Novel surfactant-free route to delaminated all-silica and titanosilicate zeolites derived from a layered borosilicate MWW precursor

Abstract

Layered borosilicate zeolite precursor ERB-1P (Si/B = 11) is delaminated via simultaneous deboronation and SDA removal, to yield material DZ-1 consisting of silanol nests, using a simple aqueous Zn(NO3)2 treatment. Characterization of this synthesis process by PXRD shows loss of long-range order, and transmission electron microscopy (TEM) demonstrates transformation of rectilinear layers in the layered zeolite precursor to single and curved layers in the delaminated material. N2 physisorption confirms the expected decrease of micropore volume and increase in external surface area for delaminated materials relative to their calcined 3D zeolite counterpart. Elemental analysis shows loss of B and absence of Zn in the delaminated material. Resonances corresponding to silanol nests are evident via29Si solid-state NMR spectroscopy in DZ-1, which should be located within 12-MR pockets near the external surface. We have successfully utilized these nests as tetrahedral recognition sites for incorporation of Ti within an isolated framework coordination environment in material Ti-DZ-1. Diffuse-reflectance ultraviolet (DR-UV) spectroscopy of Ti-DZ-1 confirms isolated framework Ti sites, which are assigned to bands in the range of 210 nm–230 nm. Infrared spectra of Ti-DZ-1 consist of a distinct absorption band at 960 cm−1, which is absent in DZ-1 prior to Ti incorporation and has been previously correlated with the presence of framework Ti species. Infrared spectra after pyridine adsorption demonstrate bands consistent with Lewis-acid sites in the resulting Ti-substituted delaminated zeolite. The accessibility of these Lewis-acid sites is confirmed when using Ti-DZ-1 as a catalyst for cyclohexene epoxidation using tert-butyl hydroperoxide as the organic oxidant – a reaction for which both DZ-1 and TS-1 are inactive.

Graphical abstract: Novel surfactant-free route to delaminated all-silica and titanosilicate zeolites derived from a layered borosilicate MWW precursor

Supplementary files

Article information

Article type
Paper
Submitted
05 ก.พ. 2557
Accepted
19 มี.ค. 2557
First published
19 มี.ค. 2557

Dalton Trans., 2014,43, 10417-10429

Author version available

Novel surfactant-free route to delaminated all-silica and titanosilicate zeolites derived from a layered borosilicate MWW precursor

X. Ouyang, Y. Wanglee, S. Hwang, D. Xie, T. Rea, S. I. Zones and A. Katz, Dalton Trans., 2014, 43, 10417 DOI: 10.1039/C4DT00383G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements