Heteroatom dopings and hierarchical pores of graphene for synergistic improvement of lithium–sulfur battery performance

Abstract

Lithium–sulfur batteries have attracted wide research interest due to their high specific capacity (1675 mA h g−1) and high specific energy (2500 W h kg−1). Herein, the two-dimensional nitrogen/sulfur synchronous-doped few-layer graphene (N,S-FLG) was prepared by a simple calcination route at 900 °C under an argon atmosphere with g-C3N4 as a structural template. The calcination temperature favorably adjusted the doping levels and surface texture of the as-obtained samples. Relying on the synergistic interaction of the structural traits, as the reservoir of sulfur, NS-FLG-900 (calcination temperature 900 °C) can maintain a reversible capacity of 602 mA h g−1 after 300 cycles at a current density of 0.8 A g−1 and 506.4 mA h g−1 after 500 cycles at a current density of 1.6 A g−1. The outstanding performance is obtained due to the synergistic effect of the introduction of N and S into the carbon lattice, the high pore volume (1.31 cm3 g−1) and large specific surface area (460.9 m2 g−1).

Graphical abstract: Heteroatom dopings and hierarchical pores of graphene for synergistic improvement of lithium–sulfur battery performance

Supplementary files

Article information

Article type
Research Article
Submitted
21 Şub 2018
Accepted
12 Mar 2018
First published
12 Mar 2018

Inorg. Chem. Front., 2018,5, 1053-1061

Heteroatom dopings and hierarchical pores of graphene for synergistic improvement of lithium–sulfur battery performance

J. Li, C. Xue, B. Xi, H. Mao, Y. Qian and S. Xiong, Inorg. Chem. Front., 2018, 5, 1053 DOI: 10.1039/C8QI00160J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements