Reconfigurable 3D-printable magnets with improved maximum energy product

Abstract

In conventional magnets, neodymium with added heavy rare-earths is used in order to induce high output and size reduction. But as deposits of heavy rare-earths such as dysprosium (Dy) and terbium (Tb) are disproportionately distributed, it is important to reduce the amount used due to supply issues and material costs. Additionally, the use of rare-earths in applications that only need modest magnetic properties is disadvantageous and complicates their low-cost production in on-demand shapes. In this paper and as a new concept, reconfigurable rare-earths-free Wax/CoFe2O4 composite magnets were fabricated through 3D-printing. The evolution of magnetic properties was studied as a function of the magnetic field and CoFe2O4 ferrite content, allowing one to tune the magnetic response of permanent magnets. It was shown that saturation and remnant magnetization increase monotonously with ferrite content, reaching maximum values of 38.6 emu g−1 and 22.1 emu g−1, respectively, for the sample with 90% in weight of CoFe2O4 (wt%). On the other hand, the coercive field (≈2500 Oe) remained constant for all samples. Additionally, the addition of ferrite nanoparticles into Wax increased the Young's modulus (from 0.06 GPa to 0.47 GPa) and improved the thermal stability of the matrix as shown by the increase of the maximum degradation rate temperature and the temperature at which 25 wt% of the sample is degraded (from 412 °C to 429 °C and from 393 °C to 424 °C, respectively). In addition, the (coercive field) × (remanence field) maximum energy product (HC × BC)MAX, which is the figure of merit of permanent magnets, was evaluated, with the value obtained being the highest reported in the literature for CoFe2O4-based magnets (i.e., 4.44 MG Oe for the sample with 90 wt% of ferrite content). Thus, the present study allowed one to establish a new way to prepare reconfigurable printable magnets based on Wax/CoFe2O4 nanoparticles for advanced technologies.

Graphical abstract: Reconfigurable 3D-printable magnets with improved maximum energy product

Article information

Article type
Communication
Submitted
06 Лис 2019
Accepted
20 Гру 2019
First published
20 Гру 2019

J. Mater. Chem. C, 2020,8, 952-958

Reconfigurable 3D-printable magnets with improved maximum energy product

R. Brito-Pereira, C. Ribeiro, N. Peřinka, S. Lanceros-Mendez and P. Martins, J. Mater. Chem. C, 2020, 8, 952 DOI: 10.1039/C9TC06072C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements