Open Access Article
This Open Access Article is licensed under a
Creative Commons Attribution 3.0 Unported Licence

2D bifunctional tungsten disulfide-embedded UiO-66 (WS2@UiO-66) as a highly active electrocatalyst for water splitting

Muhabbat Shah , Uzair Abdullah , Erum Pervaiz * and Maryum Ali
Heterogeneous Catalysis Lab, Department of Chemical Engineering, School of Chemical and Materials Engineering (SCME), National University of Sciences & Technology (NUST), Sector H-12, Islamabad, 44000, Pakistan. E-mail: erum.pervaiz@scme.nust.edu.pk; Tel: +92-5190855103

Received 24th July 2023 , Accepted 17th December 2023

First published on 18th December 2023


Abstract

Effective water-splitting electrocatalysts provide great potential for the production of hydrogen as fuel in renewable and sustainable energy devices. Electrocatalysts become the bottleneck in the process of achieving easy and cost-effective water-splitting and require tremendous attention on the catalyst design. An economical, greatly stable, and effective electrocatalyst with low activation potential is usually required. In this study, we present a solvothermal method for the synthesis of a highly effective electrocatalyst, denoted as WS2@UiO-66, to facilitate rapid and efficient water splitting. WS2@UiO-66 forms a heterostructure, allowing for efficient overall water splitting. Open structures with many active sites are accessible to the reactants in this bifunctional design, which promotes mass diffusion and electron transport. In an alkaline solution, WS2/UiO-66 exhibits exceptional HER and OER activity, requiring an HER overpotential of 121 mV and OER overpotential of 220 mV to yield a current density of 10 mA cm−2. The best catalyst shows a smaller Tafel value of 272 mV dec−1 and 140 mV dec−1 for HER and OER, respectively. Furthermore, at a current density of 10 mA cm−2, WS2@UiO-66 can sustain HER/OER without a substantial loss for 24 hours. The outstanding bifunctional catalytic performance of WS2@UiO-66 can significantly accelerate its utilization in water splitting. This research may pave the way for the development of new methods for cost-effective energy conversion and storage catalysts.


1. Introduction

Because of the rising energy crises and environmental pollution, exploration and advancement in the field of hydrogen energy have become highly urgent.1–3 Hydrogen is considered a sustainable fuel and a favorable future energy carrier owing to the unlimited source of water and zero greenhouse gas emissions.4,5 Hydrogen production by electrocatalytic water splitting is one of the most innovative technologies for resolving environmental challenges and finding a sustainable energy source. For its extremely high energy density and caloric values, hydrogen can be broadly employed as a fuel in transportation and stationary power.6,7 However, many parameters, other than cost, limit its large-scale application. To manage these parameters, designing a suitable catalyst is the way forward. A variety of transition metal sulfides, nitrides, and carbides are being investigated as water-splitting electrocatalysts. These materials are suitable for HER and OER because of their high catalytic activity, exceptional durability, and efficient charge transfer. They are dependable for long-term applications owing to their stability under challenging electrochemical conditions. Additionally, because of their adjustable electronic and structural characteristics, the performance of the catalyst can be customized. Some metal nitrides and sulfides, such as iron nitride (FeN) and molybdenum disulfide (MoS2), have abundant resources, which lowers production costs. Researchers are continually fine-tuning the properties of these materials to improve their performance in a variety of electrochemical environments.8–10 By decreasing the activation energy of a reaction, we can increase the reaction rate and improve the energy conversion efficiency, which is a crucial aspect of catalyst design.11 Developing catalytically active bifunctional catalysts with suitable conductivity and charge transfer for an efficient OER and HER is difficult and tedious. For HER and OER, researchers are looking at novel catalyst materials with high energy conversion rates and low overpotentials. Some of these bifunctional heterostructures exhibit the increased performance of OER and HER processes, resulting in the production of hydrogen fuel. Water splitting, powered by variable renewables such as wind power and solar, may create sustainable and high-purity hydrogen at a low cost.12,13 Although noble metal catalysts are currently the most efficient for water splitting, their scarcity and high cost make them impractical for large-scale applications from an economic standpoint.14,15 As an alternative to noble-metal catalysts, transition metal sulfides are being constantly explored for their potential. As they are abundant in nature, the cost of the catalysts will be significantly reduced.16,17 However, their poor efficiencies for HER and OER fall short of the commercial need for water electrolysis. As a result, the exploitation of highly stable and active earth-abundant catalysts should be given top priority.14,18,19 Heterostructure electrocatalysts have recently demonstrated advantages in water splitting over single-component catalysts. The heterostructures exhibit abundant exposed edges and surface defects, which arise from lattice distortion and ligand mismatch.20–22 During the HER or OER processes, these defect centers have the potential to serve as active sites for the adsorption of intermediates. Furthermore, the 3D design enables rapid mass dispersion and greatly lowers the overpotential, notably at high current densities for OER and HER.23,24 A recent study has shown that 2D materials based on WS2 might be effective electrocatalysts due to the hydrogen adsorption free energy being close to the thermoneutral zone (ΔG ≈ 0, i.e., the Gibbs free energy change is approximately zero), of transition metals and chalcogenides.25–27 Exfoliation of the WS2 liquid phase nanosheets is widely acknowledged as a reliable method for producing large yields of active layered LPE (liquid phase exfoliated)-WS2 nanosheets. The electrocatalysts are greatly aided by LPE-WS2, which has extensively exposed edges and a low impedance-to-charge transfer.26 Tungsten disulfide (WS2) is another TMD material that has a similar crystal and electrical structure to MoS2, and has been the subject of current research due to its high HER activity.28,29 The HER performance of the WS2 catalysts is comparable to that of well-known catalysts, such as MoS2, CoSe2, and CoS2. However, WS2 is a preferable alternative electrocatalyst material due to its abundant reserves, low cost, and higher conductivity. The stability of the material is considered to be a key factor for hydrogen energy production. WS2 is more stable than other electrocatalysts, and has been shown to have highly efficient electrocatalytic activity for HER. The electrocatalytic activity of WS2 can be enhanced via defect engineering.30–32 The catalytic efficiency can be considerably increased by changing the structure of WS2, a typical two-dimensional material, to expose more active sites.33

UiO-66 is a metal–organic framework (MOF) that comprises Zr as the active metal center and benzen-1,4-dicarboxylate (BDC) as the organic linker. It forms octahedral nanoparticles with a substantial surface area. The strong bond between Zr(IV) and the carboxylate O atom leads to high charge density and bond polarization. Remarkably, UiO-66 demonstrates exceptional stability in both organic solvents and water, showcasing outstanding chemical, electrical, and mechanical properties. These advantageous attributes make UiO-66 a highly promising candidate for water-splitting applications.34,35 Developing composites is one of the many strategies for enhancing electrical conductivity that can be used to overcome the big barrier.36,37

Changqi Sun et al. discovered that the HER activity can be enhanced by tuning the intrinsic conductivity of WS2 in N-doped WS2 nanosheets. Despite substantial progress, the exploration for HER catalysts is mostly focused on the development of noble metal-free electrocatalysts, overlooking the incorporation of additional driving elements.27 The strong connection between WS2 and the positively charged surfactant made 1T′-WS2 very stable after surface treatment, allowing it to stand effective dissemination in a polar solvent. The 1T′-WS2 catalyst exhibited a low overpotential of 200 mV, a small Tafel slope of 50.4 mV dec−1, and demonstrated exceptional stability at a current density of 10 mA cm−2.38 Additionally, during the alkaline HER process, enhanced cycle stability was discovered, viewing its potential for future applied applications.39 Tayebi et al. studied WS2/WO3, which was synthesized for the photoelectrochemical water splitting process. The current density of the produced catalyst was extremely high. When the WS2 nanosheets were deposited, the current density rose dramatically, especially for the WO3/WS2 electrode, with peaks of about 6.6 mA cm−2 current density at 1.75 V vs. Ag/AgCl.40 Another study found that the electrocatalyst activity significantly improved when WS2 nanosheets and CdS were combined (WS2/CdS). In the photoelectrochemical overall water splitting, the nanostructures showed a significantly higher photocurrent density than the pristine sulfide of 0.15 mA cm−2 at 1.23 V vs. RHE.41 Peng et al. studied the 3D Co9S8/WS2 electrode material configuration and reported it an effective electrocatalyst for splitting water. In an alkaline medium, electrocatalysts with hydrogen-evolving 3-D electrodes may yield current densities of up to 10 mA cm−2 with an overpotential of 138 mV. This multifunctional electrode may also be used to build a high-performance alkaline electrolytic cell boasting a cell voltage of 1.65 V at 10 mA cm−2.42

This paper proposes a rational design of a WS2@UiO-66 2D nanostructure for overall alkaline water splitting. These WS2@UiO-66 2D nanostructures on nickel foam can minimize WS2 agglomeration, promote mass diffusivity, advance the electron transport, and provide HER and OER additional active sites. The heterojunction interface between the WS2 and UiO-66 phases generates a synergistic effect, enabling rapid charge transit, which may dramatically improve the HER and OER activity in alkaline media. The WS2 film is made up of tiny WS2 clusters built up of smaller WS2 nanosheets, and this hierarchical film may be employed as a self-supported electrode for HER when combined with a metal substrate. The WS2 nanosheets' random orientations and small sizes would considerably aid in exposing active edge locations. As a result, the WS2 film electrocatalyst exhibits superior electrocatalytic activity, including a low overpotential (121 mV) to reach a current density of 10 mA cm−2 and excellent catalytic durability by performing ultra-long HER operations in a basic environment at a static overpotential (>24 h).

2. Experimental section

2.1 Chemicals

For the fabrication of all of the electrocatalysts, analytical grade chemicals and compounds were utilized (with no processing or purification). Chemicals include sodium tungstate dihydrate (Na2WO4·2H2O) (CAS# 10213-10-2), sodium sulfide (Na2S) (CAS# 1313-82-2), zirconium(IV) chloride (ZrCl4) (CAS# 10026-11-6), and polyvinyldieneflouride (PVDF) (–(C2H2F2)n–) (CAS#24937-79-9) from Sigma-Aldrich. Merck supplied dimethylformamide (DMF) (CAS # 68-12-2), N-methyl-2-pyrrolidone (NMP) (CAS# 872-50-4), and benzene-1,4-dicarboxylic acid (terephthalic acid) (C6H4(CO2H)2) (CAS# 100-21-0). Powdered activated carbon was sourced from Duksan Pure Chemicals. Ethanol (C2H5OH) (CAS# 64-17-5) was obtained from BDH, and deionized water was obtained from the Vitro diagnostics laboratory.

2.2 Synthesis of pure WS2

The WS2 bulk nanosheets were prepared by analytical grade Na2WO4·2H2O and Na2S in a hydrothermal process with no additional purification. Quantities of 20 mmol Na2WO4·2H2O and 20 mmol Na2S were mixed in 50 mL distilled water and constantly agitated for 30 minutes to generate a clear solution in a conventional synthesis. This mixture was introduced to a stainless-steel autoclave lined with Teflon and heated to 220 °C for the duration of 6 h. The prepared powder was then washed and separated via centrifugation several times with ethanol and DI water. The bulk sheets were then obtained after vacuum drying at 70 °C. The prepared nanosheets were then exfoliated with the help of probe sonication for 6 hours to obtain the exfoliated nanosheets of pure WS2.

2.3 Synthesis of WS2/UiO-66 hybrids

A one-pot solvothermal synthesis was used to synthesize WS2 and MOF hybrids at various concentrations. Exfoliated WS2 and ZrCl4 were added to a solution of BDC, DMF, and acetic acid in different weight percent ratios (1[thin space (1/6-em)]:[thin space (1/6-em)]1, 1[thin space (1/6-em)]:[thin space (1/6-em)]2, 1[thin space (1/6-em)]:[thin space (1/6-em)]3). For full inclusion of the reactants, the solution was agitated for 30 minutes and then sonicated for 2 hours. The mixtures underwent a 24 hour heating process in a Teflon-lined stainless-steel autoclave at 120 °C. Once the reaction period concluded, the autoclave was cooled to room temperature. Centrifugation was used to separate the solid product, which was washed thrice with DMF and ethanol. Finally, the obtained powder was dried overnight at 70 °C.

2.4 Bulk and exfoliated WS2

The primary distinction between bulk WS2 and exfoliated WS2 is in the form of monolayers or few-layer nanosheets, which influence the electrical and structural properties. Exfoliation of WS2 refers to the process of separating the three-dimensional layered structure of bulk WS2 to produce individual or a few layers of WS2. As more catalytic active sites are exposed, the surface area increases considerably. When WS2 is exfoliated into monolayers or few layers, the electrical characteristics of the material, such as the temperature-dependent resistivity, contact resistance, band structure, and electronic excitation, can change dramatically.43,44 Exfoliated WS2 has been shown to have greater electrical conductivity than its bulk form. Exfoliated WS2 was found to be highly conductive at room temperature, with values of around 7 S cm−1, which is an order of magnitude higher than the conductivity of bulk WS2 evaluated under similar conditions.45

Electrical conductivity is critical for electrode electrocatalytic activity in water splitting reactions. A high electrical conductivity of the electrode material increases charge transfer at the electrode–electrolyte interface, hence speeding up the electrocatalytic reactions involved in the water splitting process. This leads to faster reaction times and lower overpotentials. Furthermore, electrodes with high electrical conductivity help to reduce ohmic losses and, as a result, energy consumption during water splitting.46,47

2.5 Electrocatalysts characterization

An X-ray diffractometer was used to perform compositional analyses and phase studies on the developed catalyst (XRD; STOE Germany). The 2θ range for the test was 10°–90°, and Cu-K radiation was used. SEM (JEOL-instrument JSM-6490A) was used to study and investigate the catalyst's structure and morphology and the lattice structure. Brunauer–Emmett–Teller (BET) was performed to evaluate the pore size distribution and available active surface.

2.6 Electrochemical study

The electrocatalytic activity was determined under ambient conditions using a three-electrode cell configuration. 1.0 M KOH was used as an electrolyte. The counter electrode was composed of Pt-wire. Ag/AgCl is preferred as a reference electrode in water-splitting experiments because it is highly stable in aqueous solutions, and does not undergo significant changes in potential over time. It also has a well-defined and known standard potential with easily reproducible results. The working electrode was constructed of the catalyst on Ni-foam. For calculations following the formula, the potential was changed to a reversible hydrogen electrode (RHE) for the standardization equation.
 
ERHE = EAg/AgCl + 0.059 pH + E0Ag/AgCl(1)
where pH = 14; E0Ag/AgCl = 0.1976.

The electrocatalysts' performance was assessed through several techniques, including cyclic voltammetry (CV), linear sweep voltammetry (LSV), electrochemical impedance spectroscopy (EIS), and chronopotentiometry. For the linear sweep voltammetry (LSV) analysis, a scan rate of 10 mV s−1 was used within a potential range of 0 to 1.5 V. Cyclic voltammetry measurements were conducted within the potential range of 0 to 0.6 V, employing various scan speeds (10, 20, 50, 100, 150), and the results were reported at 50 mV s−1. Tafel plots were generated, where the y-axis represented the overpotential, and the x-axis displayed the logarithm of the current density. The slope of the Tafel plots was determined using a linear equation (eqn (2)).

 
image file: d3ya00348e-t1.tif(2)
where image file: d3ya00348e-t2.tif; m = Tafel slope; j = current density; a = Tafel constant.

In electrochemical impedance spectroscopy (EIS), the frequency range utilized was from 0.1 Hz to 2 MHz, with an alternating voltage amplitude of 10 mV. To assess the stability of the electrocatalyst, chronopotentiometry was employed. In chronopotentiometry, the rate of the potential change over time was calculated while maintaining a constant current of 10 mA cm−2. Frequently, stability curves were supplied within 24 hours.

3. Results and discussion

3.1 X-ray diffraction

Fig. 1 displays the XRD pattern of all the prepared samples. Fig. 1(a) reveals the pure and well-formed crystalline peaks of tungsten disulfide nanosheets at 14.36°, 32.76°, 39.59°, 44.05°, 49.79°, and 58.49°, which are analogous to the diffraction planes of (002), (100), (103), (006), (105) and (110), respectively. These patterns are well matched with the XRD patterns of the conventional WS2 having a hexagonal lattice (JCPDS: 84-1398).48
image file: d3ya00348e-f1.tif
Fig. 1 Powder X-ray diffractometry: (a) pure UiO-66, (b) exfoliated WS2, (c) bulk WS2, (d) WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1), (e) WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2), (f) WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3).

Other modest diffractions were seen in the (100), (103), (105), and (110) planes. For the hexagonal phase, the diffractions and peak intensities correspond well with the standard JCPDS (JCPDS 08-0237) database.49 UiO-66 was effectively synthesized, as evidenced by the emergence of three distinct peaks at 2θ = 7.38, 8.56, and 25.67°.50 Any defect in its crystalline structure is not visible. All of the hybrids display the characteristic UiO-66 peaks corresponding to the crystallographic planes (111) and (002) at 7.2° and 8.0°, respectively. Moreover, the crystallite size is calculated using the Scherrer formula given in eqn (3).51

 
D = /(FWHM) × (cos[thin space (1/6-em)]θ)(3)
In the above equation, FWHM is the integral width (it is the area under the curve divided by the maximal height, taken in radians), D is the apparent size of the crystal, and k is a constant with a value near 1 (i.e., 0.94), Cu-Kα 1.54 is the X-ray wavelength, and θ is the Bragg angle. An average crystal size of 240 Å (24 nm) of the bulk tungsten disulfide was calculated using the Scherrer calculator, exfoliated WS2 is 277 Å (27.7 nm), WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1) is 244 Å (24.4 nm), WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) is 234.5 Å (23.45 nm), WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3) is 179 Å (17.9 nm) and pure UiO-66 is 172 Å (17.2 nm). The XRD graphs of bulk WS2 and exfoliated WS2 show that bulk WS2 has broader peaks than exfoliated WS2, which is why bulk WS2 has a greater FWHM value and smaller crystallite size than exfoliated WS2. To create hybrids, exfoliated WS2 with a crystallite size of 27.7 nm was utilized. As the concentration of UiO-66 in the hybrids increased, the crystallite size was notably reduced. This can be ascribed to the smaller crystallite size and higher concentration of UiO-66. The peaks observed in WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3) are wider than those in WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) due to this effect. Consequently, WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3) has a smaller crystallite size compared to all of the other hybrids.

3.2 Scanning electron microscope (SEM)

The microstructures of the synthesized material were observed via SEM examination. Irregular nanosheets of the synthesized WS2 are produced, as shown in Fig. 2(a) and (b). Based on the SEM morphology of WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1), the two structures may be fused to generate shapeless nanoparticles, with no single morphology of either structure dominating, which is also due to aggregation. Although certain particles can be observed embedded in the structure, there is no way to tell them apart. This method of synthesis resulted in a chaotic structure with aggregated particles. UiO-66 structures formed in clusters can be seen in WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) (Fig. 2(d). It is possible that the UiO-66 polyhedral was formed on the WS2 sheets as a foundation. UiO-66 has difficulty developing a stable crystalline structure.52 The morphologies of the UiO-66 samples described in the literature generally have irregular intergrown microcrystalline polyhedral shapes.7,53
image file: d3ya00348e-f2.tif
Fig. 2 SEM images of (a) bulk WS2, (b) exfoliated WS2, (c) WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1), (d) WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2), (e) WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3).

3.3 EDX

Fig. 3(a) display the EDX plots for the hybrid WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2), revealing the presence of all of the crucial elements, such as Tungsten, Sulphur, Zirconium, Carbon, and Oxygen, as indicated by the corresponding ratios in the inset. It needs to be mentioned that the composition was uniform throughout the samples. The EDX elemental analysis serves as additional confirmation of the successful synthesis of the UiO-66 and WS2 hybrid.
image file: d3ya00348e-f3.tif
Fig. 3 EDX analysis of hybrid WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2).

3.4 BET

Nitrogen adsorption was used to measure the surface area of the structure. Many properties can be determined using the pore size distribution curves and BET analysis, like the pore size distribution, pore volume of the hybrid, and surface area, as shown in Fig. 4(a) and (b). According to the Brunauer–Deming–Deming Teller classification, the isotherm produced for WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) is of type IV. The WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) nanosheets had a pore volume, pore diameter, and surface area of 0.23165 cm3 g−1, 4.9 nm, and 125.06 m2 g−1, respectively, which is very large compared to the previously reported WS2 nanosheets (pore volume is 0.067 cm3 g−1, and surface area of 65.05 m2 g−1, respectively).54 Because the prepared materials have a large surface area, the synthesized material might have many available sites on the surface and help with electrolyte interaction.
image file: d3ya00348e-f4.tif
Fig. 4 (a) BET adsorption isotherm and the (b) pore size distribution curve.

4. Electrochemical study

4.1 Hydrogen evolution reaction (HER)

Fig. 5(a) illustrates the electrocatalytic HER performance curves for bulk WS2, exfoliated WS2, WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3), WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2), and WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1). Part (a) of Fig. 5 shows the LSV charts of all materials determined in 1.0 M KOH, with an applied potential range from 0 to −1.5 V and sweep rate of 10 mV s−1. LSV is a metric for the electroactive substances' chemical reactivity. The overpotential plays a crucial role in assessing the potential of a catalyst for water-splitting. It refers to the potential applied beyond the equilibrium potential to initiate the reaction and facilitate the release of entities at the electrodes. The calculation of the overpotential at a specific current density allows for the evaluation of the electrode's activity. A lower overpotential indicates a higher electrochemical activity of the catalyst. As a standard practice, the overpotential is measured and compared at a current density of 10 mA cm−2 for all prepared catalysts.43 At the current density of 100 mA cm−2, WS2 bulk, exfoliated WS2, WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1), and WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3) demonstrated HER overpotentials of 149 mV, 153 mV, 123 mV, and 136 mV, respectively. WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) demonstrated improved HER activity as compared to pure compounds and other hybrids with a small overpotential of 121 mV at a current density of 10 mA cm−2. The Tafel plots show how the overpotential response rate is related. The Tafel slope in Fig. 5(b) can be used to deduce the reaction mechanism and check the activity in the HER.
image file: d3ya00348e-f5.tif
Fig. 5 (a) LSV HER curves of bulk WS2, exfoliated WS2, and WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1, 1[thin space (1/6-em)]:[thin space (1/6-em)]2, and 1[thin space (1/6-em)]:[thin space (1/6-em)]3) at a scan rate of 10 mV s−1 in 1.0 M KOH. (b) Corresponding Tafel plots of bulk WS2, exfoliated WS2 and WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1, 1[thin space (1/6-em)]:[thin space (1/6-em)]2, 1[thin space (1/6-em)]:[thin space (1/6-em)]3).

The Tafel plot of HER might give the rate-limiting phase. The electron transport is faster in the sample with a low Tafel plot. So, achieving a high current density and low Tafel slope is needed, along with a low overpotential. The bulk WS2, exfoliated WS2, WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1), and WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3) had Tafel values of 163 mV dec−1, 298 mV dec−1, 115 mV dec−1, and 113 mV dec−1, respectively, whereas WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) had the lowest Tafel value of 83 mV dec−1. A high Tafel value denotes a high charge transfer resistance, while a low Tafel value denotes a quick hydrogen production rate. After a 24 hour chronopotentiometry test, WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) exhibits HER stability with a small reduction in performance. WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2), in conclusion, delivers the highest production for HER electrocatalytic water-splitting and is comparable to several previously reported highly efficient catalysts (Table 3). The increased surface area, synergistic effects amongst metals, and the presence of conductive channels provided by the MOF network all contribute to the increased performance. Bimetallic catalysts often outperform catalysts composed of a single metal component due to various factors. These include synergistic effects, structural and composition-dependent enhancements in the active sites, and the ability to improve the current density and over-potential characteristics in the water oxidation process. The presence of a larger number of accessible catalytic sites, along with an open structure and bimetallic synergy, promotes rapid mass movement and enhances electron transmission.55 The more negative conduction band potential of WS2 compared to UiO-66 facilitates the rapid and efficient flow of electrons from WS2 to UiO-66, thereby enhancing the process of water splitting. The covalent interaction between WS2 and UiO-66 leads to the formation of heterojunctions, enabling swift electron transfer and consequently enhancing the HER.

4.2 Oxygen evolution reaction (OER)

Fig. 6(a) shows the LSV polarization curves used to assess the OER activity of the prepared electrocatalysts in 1.0 M KOH, applied potential range from 0 to 1.5 V and sweep rate of 10 mV s−1. An anodic peak near 1.45 V is observed. This peak is mainly attributed to the change in the electronic state of the involved metals via oxidation. It is an acceptable practice to compare and use a higher overpotential point to compensate for the offset effect of the oxidation peaks. Since the oxidation reaction has occurred and the state of the metal is changed, this changed electronic configuration will now take part in the OER.56–62 The overpotential is measured and compared at 100 mA cm−2. WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) requires an overpotential of around about 550 mV to attain 100 mA cm−2 current density, which is less than bulk WS2 (650 mV), exfoliated WS2 (610 mV), WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1) (570 mV), and WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3) (570 mV). Fig. 6(b) shows a Tafel diagram of the OER reaction kinetics. In comparison to bulk WS2 (198 mV dec−1), exfoliated WS2 (206 mV dec−1), WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1) (191 mV dec−1), WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3) (186 mV dec−1) and WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) (136 mV dec−1), WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) exhibits the smallest Tafel slope at 136 mV dec−1. The OER and HER results are summarized in Table 1.
image file: d3ya00348e-f6.tif
Fig. 6 (a) LSV OER curves of bulk WS2, exfoliated WS2, WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1, 1[thin space (1/6-em)]:[thin space (1/6-em)]2, 1[thin space (1/6-em)]:[thin space (1/6-em)]3) at a scan rate of 10 mV s−1 in 1.0 M KOH. (b) Corresponding Tafel plots of bulk WS2, exfoliated WS2 and WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1, 1[thin space (1/6-em)]:[thin space (1/6-em)]2, 1[thin space (1/6-em)]:[thin space (1/6-em)]3).
Table 1 Summary of the HER and OER
Electrocatalysts Overpotential HER (mV at 10 mA cm−2) Tafel slope HER (mV dec−1) Overpotential OER (mV at 100 cm2) Tafel slope HER (mV dec−1)
Bulk WS2 149 163 650 198
Exfoliated WS2 153 283 610 206
WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1) 123 115 570 191
WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) 121 83 550 136
WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3) 136 113 570 186


WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) offers the highest production for the HER and OER electrocatalytic water-splitting, and is comparable to several highly effective catalysts that were previously reported (Table 2). The higher surface area and the efficient electron transport networks with the appearance of conducting passageways supplied by the MOF network are responsible for the enhanced performance. EIS is yet another parameter that is important for the understanding of the kinetic mode of the prepared catalyst. The frequency range used for EIS was 200 kHz–0.1 Hz. Fig. 7(a) demonstrates a Nyquist plot with actual impedance on the x-axis and fictitious impedance on the y-axis. The Nyquist plot, which has a simple Randles circuit, gives information on the charge transfer resistance (Rct), solution resistance (Rs), and faradaic capacitance at the electrode/electrolyte interface (Cf). Table 2 shows the comparative values. In general, small charge transfer resistance (Rct) values are associated with rapid charge transfer kinetics.2,63

Table 2 Comparative values of Rct, Rs, and ECSA
Electrocatalyst R ct (Ohms) R s (Ohms) ECSA (cm2)
Bulk WS2 220 3.05 356
Exfoliated WS2 160 2.8 507.5
WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1) 5.4 2 1106
WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) 2.65 2.45 1262.5
WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]3) 9.895 2.75 957.5



image file: d3ya00348e-f7.tif
Fig. 7 (a) EIS Nyquist plots of all the prepared hybrids with fitted curves. (b) CV of WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) at different scan rates. (c) CV of all the prepared hybrids at a scan rate of 50 mV s−1. (d) Stability test at a fixed current density of 10 mA cm−2.

In comparison, WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) exhibits an interface between the catalyst and electrolyte with the lowest charge transfer resistance. Rapid kinetics is proposed by the tiny Rct of WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2), which corresponds with the Tafel slope attributes and LSV results. Electrochemical active surface area (ECSA) is an excellent method for determining the catalyst activity. Electrocatalysts with higher ECSAs require lower reaction overpotentials. ECSA is calculated by determining the double-layer capacitance (Cdl) using eqn (4) and (5).64

 
ECSA = Cdl/Cf(4)
 
image file: d3ya00348e-t3.tif(5)
Cdl = double-layer capacitance, Cf = specific capacitance of an ideal flat surface catalyst known as individual capacitance (average value of 40 F cm−2), Y0 = magnitude of capacity (dimensionless measure indicating the extent to which a catalyst diverges from a genuine capacitor), Rp = polarization resistance.

To check the cyclic stability of the prepared hybrid, cyclic voltammetry of WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) was done at various scan rates. Fig. 7(b) demonstrates a steady increase in the exchange current density when the voltage is increased, indicating the cyclic stability, strong electrocatalyst efficiency, low resistance of the prepared catalysts, and a considerable drop in the charge transfer resistance as the potential is increased. CV measurements of the bulk WS2, exfoliated WS2, and WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]1, 1[thin space (1/6-em)]:[thin space (1/6-em)]2, 1[thin space (1/6-em)]:[thin space (1/6-em)]3) were carried out at 100 mV s−1 scan rate in 1.0 M KOH electrolyte solution to identify the relationship between the current density and voltage over a range (Fig. 7(c)). The CV graphs provide information on the redox reaction thermodynamics and the electron-transfer reaction kinetic model. The CV curves reveal two well-defined redox peaks. In comparison, WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) has a larger current density, implying lower diffusion layer resistance and cyclic stability. The charge that travels through the cell is equivalent to the current density. Furthermore, the catalyst's durability is crucial for commercializing hydrogen production as a fuel concept. Fig. 7(d) shows the stability of WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) after 24 hours of testing. The potential response remained consistent after the WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) catalyst was activated, with no significant reduction in activity. A bifunctional electrocatalytic cell was constructed to evaluate the hybrid WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) ability to split water. In this two-electrode assembly, WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) on the Ni-foam acted as both cathode and anode in 1.0 M KOH. Bare Ni-foam was also investigated under similar process conditions (results are shown in Fig. 8). To achieve a current density of 10 mA cm−2, an electrolyzer cell voltage of 1.41 Volts was required, which is significantly lower than the standard Pt/C||IrO2 with an electrolysis potential of 1.60 V65 and several other reported bifunctional water-splitting electrocatalysts mentioned in Table 3.


image file: d3ya00348e-f8.tif
Fig. 8 The bifunctional overall cell performance of WS2/UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) and bare-Ni foam electrocatalysts.
Table 3 Comparisons of the HER and OER electrocatalyst activity with previously reported catalysts
Electrocatalysts Current density (mA cm−2) Overpotential HER (mV) Overpotential OER (mV) Stability (hours) Ref.
WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) 10 121 220 24 This work
MoS2/UiO-66 10 129.4 180 24 7
CoOx/UiO-66-300 10 283 10 66
WS2@Co3S4 NW/CC 10 82 280 24 1
Ag/WS2 10 180 24 67
WS2–Co 10 210 24 68
Ni/WS 8.6 250 24 69
W1−xS2–Mox@CFP 10 178 18 70
WS2@Co(1−x), S, N 10 220 365 71


The improved performance of the WS2 and UiO-66 hybrids as electrocatalysts for water splitting, compared to pristine WS2, can be attributed to several key factors. Hybrid catalysts, consisting of a combination of different metal components (Tungsten in WS2 and Zirconium in UiO-66), have demonstrated superior performance compared to single metal catalysts. The diverse metal sites in the hybrid catalyst can facilitate multiple reaction pathways, leading to improved catalytic activity. Synergistic interactions between WS2 and UiO-66 lead to improved charge transfer kinetics, reducing overpotentials for these reactions. Additionally, the hybrid's unique structural features, such as increased surface area and enhanced electron mobility, further enhance its electrocatalytic properties. These hybrids can significantly enhance the catalytic activity of WS2 by providing additional active sites for HER and OER.

Certain parameters need to be addressed that limit large-scale applications. High catalyst loading is often required to achieve efficient water splitting, which can be challenging on a large scale. Ensuring efficient mass transport of reactants (water, protons, etc.) to the catalytic sites and removal of products (hydrogen and oxygen) can be challenging, especially at large scales. The reproducible synthesis of high-quality electrocatalysts can be complex. Scaling up the production of such catalysts while maintaining their quality can be a challenge. The kinetics of the HER may not be as fast as desired on a larger scale, leading to lower reaction rates.

5. Conclusions

This work demonstrates the one-pot solvothermal method used to produce the 2D bifunctional tungsten disulfide embedded with UiO-66 (WS2@UiO-66) hybrids, and how their structure affects its properties and performance of water splitting. The results also showed that using different reactants and reaction conditions for hybrid production results in varied interactions between WS2 and UiO-66. As a result, the catalysts' morphological geometry and electrocatalytic characteristics are affected. WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) demonstrated exceptional electrocatalytic activity, achieving a current density of 10 mA cm−2 with a HER overpotential of 121 mV and OER overpotential of 220 mV. The WS2@UiO-66(1[thin space (1/6-em)]:[thin space (1/6-em)]2) maintains its stability after 24 hours, so this electrocatalyst is very suitable for commercialization. The increased surface area, metal synergistic effects, excellent electron transport route adjustment, and the MOF network's presence of conductive pathways all contribute to the enhanced performance. These discoveries lay the foundation for the design and production of bifunctional hybrid electrocatalysts in water-splitting devices. To develop a better understanding of the catalyst, a deeper understanding of the molecular level of process kinetics, the electron transfer mechanism, and the structural information of electrocatalysts is required.

Conflicts of interest

The authors declare no deliberate competing interests regarding research, financial benefit, authorship, and/or publication that could have influenced this paper.

Acknowledgements

The Higher Education Commission of Pakistan funded this work under the grant allocated as 2017/HEC/NRPU-10482.

References

  1. T. Zhang, et al., Bifunctional WS2@Co3S4 core-shell nanowire arrays for efficient water splitting, Electrochim. Acta, 2022, 404, 139648 CrossRef CAS .
  2. U. Abdullah, M. Ali and E. Pervaiz, An inclusive review on recent advancements of cadmium sulfide nanostructures and its hybrids for photocatalytic and electrocatalytic applications, Mol. Catal., 2021, 508, 111575 CrossRef CAS .
  3. R. Kumar, et al., Strong interactions between the nanointerfaces of silica-supported Mo2C/MoP heterojunction promote hydrogen evolution reaction, ACS Appl. Mater. Interfaces, 2020, 12(52), 57898–57906 CrossRef CAS .
  4. Z. Pu, et al., Single-atom catalysts for electrochemical hydrogen evolution reaction: recent advances and future perspectives, Nano-Micro Lett., 2020, 12(1), 1–29 Search PubMed .
  5. U. Abdullah, M. Ali and E. Pervaiz, Cadmium sulfide embedded Prussian Blue as highly active bifunctional electrocatalyst for water-splitting process, Int. J. Hydrogen Energy, 2022, 47(49), 21160–21172 CrossRef CAS .
  6. H. Hosseini and M. Roushani, Rational design of hollow core-double shells hybrid nanoboxes and nanopipes composed of hierarchical Cu-Ni-Co selenides anchored on nitrogen-doped carbon skeletons as efficient and stable bifunctional electrocatalysts for overall water splitting, Chem. Eng. J., 2020, 402, 126174 CrossRef CAS .
  7. M. Ali and E. Pervaiz, Effect of synthesis route on electrocatalytic water-splitting activity of MoS2/UiO-66 hybrid, Mol. Catal., 2022, 519, 112136 CrossRef CAS .
  8. P. Chen, et al., Recent progress of transition metal carbides/nitrides for electrocatalytic water splitting, J. Alloys Compd., 2021, 883, 160833 CrossRef CAS .
  9. S. Tang, et al., Recent advances in transition metal nitrides for hydrogen electrocatalysis in alkaline media: From catalyst design to application, Front. Chem., 2022, 10, 1073175 CrossRef CAS PubMed .
  10. T. Wang, et al., Precious metal-free approach to hydrogen electrocatalysis for energy conversion: From mechanism understanding to catalyst design, Nano Energy, 2017, 42, 69–89 CrossRef CAS .
  11. J. Yang, et al., From hexagonal to monoclinic: engineering crystalline phase to boost the intrinsic catalytic activity of tungsten oxides for the hydrogen evolution reaction, ACS Sustainable Chem. Eng, 2021, 9(16), 5642–5650 CrossRef CAS .
  12. J. Hei, et al., NiFeP nanosheets on N-doped carbon sponge as a hierarchically structured bifunctional electrocatalyst for efficient overall water splitting, Appl. Surf. Sci., 2021, 549, 149297 CrossRef CAS .
  13. T. S. ZelekeA, et al., Immobilized single molecular molybdenum disulfide on carbonized polyacrylonitrile for hydrogen evolution reaction, ACS Nano, 2019, 13(6), 6720–6729 CrossRef .
  14. U. Abdullah, et al., An inclusive perspective on the recent development of tungsten-based catalysts for overall water-splitting: A review, Int. J. Energy Res., 2022 Search PubMed .
  15. X. Chen, et al., Design principles for tungsten oxide electrocatalysts for water splitting, ChemElectroChem, 2021, 8(23), 4427–4440 CrossRef CAS .
  16. Z. Feng, et al., Controllable synthesis of flower-like Mn-Co-P nanosheets as bifunctional electrocatalysts for overall water splitting, Colloids Surf., A, 2021, 615, 126265 CrossRef CAS .
  17. D. R. Paudel, et al., Fe and P doped 1T-phase enriched WS23D-dendritic nanostructures for efficient overall water splitting, Appl. Catal., B, 2021, 286, 119897 CrossRef CAS .
  18. T. Kou, S. Wang and Y. Li, Perspective on high-rate alkaline water splitting, ACS Mater. Lett., 2021, 3(2), 224–234 CrossRef CAS .
  19. B. Zhou, et al., Engineering P-doped Ni3S2-NiS hybrid nanorod arrays for efficient overall water electrolysis, J. Alloys Compd., 2021, 862, 158391 CrossRef CAS .
  20. R. Khan, et al., 3D hierarchical heterostructured LSTN@ NiMn-layered double hydroxide as a bifunctional water splitting electrocatalyst for hydrogen production, Fuel, 2021, 285, 119174 CrossRef CAS .
  21. H. Zhang, et al., Bifunctional heterostructured transition metal phosphides for efficient electrochemical water splitting, Adv. Funct. Mater., 2020, 30(34), 2003261 CrossRef CAS .
  22. R. Zhang, et al., Dual synergistic effect of S-doped carbon bridged semi crystalline MILN-based Co3S4/MnS2 nanostructure in electrocatalytic overall water splitting, Electrochim. Acta, 2021, 366, 137438 CrossRef CAS .
  23. Y. Li, et al., Heterostructured MoO2@MoS2@Co9S8 nanorods as high efficiency bifunctional electrocatalyst for overall water splitting, Appl. Surf. Sci., 2021, 543, 148804 CrossRef CAS .
  24. Y. Liu, et al., Hierarchically heterostructured metal hydr (oxy) oxides for efficient overall water splitting, Nanoscale, 2019, 11(24), 11736–11743 RSC .
  25. D. Vikraman, et al., Improved Hydrogen Evolution Reaction Performance using MoS2–WS2 Heterostructures by Physicochemical Process, ACS Sustainable Chem. Eng., 2018, 6(7), 8400–8409 CrossRef CAS .
  26. W. Yin, et al., Low-temperature one-pot synthesis of WS2 nanoflakes as electrocatalyst for hydrogen evolution reaction, Nanotechnology, 2018, 30(4), 045603 CrossRef .
  27. C. Sun, et al., N-doped WS 2 nanosheets: a high-performance electrocatalyst for the hydrogen evolution reaction, J. Mater. Chem. A, 2016, 4(29), 11234–11238 RSC .
  28. F. M. Pesci, et al., MoS2/WS2 heterojunction for photoelectrochemical water oxidation, ACS Catal., 2017, 7(8), 4990–4998 CrossRef CAS .
  29. D. Voiry, et al., Enhanced catalytic activity in strained chemically exfoliated WS2 nanosheets for hydrogen evolution, Nat. Mater., 2013, 12(9), 850–855 CrossRef CAS PubMed .
  30. T. Van Nguyen, et al., Electrocatalysts based on MoS2 and WS2 for hydrogen evolution reaction: An overview, Battery Energy, 2023, 20220057 CrossRef CAS .
  31. Z. Thiehmed, A. Shakoor and T. Altahtamouni, Recent advances in WS2 and its based heterostructures for water-splitting applications, Catalysts, 2021, 11(11), 1283 CrossRef CAS .
  32. Z. Wu, et al., WS2 nanosheets as a highly efficient electrocatalyst for hydrogen evolution reaction, Appl. Catal., B, 2012, 125, 59–66 CrossRef CAS .
  33. D. Voiry, et al., Enhanced catalytic activity in strained chemically exfoliated WS 2 nanosheets for hydrogen evolution, Nat. Mater., 2013, 12(9), 850–855 CrossRef CAS PubMed .
  34. Y. Feng, et al., Tailoring the properties of UiO-66 through defect engineering: A review, Ind. Eng. Chem. Res., 2019, 58(38), 17646–17659 CrossRef CAS .
  35. M. Ali, et al., A review on the recent developments in zirconium and carbon-based catalysts for photoelectrochemical water-splitting, Int. J. Hydrogen Energy, 2021, 46(35), 18257–18283 CrossRef CAS .
  36. H. Zhu, et al., When cubic cobalt sulfide meets layered molybdenum disulfide: a core–shell system toward synergetic electrocatalytic water splitting, Adv. Mater., 2015, 27(32), 4752–4759 CrossRef CAS PubMed .
  37. J. Zhang, et al., Interface engineering of MoS2/Ni3S2 heterostructures for highly enhanced electrochemical overall-water-splitting activity, Angew. Chem., Int. Ed. Engl., 2016, 128(23), 6814–6819 CrossRef .
  38. Z. Liu, et al., Colloidal synthesis of 1T′ phase dominated WS2 towards endurable electrocatalysis, Nano Energy, 2018, 50, 176–181 CrossRef CAS .
  39. S. Liu, et al., Ultrathin WS2 nanosheets vertically aligned on TiO2 nanobelts as efficient alkaline hydrogen evolution electrocatalyst, Int. J. Hydrogen Energy, 2020, 45(3), 1697–1705 CrossRef CAS .
  40. M. Tayebi, Z. Masoumi and B.-K. Lee, Ultrasonically prepared photocatalyst of W/WO3 nanoplates with WS2 nanosheets as 2D material for improving photoelectrochemical water splitting, Ultrason. Sonochem., 2021, 70, 105339 CrossRef CAS PubMed .
  41. M. Velpandian, et al., Improved charge carrier dynamics of WS 2 nanostructures by the way of CdS@WS2 heterostructures for use in water splitting and water purification, Sustainable Energy Fuels, 2020, 4(8), 4096–4107 RSC .
  42. S. Peng, et al., Engineering Co 9 S 8/WS 2 array films as bifunctional electrocatalysts for efficient water splitting, J. Mater. Chem. A, 2017, 5(44), 23361–23368 RSC .
  43. A. Roy, P. Kalita and B. Mondal, Structural, spectroscopic and electrical properties of liquid phase exfoliated few layered two-dimensional tungsten disulfide (WS2) using anionic surfactant, J. Mater. Sci.: Mater. Electron., 2023, 34(3), 224 CrossRef CAS .
  44. D. Ovchinnikov, et al., Electrical transport properties of single-layer WS2, ACS Nano, 2014, 8(8), 8174–8181 CrossRef CAS .
  45. H.-L. Tsai, et al., Exfoliated – restacked phase of WS2, Chem. Mater., 1997, 9(4), 879–882 CrossRef CAS .
  46. M. N. Uddin, et al., Improving water-splitting efficiency of water electrolysis process via highly conductive nanomaterials at lower voltages, Energy, Ecol. Environ., 2020, 5, 108–117 CrossRef .
  47. G. Yang, et al., Role of electron pathway in dimensionally increasing water splitting reaction sites in liquid electrolytes, Electrochim. Acta, 2020, 362, 137113 CrossRef CAS .
  48. X. Zhang, et al., Preparation and tribological properties of WS2 hexagonal nanoplates and nanoflowers, Nanomaterials, 2019, 9(6), 840 CrossRef CAS PubMed .
  49. Z. Liu, et al., Colloidal synthesis of 1T′phase dominated WS2 towards endurable electrocatalysis, Nano Energy, 2018, 50, 176–181 CrossRef CAS .
  50. X.-F. Zhang, et al., Adsorptive desulfurization from the model fuels by functionalized UiO-66 (Zr), Fuel, 2018, 234, 256–262 CrossRef CAS .
  51. A. R. Bushroa, et al., Approximation of crystallite size and microstrain via XRD line broadening analysis in TiSiN thin films, Vaccum, 2012, 86(8), 1107–1112 CrossRef CAS .
  52. A. Schaate, et al., Modulated synthesis of Zr-based metal–organic frameworks: from nano to single crystals, Chem. - Eur. J., 2011, 17(24), 6643–6651 CrossRef CAS PubMed .
  53. H. Chen, et al., Silver nanoparticles on UiO-66 (Zr) metal-organic frameworks for water disinfection application, Food Sci. Hum. Wellness, 2022, 11(2), 269–276 CrossRef CAS .
  54. S. Swathi, et al., Surfactant-assisted tungsten sulfide mesoporous sphere for hydrogen production, Int. J. Hydrogen Energy, 2021, 47(100), 41984–41993 CrossRef .
  55. M. A. Ehsan, A. S. Hakeem and A. Rehman, Synergistic effects in bimetallic Pd–CoO electrocatalytic thin films for oxygen evolution reaction, Sci. Rep., 2020, 10(1), 1–11 CrossRef PubMed .
  56. M. S. Amer, et al., Bifunctional electrocatalyst of low-symmetry mesoporous titanium dioxide modified with cobalt oxide for oxygen evolution and reduction reactions, Catalysts, 2019, 9(10), 836 CrossRef CAS .
  57. L. Yu, et al., Hierarchical Cu@ CoFe layered double hydroxide core-shell nanoarchitectures as bifunctional electrocatalysts for efficient overall water splitting, Nano Energy, 2017, 41, 327–336 CrossRef CAS .
  58. D. Zhao, et al., Bifunctional ZnCo2S4@ CoZn13 hybrid electrocatalysts for high efficient overall water splitting, J. Energy Chem., 2022, 69, 292–300 CrossRef CAS .
  59. W. Zhang, et al., Multi-active site CoNi-MOFs as non-noble bifunctional electrocatalysts for highly efficient overall water splitting, Int. J. Hydrogen Energy, 2022, 47(3), 1633–1643 CrossRef CAS .
  60. L. Zhi, et al., 3D holey hierarchical nanoflowers assembled by cobalt phosphide embedded N-doped carbon nanosheets as bifunctional electrocatalyst for highly efficient overall water splitting, J. Colloid Interface Sci., 2022, 616, 379–388 CrossRef CAS PubMed .
  61. L. Zhi, et al., 3D holey hierarchical nanoflowers assembled by cobalt phosphide embedded N-doped carbon nanosheets as bifunctional electrocatalyst for highly efficient overall water splitting, J. Colloid Interface Sci., 2022, 616, 379–388 CrossRef CAS PubMed .
  62. Z. Xu, et al., Co (OH) 2 Nanoflowers Decorated α-NiMoO4 Nanowires as a Bifunctional Electrocatalyst for Efficient Overall Water Splitting, Catalysts, 2022, 12(11), 1417 CrossRef CAS .
  63. X. Hu, et al., Nickel foam and stainless steel mesh as electrocatalysts for hydrogen evolution reaction, oxygen evolution reaction and overall water splitting in alkaline media, RSC Adv., 2019, 9(54), 31563–31571 RSC .
  64. P. Connor, et al., The determination of electrochemical active surface area and specific capacity revisited for the system MnOx as an oxygen evolution catalyst, Z. Phys. Chem., 2020, 234(5), 979–994 CrossRef CAS .
  65. G. Zhang, et al., Phosphorus and yttrium codoped Co (OH) F nanoarray as highly efficient and bifunctional electrocatalysts for overall water splitting, Small, 2019, 15(42), 1904105 CrossRef CAS .
  66. V. Charles, et al., CoOx/UiO-66 and NiO/UiO-66 heterostructures with UiO-66 frameworks for enhanced oxygen evolution reactions, New J. Chem., 2021, 45(32), 14822–14830 RSC .
  67. P. M. Pataniya and C. Sumesh, Enhanced electrocatalytic hydrogen evolution reaction by injection of photogenerated electrons in Ag/WS2 nanohybrids, Appl. Surf. Sci., 2021, 563, 150323 CrossRef CAS .
  68. X. Shi, et al., Rapid flame doping of Co to WS 2 for efficient hydrogen evolution, Energy Environ. Sci., 2018, 11(8), 2270–2277 RSC .
  69. L. Yang, et al., Amorphous nickel/cobalt tungsten sulfide electrocatalysts for high-efficiency hydrogen evolution reaction, Appl. Surf. Sci., 2015, 341, 149–156 CrossRef CAS .
  70. Q. Yang, et al., Composite electrocatalyst MoxW1-xS2 nanosheets on carbon fiber paper for highly efficient hydrogen evolution reaction, J. Solid State Electrochem., 2018, 22(10), 2969–2976 CrossRef CAS .
  71. Z. Huang, et al., Polyoxometallates@zeolitic-imidazolate-framework derived bimetallic tungsten-cobalt sulfide/porous carbon nanocomposites as efficient bifunctional electrocatalysts for hydrogen and oxygen evolution, Electrochim. Acta, 2020, 330, 135335 CrossRef CAS .

This journal is © The Royal Society of Chemistry 2024