Issue 24, 2016

Reversible control of the chromium valence in chemically reduced Cr-doped SrTiO3 bulk powders

Abstract

The effect of chemical reduction by NaBH4 on the electronic structure of Cr-doped SrTiO3−δ bulk powders prepared by a solid-state reaction was systematically studied as a function of reduction temperature. Electron paramagnetic resonance (EPR) and diffuse reflectance spectroscopies (DRS) were utilized to monitor changes in the electronic structures of both intrinsic defects (oxygen vacancies and/or Ti3+) and extrinsic dopants (Cr3+) at different reduction temperatures. We identify the existence of two temperature regimes where changes occur within 30 min. The first temperature regime occurs between 300–375 °C and results in (1) reduction of oxygen-related surface defects, and (2) an increase in the concentration of Cr3+ by over an order of magnitude, suggesting that EPR-silent Cr4+ or Cr6+ is being reduced to Cr3+ by NaBH4. The second temperature regime occurs between 375–430 °C where we observe clear evidence of Ti3+ formation by EPR spectroscopy that indicates chemical reduction of the SrTiO3 lattice. In addition, the oxygen-related surface defects observed in regime 1 are not formed in regime 2, but instead lattice oxygen vacancies (VO) are observed by EPR. The changes to the Cr-doped SrTiO3 electronic structure after chemical reduction in regime 1 are quantitatively reversible after aerobic annealing at 400 °C for 30 min. The internal oxygen vacancies formed during the higher temperature reductions in regime 2 require increased temperatures of at least 600 °C to be fully reoxidized in 30 min. The effect of these different oxygen-related defects on the EPR spectrum of substitutional Cr3+ dopants is discussed. These results allow us to independently tune the dopant and host electronic structures of a technologically-relevant multifunctional material by a simple ex situ chemical perturbation.

Graphical abstract: Reversible control of the chromium valence in chemically reduced Cr-doped SrTiO3 bulk powders

Supplementary files

Article information

Article type
Paper
Submitted
23 ก.พ. 2559
Accepted
17 เม.ย. 2559
First published
27 เม.ย. 2559

Dalton Trans., 2016,45, 10034-10041

Reversible control of the chromium valence in chemically reduced Cr-doped SrTiO3 bulk powders

K. A. Lehuta and K. R. Kittilstved, Dalton Trans., 2016, 45, 10034 DOI: 10.1039/C6DT00706F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements