-Alled, B. Robertson, M. Mathias, P. Gorgojo and P. M. Budd, J. Mater. Chem. A, 2021, 9, 21807 DOI: 10.1039/D1TA03712A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements