Lithium nitrate-assisted hydrothermal synthesis of ultrathin Bi2O2Se nanosheets and their photoelectrochemical performance

Abstract

Two-dimensional Bi2O2Se has drawn a lot of attention recently, due to its ultrahigh mobility and excellent performance in electronics and optoelectronics. However, the facile synthesis of two-dimensional Bi2O2Se nanocrystals is urgently required for their fundamental study and practical applications. In this work, we develop a controllable synthetic route to ultrathin Bi2O2Se nanosheets through the assistance of lithium nitrate (LiNO3) in a hydrothermal process. TEM, AFM, XRD, XPS and Raman demonstrate the successful synthesis of ultrathin Bi2O2Se nanosheets with a tetragonal phase. With Li+ adsorbing on {001} facets to inhibit crystal growth along the [001] direction, the lateral size of the Bi2O2Se nanosheets can be controlled through the amount of LiNO3 in the system. Photoelectrochemical tests reveal the good performance of the ultrathin Bi2O2Se nanosheets as a photoanode material in neutral solution. Detailed analysis of electrochemical impedance spectra and specific surface areas reveals that a high surface area and low recombination rate are responsible for the good photoelectrochemical activity of the larger Bi2O2Se nanosheets. Besides, the stability test shows negligible reduction of current density after 10 hours, and the TEM test demonstrates that the structure of the Bi2O2Se nanosheets is well preserved after long-term electrolysis, revealing great stability of the Bi2O2Se nanosheets as a photoanode material. This work indicates that two-dimensional Bi2O2Se could be a competitive candidate for the future energy systems.

Graphical abstract: Lithium nitrate-assisted hydrothermal synthesis of ultrathin Bi2O2Se nanosheets and their photoelectrochemical performance

Supplementary files

Article information

Article type
Communication
Submitted
11 Вер 2020
Accepted
07 Жов 2020
First published
08 Жов 2020

J. Mater. Chem. C, 2020,8, 14711-14717

Lithium nitrate-assisted hydrothermal synthesis of ultrathin Bi2O2Se nanosheets and their photoelectrochemical performance

Y. Sun, S. Ye, J. Zhang, J. Song, F. Zhou and J. Qu, J. Mater. Chem. C, 2020, 8, 14711 DOI: 10.1039/D0TC04352D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements