Sublimation-doping with super bases for high-performance solution-processed heterojunction oxide thin film transistors

Abstract

We elucidate how non-destructive sublimation-doping of In2O3/ZnO heterojunctions with various amidine-based organic dopants affects the degree of band bending of the heterojunction and thus the overall performance of solution-processed heterojunction oxide thin-film transistors (TFTs). Ultraviolet photoelectron spectroscopy and X-ray photoelectron spectroscopy analyses show that the stronger the basicity of the dopant, the smaller the ECEF of ZnO that can be induced within a short doping time, resulting in a high electron mobility due to the increased electron density of the In2O3 layer at the vicinity of the heterointerface. Mott–Schottky analysis combined with secondary ion mass spectroscopy shows the preferential modification of ECEF selectively for the ZnO layer. The use of a super base with the highest basicity exhibits a high electron mobility of 17.8 cm2 V−1 s−1 for the SiO2 and 37.8 cm2 V−1 s−1 on average (46.6 cm2 V−1 s−1 maximum) for the ZrO2 dielectric layers and enhanced operational bias-stress stability via sublimation-doping for 6 min, which can be attributed to the trap-filled, percolation-limited charge transport behavior. Reproducibility tests are conducted for more than 50 independently fabricated TFTs using the optimized doping technique, and electron mobility distributions with deviations <±10% are demonstrated. This study shows that sublimation doping with super bases can be a good solution for high mobility oxide TFTs with stability and reliability.

Graphical abstract: Sublimation-doping with super bases for high-performance solution-processed heterojunction oxide thin film transistors

Supplementary files

Article information

Article type
Communication
Submitted
14 Jun 2021
Accepted
27 Ago 2021
First published
31 Ago 2021

Mater. Horiz., 2021,8, 3105-3112

Sublimation-doping with super bases for high-performance solution-processed heterojunction oxide thin film transistors

J. Lee, M. Jae, S. Z. Hassan and D. S. Chung, Mater. Horiz., 2021, 8, 3105 DOI: 10.1039/D1MH00929J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements