Li-Mei
Chang
ab,
Zhi-Zhou
Ma
ab,
Jiandong
Huang
a and
Zhi-Gang
Gu
*bcd
aCollege of Chemistry, Fuzhou University, Fuzhou, Fujian 350108, China
bState Key Laboratory of Structural Chemistry, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, Fuzhou, Fujian 350002, China. E-mail: zggu@fjirsm.ac.cn
cInstitute of Functional Interfaces (IFG), Karlsruhe Institute of Technology (KIT), 76344, Eggenstein-Leopoldshafen, Germany
dFujian Science & Technology Innovation Laboratory for Optoelectronic Information of China, Fuzhou, Fujian 350108, China
First published on 29th December 2022
The development of multiple metal–organic framework (MOF) thin films with high lattice mismatch is still a challenging task. Herein we report a series of single and multiple (bi-varietal and tri-varietal) pillar-layered MOF thin films (surface-coordinated MOF thin films, SURMOFs) [Cu2L2dabco]n (L = bdc, bpc and tpdc) with preferred [001]-orientation on the substrate surfaces using a liquid-phase epitaxial (LPE) layer by layer pump method. The single SURMOFs with the same c-lattice parameters but different a- and b-lattice parameters result in the successful growth of oriented multiple SURMOFs with high lattice mismatch (up to 77.8%). The vapor adsorption results show that the representative bi-varietal SURMOF with large lattice mismatch has different adsorption behavior from single SURMOFs, providing a new strategy to achieve tuning of the adsorption kinetics performance in sensing applications.
In the last decade, MOF thin films have been greatly prepared due to their large surface active sites, conveniently accessible in sensing and device applications.25–32 Among the preparation methods of MOF thin films, the liquid-phase epitaxial (LPE) layer by layer method is realized for use in growth of MOF thin films (also called surface-coordinated MOF thin films, SURMOFs) on functionalized substrates, displaying unique features including high degree of controlled growth orientation, tunable thickness, and good homogeneity.23,33–36 Recently, although some multiple MOF thin films have been reported,34 obtaining multiple MOF thin films with high lattice mismatch is still a challenging task.
For preparing multiple MOF thin films with high lattice mismatch, in this work, a liquid phase epitaxy (LPE) layer by layer pump procedure (Scheme S1†) was used to yield oriented MOF thin films (referred to as SURMOFs). A series of multiple 3D MOF thin films are constructed from three isoreticular pillar-layered MOFs [Cu2L2dabco]n,38,39 [Cu2bdc2dabco]n (SURMOF-a) (bdc = 1,4-benzenedicarboxylate and dabco = diazabicyclo[2,2,2]octane), [Cu2bpdc2dabco]n (SURMOF-b) (bpdc = biphenyl-4,4′-dicarboxylate), and [Cu2tpdc2dabco]n (SURMOF-c) (tpdc = terphenyl-4,4-dicarboxylate). These MOFs are constructed from classic Cu2+ “paddle-wheel” units connected with three linear dicarboxylic acid ligands (H2bdc, H2bpdc, and H2tpdc) to form layers along the [001] plane pillared by bitopic N-containing linkers as shown in Scheme 1. SURMOF-a and SURMOF-b have the same c-lattice parameters but 38.6% lattice mismatch in a- and b-lattice parameters while SURMOF-a and SURMOF-c have 77.8% lattice mismatch. They were selected to prepare the heterostructural SURMOFs on 11-mercapto-1-undecanol (MUD) SAM modified Au surfaces.40 Using a home-made LPE layer by layer pump instrument,41,42 mono-varietal SURMOFs (SURMOF-a, SURMOF-b, and SURMOF-c), bi-varietal SURMOFs (SURMOF-b on a, SURMOF-c on a, SURMOF-a on b, SURMOF-c on b, SURMOF-a on c, and SURMOF-b on c), and tri-varietal SURMOFs (SURMOF-a on b on c, and SURMOF-c on b on a) with preferred [001]-orientation can be successfully prepared on the substrate surfaces. Since the length of a-lattice parameter (a2) in SURMOF-b is close to that of √2a1 (a-lattice parameter in SURMOF-a), the a3 (a-lattice parameter in SURMOF-c) is close to that of √2a2, and they have similar c-lattice parameters, and the MOF-on-MOF showed diagonal growth (see Scheme 1, bottom), leading to large lattice mismatch (38.6% and 77.8%). The quartz crystal microbalance (QCM) uptakes of ethoxyethane and mesitylene show that the multiple SURMOF has different adsorption behavior from single SURMOFs, demonstrating that the synergistic effect of the multiple SURMOF with large lattice mismatch has the advantage of tuning the adsorption kinetics performance, which provides new platforms to combine multiple functional MOF thin films for extending their sensing applications.
Pillar-layered SURMOFs [Cu2L2dabco]n (L = bdc, bpc and tpdc) consist of dicarboxylic acids, H2bdc, H2bpdc and H2tpdc as layers and dabco as the pillar. The pore size of 3D SURMOFs [Cu2L2dabco]n grown on substrate surfaces can be tuned by choosing appropriate dicarboxylate ligands. It's noted that a well-known binuclear “paddle-wheel” copper carboxylate complex [Cu2(COO)4N2] is in this series of SURMOFs, resulting in the formation of a 2D [Cu2L2]n layer.37 The linear N-donor ligand dabco is coordinated to the Cu empty axial centers, forming a pillar that is perpendicular to [Cu2L2]n layers (Fig. 1a, b and c). The 3D pillar-layered isostructural SURMOFs possessed different lattice cells with the same c-lattice parameter. The lattice cell parameters are 10.8 × 10.8 × 9.5 Å3 for [Cu2bdc2dabco]n, 14.9 × 14.9 × 9.5 Å3 for [Cu2bpdc2dabco]n, and 19.2 × 19.2 × 9.5 Å3 for [Cu2tpdc2dabco]n. The growth orientation of isostructural SURMOFs is along [001], which is shown in the XRD data in Fig. 1d, e and f.
Fig. 1 The structure of mono-varietal SURMOFs: (a) SURMOF-a; (b) SURMOF-b; (c) SURMOF-c; the out-of-plane and in-plane XRD pattern of SURMOFs: (d) SURMOF-a; (e) SURMOF-b; (f) SURMOF-c. |
It has been demonstrated that self-assembled monolayers (SAMs) containing functional groups are specially used as nucleation sites for epitaxial growth of MOF thin films.43,44 The pillar-layered SURMOFs [Cu2L2dabco]n can be easily grown on the SAM surfaces by using the LPE layer by layer approach.45–48 Since the preparation procedures of isoreticular SURMOFs (Fig. 2a, b and c) are similar, the preparation of SURMOF-a is described in detail. The OH-group functionalized Au substrate (Fig. S1†) was subsequently filled with Cu(OAc)2 and H2L/dabco (L = bdc, bpc and tpdc) ethanolic solutions in the sample cell of the pump system for 30 min at 50 °C. There was 2 min ethanol washing in each step. Then 30 repeated cycles of preparation process resulted in the formation of homogeneous SURMOF-a, -b, -c. Out-of-plane XRD patterns (Fig. 1d) showed two clear diffraction peaks located at 9.26° and 18.52°, corresponding to the (001) and (002) diffraction peaks in the XRD patterns simulated. The in-plane XRD patterns showed distinct peaks at 8.18°, 11.58°, 16.36°, and 18.34°, which are related to the (100), (1–10), (200), and (210) peaks. The high-quality out-of-plane and in-plane XRD patterns as well as the small width of the diffraction peaks clearly revealed the successful growth of highly crystalline SURMOF-a with its [001]-direction perpendicular to the substrate surface. Similarly, two clear peaks are located at the (001) and (002) diffraction peaks in the out-of-plane XRD patterns of SURMOF-b and SURMOF-c, respectively. The in-plane XRD peaks at 5.92°, 11.84°, 15.16°, and 17.78° are related to the (100), (001), (020), and (210) peaks (Fig. 1e) of SURMOF-b, while the distinct peaks at 4.62°, 9.24°, 13.78°, and 18.48° are related to the (100), (200), (300), and (400) peaks (Fig. 1f) of SURMOF-c, which clearly revealed the successful growth of highly crystalline SURMOF-b and SURMOF-c with their [001]-orientation. The IR spectra (Fig. S2†) of SURMOF-a exhibited two characteristic bands centred at 1628 cm−1, which can be assigned to the COO vibrations of the carboxylate groups of the bdc linker, and provide additional evidence of the successful growth of SURMOF-a. Similarly, the IR spectra (Fig. S3 and 4†) of SURMOF-b (1624 and 1420 cm−1) and SURMOF-c (1590 and 1425 cm−1) revealed the symmetric and asymmetric –COO vibrations of the carboxylate groups from bpdc and tpdc linkers, and provide additional evidence of the successful growth of SURMOF-b and SURMOF-c. In addition, the surface SEM images (Fig. 2d and e) of the single (mono-varietal) SURMOFs prepared with 30 cycles clearly revealed homogeneous thin films.
