DOI:
10.1039/D3TA06257K
(Paper)
J. Mater. Chem. A, 2024,
12, 2796-2806
Multi-mode mechanoluminescence of fluoride glass ceramics from rigid to flexible media toward multi-scene mechanical sensors†
Received
14th October 2023
, Accepted 14th December 2023
First published on 19th December 2023
Abstract
The smart mechanical sensing technology based on mechanoluminescence (ML) has potential applications in the fields of wearable mechanical sensors and remote detection of human health due to its characteristics of non-contact, visualization, and remote signal transmission. Herein, a new strategy for multi-mode ML in a rigid and flexible medium by embedding fluoride nanocrystals (CaF2: Tb3+) in amorphous media was proposed and the intrinsic physical mechanism of energy conversion was clarified. For the rigid transparent CaF2: Tb3+ glass ceramics (GCs), without being fabricated with any special medium, recoverable trap-controlled ML can be generated under friction after X-ray pre-irradiation. Furthermore, the ML composite device fabricated using CaF2: Tb3+ GC powder and flexible stretchable polydimethylsiloxane (PDMS) can achieve self-recovery ML under multimode mechanical stimulation due to the induction of inorganic-organic interface triboelectrification. Finally, rigid accurate stress detection at non-stressed point positions is designed based on the remote transmission of a ML signal owing to the unique optical waveguide effect of GCs, and a flexible mechanical-sensing optical skin for real-time monitoring of human health status is realized by using the CaF2: Tb3+ GC powder/PDMS composite device. This work opens up a new avenue for the realization of multi-scene stress detection based on a rigid/flexible ML material.
1 Introduction
Mechanoluminescence (ML) is a mechanical–optical energy conversion process that occurs under mechanical stimulation, such as compression, stretching, friction, scratching, and impacts, forming a link between luminescence and mechanics,1–11 which has broad applications in visualization,12 non-contact mechanical sensing,13–21 structural health monitoring,22 artificial intelligence skin,23–25 and wearable devices.26,27 Currently, various ML materials have been developed based on the structure composition of the material, mechanical stimulation mode, delocalization/recombination path of the electron–hole pair, fabricating medium of composite devices, and energy conversion modes.28–31 The macroscopic mechanical–optical energy conversion, which is the essential physical mechanism of ML, is an indirect conversion that comprises two or more microscopic energy conversion processes, such as mechanical-electrical and electrical–optical energy conversion. In the ML generation process, an intermediate physical field, such as piezoelectricity/triboelectricity, serves as a bridge for the conversion of mechanical energy to optical energy.6 In addition to the structure and performance of the ML material, the intermediate physical field is often closely related to the mechanical stimulation mode and the type of fabricated medium used in ML devices.
Currently, most ML materials can only generate luminescence using ML phosphors and organic elastomers, such as epoxy resin (ER) and polydimethylsiloxane (PDMS), to form composite devices. These organic elastomers can act as a stress conduction medium, transferring the macroscopic mechanical force received by the ML composite device to the luminescent particles and producing an interface interaction with the luminescent particles when subjected to macroscopic mechanical force or deformation, both of which can determine ML generation. For example, piezoelectric crystal-based luminescent particles can generate piezoelectric ML under stress,1,3 while triboelectric ML can be generated when the triboelectric potential is induced at the interface between the inorganic luminescent particles and organic elastomer medium.32–42
When CaF2: Tb3+ glass ceramics (GCs) were subjected to macroscopic mechanical stimulation as a typical transparent and rigid medium,43–48 generating obvious elastic deformation related to the direction of the stress application was challenging, except for a small amount of elastic deformation in the specific direction of large area glass. Producing ML in such rigid CaF2: Tb3+ GCs is challenging using the existing ML mechanisms. In our previous study, we found that trap-controlled ML was achieved in BaLaF3: Tb3+ GCs after pre-irradiation with a high-energy femtosecond laser, and remote transmission of the ML signal was achieved because of the unique optical waveguide effect of CaF2: Tb3+ GCs, leading to the study of rigid medium ML.49,50 However, the difference in mechanical properties of the rigid and flexible organic media leads to different application prospects for ML. Thus, studying the same material in rigid and flexible media will further promote the popularization and application of ML in CaF2: Tb3+ GCs.
This work investigates the ML performance of CaF2: Tb3+ GCs in their original rigid and flexible device fabricated with PDMS (Fig. 1a). The rigid CaF2: Tb3+ GCs produce recoverable ML under friction after X-ray pre-irradiation. Furthermore, the CaF2: Tb3+ GCs/PDMS composite device can produce recoverable ML under mechanical stimulation. This study provides a detailed examination of ML characteristics and physical mechanisms in different media, proposes the application of CaF2: Tb3+ GCs in various scenarios, and offers theoretical support for the selection of ML materials for different applications.
![image file: d3ta06257k-f1.tif](/image/article/2024/TA/d3ta06257k/d3ta06257k-f1.gif) |
| Fig. 1 (a) Schematic diagram of multimode ML based on CaF2: Tb3+ GCs in different media. (b) XRD patterns of PG and CaF2: Tb3+ GCs. (c) Crystal structure of CaF2. (d) DTA curve of CaF2: Tb3+ GCs. | |
2 Experimental section
2.1 Materials and synthesis
A series of glass samples were prepared by using conventional melting-quenching techniques with specific components. The raw materials B2O3 (99.99%), SiO2 (99.99%), ZnO (99.9%), and Na2CO3 (99.99%) were ground into a powder by using an agate mortar. All chemical reagents were of analytical grade purity and were purchased from Aladdin Chemical Reagents Ltd. The evenly mixed raw material was then placed in an alumina crucible and melted in air at 1200 °C for 15 min. Furthermore, the melt was poured into a 450 °C preheated copper plate and pressed with another copper plate to form precursor glass (PG). The PG sample was cooled to room temperature (RT) and annealed in a muffle furnace to obtain the CaF2: Tb3+ GCs. Finally, the obtained products were cut and polished for further characterization.
2.2 Preparation of the application device
The flexible film was fabricated by dispersing the CaF2: Tb3+ GC powder in polydimethylsiloxane (PDMS, Sylgard 184, Dow Corning). The ML powder (CaF2: Tb3+ GCs, CaF2: Eu3+ GCs, CaF2: Eu2+ GCs) was mixed well with PDMS (1.5
:
2.5) and then uniformly placed on a mold. The mold with the composite was then placed in an oven and heated at 80 °C for 60 min. Then a flexible ML film was fabricated for the measurement (CaF2: Tb3+ GCs/PDMS, CaF2: Eu3+ GCs/PDMS, CaF2: Eu2+ GCs/PDMS).
2.3 Characterization
An X-ray diffraction (XRD) instrument was operated in the range of 10°–80° at 2θ (Bruk BRUKER D2 PHASER, Germany). The photoluminescence (PL) and photoluminescence excitation (PLE) spectra were recorded with a Hitachi F-7000 fluorescence spectrophotometer with a 150 W Xe lamp as the excitation source. The microstructures of the GCs were analyzed using transmission electron microscopy (TEM) and high-resolution field TEM with a JEM-F200 at 200 kV. Sample morphology was investigated by using a scanning electron microscope (SEM) TESCAN VEGA 3 SEM (Tescan China, Ltd). Energy-dispersive spectrum (EDS) and element mapping were obtained by using energy dispersive spectrometer (Ametek Materials Analysis Division). The differential thermal analysis (DTA) curve was recorded with a heating rate of 15 °C min−1 (STA7300, Japan Corporation, Hitachi High-tech Science). The transmission spectrum in the wavelength range of 200–800 nm was recorded by using a Hitachi U-4100 spectrophotometer (Hitachi, Tokyo, Japan). The thermoluminescence (TL) curves were measured by using an FJ-427A pyrometer (Nuclear Instrument Factory, Beijing, China). The electron paramagnetic resonance (EPR) spectrum of the samples was measured by using a Bruker X-band A300-6\1 paramagnetic resonance spectrometer at a frequency of 9.2 GHz at RT. The ML intensity was characterized by using an MS-T3001 friction and wear testing machine, a multi-mode force-luminescence detection system (Qingdao Qingke Longnuo Environmental Technology Co., Ltd QKLN-ML-2), and the use of an Ocean Insight QE Pro fiber optic spectrometer (FLAME-S-XP1-ES). The distance between the friction interface and the electrostatic measurement probe was fixed at 10 cm, and the wavelength range of the test was from 300–1000 nm. The triboelectric properties were detected through a CSM friction testing machine (Tribometer 3, Switzerland) equipped with an electrostatic measuring probe (SK050, KEYENCE (Japan) Co., Ltd). The distance from the friction interface to the electrostatic measuring probe is fixed at 10 cm, and the CSM friction machine adopts a rotating module with a rotation radius of 3 mm and a speed of 60 rpm. The cathodoluminescence (CL) performance was tested on a modified Mp-Micro-S instrument attached to a SEM. All photographs were captured by using a digital camera (Nikon D7100) at RT.
3 Results and discussion
This work focused on investigating the physical mechanism, energy transfer process, and corresponding luminescence behavior during ML generation in different media with various mechanical stimulations. Fig. 1a depicts the ML phenomenon in different media and the flexible ML composite device fabrication processes. Transparent CaF2: Tb3+ GCs after X-ray pre-irradiation generated recoverable trap-controlled green emitting ML under friction, regardless of the bright and dark environments. By grinding CaF2: Tb3+ GCs (i.e., turning glass into powder) and mixing them with PDMS (CaF2: Tb3+ GCs/PDMS), we designed a self-recovery ML composite device resulting from the triboelectric potential induction of the inorganic-organic mechanical interface. Bright green emitting ML can be observed in the CaF2: Tb3+ GCs/PDMS composite device under different mechanical stimuli, such as compression, friction, stretching, tearing, and folding.
3.1 Phase and structure characterization
As a proof-of-concept experiment, we chose CaF2: Tb3+ GCs as the research material in this work. Fig. 1b and S1 (ESI)† show the X-ray diffraction (XRD) patterns of CaF2: Tb3+ GCs before and after the thermal treatment and the CaF2: x% Tb3+ (x = 0.1, 0.3, 0.5, 0.7, and 0.9) samples quenched at 530 °C for 6 h, respectively. These figures demonstrate that heat treatment gradually crystallizes the original amorphous precursor glass (PG) sample, and the precipitated microcrystalline peaks belonging to the (111), (220), and (311) crystal surfaces of the CaF2 phase are consistent with the standard card (JCPDS NO. 75-0097), indicating that the precipitated microcrystalline phase is CaF2 and the introduction of Tb3+ does not form any impurity phase during the doping process. The transmission electron microscopy (TEM) image of CaF2: Tb3+ GCs in Fig. S2a (ESI)† shows that the microcrystal particles are evenly distributed in the glass matrix. In addition, Fig. S2b (ESI)† shows that the (111) surface average surface spacing of CaF2: Tb3+ GC crystals is 0.3164 nm, and the corresponding fast Fourier transform image verifies the successful precipitation of CaF2: Tb3+ nanocrystals from the amorphous matrix (Fig. S2c ESI†). The scanning electron microscope (SEM) image and energy-dispersive spectrum (EDS) mapping of the GCs (Fig. S3 ESI†) clearly show that the elements are uniformly distributed throughout the sample. The crystal structure diagram of CaF2 in Fig. 1c shows that F occupies eight sites of the hexahedron and Ca is surrounded by eight F to form a center cube, occupying the Ca sites after doping with Tb. The CaF2 crystal is a cubic crystal system, with space group Fm
m belonging to the cubic system and a centrosymmetric structure. Previous studies revealed that a crystal with this structure is nonpiezoelectric. Fig. 1d presents the differential thermal analysis (DTA) curve of the sample at a heating rate of 15 °C min−1, which was used to assess the glass characteristics of the annealed samples. The sample exhibits a weak heat absorption tendency at 539 °C, indicating the amorphicity of the sample. The thermal stability (Tc − Tg) is around 80 °C, which is a low value, indicating that the crystallization of the system starts below the crystallization temperature. Thus, according to the peak crystallization temperature of 539 °C, we selected 530 °C as the optimal annealing temperature. Further analysis determined that the glass transition temperature (Tg) is 459 °C, the starting crystallization temperature (Tx) is 525 °C, the peak crystallization temperature (Tc) is 539 °C, and the final crystallization temperature (Tp) is 589 °C.
3.2 ML performance characterization
CaF2: Tb3+ GCs were obtained using the melting and quenching method as well as through heat treatment from a rigid transparent medium. The transmittance of all the CaF2: Tb3+ GCs samples was more than 80% (Fig. S4a ESI†), and the corresponding transmittance and PL characteristics are presented in the ESI† (Fig. S4 ESI†). Because the CaF2: Tb3+ GCs serve as a rigid medium, the physical mechanism of their ML generation is different from that of composite ML devices fabricated in a flexible medium with inorganic phosphors. Thus, the CaF2: Tb3+ GCs were irradiated with X-rays to charge for ML performance characterization. Fig. 2a shows the ML spectrum of the CaF2: Tb3+ GC sample surface under friction pair. The ML spectrum is similar to the PL spectrum originating from Tb3+ ions, indicating that only a luminescence center is present.49 To quantitatively assess the relation between ML intensity and applied loading, Fig. 2b shows the changing relation between ML intensity and applied loading and the linear fitting data, and the insets show ML photos corresponding to various applied loadings. As shown in the photographs, the ML intensity of CaF2: Tb3+ GCs gradually increases with increasing load, and the corresponding ML spectra are presented in Fig. S5a (ESI).† The linear fitting factor is 0.99132 and the friction-induced mechanical-optical response sensitivity is 1.94786. Additionally, a linear relation (Fig. S5c ESI†) was observed between the ML intensity of the CaF2: Tb3+ GCs and the friction speed (Fig. S5b ESI†) under a constant friction load. Fig. 2c shows the ML spectrum before and after the X-ray pre-irradiation of CaF2: Tb3+ GCs. Furthermore, ML is not generated unless the CaF2: Tb3+ GCs are irradiated with X-ray, indicating that X-ray pre-irradiation plays a crucial role in the ML phenomenon of the CaF2: Tb3+ GCs. High-energy ray irradiation of glass materials can cause some point defects within the glass matrix owing to photoionization. Fig. 2d shows the electron paramagnetic resonance (EPR) spectra of the CaF2: Tb3+ GCs before and after X-ray irradiation. The EPR signal (g = 1.9965) was observed only after X-ray irradiation, which is attributed to the oxygen-vacancy defects in the glass,48,55 indicating that the pre-irradiation with X-ray can generate oxygen vacancies within the CaF2: Tb3+ GC matrix. The TL curves before and after X-ray pre-irradiation are shown in Fig. 2e. A series of continuously distributed traps, trap 1 (350 K), trap 2 (403 K), and trap 3 (522 K), appear after X-ray pre-irradiation which can be fitted using Gaussian fitting. The trap depth E can be estimated from the TL curves using an approximate equation as follows:where E is the thermo-active energy of trap depths (eV), which is the energy gap between the electron trap and the conduction band, and T is the TL peak (K).51–53 The depths of the three traps are 0.7, 0.806, and 1.044 eV, respectively. This result reveals that the oxygen vacancy trap in the CaF2: Tb3+ GCs can effectively capture and store the charge carriers. The TL and ML spectra (Fig. S6a and b ESI†) of the CaF2: x% Tb3+ GCs (x = 0.1, 0.3, 0.5, 0.7, and 0.9) indicate that the TL intensity is quenched at x = 0.7, which is consistent with the PL quenching concentration. Fig. S6c and d (ESI)† show the filling time-dependent TL curves and ML spectra of the CaF2: Tb3+ GCs, respectively. X-Ray irradiation at 40 kV and 30 mA can achieve the upper trap filling limit within 15 min, leading to the maximum TL and ML intensity. Furthermore, the TL after X-ray pre-irradiation follows the same tendency as the ML. This sequence of evidence demonstrates that X-ray pre-irradiation introduced and filled the trap in the glass and the fundamental mechanism of this trap-controlled ML generation is to release the carrier in the trap by mechanical stimulation.
![image file: d3ta06257k-f2.tif](/image/article/2024/TA/d3ta06257k/d3ta06257k-f2.gif) |
| Fig. 2 (a) ML spectrum of the CaF2: Tb3+ GCs (the illustrations show an ML visualization of a handwriting trajectory through long exposure and extracted dimensional color maps from the corresponding photos). (b) The relationship between ML intensity of CaF2: Tb3+ GCs and applied load (insets show the corresponding ML photographs). (c) ML spectra of CaF2: Tb3+ GCs before and after X-ray pre-irradiation. (d) EPR spectra before and after X-ray pre-irradiation of CaF2: Tb3+ GCs. (e) TL curves and Gaussian fitted result of CaF2: Tb3+ GCs before and after X-ray pre-irradiation. (f) Cycling stability of ML/TL in CaF2: Tb3+ GCs. | |
Theoretically, macroscopic mechanical stimulation cannot directly release the carrier for generating ML. Therefore, during ML generation, the macroscopic mechanical energy is first converted into another form of energy that can effectively release the carrier to the strap. Moreover, friction heat is generated when any two media come in contact with one another and undergo friction. Concurrently, the trap-controlled carrier is considerably sensitive to thermal stimulation. Thus, we speculate that the microscopic ML mechanism in the CaF2: Tb3+ GCs is the frictional heat-induced TL. Fig. S7a and b (ESI)† depict the TL curves of the pre-irradiated CaF2: Tb3+ GCs at RT at different times. It can be observed that with the increase in placement time, the TL intensity gradually reduces because of the effect of RT thermal excitation. After 14 days of placement, the shallow trap retained about 40% of its initial intensity, while the deep trap retained more than 70% of its initial intensity. The variable temperature TL curves (Fig. S7c ESI†) and ML spectra (Fig. S7d ESI†) show that the ML and TL intensity decreases with the increase in temperature, indicating that the ML intensity is directly related to the concentration of charge carriers. Fig. S7e (ESI)† depicts the temperature-dependent TL photographs of the CaF2: Tb3+ GCs after X-ray pre-irradiation for 15 min. It can be seen that the TL of the CaF2: Tb3+ GCs gradually increases with the increasing temperature and slowly decreases above 500 K. This indicates that after X-ray pre-irradiation, thermal stimulation at RT and high temperature can effectively stimulate carrier release in the traps to produce TL. The temperature dependence of the ML is consistent with TL, confirming our speculation about the ML mechanism in the CaF2: Tb3+ GCs. To verify the repeatability of ML in CaF2: Tb3+ GCs under cyclic loading, 40 experiments were performed and the energy was released through repeated charging and heat removal. The sample retained above 95% of the initial intensity (Fig. 2f), confirming that the ML performance of the prepared CaF2: Tb3+ GCs was recoverable. To further demonstrate the ML environmental stability of CaF2: Tb3+ GCs, we tested their ML in water, air, and alcohol every 2 hours for a duration of 24 hours (Fig. S8a–c ESI†). It was observed that the ML stability of CaF2: Tb3+ GC samples was considerably retained. Furthermore, we tested the ML cycling stability of CaF2: Tb3+ GCs and found that the same trends were exhibited over 10 cycles in a 60 s cycle, indicating that the ML performance was stable and repeatable (Fig. S8d ESI†).
Several studies have found that most ML materials do not exhibit ML characteristics alone but the ML phenomenon can be observed after composite encapsulation with an organic flexible medium.54 Herein, we combined the CaF2: Tb3+ GCs after grinding with various organic matrices to further investigate the effect of the medium on ML performance. As shown in Fig. 3a, no ML was observed during mechanical stimulation (grinding and compression) in the CaF2: Tb3+ GC powder. Furthermore, the composite devices were fabricated with an ER elastomer (CaF2: Tb3+ GCs/ER). When CaF2: Tb3+ GC powder is combined with a flexible matrix, such as polyurethane (PU), silicone (SG), or PDMS (CaF2: Tb3+ GCs/PU, CaF2: Tb3+ GCs/SG, and CaF2: Tb3+ GCs/PDMS), the composite devices can produce large deformations (>50%) at relatively low tensile stress (<5 MPa). As shown in Fig. 3a and S9 (ESI),† under the same strain action, CaF2: Tb3+ GCs/PU exhibited no ML, CaF2: Tb3+ GCs/SG exhibited weak ML, and CaF2: Tb3+ GCs/PDMS exhibited strong ML. To further explain the variability of ML properties of CaF2: Tb3+ GCs in different media, the surface potential of CaF2: Tb3+ GCs, ER, PU, SG, and PDMS after rubbing with CaF2: Tb3+ GCs for 1 min is obtained, as shown in Fig. 3b. It was observed that when CaF2: Tb3+ GCs-CaF2: Tb3+ GCs, ER, and PU as well as CaF2: Tb3+ GCs were rubbed, positive potentials with smaller absolute values were generated. When CaF2: Tb3+ GCs/SG and CaF2: Tb3+ GCs/PDMS are rubbed, the medium obtains electrons with a negative potential, which appears as a negative potential with a large absolute value. Thus, we believe that the absence of ML after CaF2: Tb3+ GCs/ER and CaF2: Tb3+ GCs/PU is because of insufficient triboelectric potential generated by ER and PU friction to reach the minimum threshold for ML generation. However, owing to the large triboelectric potential generated during the contact separation process of the inorganic–organic mechanical interface in CaF2: Tb3+ GCs/SG and CaF2: Tb3+ GCs/PDMS, ML can directly stimulate ML particles. Additionally, the charge decay curve in Fig. 3c well explains the different ML intensities between CaF2: Tb3+ GCs/SG and CaF2: Tb3+ GCs/PDMS. While the luminescence behavior of the ML process is similar to that of CL in the electron–hole pair delocalization/recombination path, the CL spectrum of CaF2: Tb3+ GCs/PDMS, as given in Fig. 3d, agrees with the ML spectrum.38 The results suggest that the ML mechanism of CaF2: Tb3+ GCs/SG and CaF2: Tb3+ GCs/PDMS is a direct excitation-emission process induced by the interface triboelectric field. Furthermore, the proposed ML excitation pathway of electron bombardment under a triboelectric field is also deemed reasonable. Hence, we believe that the ML mechanism of CaF2: Tb3+ GCs/SG and CaF2: Tb3+ GCs/PDMS conforms to the interface friction-induced electron bombardment model of direct excitation-emission. Furthermore, the separation of ML particles from the polymer chain weakens the interfacial binding of the composite elastomer, causing a decrease in the interface triboelectric field and the interface friction intensity. Fig. 3e shows the stress–strain curves of the CaF2: Tb3+ GCs/PDMS composite elastomer tested on a tensile test machine, with an elastic modulus and tensile intensity of 2.07712 and 2.08876 MPa, respectively. The ML intensity and stress variables exhibit a linear relation. The inset is an ML photograph of CaF2: Tb3+ GCs/PDMS during the tensile mechanical action of different shape variables. The intensity of ML gradually increases with the increase in strain. Moreover, to demonstrate the universality of this ML mechanism in a flexible medium, we also studied the ML characteristics of CaF2: Tb3+ GCs/PDMS, CaF2: Eu3+ GCs/PDMS, and CaF2: Eu2+ GCs/PDMS. The results reveal that the tri-color (red: CaF2: Eu3+ GCs/PDMS, green: CaF2: Tb3+ GCs/PDMS, and blue: CaF2: Eu2+ GCs/PDMS) ML of a single matrix is achieved in the material, displaying the ML spectrum of CaF2: Eu3+ GCs/PDMS, CaF2: Tb3+ GCs/PDMS, and CaF2: Eu2+ GCs/PDMS samples (Fig. 3f), as well as the corresponding ML visualization of handwritten traces extracted from dimension-color maps via long exposure (Fig. 3g). The photos exhibit tri-color ML (Fig. 3g(ii)), while the dimensional color diagram (Fig. 3g(i)) indicates that it can exhibit ML intensity distribution.
![image file: d3ta06257k-f3.tif](/image/article/2024/TA/d3ta06257k/d3ta06257k-f3.gif) |
| Fig. 3 (a) ML performance of CaF2: Tb3+ GC powder in various media: powder only and with ER, PU, SG, and PDMS. (b) The surface triboelectric potential of polymer matrices when rubbed with CaF2: Tb3+ GC powder for 1 min under different loads. (c) The decay rate of triboelectric potential on polymer surfaces. (d) ML/CL spectra of CaF2: Tb3+ GCs/PDMS elastomers. (e) Stress–strain curves and relationship of ML intensity versus strain. (f) ML spectra (from top to bottom) of CaF2: Eu3+ GCs/PDMS, CaF2: Tb3+ GCs/PDMS, and CaF2: Eu2+ GCs/PDMS. (g) ML photos and dimension color maps of CaF2: Eu3+ GCs/PDMS, CaF2: Tb3+ GCs/PDMS, and CaF2: Eu2+ GCs/PDMS. | |
3.3 ML mechanism analysis
The mechanisms of ML generation in CaF2: Tb3+ GCs differ in rigid and flexible media, which is primarily attributed to the variation in mechanical properties of the medium, mechanical stimulation mode, and the interaction between ML particles and the medium. First, as shown in Fig. 4a, the ML of a rigid CaF2: Tb3+ GC medium is primarily caused by TL induced via friction heat generation, and the microscopic energy conversion process is primarily the gradual conversion of mechanical energy to thermal energy and then to optical energy. The amorphous glass network structural matrix contains numerous bridging oxygen bonds, and a large number of oxygen-vacancy traps are very easily formed under X-ray pre-irradiation, which will become an effective trap center. X-Ray irradiation effectively promotes the filling of the carriers in the trap. When the object (such as the friction pair) comes into contact with the ML CaF2: Tb3+ GCs and produces relative movement, the mechanical energy generated by the friction force is converted into Joule heat to produce TL. During this, the macroscopic phenomenon presented in this instantaneous process is the ML under the action of friction. The increase in ML intensity with friction load and friction rate is attributed to the fact that the work done by the friction force increases with the load and rate, producing more Joule heat. The reproducible pre-irradiation and release of carriers in traps is the fundamental cause of recoverable trap-controlled ML.
![image file: d3ta06257k-f4.tif](/image/article/2024/TA/d3ta06257k/d3ta06257k-f4.gif) |
| Fig. 4 (a) Mechanism diagram of the ML in CaF2: Tb3+ GCs. (b) Mechanism diagram of the ML in the CaF2: Tb3+ GCs/PDMS flexible device. | |
The self-recovery ML generated by CaF2: Tb3+ GCs/PDMS can be attributed to the induction of electron bombardment because of friction potential at the inorganic–organic mechanical interface, as shown in Fig. 4b. When subjected to multimode mechanical stimulation (such as stretching and friction), an interfacial triboelectric field between the CaF2: Tb3+ GC particles and the SG or PDMS polymer chains is generated due to interfacial friction. This electric field interaction can cause excitation from the valence band to the conduction band (CB), followed by ML emission after the electrons in the CB are transferred to the Tb3+ excited state level and recombine with the holes in the ground state. The generation of ML in a flexible medium is primarily derived from the energy conversion of mechanical energy to electric energy and then to optical energy.
3.4 Potential application of ML devices
Based on the advantages of two different media, we have designed two different types of applications for CaF2: Tb3+ GC glass fibers and plate glass. First, based on the glass optical waveguide effect, as shown in Fig. 5a, we observed a change in the intensity of the waveguide with distance and force in glass fibers and plate glass. This effect can be used to monitor stress points and stress values at the edges of glass in structures such as railways, bridges, windows, and aircraft, and for structural health monitoring. We can transmit the monitoring results to a computer via a Wi-Fi signal to achieve remote stress detection as shown in Fig. 5a. Secondly, we have also prepared CaF2: Tb3+ GCs/PDMS elastomers for optical skin. The elastomer can detect mechanical data from various joints of athletes, monitor and analyze their exercise habits, and provide visual and mechanical feedback, thereby providing data support for analyzing the physical condition of athletes as shown in Fig. 5b.
![image file: d3ta06257k-f5.tif](/image/article/2024/TA/d3ta06257k/d3ta06257k-f5.gif) |
| Fig. 5 (a) Diagram of potential application of CaF2: Tb3+ GCs. (b) Diagram of potential application of CaF2: Tb3+ GCs/PDMS. | |
4 Conclusion
In summary, the CaF2: Tb3+ GCs are synthesized using the melt-quenching method. X-Ray pre-irradiation is employed to form numerous hypoxic centers in the amorphous structure of CaF2: Tb3+ GCs, serving as effective trap centers. These trap centers facilitated the transfer of carriers to the emitting center, resulting in the production of bright green ML in a rigid transparent mass. The atomic contact between CaF2 NCs and the amorphous structure played a crucial role in promoting efficient energy transfer between the trap and the emitting center. The application of force induced the carriers in the trap to transfer to the emitting center, leading to ML generation. Furthermore, the ground CaF2: Tb3+ GC powder mixed with PDMS produced flexible films that exhibited bright green ML due to direct excitation of the center through contact between the powder particles and colloids. This study achieved the first realization of rigid/flexible multi-scenario ML using the same material through trap-controlled and triboelectrification for direct excitation of two different ML mechanisms. Additionally, tri-color ML is accomplished by incorporating Eu2+, Tb3+, and Eu3+, enabling the potential use of full-spectrum stress displays. By considering the disparity between rigid and flexible media, precise detection devices for determining the stress-free point position and real-time monitoring of athletes' exercise states are designed separately. This comprehensive and in-depth study encompasses the mechanisms and applications of ML, providing valuable guidance for future research on ML materials in the field of rigid/flexible multi-scene.
Consent
I declare that I am the patient whose information is included in the manuscript entitled “Multi-mode mechanoluminescence of fluoride glass ceramics from rigid to flexible media toward multi-scene mechanical sensors”. I understand that the manuscript will be published and that my personal and medical information may be disclosed, and I hereby give my consent for the publication of this information. I have been informed of the purpose of the manuscript and the type of information that will be included. I am aware that my identification will be kept confidential and that my personal information will only be used for research purposes. I understand that my participation in this research is voluntary, and I am free to withdraw my consent at any time. I have been provided with an opportunity to ask any questions regarding my participation, and all my questions have been answered. I further understand that my withdrawal of consent will not affect the quality or outcome of the research. I understand that my consent is necessary for publication, and I consent to the publication of my personal and medical information in the manuscript.
Author contributions
Yingdan Song: conceptualization, investigation, validation, visualization, writing – original draft, supervision. Jianqiang Xiao: conceptualization, investigation, validation, visualization, supervision. Lei Zhao: conceptualization, supervision, writing – review & editing, funding acquisition. Zhichao Liu: writing – review & editing. Yami Ling: investigation, supervision, validation. Yingjuan Yan: investigation. Yixuan Xu: investigation. Alexey·Nikolaevich Yakovlev: investigation. Tingting Hu: investigation. Tatiana Grigorievna Cherkasova: investigation. Qiang Xu: funding acquisition. Canjun Wang: methodology. Xuhui Xu: conceptualization, supervision, writing – review & editing, funding acquisition. All authors contributed to data analysis, discussions, and manuscript preparation. All authors have given approval to the final version of the manuscript.
Conflicts of interest
There are no conflicts of interest to declare.
Acknowledgements
This work was supported by the International Science and Technology Cooperation and Exchanges Project of Shaanxi (Project No. 2021KW-39), the Scientific Research Program Funded by the Shanxi Provincial Education Department (Project No. 22JC002), the Key Science and Technology Program of Shaanxi Province (Project No. 2023-YBGY-370), the Scientific Research Program Funded by the Shaanxi Provincial Education Department (Grant No. 22JK0245), and the Yunnan Major Scientific and Technological Projects (Grant No. 202202AG050004 and 202202AG050016).
References
- Z. Huang, B. Chen, B. Ren, D. Tu, Z. Wang, C. Wang, Y. Zheng, X. Li, D. Wang, Z. Ren, S. Qu, Z. Chen, C. Xu, Y. Fu and D. Peng, Smart Mechanoluminescent Phosphors: A Review of Strontium-Aluminate-Based Materials, Properties, and Their Advanced Application Technologies, Adv. Sci., 2023, 10, e2204925 CrossRef
.
- P. Xiong, M. Peng and Z. Yang, Near-infrared mechanoluminescence crystals: a review, iSCI, 2020, 24(1), 101944 CrossRef
.
- J.-C. Zhang, X. Wang, G. Marriott and C.-N. Xu, Trap-controlled mechanoluminescent materials, Prog. Mater. Sci., 2019, 103, 678–742 CrossRef CAS
.
- S. Wu, B. Xiao, Y. Xiao, P. Shao, Y. Wang and P. Xiong, Cr3+-activated broadband near-infrared mechanoluminescence in garnet compound, Nano Energy, 2023, 116, 108811 CrossRef CAS
.
- A. Qasem, P. Xiong, Z. Ma, M. Peng and Z. Yang, Recent Advances in Mechanoluminescence of Doped Zinc Sulfides, Laser Photonics Rev., 2021, 15, 2100276 CrossRef CAS
.
- Y. Du, Y. Jiang, T. Sun, J. Zhao, B. Huang, D. Peng and F. Wang, Mechanically Excited Multicolor Luminescence in Lanthanide Ions, Adv. Mater., 2019, 31, e1807062 CrossRef PubMed
.
- S. M. Jeong, S. Song, S. K. Lee and N. Y. Ha, Color manipulation of mechanoluminescence from stress-activated composite films, Adv. Mater., 2013, 25, 6194–6200 CrossRef CAS PubMed
.
- J. C. Zhang, N. Gao, L. Li, S. Wang, X. Shi, M. Sun, X. Yan, H. W. He, X. Ning, B. Huang and J. Qiu, Discovering and Dissecting Mechanically Excited Luminescence of Mn2+ Activators via Matrix Microstructure Evolution, Adv. Funct. Mater., 2021, 31, 2100221 CrossRef CAS
.
- Y. Xiao, P. Xiong, S. Zhang, Y. Sun, N. Yan, Z. Wang, Q. Chen, P. Shao, M. G. Brik, S. Ye, D. Chen and Z. Yang, Cation-defect-induced self-reduction towards efficient mechanoluminescence in Mn2+-activated perovskites, Mater. Horiz., 2023, 10, 3476–3487 RSC
.
- Y. L. Yang, X. C. Yang, J. Y. Yuan, T. Li, Y. T. Fan, L. Wang, Z. Deng, Q. L. Li, D. Y. Wan, J. T. Zhao and Z. J. Zhang, Time-Resolved Bright Red to Cyan Color Tunable Mechanoluminescence from CaZnOS: Bi3+ , Mn2+ for Anti-Counterfeiting Device and Stress Sensor, Adv. Opt. Mater., 2021, 9, 2100668 CrossRef CAS
.
- Y. Bai, X. Guo, B. Tian, Y. Liang, D. Peng and Z. Wang, Self-Charging Persistent Mechanoluminescence with Mechanics Storage and Visualization Activities, Adv. Sci., 2022, 9, e2203249 CrossRef PubMed
.
- Y. Zhuang, X. Li, F. Lin, C. Chen, Z. Wu, H. Luo, L. Jin and R. J. Xie, Visualizing Dynamic Mechanical Actions with High Sensitivity and High Resolution by Near-Distance Mechanoluminescence Imaging, Adv. Mater., 2022, 34, e2202864 CrossRef PubMed
.
- Y. Zhuang and R. J. Xie, Mechanoluminescence Rebrightening the Prospects of Stress Sensing: A Review, Adv. Mater., 2021, 33, e2005925 CrossRef PubMed
.
- S. Pyo, J. Lee, K. Bae, S. Sim and J. Kim, Recent Progress in Flexible Tactile Sensors for Human-Interactive Systems: From Sensors to Advanced Applications, Adv. Mater., 2021, 33, e2005902 CrossRef PubMed
.
- X. Yang, Y. Cheng, J. Xu, H. Lin and Y. Wang, Stress Sensing by Ratiometric Mechanoluminescence: A Strategy Based on Structural Probe, Laser Photonics Rev., 2022, 16, 2200365 CrossRef
.
- H. Ji, Y. Tang, B. Shen, X. Qian, Z. Cai, F. Li, M. Su, L. Wu, Y. Ma and Y. Song, Skin-Driven Ultrasensitive Mechanoluminescence Sensor Inspired by Spider Leg Joint Slits, ACS Appl. Mater. Interfaces, 2021, 13, 60689–60696 CrossRef CAS
.
- D. J. Lipomi, M. Vosgueritchian, B. C. Tee, S. L. Hellstrom, J. A. Lee, C. H. Fox and Z. Bao, Skin-like pressure and strain sensors based on transparent elastic films of carbon nanotubes, Nat. Nanotechnol., 2011, 6, 788–792 CrossRef CAS PubMed
.
- N. Li, S. Yu, L. Zhao, P. Zhang, Z. Wang, Z. Wei, W. Chen and X. Xu, Recoverable Dual-Modal Responsive Sensing Materials Based on Mechanoluminescence and Thermally Stimulated Luminescence toward Noncontact Tactile Sensors, Inorg. Chem., 2023, 62, 2024–2032 CrossRef CAS PubMed
.
- H. Z. Wei, D. S. Xu and Q. S. Meng, A Newly Designed Fiber-Optic Based Earth Pressure Transducer with Adjustable Measurement Range, Sensors, 2018, 18, 932 CrossRef PubMed
.
- S. Lee, A. Reuveny, J. Reeder, S. Lee, H. Jin, Q. Liu, T. Yokota, T. Sekitani, T. Isoyama, Y. Abe, Z. Suo and T. Someya, A transparent bending-insensitive pressure sensor, Nat. Nanotechnol., 2016, 11, 472–478 CrossRef CAS PubMed
.
- B. Ren, B. Chen, X. Zhang, H. Wu, Y. Fu and D. Peng, Mechanoluminescent optical fiber sensors for human-computer interaction, Sci. Bull., 2023, 542–545 CrossRef PubMed
.
- S. Krishnan, H. Van der Walt, V. Venkatesh and V. B. Sundaresan, Dynamic characterization of elastico-mechanoluminescence towards structural health monitoring, J. Intell. Mater. Syst. Struct., 2017, 28, 2458–2464 CrossRef CAS
.
- P. Zhang, J. Wu, L. Zhao, Z. Guo, H. Tang, Z. Wang, Z. Liu, W. Chen and X. Xu, Environmentally Stable and Self-Recovery Flexible Composite Mechanical Sensor Based on Mechanoluminescence, ACS Sustainable Chem. Eng., 2023, 4073–4081 CrossRef CAS
.
- X. Tang, W. Yang, S. Yin, G. Tai, M. Su, J. Yang, H. Shi, D. Wei and J. Yang, Controllable Graphene Wrinkle for a High-Performance Flexible Pressure Sensor, ACS Appl. Mater. Interfaces, 2021, 13, 20448–20458 CrossRef CAS PubMed
.
- C. Wang, D. Peng and C. Pan, Mechanoluminescence materials for advanced artificial skin, Sci. Bull., 2020, 65, 1147–1149 CrossRef CAS PubMed
.
- S. Chang, Y. Deng, N. Li, L. Wang, C.-X. Shan and L. Dong, Continuous synthesis of ultra-fine fiber for wearable mechanoluminescent textile, Nano Res., 2023, 9379–9386 CrossRef CAS
.
- D. Lu, T. Liu, X. Meng, B. Luo, J. Yuan, Y. Liu, S. Zhang, C. Cai, C. Gao, J. Wang, S. Wang and S. Nie, Wearable Triboelectric Visual Sensors for Tactile Perception, Adv. Mater., 2023, 35, e2209117 CrossRef PubMed
.
- H. Deng, Z. Yang, G. Li, D. Ma, Z. Xie, W. Li, Z. Mao, J. Zhao, Z. Yang, Y. Zhang and Z. Chi, Dynamic organic mechanoluminescence (ML): The roles of Mechano-induced conformational isomer and energy transfer from ML to photoluminescence (PL), Chem. Eng. J., 2022, 438, 135519 CrossRef CAS
.
- R. A. D. M. Ranasinghe, Y. Tanaka, M. Okuya, M. Shimomura and K. Murakami, Structural characterizations of organic-based materials with extensive mechanoluminescence properties, J. Lumin., 2017, 190, 413–423 CrossRef CAS
.
- Y. Zhao, D. Peng, G. Bai, Y. Huang, S. Xu and J. Hao, Multiresponsive Emissions in Luminescent Ions Doped Quaternary Piezophotonic Materials for Mechanical-to-Optical Energy Conversion and Sensing Applications, Adv. Funct. Mater., 2021, 31, 2010265 CrossRef CAS
.
- Y. L. Zhong, S. N. Basu and Z. Sun, Nanomaterials and Composites for Energy Conversion and Storage, Jom, 2021, 73, 2752–2753 CrossRef
.
- W. Wang, Z. Wang, J. Zhang, J. Zhou, W. Dong and Y. Wang, Contact electrification induced mechanoluminescence, Nano Energy, 2022, 94, 106920 CrossRef CAS
.
- Y. Xie and Z. Li, Triboluminescence: Recalling Interest and New Aspects, Chem, 2018, 4, 943–971 CAS
.
- Z. L. Wang and A. C. Wang, On the origin of contact-electrification, Mater. Today, 2019, 30, 34–51 CrossRef CAS
.
- H. Zou, L. Guo, H. Xue, Y. Zhang, X. Shen, X. Liu, P. Wang, X. He, G. Dai, P. Jiang, H. Zheng, B. Zhang, C. Xu and Z. L. Wang, Quantifying and understanding the triboelectric series of inorganic non-metallic materials, Nat. Commun., 2020, 11, 2093 CrossRef CAS PubMed
.
- S. Lin, L. Xu, C. Xu, X. Chen, A. C. Wang, B. Zhang, P. Lin, Y. Yang, H. Zhao and Z. L. Wang, Electron Transfer in Nanoscale Contact Electrification: Effect of Temperature in the Metal-Dielectric Case, Adv. Mater., 2019, 31, e1808197 CrossRef PubMed
.
- S. Lin, C. Xu, L. Xu and Z. L. Wang, The Overlapped Electron-Cloud Model for Electron Transfer in Contact Electrification, Adv. Funct. Mater., 2020, 30, 1901418 Search PubMed
.
- S. Lin, L. Xu, L. Zhu, X. Chen and Z. L. Wang, Electron Transfer in Nanoscale Contact Electrification: Photon Excitation Effect, Adv. Mater., 2019, 31, e1901418 CrossRef PubMed
.
- X. Y. Wei, X. Wang, S. Y. Kuang, L. Su, H. Y. Li, Y. Wang, C. Pan, Z. L. Wang and G. Zhu, Dynamic Triboelectrification-Induced Electroluminescence and its Use in Visualized Sensing, Adv. Mater., 2016, 28, 6656–6664 CrossRef CAS PubMed
.
- H. Zou, Y. Zhang, L. Guo, P. Wang, X. He, G. Dai, H. Zheng, C. Chen, A. C. Wang, C. Xu and Z. L. Wang, Quantifying the triboelectric series, Nat. Commun., 2019, 10, 1427 CrossRef PubMed
.
- X. Y. Wei, L. Liu, H. L. Wang, S. Y. Kuang, X. Zhu, Z. L. Wang, Y. Zhang and G. Zhu, High-Intensity Triboelectrification-Induced Electroluminescence by Microsized Contacts for Self-Powered Display and Illumination, Adv. Mater. Interfaces, 2018, 5, 1701063 CrossRef
.
- Y. Bai, F. Wang, L. Zhang, D. Wang, Y. Liang, S. Yang and Z. Wang, Interfacial triboelectrification-modulated self-recoverable and thermally stable mechanoluminescence in mixed-anion compounds, Nano Energy, 2022, 96, 107075 CrossRef CAS
.
- Z. Cai, S. Kang, X. Huang, X. Song, X. Xiao, J. Qiu and G. Dong, A novel wide temperature range and multi-mode optical thermometer based on bi-functional nanocrystal-doped glass ceramics, J. Mater. Chem. C, 2018, 6, 9932–9940 RSC
.
- D. Chen, S. Liu, Z. Wan and Z. Ji, EuF3/Ga2O3 Dual-Phase Nanostructural Glass Ceramics with Eu2+/Cr3+ Dual-Activator Luminescence for Self-Calibrated Optical Thermometry, J. Phys. Chem. C, 2016, 120, 21858–21865 CrossRef CAS
.
- P. Li, M. Peng, L. Wondraczek, Y. Zhao and B. Viana, Red to near infrared ultralong lasting luminescence from Mn2+-doped sodium gallium aluminum germanate glasses and (Al,Ga)-albite glass-ceramics, J. Mater. Chem. C, 2015, 3, 3406–3415 RSC
.
- J. Cao, Y. Ding, R. Sajzew, M. Sun, F. Langenhorst and L. Wondraczek, Mechanoluminescence from highly transparent ZGO:Cr spinel glass ceramics, Opt. Mater. Express, 2022, 12, 3238–3247 CrossRef CAS
.
- Z. Feng, J. Zhang, X. Xu, T. Zheng, Y. Guo and J. Lv, Mechanoluminescence properties of Pr3+-doped B2O3-Al2O3-SrO system glass-ceramics, J. Non-Cryst. Solids, 2022, 590, 121676 CrossRef CAS
.
- J. Ueda, A. Hashimoto and S. Tanabe, Orange Persistent Luminescence and Photodarkening Related to Paramagnetic Defects of Nondoped CaO-Ga2O3-GeO2 Glass, J. Phys. Chem. C, 2019, 123, 29946–29953 CrossRef CAS
.
- H. Tang, L. Zhao, Z. Liu, Q. Peng, X. Yu, Q. Wang, F. Zhao, M. Deng, Y. Bai, Z. Wang, T. Wang, J. Qiu and X. Xu, A lanthanide-doped glass-ceramic fiber for stress sensing, Cell Rep. Phys. Sci., 2022, 3, 101093 CrossRef CAS
.
- L. Yuan, Y. Jin, Y. Su, H. Wu, Y. Hu and S. Yang, Optically Stimulated Luminescence Phosphors: Principles, Applications, and Prospects, Laser Photonics Rev., 2020, 14, 2000123 CrossRef CAS
.
- K. Huang, X. Dou, Y. Zhang, X. Gao, J. Lin, J. Qu, Y. Li, P. Huang and G. Han, Enhancing Light and X-Ray Charging in Persistent Luminescence Nanocrystals for Orthogonal Afterglow Anti-Counterfeiting, Adv. Funct. Mater., 2021, 31, 2009920 CrossRef CAS
.
- Z. Wei, W. Chen, Z. Wang, N. Li, P. Zhang, M. Zhang, L. Zhao and Q. Qiang, High-temperature persistent luminescence and visual dual-emitting optical temperature sensing in self-activated CaNb2O6: Tb3+ phosphor, J. Am. Ceram. Soc., 2020, 104, 1750–1759 CrossRef
.
- Y. Fu, C. Li, F. Zhang, S. Huang, Z. Wu, Y. Wang and Z. Zhang, Site preference and the optical thermometry strategy by different temperature response from two sites environment of Mn2+ in K7ZnSc2B15O30, Chem. Eng. J., 2021, 409, 128190 CrossRef CAS
.
- J. Wang, K. Yao, K. Cui, J. Zhang, Y. Gu, W. Wang, X. Jin and J. Zhou, Contact Electrification Induced Multicolor Self-Recoverable Mechanoluminescent Elastomer for Wearable Smart Light-Emitting Devices, Adv. Opt. Mater., 2023, 2203112 CrossRef CAS
.
- M. Li, Y. Jin, L. Yuan, B. Wang, H. Wu, Y. Hu and F. Wang, Near-Infrared Long Afterglow in Fe3+-Activated Mg2SnO4 for Self-Sustainable Night Vision, ACS Appl. Mater. Interfaces, 2023, 15, 13186–13194 CrossRef CAS PubMed
.
|
This journal is © The Royal Society of Chemistry 2024 |