Hydrothermal synthesis of polydopamine-functionalized cobalt-doped lanthanum nickelate perovskite nanorods for efficient water oxidation in alkaline solution

Abstract

Perovskite oxides have attracted great attention recently for their low cost and high intrinsic activity in the electrochemical oxygen evolution reaction (OER). In this work, we synthesized highly efficient OER electrocatalysts in alkaline solution by carbonization of polydopamine (PDA)-functionalized cobalt-doped lanthanum nickelate perovskite nanorod (La5Ni3Co2) complexes. The calcination temperature and molar ratio for La, Ni, and Co were optimized. The as-prepared complex with a molar ratio of 5 : 3 : 2 (La : Ni : Co) and a calcination temperature of 500 °C displayed enhanced OER activity and excellent durability. In 1.0 M KOH, the overpotential of the as-prepared catalyst at a current density of 10 mA cm−2 was 0.360 V, which is comparable to those of noble metal-based materials or perovskite-based materials. The Tafel slope is 48.1 mV dec−1, which is smaller than those of prepared composites. The satisfactory oxygen evolution activity could be attributed to the increased Co3O4, O22−/O, pyridine N, and quaternary N species after calcination treatment, and the improved amount of Ni3+ during the OER process, as well as the high surface area and electrochemical surface area.

Graphical abstract: Hydrothermal synthesis of polydopamine-functionalized cobalt-doped lanthanum nickelate perovskite nanorods for efficient water oxidation in alkaline solution

Supplementary files

Article information

Article type
Paper
Submitted
30 Maw 2019
Accepted
06 Nhl 2019
First published
08 Nhl 2019

Nanoscale, 2019,11, 19579-19585

Hydrothermal synthesis of polydopamine-functionalized cobalt-doped lanthanum nickelate perovskite nanorods for efficient water oxidation in alkaline solution

Y. Han, Z. Zhu, L. Huang, Y. Guo, Y. Zhai and S. Dong, Nanoscale, 2019, 11, 19579 DOI: 10.1039/C9NR06519A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements