Non-stoichiometry, structural defects and properties of LaMnO_3+δ with high δ values (0.11≤δ≤0.29)

Abstract

Strongly oxygenated LaMnO_3+δperovskites, with nominal Mn^IV contents up to 58%, have been prepared by thermal decomposition of metal citrates followed by annealings either in air or under high oxygen pressure (200 bar). A high-resolution neutron powder diffraction study of four representative samples with 0.11≤δ≤0.29 reveals the presence of both La and Mn vacancies. Contrary to previous studies, it is found that there are a substantially higher proportion of Mn vacancies, depending rather sensitively on the oxidation conditions. The oxidation state for Mn calculated for the refined stoichiometry La_1–xMn_1–yO₃ is in good agreement with the δ values previously determined by thermal analysis. Further to this, it is also found that as δ increases the Mn–O bond lengths shorten, the Mn–O–Mn angles progressively increase and the perovskite structure becomes more regular, which is consistent with the incorporation of Mn^IV cations. The presence of Mn vacancies (as much as 13% in samples prepared under high oxygen pressure) perturbs the conduction paths for the transport of holes across Mn–O–Mn, weakening the double-exchange interaction. This structural disorder explains the observed decrease of the ferromagnetic Curie temperature (T_C) as δ increases.

References

1. G. H. Jonker and J. H. Van Santen, Physica, 1950, 16, 337.
2. E. O. Wollan and W. C. Koeler, Phys. Rev., 1955, 100, 545.
3. R. von Helmholt, J. Wecker, B. Holzapfel, L. Schultz and K. Samwer, Phys. Rev. Lett., 1993, 71, 2331.
4. G. H. Rao, J. R. Sun, Y. Z. Sun, Y. L. Zhang and J. K. Liang, J. Phys: Condens. Matter., 1996, 8, 5393.
5. B. C. Hauback, H. Fjellvag and N. Sakai, J. Solid State Chem., 1996, 124, 43.
6. J. B. A. A. Elemans, B. Van Laar, K. R. Van der Veen and B. O. Loopstra, J. Solid State Chem., 1971, 3, 238.
7. P. Norby, I. G. K. Andersen, E. K. Andersen and N. H. Andersen, J. Solid State Chem., 1995, 119, 191.
8. R. Mahendiran, S. K. Tiwary, A. K. Raychadhuri, T. V. Ramakrisnan, R. Mahesh, N. Raganvittal and C. N. R. Rao, Phys. Rev. B, 1996, 53, 3348.
9. C. N. R. Rao and A. K. Cheetham, Science, 1996, 272, 369.
10. A. Wold and R. J. Arnott, J. Phys. Chem. Solids, 1959, 9, 176.
11. J. Töpfer, J. P. Doumerc and J. C. Grenier, J. Mater. Chem., 1996, 6, 1511.
12. B. C. Tofield and W. R. Scott, J. Solid State Chem., 1974, 10, 183.
13. J. A. M. Van Roosmalen, E. H. P. Cordfunke, R. B. Helmholdt and H. W. Zandbergen, J. Solid State Chem., 1994, 110, 100.
14. J. A. M. Van Roosmalen and E. H. P. Cordfunke, J. Solid State Chem., 1994, 110, 106.
15. J. A. Alonso, M. J. Martínez-Lope and M. T. Casais, Eur. J. Solid State Inorg. Chem., 1996, 33, 331.
16. H. M. Rietveld, J. Appl. Crystallogr., 1969, 2, 65.
17. J. Rodríguez-Carvajal, Physica B, 1993, 192, 55.
18. J. L. García-Muñoz, J. Rodríguez-Carvajal, P. Lacorre and J. B. Torrance, Phys. Rev. B, 1992, 46, 4414.
19. R. D. Shannon, Acta Crystallogr. Sect. A, 1976, 32, 751.
20. I. D. Brown, in Structure and Bonding in Crystals, ed. M. O'Keefe and A. Navrotsky, New York, 1981, vol. 2, pp. 1–30.
21. N. E. Brese and M. O'Keefe, Acta Crystallogr. Sect. B, 1991, 47, 192.
22. P. S. I. P. N. de Silva, F. M. Richards, L. F. Cohen, J. A. Alonso, M. J. Martínez-Lope, M. T. Casais, T. Kodenkandath and J. L. MacManus-Driscoll, J. Appl. Phys., submitted.
23. J. A. Alonso, M. J. Martínez-Lope, M. T. Casais and A. Muñoz, Solid State Commun., 1997, 102, 7.
24. L. Ranno, M. Viret, A. Mari, R. M. Thomas and J. M. D. Coey, J. Phys: Condens. Matter, 1996, 8, L33.
25. J. Fontcuberta, B. Martínez, A. Seffar, S. Piñol, J. L. García-Muñoz and X. Obradors, Phys. Rev. Lett., 1996, 76, 1122.