One-pot synthesis of LiAlO2-coated LiNi0.6Mn0.2Co0.2O2 cathode material

Abstract

For the first time, a one-pot synthesis of LiAlO2-coated LiNi0.6Mn0.2Co0.2O2 particles, using a continuous stirred-tank reactor, is reported. Two methods of surface coating were compared with the pristine sample. The composition and morphology of the coated and uncoated cathode materials were characterised by MP-AES, XPS, SEM, and EDX. 27Al MAS NMR coupled with structural characterisation of the materials confirms the presence of a coating layer of LiAlO2 on the surface of the NMC particle with partial diffusion of Al3+ from the surface coating to the NMC structure. By comparing electrochemical performances and thermal stabilities of the coated and uncoated NMC particles at high temperature (45 °C) and at high cut-off voltage (3.0–4.4 V vs. Li+/Li), the coated samples indicate a significant improvement in cycling performance (specific capacity, capacity retention, and rate capability). EIS confirms that the LiAlO2 coating layer prevents side reactions resulting in reduced cathode electrolyte interphase formation and charge-transfer resistance.

Graphical abstract: One-pot synthesis of LiAlO2-coated LiNi0.6Mn0.2Co0.2O2 cathode material

Article information

Article type
Paper
Submitted
04 фев 2023
Accepted
20 мар 2023
First published
20 мар 2023
This article is Open Access
Creative Commons BY-NC license

Energy Adv., 2023,2, 701-711

One-pot synthesis of LiAlO2-coated LiNi0.6Mn0.2Co0.2O2 cathode material

O. Touag, G. Coquil, M. Charbonneau, G. Foran, A. Ghosh, D. Mankovsky and M. Dollé, Energy Adv., 2023, 2, 701 DOI: 10.1039/D3YA00061C

This article is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported Licence. You can use material from this article in other publications, without requesting further permission from the RSC, provided that the correct acknowledgement is given and it is not used for commercial purposes.

To request permission to reproduce material from this article in a commercial publication, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party commercial publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements