High-performance green-emitting Ca2YScAl2Si2O12:Ce3+ garnet phosphors and their applications in high-quality blue-chip-pumped white LEDs

Abstract

Green phosphors have attracted much attention in recent years due to their great potential for achieving high-quality white light-emitting diode (LED) lighting. Herein, we report the discovery and characterization of a novel green-emitting Ca2YScAl2Si2O12:Ce3+ (abbreviated as CYSAS:Ce3+) garnet-type inorganic phosphor showing outstanding photoluminescence features. A family of CYSAS:Ce3+ samples are intentionally incorporated with different Ce3+ doping concentrations ranging from 1 mol% to 8 mol%, and they were successfully prepared by using the conventional high-temperature solid-state reaction method at 1400 °C calcination temperature and a reducing atmosphere. These CYSAS:Ce3+ phosphors crystallize into the garnet phase with the Ia[3 with combining macron]d space group, and their crystallographic data are obtained by using the Rietveld refinements. Photoluminescence characterization reveals that the CYSAS:Ce3+ phosphors exhibit broadband excitation spectra in the 250–500 nm spectral range with a peak at 452 nm, which matches well with commercial blue LED chips (440–480 nm). The concentration quenching effect is observed for CYSAS:Ce3+ phosphors, and the related mechanism has been discussed. In particular, under 452 nm excitation, the optimal CYSAS:4%Ce3+ sample produces a broad, asymmetric, green emission band in the 470–750 nm wavelength range with an emission peak at 538 nm and a bandwidth of 121 nm. The corresponding CIE chromaticity coordinates are (0.3662, 0.5446). Notably, luminescence quantum efficiency (QE) measurements demonstrate that the CYSAS:4%Ce3+ sample has an excellent internal QE of 91.1% and an external QE of 51.7%. In addition, temperature-dependent emission properties indicate its good thermal stability (66%@150 °C) and good color stability (chromaticity shift ΔE = 3.15 × 10−3) for the CYSAS:4%Ce3+ phosphor. By combining the CYSAS:4%Ce3+ green phosphor with the 450 nm blue chip and the (Ca,Sr)AlSiN3:Eu2+ commercial red phosphor, a white LED device with excellent light efficiency and high light color quality was fabricated. When the driving current is 20 mA, the LED device exhibits a high color rendering index (92.6), low correlated color temperature (4726 K), and high luminous efficacy (109.89 lm W−1). In summary, the above results show that the CYSAS:Ce3+ phosphor has great application potential in achieving high-quality white LEDs, and it also provides a new exploration idea for the development of new green-emitting phosphors.

Graphical abstract: High-performance green-emitting Ca2YScAl2Si2O12:Ce3+ garnet phosphors and their applications in high-quality blue-chip-pumped white LEDs

Article information

Article type
Paper
Submitted
17 mai 2024
Accepted
03 jul 2024
First published
04 jul 2024

J. Mater. Chem. C, 2024,12, 12378-12388

High-performance green-emitting Ca2YScAl2Si2O12:Ce3+ garnet phosphors and their applications in high-quality blue-chip-pumped white LEDs

C. Xian, X. Chen and X. Huang, J. Mater. Chem. C, 2024, 12, 12378 DOI: 10.1039/D4TC02039A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements