Elizabeth
Howard‡
a,
Minghao
Li‡
b,
Michael
Kozma
a,
Jiayu
Zhao
a and
Jinhye
Bae
*abc
aDepartment of Nanoengineering, University of California, San Diego, La Jolla, CA 92093, USA. E-mail: j3bae@ucsd.edu
bMaterials Science and Engineering Program, University of California San Diego, La Jolla, CA 92093, USA
cChemical Engineering Program, Department of Nanoengineering, University of California, San Diego, La Jolla, CA 92093, USA
First published on 28th November 2022
Stimuli-responsive hydrogels with self-strengthening properties are promising for the use of autonomous growth and adaptation systems to the surrounding environments by mimicking biological materials. However, conventional stimuli-responsive hydrogels require structural destruction to initiate mechanochemical reactions to grow new polymeric networks and strengthen themselves. Here we report continuous self-strengthening of a nanocomposite hydrogel composed of poly(N-isopropylacrylamide) (PNIPAM) and nanoclay (NC) by using external stimuli such as heat and ionic strength. The internal structures of the NC-PNIPAM hydrogel are rearranged through the swelling–deswelling cycles or immersing in a salt solution, thus its mechanical properties are significantly improved. The effects of concentration of NC in hydrogels, number of swelling–deswelling cycles, and presence of salt in the surrounding environment on the mechanical properties of hydrogels are characterized by nanoindentation and tensile tests. The self-strengthening mechanical performance of the hydrogels is demonstrated by the loading ability. This work may offer promise for applications such as artificial muscles and soft robotics.
Currently, the self-strengthening behavior of nanocomposite hydrogels that their mechanical properties can be improved with use has gained great attraction as living materials. Recent research in producing artificial muscles has shown that hydrogel actuators can be strengthened through training like living muscle tissue.37,38 These material systems require structural destruction to initiate the chemical reaction, thus forming a new polymer network to achieve self-strengthening. NC-PNIPAM hydrogels can also be strengthened by physical methods such as uniaxial elongation,39 freezing treatment,40 and drying treatment.41 Nevertheless, these methods require applying mechanical force or damaging the original structures. Furthermore, Tong et al. reported a mechanical enhancement in NC-PNIPAM hydrogels by a single heat treatment that leads to the formation of a denser microstructure upon deswelling.42 However, the multiple or cyclic treatments for continuous self-strengthening of NC-PNIPAM hydrogels to mimic muscle training have not been studied to our best knowledge.
In this work, we demonstrate a non-invasive and non-destructive approach to self-strengthen NC-PNIPAM nanocomposite hydrogels through deswelling–reswelling (DS–RS) cycles, and study its mechanism. The materials and preparation of NC-PNIPAM hydrogel are shown in Fig. 1a. The aqueous NC-PNIPAM precursor solution was prepared by mixing N-isopropylacrylamide (NIPAM) as the monomer, methylenebisacrylamide (BIS) as the chemical crosslinker, Irgacure 2959 as the photoinitiator and NC as the physical crosslinker in deionized (DI) water. The NC-PNIPAM precursor was then transferred into a glass mold and exposed to 365 nm ultraviolet (UV) light at an intensity of 180 mW cm−2 for 1 min to photopolymerize and photocrosslink NC-PNIPAM hydrogels with a thickness of 1 mm. Further details outlining the NC-PNIPAM preparation process can be found in the ESI.† The NC-PNIPAM hydrogels were prepared with 3, 10, and 17 wt% NC, respectively, denoted as NC-X where X represents the wt% of NC. Additionally, the NC-PNIPAM hydrogels that were swelled, deswelled, and reswelled in water were abbreviated as NC-X-S, NC-X-DS, and NC-X-RS, respectively, while the NC-PNIPAM hydrogels treated with 0.01 M KCl were abbreviated as NC-X KCl. We note that NC-0 was not studied in this work as its crosslinking density was not enough to maintain its form due to no addition of NC as the physical crosslinker (Fig. S1†).
We first characterized the NC-PNIPAM samples at different concentrations of NC through DS–RS cycles after initial swelling. For each NC concentration (NC-3, NC-10 and NC-17), three as-prepared NC-PNIPAM hydrogel disks with a diameter of 5 mm and a thickness of 1 mm were swelled for at least 24 hours in water at 23 °C, then they were moved into a water bath at 50 °C for 24 hours to deswell and a bath at 23 °C for 24 hours to reswell. This timescale allows the NC-PNIPAM hydrogels to reach equilibrium (Fig. S2†), which also agrees with the calculation by the poroelastic diffusion constant for PNIPAM hydrogels ∼10−11 m2 s−1 regarding a 1 mm hydrogel disk.26 A hydrogel sample that was initially swelled, then deswelled and reswelled went through one cycle, and was denoted NC-X-RS1, this cycle number increases each time the sample is deswelled and reswelled again. During this process, we measured the swelling ratio as the diameter of the NC-X disk at different cycles divided by the diameter of the as-prepared disk (Fig. 1b). The swelling ratios of the NC-PNIPAM hydrogels were not fully recovered to the initial swelling ratios after DS–RS cycles. Overall, the swelling ratios of the NC-PNIPAM hydrogels decrease until the third cycle (RS3), where they are 26%, 34%, and 15% lower than the initial swelling ratios for the NC-3, NC-10, and NC-17, respectively. This phenomenon manifests that there is an increase in physical crosslinking within the polymer network due to the hydrophobic aggregation of PNIPAM chains which creates more crosslink sites between PNIPAM chains and NC when the temperature is above LCST.42 We further explored the swelling and deswelling behaviors for NC-PNIPAM with different concentrations of NC by gel weight fractions, η = (W23 − Wdry)/(W50 − Wdry), where W23 and W50 is the weight of hydrogel equilibrated at 23 or 50 °C, respectively, Wdry is the weight of the dried hydrogel. The values of η indicate the water absorption ability per unit hydrogel weight between swelling and deswelling states. The result in Table 1 reveals that η has an overall similar trend with the linear swelling ratios in Fig. 1b as η decreases by increasing NC concentration. Next, we measured the Young's moduli of NC-3, NC-10, and NC-17 from the swelled state until the fifth reswelled state (RS5) using nanoindentation to characterize the mechanical properties based on the concentration of NC and the number of DS–RS cycle. Unlike conventional tensile testing, nanoindentation measures the Young's modulus of samples submerged in water at a controlled temperature, so the results were not affected by changes in the swelling ratio due to temperature changes or water evaporation during the measurement. The Young's modulus of NC-PNIPAM increases as NC concentration increases (Fig. 1c), similar to previously reported data, due to the increase in crosslinking density.43 The Young's modulus continuously increased from the initial swelled state until reaching the third reswelled state (RS3), where NC-3 increased 420% from 0.49 kPa to 2.5 kPa, NC-10 increased 830% from 3.7 kPa to 19 kPa, and NC-17 increased by 1590% from 14 kPa to 230 kPa. Note that the Young's modulus of NC-10 and NC-17 for RS5 are 27.3 ± 11.6 kPa and 258 ± 84.1 kPa, respectively. They are slightly offset to Young's modulus of NC-10 and NC-17 for RS4 as 44.3 ± 26 kPa and 225 ± 81.4 kPa, respectively, but still within the range of the standard deviation of the fourth cycle. We hypothesize that this offset is due to the presence of local aggregation of the NC through DS–RS cycles.