Fig. 2 (a) Preparation process of SURMOF-c on a; out-of-plane (b) and in-plane XRD patterns (c) and SEM images (d and e) of SURMOF-c on a. |
For further preparation of heterostructural (bi-varietal and tri-varietal) MOF thin films, the LPE layer by layer pump method was still used to prepare multiple SURMOFs. Briefly, the pre-prepared SURMOF-a was used as the growth substrate, and then this layer by layer pump process allows us to separately control the Cu(OAc)2 and organic linker H2tpdc deposition on the SURMOF-a to form SURMOF-c on a (Fig. 2a). The out-of-plane XRD patterns (Fig. S6b†) of SURMOF-c on a showed a strong diffraction peak at 9.36° and weak peak at 18.80° corresponding to (001) and (002) diffraction peaks in the simulated XRD patterns (Fig. 2c). In addition, the related in-plane XRD patterns (Fig. 2c) contained both in-plane XRD peaks of SURMOF-a and SURMOF-c. These XRD patterns clearly displayed the successful growth of SURMOF-c on a with high crystallization along [001]-orientation on the functionalized substrate surface. The other bi-varietal SURMOFs (SURMOF-a on b, SURMOF-a on b, SURMOF-c on a, SURMOF-a on c, and SURMOF-b on c) can be prepared successfully using the same process, which can be demonstrated by the XRD, SEM and IR data (see Fig. S6–11†). Furthermore, the tri-varietal SURMOF (SURMOF-c on b on a) was also prepared by using the LPE layer by layer pump method (Fig. 3a). The pre-prepared SURMOF-a was used as the growth substrate, and then the Cu(OAc)2 and organic linker H2bpdc were separately deposited on the SURMOF-a (30 cycles) to form SURMOF-b on a. Finally, Cu(OAc)2 and organic linker H2tpdc were separately deposited on the top of SURMOF-b on a to further form SURMOF-c on b on a. The successful growth was demonstrated by out-of-plane XRD patterns (Fig. 3b and c). The XRD pattern data clearly revealed that SURMOF-c on b on a possessed high [001] growth orientation. Meanwhile, the tri-varietal SURMOF SURMOF-a on b on c was successfully prepared using the same strategy as shown in Fig. S12 and 13.† The related IR spectra (Fig. S14†) of tri-varietal SURMOFs revealed their symmetric and asymmetric –COO vibrations from the carboxylate groups of the organic linkers.
Fig. 3 (a) Preparation process of SURMOF-c on b on a; out-of-plane (b) and in-plane XRD patterns (c) of SURMOF-c on b on a. |
To better understand the mismatched lattice of the heterostructural SURMOFs, we calculated the lattice mismatch by using the unit cell parameters of the mono-varietal SURMOFs. The a1, a2 and a3 are the lattice distances of SURMOF-a, SURMOF-b and SURMOF-c, respectively. Interestingly, the length of a2 is close to that of √2a1, while the length of a3 is close to that of √2a2 (Fig. S15†). Since SURMOF-a and SURMOF-b have the same c-lattice parameter, the lattice mismatch [(a2 − a1)/a1] is calculated to be 38.6% in a- and b-lattice parameters. It's noted that the lattice mismatch [(a3 − a1)/a1] between SURMOF-a and SURMOF-c was calculated to be 77.8%, which was much higher than that of the reported hetero-MOF materials.
The highly oriented, well-defined multiple SURMOFs can offer unique adsorption properties toward guest molecules. In this work, a quartz crystal microbalance (QCM) with a sensing chip is a promising option for this adsorption kinetic study.49–51 Herein the representative mono-varietal (SURMOF-a and SURMOF-c) and multiple SURMOFs (SURMOF-c on a) were prepared on MUD modified Au QCM electrodes for 30 cycles using the same process. Two kinds of guest molecules ethoxyethane (chain-shape with a size of ∼1.0 × 7.0 Å2) and mesitylene (diameter of ∼7.0 Å) with different sizes were selected as the probe molecules since both of them hardly have interactions with SURMOFs and their sizes are largely different. As shown in Fig. 4a, both SURMOFs had high mass uptakes of ethoxyethane, which were calculated to be ∼177 μg cm−2 for SURMOF-a and ∼144 μg cm−2 for SURMOF-c, respectively. To further evaluate the adsorption kinetics, the uptake amount m(t) can be described by an exponential decay equation: m(t) = meq(1 − exp(−t/τ), where τ denotes the time constant, meq is the equilibrium adsorption and t is the adsorption time. After fitting the uptake curves with the nonlinear exponential equation, the time constant (τ) of ethoxyethane adsorption in SURMOF-a was 1146 s, which was much slower than the adsorption time (404 s) in SURMOF-c. Using the same uptake testing process in the mesitylene adsorption (Fig. 4b) of SURMOF-a and SURMOF-c, the mass uptake in SURMOF-a was calculated to be ∼330 μg cm−2, while that in SURMOF-c was very low (∼26 μg cm−2), which can be attributed to that the pore size (square shape with a size of ∼6.7 × 6.7 Å2 calculated from the space filling model) of SURMOF-a is close to the size of mesitylene. In order to study the adsorption kinetic performance of multiple SURMOFs, the representative bi-varietal SURMOF-c on a (15 cycles SURMOF-c on 15 cycles SURMOF-a) was studied. Interestingly, the kinetics adsorption curve of mixed ethoxyethane and mesitylene (1:1 v/v%) on SURMOF-c on a is not like that of any of the mono-varietal SURMOFs (Fig. 4c); two distinct stages in terms of kinetic adsorption rate can be divided. The first uptake stage is mainly caused by the chain-shaped ethoxyethane with small size, which reached the adsorption capacity of ∼86 μg cm−2 with fast diffusion (∼3 s). In the second stage, the adsorption rate was much slower than that in the first stage, which can be attributed to the main adsorption of large size mesitylene on the SURMOF-c layer, causing slow pore diffusion of guest molecules. Finally the total amount of the uptake reached ∼245 μg cm−2. To understand the adsorption mechanism, the diffusion models of guest molecules in the SURMOFs are shown in Fig. 4d. Since the pore size of SURMOF-a is smaller than that (square shape with a size of ∼11.0 × 11.0 Å2 calculated from the space filling model) of SURMOF-c, the small size ethoxyethane has a faster diffusion in SURMOF-c than in SURMOF-c. The size of mesitylene is close to the pore size of SURMOF-a but smaller than that of SURMOF-c, resulting in a huge adsorption difference. Furthermore, the SURMOF-c on a with hierarchical pores possessed unique molecule diffusion behavior—first fast diffusion of small molecule ethoxyethane and then slow diffusion of large molecule mesitylene. The advantage of multiple SURMOFs with large lattice mismatch is that the synergistic effect emanated from the different MOF thin films could significantly tune the adsorption kinetic performance.
Footnote |
† Electronic supplementary information (ESI) available. See DOI: https://doi.org/10.1039/d2qi02464k |
This journal is © the Partner Organisations 2023 |