Compsite hydrogel | NC-3 | NC-10 | NC-17 |
---|---|---|---|
η | 19.4 ± 2.4 | 2.16 ± 0.10 | 1.01 ± 0.02 |
X-ray diffraction (XRD) characterization and transmittance characterization provide insight into the evolving internal interactions of NC-PNIPAM hydrogels during the DS–RS cycles. The XRD peak intensities between the NC-X-S and NC-X-RS3 samples were analyzed using the Bragg equation, nλ = 2dsinθ, where n is the diffraction order, λ is the wavelength, d is the lattice spacing, and θ is the incident angle.44 Based on the values of 2θ, the d-spacings decrease from NC-3-S = 4.37 nm, NC-10-S = 3.47 nm, and NC-17-S = 2.89 nm to NC-3-RS3 = 4.09 nm, NC-10-RS3 = 3.08 nm, and NC-17-RS3 = 2.72 nm, respectively (Fig. 1d). The result shows the interparticle distance of NC decreases through the DS–RS cycles. This indicates a structural rearrangement is occurring in NC-PNIPAM hydrogels through the DS–RS cycles. Furthermore, through ultraviolet-visible (UV-Vis) spectroscopy examination of NC-X-S and NC-X-RS3, the transmittance decreases from NC-10-S = 37% to NC-10-RS3 = 28% and from NC-17-S = 18% to NC-17-RS3 = 13% while the change in transmittance of NC-3 is not statistically significant (Fig. 1e). In addition, this change in transparency agrees with optical images shown in Fig. S3.† Initially, the transparency of NC-PNIPAM hydrogels after polymerization decreases as the NC concentration increases due to the aggregation of NC.45 After DS–RS cycles, the further decreasing of the transmittance of NC-PNIPAM hydrogels could be correlated with an increase in inhomogeneity of the crosslinking in the polymer networks through the rearrangement and aggregation of the NC.46 This result agrees with the XRD data which indicates the decreasing of interparticle spacing between NC through DS–RS cycles.
To further explain the changes in swelling ratio and the Young's modulus of NC-PNIPAM hydrogels through the DS–RS cycles. We correlated the structural rearrangement of the NC-PNIPAM hydrogels with different NC concentrations by the interparticle spacing L and with the diameter of NC (dNC = 30 nm). Here, L is expressed as:47
The internal microstructures of NC-PNIPAM hydrogels with different concentrations of NC in either the swelled or reswelled state were investigated utilizing scanning electron microscopy (SEM). The NC-X-S and NC-X-RS1 samples were freeze-dried for SEM imaging, following the procedure and analysis detailed in the SEM section of the ESI.† The average pore sizes of diameter decrease from NC-3-S = 14.3 ± 4.7 μm to NC-3-RS1 = 3.4 ± 1.1 μm, from NC-10-S = 17.2 ± 7.8 μm to NC-10-RS1 = 12.7 ± 4.2 μm, and from NC-17-S = 4.7 ± 3.6 μm to NC-17-RS1 = 4.5 ± 4.1 μm (Fig. 3). The decreasing pore size is caused by increasing physical crosslinking points between NC and PNIPAM chains.47 According to the SEM images, the pore size of the NC-3 samples significantly decreased from the swelled state (S) to the reswelled state (RS). NC-10 and NC-17 showed trivial changes in pore size, but increases in inhomogeneity through the DS–RS cycles (Fig. S5†). Therefore, the energy-dispersive X-ray spectroscopy (EDX) analysis was performed to map the element distribution of NC in PNIPAM. Mg and Si were selected to represent NC (chemical formula H12Li2Mg16Na2O72Si24). The distribution of NC is highly uniform in NC-3-RS2 whereas NC is aggregated in NC17-RS2 (Fig. S6†). Such results support the mechanisms that the self-strengthening is dominated by the increasing crosslinking points between PNIPAM chains and NC for the low concentration of NC (i.e., NC-3) shown in Fig. 2. However, when the concentration of NC is high (i.e., NC-10 and NC-17), the aggregations of NC lead to the self-strengthening thus their Young's moduli still improve without pronounced pore size change through DS–RS cycles.
Next, we investigated the effect of the ionic strength of the surrounding aqueous environment on the swelling ratio and Young's modulus of NC-PNIPAM to observe the self-strengthening behavior in response to ionic strength. After the NC-X-S hydrogels were placed in the 0.01 M KCl for at least 24 hours at 23 °C, their swelling ratio and Young's modulus were measured. Similar to the results of DS–RS cycles, the swelling ratios of NC-PNIPAM hydrogels reduced after KCl treatment by 20%, 36% and 11% for NC-3, NC-10 and NC-17, respectively (Fig. 4a). Furthermore, the Young's modulus increased by 117%, 795% and 278% for NC-3, NC-10 and NC-17, respectively (Fig. 4b), which indicates NC-PNIPAM hydrogels are strengthened by the KCl treatment. We note that the 0.01 M KCl concentration was chosen since it can significantly improve the Young's modulus of NC-PNIPAM hydrogels but not significantly affect the LCST of PNIPAM.52,53 The self-strengthening mechanism for NC-PNIPAM hydrogels by the KCl treatment is both due to the reduced Debye screening length (λD) (Fig. 4c) and the enhanced ionic interaction between NC and PNIPAM chains. Through the permeation of ions, the NC disks are brought closer to each other with a reduced λD, which drives water expelling due to osmotic pressure and the NC-PNIPAM hydrogel is thus less swelling.54 Furthermore, the addition of K+ ions can be absorbed on the negatively charged NC surface and then bonded with the CO groups on the PNIPAM chains.52 Therefore, NC-PNIPAM hydrogels prepared in a salt-free environment undergo a self-strengthening process by increasing the crosslinking density while placed in a salt solution.
We further explored the mechanical properties of NC-X-S, NC-X-RS1, and NC-X KCl through tensile tests and loading tests to understand the self-strengthening effect on the bulk behaviors of NC-PNIPAM. Note that NC-3 was excluded from these bulk experiments since it was not strong enough to undergo tensile and loading tests without deforming or breaking during setup. The toughness and Young's modulus of NC-10 and NC-17 can be deduced from the bulk tensile tests (Fig. 5a). The toughness of NC-10 increased from NC-10-S = 0.063 mJ m−3 to NC-10 KCl = 0.13 mJ m−3 or NC-10-RS3 = 0.18 mJ m−3. The toughness of NC-17 increased from NC-17-S = 0.13 mJ m−3 to NC-17 KCl = 0.24 mJ m−3 or NC-17-RS3 = 0.19 mJ m−3. The increases in toughness of NC-PNIPAM hydrogels through DS–RS cycles and KCl treatment, respectively, indicate that the self-strengthening effect increases the amount of energy NC-PNIPAM can absorb without breaking. The Young's modulus of bulk NC-PNIPAM hydrogels increased by 42% from NC-10-S to NC-10 KCl, 105% from NC-10-S to NC-10-RS3, 95% from NC-17-S to NC-17 KCl and 184% from NC-17-S to NC-17-RS3. The increase in toughness and Young's modulus measured by the bulk tensile test indicates that NC-PNIPAM self-strengthens in response to both DS–RS cycles and exposure to 0.01 M KCl. The average ultimate tensile strength (UTS) was determined by the highest tensile strength achieved by NC-PNIPAM samples before failure. The UTS of NC-PNIPAM hydrogel increases after both the DS–RS cycle and KCl treatment, respectively (Fig. 5b). The average elongation at break was determined by the largest tensile strain achieved before sample failure. This value either remains nearly the same after the third DS–RS cycle and increases when the NC-X-S sample is treated with the 0.01 M KCl salt solution (Fig. 5c). The increase in the mechanical properties can be attributed to the increase in overall crosslinking density within NC-PNIPAM hydrogels after undergoing DS–RS cycles or KCl treatments. We attribute the higher elongation at break values of NC-X KCl hydrogels to the trapping of nonporous surface structures in water as PNIPAM chains collapse above their LCST, producing voids deeper within NC-PNIPAM where free water aggregates, resulting in a more heterogeneous structure.26 The load-bearing test demonstrates the variation in elongation length holding the same weight. These hydrogels were cut into rectangular thin strips with a width of 1 cm, length of 6.35 cm, and thickness of 1 mm in the as-prepared state. The NC-10 samples could each support a 37 g load and the length of the sample was reduced by 13% after being treated with 0.01 KCl and 20% after undergoing DS–RS cycles compared to the swelled state (Fig. 5d). The NC-17 samples can support 117 g and the length of the sample was reduced by 30% after undergoing a DS–RS cycle and 47% after being treated with 0.01 M KCl, compared to the swelled state (Fig. 5e). Furthermore, when 5 strips of NC-17 samples are stacked, they can support a combined total mass of 738 g, which is 6.3 times more than the single NC-17 strip (Fig. 5f). Our samples can fully recover to their original length within a few minutes due to a relatively small deformation (strain <150%). Therefore, utilizing multiple layers of NC-17 enhances the strength, like a muscle, to support a higher combined total mass.
Footnotes |
† Electronic supplementary information (ESI) available: Experimental sections and figures. See DOI: https://doi.org/10.1039/d2nr05408f |
‡ These authors contributed equally. |
This journal is © The Royal Society of Chemistry 2022 |